• Journal of Nuclear Fuel Cycle and Waste Technology(JNFCWT)
• /
• v.18 no.4
• /
• pp.509-516
• /
• 2020

An important property of glass and ceramic solid waste forms is processability. Tellurite materials with low melting temperatures and high halite solubilities have potential as solid waste forms. Crystalline TiTe3O8 was synthesized through a solid-state reaction between stoichiometric amounts of TiO2 and TeO2 powder. The resultant TiTe3O8 crystal had a three-dimensional (3D) structure consisting of TiO6 octahedra and asymmetric TeO4 seesaw moiety groups. The melting temperature of the TiTe3O8 powder was 820℃, and the constituent TeO2 began to evaporate selectively from TiTe3O8 above around 840℃. The leaching rate, as determined using the modified American Society of Testing and Materials static leach test method, of Ti in the TiTe3O8 crystal was less than the order of 10-4 g·m-2·d-1 at 90℃ for durations of 14 d over a pH range of 2-12. The chemical durability of the TiTe3O8 crystal, even under highly acidic and alkaline conditions, was comparable to that of other well-known Ti-based solid waste forms.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.65 no.5
• /
• pp.819-824
• /
• 2016

The accelerated thermal aging of CSPE (chlorosulfonated polyethylene) was carried out for 33.64 and 67.27 days at 110[$^{\circ}C$], equivalent to 40 and 80 years of aging at 50[$^{\circ}C$], respectively. These samples were referred to as CSPE-0y, CSPE-40y and CSPE-80y, respectively. As the accelerated thermally aged years of the CSPE increase, the insulation resistance[$\Omega$] at 20[Hz], 500[Hz], and 2[KHz], and the percent elongation [%EL] of the CSPE decrease. However, the dissipation factor($tan{\delta}$) at 20[Hz], 500[Hz], and 2[KHz], the apparent density[$g/cm^3$], the glass transition temperature and the melting temperature of the CSPE were increased. The period of time that the voltage has to be applied until electric breakdown of the CSPE-0y is longer than that of the CSPE-40y, and the CSPE-80y, but the dielectric strength of the CSPE-80y is lower than that of the CSPE-0y and the CSPE-40y. The differential temperatures after the AC and DC voltages are applied to CSPE-0y, CSPE-40y and CSPE-80y are 0.026~0.028[$^{\circ}C$], 0.030~0.042[$^{\circ}C$], 0.018~0.045[$^{\circ}C$], respectively. The variations of temperature for the AC voltage are higher than those for the DC voltage when an AC voltage is applied to CSPE-0y, CSPE-40y and CSPE-80y. It is found that the dielectric loss owing to the dissipation factor[$tan{\delta}$] is related to the electric dipole conduction current. It is ascertained that the ionic (electron or hole) leakage current is increased by the separation of the branch chain of CSPE polymer from the main chain of the polyethylene as a result of thermal stress due to accelerated thermal aging as well as by conducting ions such as $Na^+$, $Cl^-$, $Mg^{2+}$, $SO_4^{2-}$, $Ca^{2+}$ and $K^+$ after seawater soaking.

• Journal of the Korean Wood Science and Technology
• /
• v.32 no.5
• /
• pp.29-38
• /
• 2004

In this study, we investigated the thermal properties of corn-starch filled polybutylene succinate-adipate (PBS-AD) bio-composites. Thermal analysis (TA) is used to describe the analytical method for measuring the chemical property and weight loss of composite materials as a function of temperature. The thermal stability of corn-starch was lower than that of pure PBS-AD. As corn-starch loading increased, the thermal stability and degradation temperature of the bio-composites decreased and the ash content increased. It can be seen that the degree of compatibility and interfacial adhesion of the bio-composites decreased because of the increasing mixing ratio of the corn-starch. As the content of corn-starch increased, there was no significant change in the glass transition temperature (T_g) and the melting temperature (T_m) for the bio-composites. The storage modulus (E') and loss modulus (E") of the corn-starch flour filled PBS-AD bio-composites were higher than those of PBS-AD, because of the incorporation of corn-starch increased the stiffness of the bio-composites. At higher temperatures, the decreased storage modulus (E') of bio-composites was due to the increased polymer chain mobility of the matrix polymer. From these results, we can expect that corn-starch has potential as a reinforcing filler for bio-composites. Furthermore, we recommend using a coupling agent to improve the interfacial adhesion between corn-starch and biodegradable polymer.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.15 no.6
• /
• pp.3990-3996
• /
• 2014

Because the physical properties can be decreased when a Nylon 66/glass fiber composite is injected into a mold over $300^{\circ}C$, a systematic study of the thermal history in the case of re-use is needed. Nylon 66/glass fiber extrudates as a function of the extrusion number were prepared using a twin screw extruder at 305/290/273/268/265/$260^{\circ}C$. The chemical structure, thermal properties, melt index, crystal structure, Izod impact strength, and rheological properties were measured by Fourier transform infra-red (FT-IR), melt indexer, DSC, TGA, XRD, Izod impact tester, and dynamic rheometer. The FT-IR spectra indicated that the number of extrusions did not affect the chemical structure. The decrease in molecular weight with increasing extrusion number was confirmed by the melt index and the complex viscosity of extrudates. Based on the DSC and TGA results, the thermal history had no effect on the melting temperature, regardless of the number of extrusions, but the degradation temperature decreased up to $20^{\circ}C$ with increasing extrusion number. The Izod impact strengths of the extrudates were found to decrease with increasing extrusion number. No structural change after extrusion was also confirmed because there was no change in the slope and shape of the G'-G" plot.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.29 no.5
• /
• pp.208-214
• /
• 2019

