• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2002년도 춘계학술대회 논문집 초전도 자성체
• /
• pp.64-67
• /
• 2002

The Physical and magnetic properties such as microstructure, permeability and power loss of Ni-Zn ferrite with composition of $Ni_{0.8}Zn_{0.2}Fe_2O_4$, were investigated as the function of $Bi_2O_3$ and CaO contents. The power loss increased in proportion to the amount of $Bi_2O_3$ up to 0.3 wt% but it decreased over than 0.3 wt% addition. The highest permeability of 134 was obtained to the specimen added 1.0 wt% $Bi_2O_3$ since $Bi_2O_3$ contents were strongly dominant to grain growth and size than that of CaO. $Bi_2O_3$ liquid phase created during sintering process promoted sintering and grain growth so that grain size and permeability increased compared to that of the specimens which were sintered with free-additive and CaO. Also, lots of pores existed in the specimen which was added $Bi_2O_3$ wt% with the biggest grain size.

• 대한기계학회논문집
• /
• 제12권6호
• /
• pp.1343-1349
• /
• 1988

In this study, it is investigated for the effects of stress ratio and grain size on fatigue crack growth behavior and crack closure, in ferrite-martensite dual phase steels. The results obtained are as follows ; .DELTA. $K_{th}$ is independent of the ferrite grain size, but decreases with increasing stress ratio. The relation between .DELTA. $K_{th}$ and stress ratio R is as follows : .DELTA. $K_{th}$ =15.1(1-0.95R). But (.DELTA. $K_{eff}$)$_{th}$ in terms of crack closure is approximately 2.5 MPa.root.m. Also, variation of the degree of crack deflection to crack tip opening displacement at the minimum load is considered as a parameter of crack closure.e.e.

• Nuclear Engineering and Technology
• /
• 제32권1호
• /
• pp.77-87
• /
• 2000

It is reported that the toughness and safety margins of the SA106 Gr.C main steam line piping steel is reduced due to dynamic strain aging (DSA) at the reactor operating temperature for Leak-Before-Break (LBB) application. In this study, intercritical annealing in two-phase ($\alpha$+${\gamma}$）region was performed to investigate the possibility of improving the toughness and reducing DSA susceptibility. The manifestations of DSA were still observed in the tensile tests of the annealed specimens. However, the ductility loss caused by DSA was smaller than that in the as-received material. Furthermore, the intercritical annealing was able to increase the Charpy impact toughness by 1.5 times compared to as-received. With the heat treatment, we could obtain microstructural changes such as the cleaner retained ferrite, increased ferrite content and somewhat finer grain size. It is considered that the reduced DSA was induced by cleaner retained ferrite, which in turn resulted in higher impact toughness in addition to the general toughening due to finer grain sizes and increased ferrite content.

• 대한기계학회논문집
• /
• 제5권3호
• /
• pp.223-229
• /
• 1981

A study has been made of the fracture strength and ductility of the dual phase microstructure, in which the martensitic phase encapsulated islands of ferritic phase in association with the cleavage cracking of ferrite grains. It was found the final fracture occured in a brittle manner, starting from the Griffith crack which consisted of the cleavage crack in the ferrite grains and the cracks in second phase. Furthermore, the effects of the ferrite grain sizes on the Griffith crack were also discussed.

• International Journal of Korean Welding Society
• /
• 제2권1호
• /
• pp.25-28
• /
• 2002

In the coarse grain HAZ adjacent to the fusion line, most of the TiN particles in conventional Ti added steel are dissolved and austenite grain growth is easily occurred during welding process. To avoid this difficulty, thermal stability of TiN particle is improved by increasing the nitrogen content in steel. In this study, the effect of hlgh nitrogen TiN particle on preventing austenite grain growth in HAZ was investigated. Increased thermal stability of TiN particle is helpful for preventing the austenite grain growth by pinning effect. High nitrogen TiN particle in simulated HAZ were not dissolved even at high temperature such as 1400'E and prevented the austenite grain growth in simulated HAZ. Owing to small austenite grain size in HAZ the width of coarse grain HAZ in high nitrogen TiN steel was decreased to 1/10 of conventional TiN steel. Even high heat input welding, the microstructure of coarse grain HAZ consisted of fine polygonal ferrite and pearlite and toughness of coarse grain HAZ was significantly improved.

• Journal of Magnetics
• /
• 제18권3호
• /
• pp.308-310
• /
• 2013

Translation induced by the field-gradient force is being observed for a single ferromagnetic iron grain and a ferrimagnetic grain of a ferrite sample ($CuFe_2O_4$). From measurements on the translation, precise saturated magnetization of $M_S$ is possible for a single grain. The method is based on the energy conservation rule assumed for the grain during its translation and the grain is translated through a diffuse area under microgravity conditions. The results of the two materials indicate that a field-induced translation of grain bearing spontaneous moment is generally determined by a field-induced potential $-mM_SH(x)$ where m denotes the mass of sample. According to the above translations, the detection of $M_S$ is not interfered by any signals from the sample holder. The $M_S$ measurement does not require m value. By observing translations resulting from fieldinduced volume forces, the magnetization of a single grain is measurable irrespective of its size; the principle is also applicable to measuring susceptibility of diamagnetic and paramagnetic materials.

