• Journal of Korea Foundry Society
• /
• v.44 no.3
• /
• pp.59-69
• /
• 2024

The tensile properties of the single crystal superalloy CMSX-4 were examined at various temperatures. In the heat-treated state, some portion of the eutectic γ-γ' remained, and a uniform cuboidal γ' particles existed across the entire material. The yield strength and tensile strength reached highest at 750℃ and decreased with raising testing temperature. The elongation was lowest at 650℃ due t℃oncentrated deformation near the fracture area. However, the elongation increased at higher temperatures due to uniform deformation throughout the entire specimen. Fracture surface analysis tested at 850℃ and 950℃ revealed that cracks originated from casting defects. TEM observations conducted after the tensile test indicated that the primary deformation mechanism at room temperature involved dislocation shearing within the γ' phase. However, the increased strength both at 750℃ where stacking faults generated and at 650℃ was caused by the increased resistance of γ' phase to dislocation. The strength decreased because the movement of dislocations became easier due to the thermal activation process at and above 850℃.

• Journal of Korea Foundry Society
• /
• v.44 no.2
• /
• pp.31-39
• /
• 2024

Dendrite boundaries and γ/γ' structure of a second generation single crystalline superalloy CMSX-4 almost disappeared during solution treatment above 1310℃. γ' size in the dendrite core was uniform and fine, however, that in the interdendritic region was coarse and nonuniform. With increasing solutionizing temperature and time, γ' size in the interdednritic region became fine and segregation of alloying elements between dendrite core and interdendritic region diminished. Segregation of solid solution strengthening elements such as W, Co, Re in the dendrite core was not fully removed through the heat treatments, especially that of Re still remained to some extent. Tensile properties at room temperature at which does not cause precipitaion of harmful phases, were improved with increasing solutionizing temperature and time.

• Development and Reproduction
• /
• v.10 no.4
• /
• pp.263-269
• /
• 2006

To evaluate the potentiality of industrial use of cysteine proteinase inhibitor (cystatin) of tilapia egg and serum stability of the tilapia cystatin on low temperature storage and heat treatment was studied. When the eggs were stored at $4^{\circ}C$ for 3 days the cystatin activity was not changed much, while the supernatant of egg homogenate lost its cystatin activity significantly, remaining only about 65% of initial activity. When the eggs and serum were subjected to repeated freeze at $-20^{\circ}C$ and thaw at room temperature once a day, the egg cystatin was decreased after 5 cycles of freeze and thaw. However the serum cystatin was not changed by the 5 times repetition of freeze and thaw. More than 80% of egg cystatin activity was remained when the egg was heated at $35^{\circ}C$ for 30 min, but less than 10% was remained when heated at $50^{\circ}C$. On the other hand, the serum cystatin was very resistant to heat, remaining about 74% after heating at as high as $80^{\circ}C$ for 30 min. In summary, the egg cystatin was more stable when stored as intact form of egg rather than as supernatant of homogenate when stored at refrigeration. Egg cystatin was relatively stable against repeated freeze-thaw, and serum was found to be more stable in cysteine proteinase inhibitory activity than egg. Egg cystatin was not very resistant to heat treatment, while serum cystatin was quite resistant to high temperature heat treatment. These results suggest that tilapia egg and serum, especially the serum, would be a useful source for cysteine proteinase inhibitor in surimi production.

• Journal of the Korean Society of School Health
• /
• v.9 no.1
• /
• pp.55-67
• /
• 1996

