• Macromolecular Research
• /
• 제17권4호
• /
• pp.271-275
• /
• 2009

This paper describes the out-of-plane order of a liquid crystalline(LC) methacrylate copolymer(3) comprised of a methacrylate(1) with a 4-styrylpyridine moiety as the photo-cyclodimerizable group and a benzoate moiety as the mesogenic group in the side chain, and another methacrylate(2) with a 4-(4-methoxyphenyl)benzoate moiety as the mesogenic group. The composition of 1 and 2 units in 3 was estimated to have a molar ratio of 54.2:45.8 by $^{1}H$ NMR spectroscopy. The X-ray diffraction study revealed that the copolymer forms a partial bilayer smectic structure. The copolymer gave rise to a high out-of-plane order parameter of about 0.74 in a wide LC temperature range of $110{\sim}160^{\circ}C$ after linearly polarized, UV light irradiation and subsequent annealing. Moreover, the external reflection IR analysis indicated that excess UV-light irradiation makes the out-of-plane LC structure of the copolymer appear in a higher and wider temperature range.

• Journal of Electrochemical Science and Technology
• /
• 제8권3호
• /
• pp.257-264
• /
• 2017

A polymeric ionic liquid, poly(1-methyl 3-(2-acryloyloxypropyl) imidazolium iodide) (PMAPII), was synthesized as a single-iodide-ion-conducting polymer and employed in a gel polymer electrolyte. Gel polymer electrolytes prepared from iodine, 4-tert-butylpyridine, ${\gamma}$-butyrolactone, and PMAPII were applied in quasi-solid-state dye-sensitized solar cells (DSSCs). The addition of 16 wt.% PMAPII provided the most favorable environment, striking a compromise between the iodide ion concentration and the ionic mobility, which resulted in the highest conversion efficiency of the resulting DSSCs. The quasi-solid-state DSSC assembled with the optimized gel polymer electrolyte exhibited a relatively high conversion efficiency of 7.67% under AM 1.5 illumination at $100mA\;cm^{-2}$ and better stability than that of the DSSC with a liquid electrolyte.

• 콘크리트학회논문집
• /
• 제14권3호
• /
• pp.315-320
• /
• 2002

본 연구에서는 고로슬래그 미분말을 이용한 SBR혼입 폴리머 시멘트 콘크리트의 강도 성상에 미치는 고로슬래그 치환율 및 폴리머 결합재비의 영향에 대하여 구명하였다. 그 결과, 고로슬래그 미분말을 이용한 SBR혼입 폴리머 시멘트 콘크리트의 압축, 인장 및 휨강도는 폴리머-결합재비 및 고로슬래그 치환율의 증가에 따라 증가하였으며, 고로슬래그 치환율 40%에서 가장 높은 강도를 나타내었다. 특히 고로슬래그 치환율 40%의 SBR혼입 폴리머 시멘트 콘크리트의 인장 및 휨강도는 폴리머 미혼입의 강도보다 약 2배 이상의 높은 강도를 보였다. 이와 같이 높은 강도의 발현은 SBR 폴리머의 높은 인장강도와 SBR라텍스의 혼입에 의한 시멘트 수화물과 골재간의 접착성이 개선되었기 때문이라 판단된다.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2008년도 춘계 학술발표회 제20권1호
• /
• pp.945-948
• /
• 2008

본 연구는 초속경 아크릴 개질 폴리머 시멘트 콘크리트의 강도 특성에 미치는 폴리머-시멘트비의 영향을 검토한 것이다. 그 결과, 초속경 아크릴 개질 폴리머 시멘트 콘크리트의 윔 및 인장강도는 폴리머-시멘트비의 증가에 따라 증가하였다. 특히 폴리머-시멘트비 20%의 휨 및 인장강도는 폴리머를 혼입하지 않은 콘크리트보다 1.5배 이상의 강도발현을 나타냈다. 이와 같은 강도발현은 아크릴 에멀젼을 혼입함으로써 시멘트 수화물과 골재사이의 부착력이 증가되기 때문이라 판단된다.

• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2009년도 9th International Meeting on Information Display
• /
• pp.767-770
• /
• 2009

We synthesized a spirobenzofluorene type phosphine oxide (SPPO2) as a new triplet host and an universal electron transport material for phosphorescent organic light-emitting diodes(PHOLEDs). Red PHOLEDs with the SPPO2 host material showed a high quantum efficiency of 14.3 % with a current efficiency of 20.4 cd/A. In addition, the SPPO2 could be applied as an electron transport material which can be matched with any host material due to the lowest unoccupied molecular orbital of 2.4 eV. Electron injection from a cathode to the SPPO2 electron transport layer was better than common electron transport materials. In particular, the SPPO2 was effective as the electron transport material in blue PHOLEDs and the quantum efficiency was more than doubled and driving voltage was lowered by more than 3 V using the SPPO2 instead of common electron transport material.

• 한국재료학회지
• /
• 제29권10호
• /
• pp.639-646
• /
• 2019

Ink-jet printing is a manufacturing process technology that directly prints a digitalized design pattern onto a substrate using a fine ink jetting system. In this study, environmentally friendly yellow aqueous ceramic ink is synthesized by mixture of distilled water, yellow ceramic pigment and additives for ink-jet printing. The graft polymer, which combines electrostatic repulsion and steric hindrance mechanism, is used as a surfactant for dispersion stability of aqueous ceramic ink. Synthesized ceramic ink with graft polymer surfactant shows better dispersion stability than did ceramic ink with PAA surfactant; synthesized ink also shows desirable ink-jet printability with the formation of a single ink droplet during printability test. Finally, ceramic ink printed on glass substrate and ceramic ink with graft polymer surfactant shows a high contact angle without surface treatment on glass substrate. Consequently, it is confirmed that the ceramic ink with graft polymer surfactant can achieve high printing resolution without additional surface treatment process.

