• Journal of Powder Materials
• /
• v.28 no.4
• /
• pp.325-330
• /
• 2021

In this study, a ZnS film of 8-mm thickness was prepared on graphite using a hot-wall-type CVD technique. The ZnS thick film was then hot isostatically pressed under different pressures (125-205 MPa) in an argon atmosphere. The effects of pressure were systematically studied in terms of crystallographic orientation, grain size, density, and transmittance during the HIP process. X-ray diffraction pattern analysis revealed that the preferred (111) orientation was well developed after a pressure of 80 MPa was applied during the HIP process. A high transmittance of 61.8% in HIP-ZnS was obtained under the optimal conditions (1010℃, 205 MPa, 6 h) as compared with a range of approximately 10% for the CVD-ZnS thick film under a 550-nm wavelength. In addition, the main cause of the improvement in transmittance was determined to be the disappearance of the scattering factor due to grain growth and the increase in density.

• Korean Journal of Mineralogy and Petrology
• /
• v.35 no.3
• /
• pp.259-271
• /
• 2022

Lattice preferred orientation (LPO), which shows a specific lattice-orientation of minerals, is affected by the deformation conditions of minerals. Because of this reason, LPO is very useful to study the deformation conditions of the minerals and the rocks. In this study, we collected amphibole-rich rocks from the Geumgye Mountain, Chugye-ri, Yugu-eup, Chungcheongnamdo, located in the southwestern part of the Gyeonggi Massif, and analyzed the LPO of amphibole and plagioclase using electron backscattered diffraction. Two types of LPOs of amphibole, type I and type IV, were observed in Yugu amphibole-rich rocks. Our data suggest that the amphibole-rich rocks in Yugu were deformed by rigid body rotation regardless of the LPOs and grain size of amphibole, and the LPOs are considered to have been affected by the degree of deformation (i.e. strain). In the low strained amphibole-rich rock, a strong type I LPO and a large grain size of amphibole were observed. On the other hand, in the highly strained amphibole-rich rocks, a weak type IV LPO and a small grain size of amphibole were observed. The various degree of deformation observed in the Yugu amphibole-rich rocks were also observed in the adjacent peridotites, indicating that the rocks in Yugu experienced various levels of deformation.

• Korean Journal of Materials Research
• /
• v.4 no.1
• /
• pp.37-43
• /
• 1994

Y-Ra-Cu-0 oxide superconductors were fabricated by the sinter-forging method to make the critical current density improve through controlling of microstructure and crystal texture. The grain alignment of oxide superconductor was formed by the sinter-forging process and it's c-axis orientation was parallel to the press direction.The orientation factor of texture increased with sinking temperature and pressure, and also grain alignment was improved by the addition of Ag. As for the sinterforged Y-Ba-Cu-O/Ag sample, the $T_c$(on-set) was not almost varied with the sinter-forging temperature, but $T_c\;^{zero}$ decreased more or less at high sinter-forging temperatures. In addition, it was observed that added-Ag was mainly distributed along the grain boundar~es in the (123) matrix, resulting in the densification of microstructure. From these results, i t was thought that the improvement of $J_c$ over 2000A/$\textrm{cm}^2$ was attributed to the texture, densification of microstructure, and (123) grain growth due to the Ag addition.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.18 no.4
• /
• pp.338-343
• /
• 2005

Pb(Zr,Ti)O₃[PZT] thin films were prepared on a highly (100) oriented LaNiO₃[LNO] and a randomly oriented LNO by sol-gel process. The PZT thin films on a highly (100) oriented LNO show a high (100) crystal orientation (F=100 ％), those on a randomly oriented LNO show a random crystal orientation (F=60 ％). All the PZT layer have a flat and dense microstructure with large columnar grains and their grain size are 25 nm. In the ferroelectric curves at electric field of 40 kV/cm, a highly (100) oriented PZT/LNO samples show coercive field, E/sub c/=10 kV/cm and remanent polarization, P/sub r/=14.5 μC/㎠, while a randomly oriented PZT/LNO sample show E/sub c/=10 kV/cm and P/sub r/=5.4 μC/㎠.

• Journal of the Korean Wood Science and Technology
• /
• v.40 no.6
• /
• pp.363-369
• /
• 2012

Shear tests parallel to the grain were conducted on domestic wood samples with different growth ring orientations. Shear strength was dependent on the angles between the direction of growth ring orientation and the applied force. The maximum shear strength showed at the intermediate growth ring orientations. Results of shear tests were also used to modify the formula which had previously been developed to predict the withdrawal strength of screw on the face of lumber. Predicted equations were fitted to the results of previous study with different length of No. 8 screw. Predicted equation was under-predicted the withdrawal strength of 25 and 30 mm length of screw within 8% and over-predicted withdrawal strength of 18 and 38 mm length of screw. A little differences between the predicted by shear strength with different growth ring orientation and observed values was existed.

