• Journal of the Korean Society for Heat Treatment
• /
• v.6 no.4
• /
• pp.230-236
• /
• 1993

The laser beam hardening has been experimentally tried to find the hardened characteristics of STD11. Experiment was performed on the optimum hardening condition with 2kW $CO_2$ laser. The microstructure of the hardened layers was observed using the microscope. The hardened zones exhibits very high Vickers microhardness of 720 Hv, however, the deoxidation was observed under the surface of hardened area. The case depth of hardened zones is about 0.6mrn and case width is 4mm. FEM-simulation on laser surface hardening of STD11 steel are described. With the proper assumption of the absorbed energy density, the calculated case depth and width in 2 kW $CO_2$ laser hardening were in good agreement with the experimental result. It was found that there is optimum absorbed energy density of STD11.

• Proceedings of the KIEE Conference
• /
• 2002.07d
• /
• pp.2319-2321
• /
• 2002

This paper suggests a computer-based on-line measurement method of tan$\delta$ and capacitance for HV capacitor. The method employs V-I technique using scaled down analog voltage and current signal obtained by digital oscilloscope. The measurement results are displayed by graphic user interface with graphic language. Field tests were tarried out at 6.6kV testing voltage in Samhwa Capacitor company.

• Proceedings of the KIEE Conference
• /
• 1999.07e
• /
• pp.2041-2043
• /
• 1999

In order to investigate the radiation characteristics of unmixed line noise from overhead high voltage AC transmission lines, a gap noise generator was manufactured. Disk size which decides capacitance between the noise generator and earth was selected through preliminary indoor experiments and analysis by charge simulation method. The capacitance is one of principal parameters related to inject a proper noise current into lines. The field experiments were performed with the noise generator installed in Kochang 765 kV full scale test line. As the results, the useful data which can be used to analysis the radiation characteristics of noise from transmission lines was obtained. Those are lateral profiles the directivity of antenna toward lines, frequency spectra and so on.

• Proceedings of the KIEE Conference
• /
• 1999.07e
• /
• pp.2299-2301
• /
• 1999

In this work, experimental investigation was carried out for the breakdown characteristics of $SF_6$, $N_2$ and their mixtures under the uniform and non-uniform electric field, by use of HVAC and standard impulse testing voltages, as a function of different gas pressures from 1 atm to 5 atm. The results show that the dielectric strength of the $SF_6$ mixed in $N_2$ was significantly increased at its portion of 10%, which might imply that the optimum mixture of $SF_6$ for the HV switch gear could be proposed to be 10%.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.05c
• /
• pp.212-216
• /
• 2001

The conventional tracking testing as IEC-60587 is widely used in surface aging measurement of outdoor insulator because those testing can carry out very short time in Lab-testing. Also IEC-60587 testing is able to offer the standard judgement of relative degradation level of outdoor HV machine/system. Therefore it is very useful method compare to previous conventional tracking testing method and effective Lab-testing method. But surface discharges(SD) have very complex characteristics of discharge pattern so it is required estimation research to development of precise analysis method. In recent, the study of IRR-camera is carrying out discover of temperature of power equipment through condition diagnosis and system development of degradation diagnosis. In this study, SD occurred from procelain insulator, used 22.9[KV] distribution, is measured with partial temperature distribution in real time, the degradation grade of SD is analyzed through produced patterns in SD concentration according to applied time.

• Journal of the Semiconductor & Display Technology
• /
• v.13 no.3
• /
• pp.51-55
• /
• 2014

Ni-CNT(Carbon Nanotubes) composite coating is often used for the surface treatment of mechanical/electronic devices to improve the properties of the Ni coating. For the Ni-CNT coating, the dispersion of CNT fibers is a critical process. In this study, ultrasonic treatment instead of the conventional ball milling was attempted as a dispersion method for the electroless Ni-CNT coating. SEM-EDX analysis was performed and contact angle, sheet resistance, and micro-hardness were measured. Results showed that the ultrasonic treatment was comparable to the ball milling, as a dispersion method, but the difference was negligible. However, combined ball milling and ultrasonic treatment(double treatment) showed much improved micro-hardness value, above 350Hv(close to the value obtained by the Ni-CNT electroplating). In addition, electroless Ni-CNT(double-treated) coatings formed on the thin Ni film deposited by the electroless plating(double coating) showed better mechanical properties. Thus, double treatment and double coating are suggested as an improved electroless Ni-CNT coating method.