• 폴리머
• /
• 제38권3호
• /
• pp.320-326
• /
• 2014

본 연구에서는 polycarbonate(PC)/acrylonitrile-butadiene-styrene(ABS) 블렌드의 고속 전단 가공 조건하에서의 열적 물성 변화에 대해 연구하였다. 고전단 압출 성형기(NHSS2-28)를 이용하여 공정조건인 스크류 회전속도와 전단 부하 시간을 변화시키면서 가공하였다. 고전단 부하 실험 후에 유리전이온도($T_g$) 변화를 조사하여, 전단 부하 조건에 따라 약 $143^{\circ}C$에서 약 $133^{\circ}C$로 감소하는 경향을 관찰하였다. 열 중량 분석(TGA)을 통해 열분해 현상을 관찰하여 전단을 가하지 않은 경우 ABS와 PC의 분해곡선이 뚜렷한 두 단계로 나타났으나, 고속 전단 가공을 한 경우 분해하는 경향이 일직선상으로 변화되어 나타났다. 이에 대한 물성변화의 원인을 조사하기 위해 주사전자현미경(SEM)으로 관찰하여 분산상의 크기 또한 감소함을 확인하였고, 만능 재료 시험기(UTM)를 이용하여 신율이 고속 전단 가공을 한 경우, 소폭 감소하다가 특정 조건 이상에서는 급격한 감소를 보임을 관찰하였다. 결론적으로 적정한 고속 전단 응력 조건 이하에서는 PC/ABS 블렌드의 유리전이온도가 수렴하고, 적정 조건 이상에서는 유리전이온도가 급감하므로 전단응력에 의해 열화되는 것을 확인하였다.

• 한국산학기술학회논문지
• /
• 제21권12호
• /
• pp.10-15
• /
• 2020

파장 400 nm 이하의 자외선은 눈 건강에 매우 해롭다. 또한 고에너지 가시광도 망막 세포에 영향을 줄 수 있음이 최근에 밝혀졌다. 따라서 자외선 및 고에너지 가시광 차단 기능의 안경렌즈 개발이 시대적으로 요청되고 있다. 본 연구에서는 m-자일릴렌 디이소시아네이트 모노머와 2,3-bis((2-mercaptoethyl)thio)-1-propanethiol 모노머 및 벤트리아졸 UV 흡수제, 알킬인산에스터 이형제, 안료혼합물(CI solvent violet 13), 이염화부틸주석 촉매제 등의 혼합물을 인젝션 몰드 방법으로 열중합 공정을 적용하여, 굴절률 1.67의 고굴절률 폴리머 안경렌즈를 제조하였다. 제조된 폴리머 안경렌즈의 양면에 전자빔 진공증착 시스템으로 다층 반사방지 코팅을 하였다. 제조된 안경렌즈의 자외선 및 고에너지 가시광 차단 기능을 UV-visible spectrophotometer로 분석하였다. 그 결과 UV 흡수제를 0.5wt% 첨가한 폴리머 안경렌즈가 411 nm 파장 이하의 자외선 및 고에너지 가시광을 99 % 이상 차단하였다. 또한 460 ~ 660 nm 파장의 명소시 시각 민감도 10% 이상의 영역에서 평균 투과율이 97.9%를 나타내어 명소시에서 선명한 상을 얻을 수 있었다.

• 한국재료학회지
• /
• 제14권6호
• /
• pp.443-450
• /
• 2004

Parylene polymer thin film shows excellent homogeneous coverage chracteristics when it was deposited onto very complex three dimensional solid matters, such as deep hole and micro crack. The parylene deposition process can be conducted at room temperature although most of chemical vapor deposition processes request relatively high processing temperature. Therefore, the parylene coating process does not induce any thermal problems. Parylene thin film is transparent and has extremly high chemical stability. For example, it shows high chemical stability with high reactive chemical solutions such as strong acid, strong alkali and acetone. The bio-stability of this material gives good chances to use for a packaging of biomedical devices and electronic devices such as display. In this review article, principle of deposition process, properties and application fields of parylene polymer thin film are introduced.

• Macromolecular Research
• /
• 제11권2호
• /
• pp.104-109
• /
• 2003

A microcellular, which combines a rubber with the conventional formulation of styrene/divinylbenzene/sorbitan monooleate/water system, was prepared using high internal phase emulsion (HIPE) polymerization. Although the open microcellular foam with low density from the conventional HIPE polymerization shows highly porous characteristics with fine, regular and isotropic structure, the one having much smaller cell size is desirable for various applications. In this study, a polybutadiene was introduced to reduce the cell size with comparable properties. Major interests were focused on the effects of rubber concentration and agitation speed on the cell sizes and compression properties. Scanning electron microscopy was used to observe the microcellular morphology and compression tests were conducted to evaluate the stress-strain behaviors. It was found that the cell size decreased as rubber concentration increased, reflecting a competition between the higher viscosity of continuous phase and the lower viscosity ratio of dispersed to continuous phases due to the addition of high molecular weight rubber into the oil phase of emulsion. A correlation for the average cell size depending on agitation speed was attempted and the result was quite satisfactory.