• Journal of the Korean Society for Heat Treatment
• /
• v.20 no.6
• /
• pp.323-328
• /
• 2007

This study has been investigated the effect of high temperature gas nitriding (HTGN) heat treatment of STS 444 (18Cr-0.01Ni-0.01C-0.2Nb) ferritic stainless steel in an atmosphere of nitrogen gas at the temperature range between $1050^{\circ}C\;and\;1150^{\circ}C$. The surface layer was changed into martensite and austenite with the nitrides of NbCrN by HTGN treatment. Due to the precipitation of nitrides and matrensite formation, the hardness of the surface layer showed $400Hv{\sim}530Hv$. The nitrogen concentration of the surface layer appeared as 0.05%, 0.12% and 0.92%, respectively, at $1050^{\circ}C,\;1100^{\circ}C\;and\;1150^{\circ}C$. When the nitrogen is permeated from surface to interior, Nb and Cr, which have strong affinities with nitrogen, also move from interior to surface. Therefore it is considered that this counter-current of atoms promotes the formation of NbCrN at the surface layer.

• Journal of the Korean Society for Heat Treatment
• /
• v.21 no.5
• /
• pp.244-250
• /
• 2008

This study has investigated the surface phase change, hardness variation, surface precipitates, nitrogen content and corrosion resistance in STS 431 (17Cr-2Ni-0.2C-0.01Nb) martensitic stainless steel after high temperature gas nitriding (HTGN) treatment at the temperature range between $1050^{\circ}C$ and $1150^{\circ}C$. The HTGN-treated surface layer appeared $Cr_2N$ of rod type, carbo-nitride of round type and fine precipitates in the austenite matrix. On the other hand the interior region where the nitrogen was not permeated, exhibited martensite phase. The surface hardness showed 250~590 HV, depending on the HTGN treatment conditions, while the interior martensitic phase represented 520 HV. The permeation depth of nitrogen increased with increasing the HTGN-treated temperature. The nitrogen concentration of the surface layer appeared approximately ~0.17% at $1100^{\circ}C$. On comparing the corrosion resistance between solution-annealed and HTGN-treated steels, the corrosion resistance of HTGN-treated steel was superior to that of solution-annealed specimens.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.16 no.10
• /
• pp.1861-1868
• /
• 1992

Laser beam hardening of 12%-Cr steel has been evaluated by using a continuous wave 3kW co$_{2}$ laser with a hardening mirror set. Experiment was performed on the hardening condition with a laser power of 2.85kW and travel speed of 1.0 and 1.5m/min. Multi passes have been also tried to find the hardening characteristics of partly overlapped zone. The black paint to use at high temperature was adopted to increase the absorptivity of laser beam energy with the wavelength of 10.6.mu.m at the surface of base metal. The microstructure of the hardened layers was observed by using a light microscopy, SEM and TEM. A fine Lamellar martensite formed in the hardened zones exhibits very high Vickers microhardness of 600Hv, whereas the tempered martensite distributes in the base metal with Vickers microhardness of 240Hv.It has been found that laser hardening with multi passes showed no significant drop of the hardness between adjacent passes.

• Journal of Biosystems Engineering
• /
• v.36 no.6
• /
• pp.416-421
• /
• 2011

This study was initiated to prevent rear-end collision which causes the most frequent human damage by agricultural tractors. Therefore, this study was aimed to evaluate the luminous performance of a stop lamp for an agricultural tractor which could reduce rear-end collision. The performance test of luminous intensity distribution was conducted for a total of 12 tractor models classified by size (above 44 kW for large, 30~43 kW for medium, and below 29 kW for small) and production area (domestic, foreign manufacture) in accordance with Regulation No.7 of UNECE Vehicle Regulations-1958 Agreement considering ${\pm}$20 standard deviation. Three out of 5 large, 3 out of 4 medium, and all small tractors were resulted as inadequate for the test criterion. This study found that the luminous performance results were better as the size of agricultural tractors became bigger. One out of 4 foreign and 2 out of 8 domestic manufacturers were suitable for the test criterion, and overall no difference from the luminosity test results was observed between domestic and foreign manufacturers. In addition, the measuring points, HV, 5L, 5R, 5U and 5D with the minimal luminosity revealed flaws (80% of the proportion of faulty products). Therefore, it is urgent to improve the quality for measuring points (HV, 5U, 5L, 5R, 5D) of stop lamps to apply Regulation No. 7.