This research has incorporated a postal survey from the principals, nurse-charging teachers and nurse-teachers of the fiftyfive elementary, middle and high school in Yang-pyeong county area where its supplementary rate of nurse-teachers is less than adequate. It is to analyse the current status of the school health service in the area and to come out with a plan to improve the school health program through the participations of the health related experts of the local community. The survey was done in the two months of period of April to May of 1994. The result of the survey follows. The student population in the Yang-pyeong county area is 13,998 and the school employee population is 904 which counts for about 19.2% of the whole population of the area. However, the supplementary rate of nurse-teachers is only 10.8% (4 in 55 schools) which is very low in terms of relativity. School health committee only exist in 17% of the whole number of schools in the area and 50 of school health committee answered that their activity do not meet the adequate level. Only 54. 3% of the whole school numbers has included the school health finance in their financial plans and the amount set for the school health finance is about 500,000 wons (100,000-1,600,000 wons). 64.9% of the schools in the Yang-pyeong county area have the permanent nursing room established in the school. But, often than the equipment for a simple physical examinations, their supply of the health related equipments are less than adequate. Particitations of school doctor in the school health service is at only 67.6% which pretty much include only the physical examinations. Nurse-charging teachers consider their utmost important role is to teach health education but, they answered that they spent most of their times and efforts on physical examinations & immunizations. The average number of students visition to the nursing room is 2.5 persons and complains for basic discomfort as headache, concussion, stomachache and indigestion problems and usual pills used are the analgesics and digestives. Physical examination is done in the most schools every year but, 51.4% of nurse-charging teachers answered the physical examination does not really help. About the emergency treatment ability, 75.7% reports that both manpower & equipment are short. The school food services are present in only 8 schools (21.6%) but, 89.2% of nurse-charging teachers answer that there is a definite need of the food service. The survey says that the utmost important environmental health and safety factors are the traffic accidents followed by improper heat system, lighting, the stools and desks that do not consider the student physical status The overall evaluation of school health program reports that there are adequate physical examination, immunization, environmental hygiene, and management of safety but, on the other hand, health education, health councelling & management of nursing room are not managed properly. The principals of the survey pool report shortage of public agency support, lack of understanding of school health, shortage of nursing equipments and school health finance as the barrier factors of school health. The nurse-charging teachers report on the same questions as their less than qualitifying expertise, extraload of work upon the nursing affairs, shortage of nursing equipments & school health finance. The head masters & nurse-charging teachers answered that they are desperate for the meetings of nurse-charging teachers, construction of school health councelling system & training education in order to improve school health and if these are available, they will actively participate in them. After the careful analysis of the survey result, it is apparent that through the relations of the manpowers, establishment of community-oriented school health is definitely in need in rural area where there is low supplementary rate of nurse-teachers and poor school health environment.

• Food Science and Preservation
• /
• v.30 no.1
• /
• pp.88-97
• /
• 2023

As livestock consumption in Korea has been gradually increasing, the quality of the final products has been improved to meet this increased demand. In particular, maintaining the water holding capacity (WHC) and minimizing the drip loss during the thawing of frozen meat are of utmost importance. This study investigated the physicochemical properties of frozen pork subjected to thawing under different conditions: at room temperature (20℃, under air), at a low temperature (4℃ refrigerator, under air), under water (20℃, under water in a vacuum bag), under microwave (microwave-thawing, 260 W), and under low-pressure tumbling (20℃, 0.015 bar, tumbling). The shortest thawing time for frozen pork was recorded upon low-pressure tumbling thus indicating a fast heat transfer. The lowest drip loss (0.2%) and highest WHC (94.5%) were also recorded under this condition. A significantly higher drip loss was observed upon microwave- (1.0%) and water-thawing (1.2%), which resulted in the lowest WHC in microwave thawing (87.2%). The highest total count of aerobic bacteria and coliform group were observed upon room temp thawing while the low pressure tumbling and thawing resulted in the lowest aerobic bacteria (1.90 log CFU/g) and coliform (0.78 log CFU/g) count. Consequently, thawing by low pressure tumbling afforded the best food quality.

• Journal of the Korean Wood Science and Technology
• /
• v.2 no.3
• /
• pp.3-16
• /
• 1974

