• Progress in Superconductivity
• /
• 제11권2호
• /
• pp.87-91
• /
• 2010

We fabricated the polyacrylic acid (PAA)-doped $MgB_2$ bulks and characterized their lattice parameters, actual C substitutions, microstructures, and critical properties. The boron (B) powder was mixed with PAA using N,N-dimethylformamide as solvent and then the solution was dried out at $200^{\circ}C$ and crushed. The C treated B powder and magnesium powder were mixed and compacted by uniaxial pressing at 500 MPa, followed by sintering at $900^{\circ}C$ for 1 h in high purity Ar atmosphere. We observed that the PAA doping increased the MgO amount but decreased the grain size, a-axis lattice constant, and critical temperature ($T_c$), which is indicative of the C substitution for B sites in $MgB_2$. In addition, the critical current density ($J_c$) at high magnetic field was significantly improved with increasing PAA addition: at 5 K and 6.6 T, the $J_c$ of 7 wt% PAA-doped sample was $6.39\;{\times}\;10^3\;A/cm^2$ which was approximately 6-fold higher than that of the pure sample ($1.04\;{\times}\;10^3\;A/cm^2$). This improvement was probably due to the C substitution and the refinement of grain size by PAA doping, suggesting that PAA is an effective dopant in improving $J_c$(B) performance of $MgB_2$.

• 한국재료학회지
• /
• 제16권8호
• /
• pp.497-502
• /
• 2006

Recently, many attention have been focused on illite as a material for the well-being industry. Illite contains various kinds of iron bearing materials and they restrict their usage. In this study, Fe impurities in the illite produced in Yeongdong-gun, Chungcheongbuk-do were characterized and their removal experiments were performed. According to the characterization of illite raw ore, it contained 1.54 wt.%$Fe_2O_3$ due to the existence of iron oxide($Fe_2O_3$) and pyrite($FeS_2$). The raw ore was crushed into 3 mm or less using cone crusher and then ground by rod mill for the liberation of impurity mineral. For the removal of iron bearing minerals, an acid treatment, a flotation, a magnetic separation, and a flotation combined with magnetic separator were performed respectively. When the illite raw ore was treated with magnetic separation and various kinds of acid, 1.54wt.%. $Fe_2O_3$ content was reduced to 0.78 and 1.0 wt.%, respectively. On the other hand $Fe_2O_3$ content was reduced to be 0.52 wt.% after flotation. These results indicate that iron bearing minerals cannot be reduced below 0.3wt.%$Fe_2O_3$. However, combination of magnetic separation and flotation enable us to get 0.24wt.% of illite concentrate. It is concluded that, for the refinement of illite from Yeongdong-gun, the flotation combined with magnetic separation is good for high purity illite.