• Journal of Welding and Joining
• /
• v.14 no.1
• /
• pp.92-98
• /
• 1996

Al-Fe alloy layers on heated steel sheet were made by Al powder spray for 30 minutes at $700^{\circ}C$, $800^{\circ}C$ and $1000^{\circ}C$, respectively. As a results, for alloy layers formed at $700^{\circ}C$ and $800^{\circ}C$, main phases were brittle phase $FeAl_3 and Fe_2Al_5$, hardnesses were very high (Hv 700~800), corrosion resistances were good and surfaces were smooth, but wear resistances were bad. For alloy layer formed at $1000^{\circ}C$, main phase was ductile phase $Fe_3Al$, hardness was low (Hv 300~400), corrosion and wear resistances were excellent, but surface was rough. Therefore, alloy layers that formed at $700^{\circ}C$ and $800^{\circ}C$ were heat treated at $1000^{\circ}C$ for 10 minutes for the purpose of smooth surface and excellent wear resistance in this study. It was investigated that brittle phase $FeAl_3 and Fe_2Al_5$ of alloy layers fromed by Al powder spray at $700^{\circ}C$ and $800^{\circ}C$ turn into ductile phase $Fe_3Al$ by heat treated at $1000^{\circ}C$ for 10 minutes without changing smooth surface. It was concluded that the alloy layers formed by Al powder spray on heated steel sheet at $700^{\circ}C$ and $800^{\circ}C$ for 30 minutes and heat treated at $1000^{\circ}C$ for 10 minutes were excellent on wear and smooth surface.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.12 no.3
• /
• pp.1105-1110
• /
• 2011

After pure titanium Ingot(G2) with 400mm in diameter was manufactured, the analysis of its ingredients showed that the oxygen content was 0.073wt% and the iron content was 0.03wt%, which made ASTM Gr.2 standardization satisfactory. The processed titanium ingot produced 42mm wire rod, and hot rolling of 18th phase produced 9mm wire rod. The hardness analysis of 15.8mm wire rod, which was processed in hot rolling of 10th phase from the surface to the center, resulted in almost constant value with Hv150~200. The last 9mm wire rod had a different yield strength and elongation percentage depending on the temperature as it was led in to a hot roller. However, tensile strength revealed an approximate value and made ASTM B863 standardization satisfactory.

• Journal of the Korean Society for Heat Treatment
• /
• v.30 no.4
• /
• pp.164-168
• /
• 2017

Intense electron beam was irradiated on the CrAlN thin films deposited in SKD61 under different incident energies and then the effect of electron beam irradiation on the enhancement of surface hardness and wear resistance was investigated. Surface hardness and wear resistance of the CrAlN films is increased proportionally with the electron beam energy. While the surface hardness of as deposited CrAlN film is Hv ($0.1g{\cdot}f$) 450, the hardness oflectron irradiated (600 eV) film is Hv ($0.1g{\cdot}f$) 2050. The width of wear track of the untreated SKD61 is $X\_{\mu}m$, while the track-width of the electron irradiated CrAlN (600 eV) film is $787{\mu}m$, respectively. From the observed results, it is supposed that the optimal electron beam irradiation can be one of the useful surface treatment technologies for the enhancement of surface hardness and wear resistance of CrAlN/SKD61, simultaneously.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.283-283
• /
• 2013

