• Journal of the Korean Magnetics Society
• /
• v.22 no.3
• /
• pp.85-90
• /
• 2012

Oxidation of the $Nd_2Fe_{14}B$ compound crystal and its effect on the coercivity of the fine $Nd_2Fe_{14}B$ crystal particles were investigated. Oxidation kinetics of the $Nd_2Fe_{14}B$ compound crystal was investigated using an excessively grown $Nd_2Fe_{14}B$ grains in the $Nd_{15}Fe_{77}B_8$ alloy ingot. Oxidation of the $Nd_2Fe_{14}B$ compound crystal occurred by dissociation of the phase into multi-phase mixture of ${\alpha}$-Fe, $Fe_3B$, and Nd oxides. Oxidation rate of the $Nd_2Fe_{14}B$ compound crystal showed no dependence on the crystallographic direction. The oxidation reaction was modeled according to simple linear relationship. Activation energy for the oxidation of $Nd_2Fe_{14}B$ compound crystal was calculated to be approximately 26.8 kJ/mol. Fine $Nd_2Fe_{14}B$ crystal particles in near single domain size was prepared by ball milling of the HDDR-treated $Nd_{15}Fe_{77}B_8$ alloy, and these particles were used for investigating the effect of oxidation on the coercvity. The near single domain size $Nd_2Fe_{14}B$ crystal particles (${\fallingdotseq}0.3\;{\mu}m$) had high coercivity over 9 kOe. However, the coercivity was radically reduced as the temperature increased in air (<2 kOe at $200^{\circ}C$). This radical coercivity reduction was attributed to the soft magnetic phases, ${\alpha}$-Fe and $Fe_3B$, which were formed on the surface of the fine particles due to the oxidation.