• Journal of Welding and Joining
• /
• v.18 no.6
• /
• pp.42-47
• /
• 2000

The object of this study is to estimate Sn-Ag-Bi-Ga solder alloy as a substitute for Sn-37Pb alloy. For Sn-Ag-Bi-Ga alloys, Ag, Bi and Ga contents are varied. (Ag : 1~5%, Ga : 3%, Bi : 3~6%) Comparing to Sn-37Pb alloy Sn-Ag-Bi-Ga alloys have wider melting temperature range up to max. $18.7^{\circ}C$. With increasing Ag, Bi contents, the wettability of the alloys increased up to max. 6.6 mN. The vickers hardness of the alloys was max. 46.4 Hv. The ultimate tensile stress of the alloys was max. 60.3 MPa and the elongation was max. 1.2%. The joint strength between circuit board and solder was max. 55.5 N and the joint strength between connector and solder was max. 176.1 N. There were no cracks in this alloys after thermal shock test.

• Journal of Welding and Joining
• /
• v.31 no.4
• /
• pp.47-53
• /
• 2013

SCMH2 steel is widely used in the industrial members of car and tractor. This study focused on material properties and evaluation technology of the SCMH2 steel regarding the surface treatment followed by carburizing and nitriding, by means of impact test, hardness test. and fatigue test including HCF (high cycle fatigue) and VHCF (very high cycle fatigue). Drop weight impact tester (Instron, 9250 Hv) and Cantilever type rotating-bending fatigue tester (YRB200, 3150 rpm) were used to characterize the SCMH2 standard specimen before and after carburizing/nitriding. In order to understand those effects on fatigue characteristics and material properties, the fractured surfaces were carefully observed and analyzed by SEM (scanning electron microscope) and EDS (energy-dispersive X-ray spectroscopy).

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.300-300
• /
• 2013

세계전자제품의 부품산업은 21세기 정보화 사회와 함께 IT 산업에서 급성장으로 인해 부품의 소형화, 경량화, 친환경화가 요구되고 있다. IT 산업에서 리드스크류(Leadsrew)는 마이크로 구동부품중의 이송장치를 구성하는 핵심 부품으로 탄소강과 합금강 및 스테인레스강 등이 사용되고 있다. 탄소강은 성형 가공성과 원가 절감에 최적의 소재로서 낮은 표면 경도로 인한 내마모성 저하와 부식 분위기에서의 내식성이 떨어지는 단점을 가지고 있다. 본 연구에서는 탄소강(S20C:${\oint}30{\times}h10$)을 이용하여 플라즈마 질화 표면처리를 통해 표면경도와 내마모성 향상 및 내식성을 높이는 연구를 수행하였다. 연구 방법으로 플라즈마 연질화 공정과 Post Oxidation 공정을 개발하였고, 질화 처리된 시험편에 대해 마이크로 비커스 경도, OEM&SEM, XRD 분석 및 염수분무(KS D 9502) 시험으로 특성을 분석하였다. 연구 결과로 탄소강(S20C)은 마이크로 비커스 경도 분석으로 표면 경도가 600Hv0.025 이상과 염수분무 시험으로 내식성은 24시간 이상의 결과를 얻었다.

• Journal of the Korean institute of surface engineering
• /
• v.48 no.6
• /
• pp.349-353
• /
• 2015

In this paper, arc thermal spray coating was conducted onto the SS400 steel using Inconel 625 wires in order to improve the durability of marine steel structures, and then investigated cavitation damage behavior of Inconel 625 coating layer in sea water. For the Inconel 625 coating layer, surface hardness appeared similar to that of existing high velocity oxy-fuel coating technology with 380~480 HV, but the porosity of about 6 % was larger relatively. During the cavitation experiment, pit damages were originated and grown at the rough surface and pore defect area of Inconel 625 coating layer. And, after the 72 hours of experimental time, weight loss of Inconel 625 coating layer exhibited gradually increasing tendency due to surface damage effect of the undercut.