One of the disadvantages of. wood and wood products is their hydroscopicity or dimensional instability. This is responsible for the loss of green volume of lumber as seasoning degrade. Dimensional stabilization is needed to substantially reduce seasoning defects and degrades and for increasing the serviceability of wood products. Recently, considerable world-wide attention has been drawn to the so-called Wood-Plastic Composites by irradiation-and heat-catalyst-polymerization methods and many research and developmental works have been reported. Wood-Plastic Composites are the new products having the superior mechanical and physical properties and the combinated characteristics of wood and plastic. The purpose of this experiment was to obtain the basic data for the improvement of wooden materials by manufacturing WPC. The species examined were Mulpurae-Namoo (Fraxinus, rhynchophylla), Sea-Namoo (Carpinus laxiflora), Cheungcheung-Namoo (Cornus controversa), Gorosae-Namoo (Acermono), Karae-Namoo(Juglans mandshurica) and Sanbud-Namoo (Prunus sargentii), used as blocks of type A ($3{\times}3{\times}40cm$) and type B ($5{\times}5{\times}60cm$), and were conditioned to about 10~11% moisture content before impregnation in materials humidity control room. Methyl methacrylate (MMA) as monomer and benzoyl peroxide (BPO) as initiator are used. The monomer containing BPO was impregnated into wood pieces in the vacuum system. After impregnation, the treated samples were polymerized with heat-catalyst methods. The immersed weights of monomer in woods are directly proportionated to the impregnation times. Monomer impregnation properties of Cheungcheung-Namoo, Mulpurae-Namoo and Seo-Namoo are relatively good, but in Karae-Namoo, it is very difficult to impregnate the monomer MMA. Fig. 3 shows the linear relation between polymer retentions in wood and polymerization times; that is, the polymer loadings are increasing with polymerization times. Furthermore species, moisture content, specific gravity and anatomical or conductible structure of wood, bulking solvents and monomers etc have effects on both of impregnation of monomer and polymer retention. Physical properties of treated materials are shown in table 3. Increasing rates of specific gravity are ranged 3 to 24% and volume swelling 3 to 10%. ASE is 20 to 46%, AE 14 to 50% and RWA 18 to 40%. Especially, the ASE in relation to absorption of liquid water increases approximately with increase of polymer content, although the bulking effect of the polymerization of monomer may also be influential. WPCs from Mulpurae-Namoo and Cheungcheung-Namoo have high dimensional stability, while its of Karae-Namoo and Seo-Namoo are-very low. Table 4 shows the mechanical properties of WPCs from 6 species. With its specific gravity and polymer loading increase, all mechanical properties are on the increase. Increasing rate of bending strength is 10 to 40%, compression strength 25 to 70%, ;impact bending absorbed energy 4 to 74% and tensile strength 18 to 56%. Mulpurae-Namoo and Cheungcheung-Namoo with high polymer content have considerable high increasing rate of strengths. But incase of Karae-Namoo with inferior monomer impregnation it is very low. Polymer retention in cell wall is 0.32 to 0.70%. Most of the polymer is accumulated in cell lumen. Effective. of polymer retention is 58.59% for Mulpurae-Namoo, 26.27% for Seo-Namoo, 47.98% for Cheungcheung-Namoo, 25.64% for Korosae-Namoo, 9.96% for Karae-Namoo and 25.84% for Sanbud-Namoo.

• Clean Technology
• /
• v.19 no.3
• /
• pp.264-271
• /
• 2013

In this study, we optimized the removal condition of contaminants attached on the scrap surface to recycle the scrap generated from the Zr alloy tube manufacturing process back to the nuclear grade. The main contaminant is remnant of watersoluble cooling lubricant that is used in the pilgering manufacture during the tube production, and it is assumed to be compressed and carbonized on the surface of tube. Zirlo alloy tube of ${\phi}9.50mm$, which has high occurrence frequency of scrap, was selected as the object to be cleaned, and cleaning abilities of reagents were evaluated by measuring the characteristics of contaminants remained and by analyzing the surface of the tube after cleaning process. For evaluation of each cleaning agent, we selected two types of sodium hydroxide series and three types of potassium hydroxide series. Furthermore, to confirm dependence on tempe-rature and ultrasonic intensities, cleaning at the room temperature, $40^{\circ}C$, and $60^{\circ}C$ was conducted, and results showed that higher the cleaning temperature and higher the ultrasonic intensity, better the cleaning effect. As a result of the bare-eye inspection, while the use of sodium hydroxide provided satisfactory condition on the tube surface, the use of potassium hydroxide series provided satisfactory condition on the tube surface only when the ultrasonic intensity was over 120 W. In the cleaning effect analysis using the gravimetric method, cleaning efficiency of sodium hydroxide series was as high as 97.6% ($60^{\circ}C$, 120 W), but since the tube surface condition was poor after the use of potassium hydroxide, the gravimetric method was not appropriate. In the analytical result of surface contaminants on the tube surface, C, O, Ca, and Zr were detected, and mainly C and O dominated the proportion of contaminants. It was also found that the degree of cleaning on the tube affected the componential ratio of C and O; if the degree of cleaning is high, or if cleaning is well-conducted, the proportion of C is decreased, and the proportion of O is increased. Based on these results, optimal cleaning for application in the industry can be expected by categorizing cleaning process into three steps of Alkali cleaning, Rinsing, and Drying and by adjusting cleaning parameters in each step.