Because of beautiful glossy and color, the value of gold leverage is very high in Europe. To improve the quality of gold alloys, we performed heat treatment on 14 K white gold alloys by variously changing age-hardening conditions. Age-hardening behavior and the related phase transformation changes were studied to elucidate the hardening mechanism of 14 K white gold alloy. For solid solution treatment [ST], casted gold alloy specimens were treated at high temperature ($750^{\circ}C$) for 30 minutes, and the specimens dropped to water to quench them. For Age-hardening treatment [AT], the specimens were treated at various temperatures ($250{\sim}300^{\circ}C$). After the heat treatment, we observed the phenomenon to increase hardness from 126 Hv to 166 Hv by Vicker's hardness tester. Through electron probe micro-analysis (EPMA) mapping analysis, we investigated that irregular particles were changed uniformly. In the SEM and OM images, two phases of matrix and particle-likestructures were observed, and the precipitation of these elements from the matrix progressed during age-hardening. By transmission electron microscope and X-ray diffraction observation, it was revealed that the formation of the Au3Cu superstructure contributed to the age-hardening at $270^{\circ}C$ in the gold alloy. After the heat treatment, this analysis shows that casted gold alloys were to improve hardness and to moderate surface defects at specific temperatures and duration.

• Microbiology and Biotechnology Letters
• /
• v.28 no.2
• /
• pp.71-79
• /
• 2000

Two typess of copolyesters, poly(3-hydroxybutyric acid-co-4-hydroxy-butyric acid)[P(3HB-co-4HB] and poly(3-hydroxybutyric acid-co-3-hydroxyvaleric acid)[P(3HB-co-3HV)], with various monomer ratios and different degree of microstructural heterogeneity were synthesized from Ralstonia eutropha H16 and Hydrogenophaga pseudoflava by using ${\gamma}$-butyrolactone and ${\gamma}$-valerolactone, respectively. The two bacteria showed a large difference in the utilization of ${\gamma}$-butyrolactone for cell growth and PHA synthesis. H. pseudoflava synthesized P(3HB-co-4HB) copolyesters with a wide range of 4HB content from 13 to 96 mol% depending on culture conditions, whiel R. eutropha H16 was able to synthesize the copolyesters containing less than 20 mol% of 4HB. An increase in the 4HB content in the P(3HB-co-4HB) copolyesters synthesized by H. pseud-oflava induced an lowering of their melting temperatures as well as their enthalpies of fusion. The increase in the 4HB content, however, increased the rate of degradation by an extracellular P(3HB) depolymerase. NMR spectros-copy and differential scanning calorimetry showed that the P(3HB-co-4HB) copolyesters from H. pseudoflava were generally microstructurally heterogeneous. The P(3HB-co-4HB) copolyesters) synthesized by R. eutropha H16 were rather random copolymers showing less microstructural heterogeneity than those synthesized by H. pseudoflava. The NMR D value analysis suggested that the monomer distribution of the P(3HB-co-3HV) copolymers from the two bacteria were relatively random.

• The Journal of the Korean Society for Microbiology
• /
• v.22 no.1
• /
• pp.1-8
• /
• 1987

Hantaan virus(HV) 76-118 strain was inoculated into suckling ICR mice by intra-nasal route with an inoculum of $10LD_{50}$. Mortality was 65% at the 3rd week after inoculation, but declined to 35% at the 4th week. Infectivity was determined by the measuring immuno-fluorescent antibody in sera. The peak of infectivity was 80% at the 4'th week after inoculation. Viremia was reached peak level of $1.7{\times}10^4\;PFU/ml$ by day 10. Immunofluorescent antibody and neutralizing antibody appeared by 2 weeks and 15-17 days respectively, but achieved similar titer by 35 days. By using a monoclonal antibody to HV 76-118, viral antigens were initially detected in inguinal and axillary lymph node by 2 days. Viral antigens in bone marrow and lung were delayed much more than in those of lymph node. These were similar with those of intra-peritoneal and intra-muscular route. Immune complex against IgG, IgM and C3 appeared by 16 days, 14 days, and 18 days respectively. The pattern of immunofluorescence in the basement membrane of glomeruli was diffuse membranous. Spotted pattern was also observed in the tissue stained with anti-mouse C3 antibody. By 20 days, control tissue was also shown immune complex in the glomeruli.