• 한국자기학회지
• /
• 제13권3호
• /
• pp.109-114
• /
• 2003

NiCuZn 페라이트에 $V_2O_{5}$를 0~0.5 wt% 첨가하여 페라이트 페이스트를 준비한 후,스크린 인쇄법으로 내부전극이 4.5회 회전된 임의의 크기(7.7$\times$4.5$\times$l.4 mm)의 칩인덕터를 제조하여, $V_2O_{5}$ 첨가량에 따른 미세구조 및 자기적 특성 변화를 분석하였다. $V_2O_{5}$첨가량이 증가할수록 액상소결이 발달하여 페라이트 입계에 내부전극 Ag의 확산과 Cu 석출 현상이 촉진되고, 이로 인하여 과대입자성장이 발달되었다. 이러한 현상은 칩인덕터의 자기적 특성에 큰 영향을 미쳐,900 $^{\circ}C$에서 소결된 $V_2O_{5}$ wt% 첨가시편의 주파수 10 MHz에서의 인덕턴스 값이 3.7$\mu$H로 0.3 wt% 첨가 시편의 4.2 $\mu$H보다 작게 나타났는데, 이는 Ag와 Cu의 석출량이 많아짐에 따라 잔류응력 발생이 심화되기 때문으로 생각된다 또한 $V_2O_{5}$ 0.5 wt% 첨가한 시편의 경우 소결온도가 증가함에 따라 품질계수 값이 감소하였는데, 이 결과도 페라이트 입계에서의 Ag나 Cu의 금속성분의 석출량 증가 및 과대입자성장에 의한 입자크기 증대로 인하여 전체 전기비저항이 감소되기 때문인 것으로 생각된다. 결론적으로 자기적 특성을 고려할 때 0.3 wt%가 적정 첨가량으로 나타났다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 춘계학술대회 논문집 초전도 자성체 연구회
• /
• pp.88-91
• /
• 2003

The magnetic porcelain materials were studied by using the porcelain materials added Sr-ferrite powders before forming and firing process. For the high magnetic property, the Sr-ferrite magnetic powders with the grain size of 1 ${\mu}m$ were agglomerated the powder size of about 1 mm. The magnetic porcelain with 30 wt% of Sr-ferrite powders indicated the magnetic characteristics such as the remanent flux density of 240 G and the intrinsic coercivity of 3910 Oe, at the firing conditions of $1250^{\circ}C$/1hr in air.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2008년도 춘계학술대회 논문집
• /
• pp.431-434
• /
• 2008

Effects of microstructure on the toughness of low carbon HSLA steels were investigated. Nickel decreased the ferrite-austenite transformation temperature, resulted in increase of the fraction of bainitic ferrite. However, it was decreased with increasing deformation amount at austenite region. Since fine austenite grains formed by dynamic recrystallization under large strain transformed to acicular ferrite or granular bainite rather than bainitic ferrite. The effective grain size, thus, was decreased by deformation and it resulted in lower ductile-brittle transition temperature (DBTT). The bainitic ferrite was thought to inhibit the fracture crack initiation and to delay the crack propagation by its high dislocation density and hard interlath $2^{nd}$ phase constituents, respectively. Thus, DBTT was also decreased by Ni addition in low carbon HSLA steels.

• 한국세라믹학회지
• /
• 제29권5호
• /
• pp.383-390
• /
• 1992

We investigated the effect of substrate on the properties of the Ni-Zn-Cu ferrite thin films deposited on SiO2 (1000∼3000${\AA}$) / Si (100) substrate at various conditions by rf magnetron sputtering. A disktype Ni-Zn-Cu ferrite sintered by conventional ceramic process and argon gas were used as a target and a sputtering gas, repectively. The compositions of the thin films measured by EPMA were similar to target composition (Fe: 65.8 at%, Ni: 12.7 at%, Cu: 6.7 at%, Zn: 14.8 at%) irrespective of substrate temperature. Amorphous thin films were deposited when substrate was not intentionally heated, but the films came to crystallize with increasing substrate temperature, and crystalline thin films were deposited at substrate temperature above 200$^{\circ}C$. Below 250$^{\circ}C$ saturation magnetization (Ms), remanence (Mr) and coercivity (Hc) of the ferrite thin film increased with the substrate temperature due to the increase of grain size and the improvement of crystallinity. And above 250$^{\circ}C$, Ms, Mr increased slightly, but Hc of the amorphous thin films increased due to crystallization, whereas that of the crystalline thin films decreased because of grain growth and stress release.