• Korean Journal of Materials Research
• /
• v.11 no.5
• /
• pp.427-430
• /
• 2001

We prepared 10cm-diameter Si(100)/500 $\AA$-Si$_3$N$_4$/Si(100) wafer Pairs adopting 500 $\AA$ -thick Si$_3$N$_4$layer as insulating layer between single crystal Si wafers. Si3N, is superior to conventional SiO$_2$ in insulating. We premated a p-type(100) Si wafer and 500 $\AA$ -thick LPCVD Si$_3$N$_4$∥Si (100) wafer in a class 100 clean room. The cremated wafers are separated in two groups. One group is treated to have hydrophobic surface and the other to have hydrophilic. We employed a FLA(fast linear annealing) bonder to enhance the bond strength of cremated wafers at the scan velocity of 0.1mm/sec with varying the heat input at the range of 400~1125W. We measured bonded area using a infrared camera and bonding strength by the razor blade crack opening method. We used high resolution transmission electron microscopy(HRTEM) to probe cross sectional view of bonded wafers. The bonded area of two groups was about 75%. The bonding strength of samples which have hydrophobic surface increased with heat input up to 1577mJ/$m^2$ However, bonding strength of samples which have hydrophilic surface was above 2000mJ/$m^2$regardless of heat input. The HRTEM results showed that the hydrophilic samples have about 25 $\AA$ -thick SiO layer between Si and Si$_3$N$_4$/Si and that maybe lead to increase of bonding strength.

• Journal of Bio-Environment Control
• /
• v.22 no.4
• /
• pp.427-431
• /
• 2013

Paprika fruits should be stored and distributed at above $7^{\circ}C$ to prevent chilling injury but the small amount of paprika that transports with other horticultural products in refrigerated container by ship usually stored less than $5^{\circ}C$ for other products. In this case, paprika fruits cannot help exposing chilling temperature, so that the paprika must be lost marketable value during a long period of transfer. This study was conducted to compare the alleviated effects of high $CO_2$ treatment (passive MAP), heat (hot water dipping), and UVc treatment on chilling injury of paprika fruits due to low temperature storage, and also to decide if these treatments can be used for transporting under $5^{\circ}C$. After each treatment the paprika were put in the low temperature storage ($4^{\circ}C$) for 20 days and afterwards change the in room temperature ($20^{\circ}C$) for 5 days. The fresh weight loss of all the treatments except the high $CO_2$ treatment showed around 7~12% after 25 days of storage and the ethylene concentration showed periodical increases and decreases as around 3 ${\mu}l/l$. The $CO_2$ concentration was rapidly increased 33% carbon dioxide in high $CO_2$ treatment during room temperature storage after cold storage for 20 days. The firmness which is key quality characteristics during storage and is decreasing caused by chilling injury was not significantly different among all treatments. However, the firmness of stored paprika was maintained highest in the treated with hot water dipping. Therefore, HWD and UVc treatment that showed 60% of electrolyte leakage in the $4^{\circ}C$ control (chilling injury control) and similar level with the $7^{\circ}C$ control (non-chilling injury control) would be effective to alleviate chilling injury in the stored paprika.

• Korean Journal of Materials Research
• /
• v.6 no.7
• /
• pp.700-708
• /
• 1996

Electroless plating technique was utilized to flip chip bonding to improve surface mount characteristics. Each step of plating procedure was studied in terms pf pH, plating temperature and plating time. Al patterned 4 inch Si wafers were used as substrstes and zincate was used as an activation solution. Heat treatment was carried out for all the specimens in the temperature range from room temperature to $400^{\circ}C$ for $30^{\circ}C$ minutes in a vacuum furnace. Homogeneous distribution of Zn particles of size was obtained by the zincate treatment with pH 13 ~ 13.5, solution concentration of 15 ~ 25% at room temperature. The plating rates for both Ni-P and Au electroless plating steps increased with increasing the plating temperature and pH. The main crystallization planes of the plated Au were found to be (111) a pH 7 and (200) and (111) at pH 9 independent of the annealing temperature.