• Journal of the Korean Magnetics Society
• /
• v.9 no.4
• /
• pp.196-202
• /
• 1999

The magnetic properties and the microstructures of the Mn-Ir/Ni-Fe multilayers with various stacking structures and buffer layer materials have been investigated. The (111) texture of Mn-Ir/Ni-Fe was observed in the top structures with Ta, Zr, or Ti buffer materials. However, all Mn-Ir/Ni-Fe multilayers with top structures exhibit high $H_{ex}$, regardless of the (111) preferred orientation of Mn-Ir film. The samples whose high $H_{ex}$ observed grain-to-grain epitaxial tendency and the large grain of Mn-Ir film at the interface. It can be explained that the $H_{ex}$ does not depend on the (111) texture of the Mn-Ir film and the interface roughness, but depends on the grain size of the Mn-Ir film and the morphology of the interface between the Mn-Ir and the Ni-Fe grains, and the $H_c$ depends on the interface roughness between the Mn-Ir and the Ni-Fe films.

• The Journal of the Korea institute of electronic communication sciences
• /
• v.8 no.4
• /
• pp.549-554
• /
• 2013

With the synthesis of graphene on Cu using CVD, it was tried to show the behavior of graphene growth depending on the size and orientation of Cu grain. It was found out that even under the same temperature and pressure the use of different gases influences on the diffusion rate of Cu. As compared to Ar gas, Cu grain growing bigger under $H_2$ and $CH_4$ was resulted in bigger graphene grain. Corrosion resistance was evaluated by potentiodynamic polarization test in room temperature and found out that the graphene on Cu was more stable in order of 10 than pure Cu due to the chemical stability of graphene. The future work of this research will focus on the synthesis of graphene having no defects including grain boundaries, and its engineering use.

• Korean Journal of Materials Research
• /
• v.4 no.7
• /
• pp.750-758
• /
• 1994

The purpose of present study is to find out the formation mechanism of hemi-spherical grained(HSG) polysilicon film. Silicon film was deposited using LPCVD. Polycrystalline silicon film was deposited at $575^{\circ}C$ contained crystalline HSG in the amorphous matrix phase. The crystalline HSG can be categorized into two grains : lower grains and upper grains. Lower grains are located at interface between silicon dioxide and silicon film, and upper grains are located at surface. The growth orientations of HSG were identified as (311) or (111) directions for lower grains and perferentially (110) direction for upper grains. This difference of growth orientations seems to be caused by the difference of formation mechanisms. That is, lower grain is formed by soild phase crystallization, on the other hand, upper grain is formed by surface diffusion of silicon atoms. It was thus, proposed that the formation of practical HSG polysilicon film is mainly controlled by surface diffusion of silicon atoms.

• Journal of the Korean Magnetics Society
• /
• v.11 no.4
• /
• pp.146-150
• /
• 2001

The effect of H$_2$ content in Ar sputtering gas on exchange coupling field(H$_{ex}$) for NiFe/FeMn interface was studied. When NiFe layer of Si(100)/Ta(50 $\AA$)/NiFe(60 $\AA$)/FeMn(250 $\AA$)Ta(50 $\AA$) was deposited at 8% H$_2$ in sputtering gas, the maximum exchange coupling field(H$_{ex}$) and minimum coercivity(H$_{c}$) were obtained. When Si(100)/Ta(50 $\AA$)/NiFe(60 $\AA$)/FeMn(250 $\AA$)/NiFe(70 $\AA$)/Ta(50 $\AA$) was deposited at 5% H$_2$ in sputtering gas, the maximum exchange coupling field(H$_{ex}$) of 148 Oe was obtained. The (111) preferred orientation and grain size of underlayer NiFe were increased and the internal stress was reduced by H$_2$ in sputtering gas. And the (111) preferred orientation and grain size of FeMn layer were also increased.d.ased.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.40 no.7
• /
• pp.653-658
• /
• 2016

High pressure components of a gas turbine engine are generally made of nickel-base superalloys, using precision casting process due to complicated geometries with intricate channels and cooling holes. Turbine components manufactured from directionally solidified and single crystal materials have columnar grains; however, it is found that the crystals do not grow in its preferred direction, although the orientation can be controlled. This anisotropy can lead to the variations of elastic and Hill's parameters in constitutive equations, and they alter stress distributions and the low cycle fatigue life. We aims to evaluate the effects of perturbed crystal orientations on the structural integrity of a directionally solidified nozzle using low cycle fatigue life. We also attempt to show the necessity for the control of allowed manufacturing errors and stochastic analysis. Our approaches included conjugate heat transfer and structural analysis, along with low cycle fatigue life assessment.