The glass of $BaO-GeO_2-La_2O_3-ZnO$ system with a transmittance of more than 75 % at mid-wave infrared (MWIR) region in the range of $3{\mu}m$ to $5{\mu}m$ is manufactured and its property is evaluated. After selecting construction that can melt glass through flow button test, $BaO-GeO_2-La_2O_3$ system where 10 mol%, 20 mol% of ZnO were added respectively were melted at $1350^{\circ}C$ for 1 hour and $BaO-GeO_2-La_2O_3$ system of glass was manufactured. Among them, with 20 mol% of ZnO, 16 mol% BaO-56 mol% $GeO_2-8mol%$ $La_2O_3-16mol%$ ZnO system of glass was found to has less than $660^{\circ}C$ of glass transition temperature, more than 1.70 of refractive index, and more than 530 of knoop hardness. Therefore, it is concluded that glass of $BaO-GeO_2-La_2O_3-ZnO$ system of glass with 20 mol% ZnO has good melting conditions at low temperatures and excellent optical properties, thus, can be utilized for special optical materials field.

• Applied Chemistry for Engineering
• /
• v.8 no.3
• /
• pp.454-462
• /
• 1997

Thermotropic block copolyester(TLCP-b-PBN) based on poly(tetramethylene 2,6-(naphthaloyldioxy)dibenzoates)(TLCP) and poly(butylene 2,6-naphthalate)(PBN) was synthesized by solution polycondensation and melt-blended with poly(ethylene 2,6-naphthalate)(PEN) for in-situ composites. The TLCP domains showed nematic behavior in melt. The composition of block copolymer was determined from $^1H-NMR$ spectroscopy. The DSC thermogram of block copolymer revealed the presence of two major melting transitions, corresponding to the separete melting of PBN and TLCP domains. The glass transition temperature(Tg) of the PEN in the blends decreased with increasing the content of TLCP-b-PBN and the TLCP-b-PBN acted as a nucleating agent for the matrix polymers. In the 20% TLCP-b-PBN blend, well oriented TLCP fibriles were observed at temperature above the melting point of the PEN by optical microscopy. By scanning electron micrographs of cryogenically fractured surfaces of extruded blends, the TLCp domains were found to be finely and uniformely dispersed in 0.15 to $0.2{\mu}m$ size. Interfacial adhesion between the TLCP and matrix polymer was seemed to be good. Under certain condition TLCP formed a fiver structure in the PEN matrix, with thin oriented TLCP fibril in the skin region and spherical TLCP domains in the core.

• Journal of Nuclear Fuel Cycle and Waste Technology(JNFCWT)
• /
• v.14 no.2
• /
• pp.169-178
• /
• 2016

The properties of wastes for melting need to be considered to minimize the maintenance of refractory and to discharge the molten slags smoothly from a plasma torch melter. When the nonflammable wastes from nuclear facilities such as concrete debris, glass, sand, etc., are melted, they become acid slags with low basicity since the chemical composition has much more acid oxides than basic oxides. A molten slag does not have good characteristics of discharge and is mainly responsible for the refractory erosion due to its low liquidity. In case of a stationary plasma torch melter with a slant tapping port on the wall, a fixed amount of molten slags remains inside of tapping hole as well as the melter inside after tapping out. Nonmetallic slags keep the temperature higher than melting point of metal because metallic slags located on the bottom of melter by specific gravity difference are simultaneously melted when dual mode plasma torch operates in transferred mode. In order to minimize the refractory erosion, the compatible refractories are selected considering the temperature inside the melter and the melting behavior of slags whether to contact or noncontact with molten slags. An acidic refractory shall not be installed in adjacent to a basic refractory for the resistibility against corrosion.

• Journal of the Korean Chemical Society
• /
• v.37 no.6
• /
• pp.570-576
• /
• 1993

1-, 3-, 9-, and 21-Monolayer Langmuir-Blodgett(LB) films of stearic acid were deposited on silver-coated glass slides at the surface pressure of 30 mN/m. Fourier transform infrared(FTIR) reflection-absorption spectra (RAS) of these LB films were recorded at various temperatures from 31 to $72^{\circ}C.$ The spectra at $31^{\circ}C$ exhibited characteristic features of highly perpendicular orientation of the hydrocarbon chain. In the 1-monolayer LB film, the C=O stretching band was not observed, presumably due to the image dipole effect on the silver surface. In the 1-and 3-monolayer LB films, the trans isomer of stearic acid was prominent, but the cis isomer was dominant in the 21-monolayer LB film. FTIR-RAS measurements at an elevated temperature indicated that the chain melting temperature increases and approached to the bulk melting point with increasing the number of monolayer, except for the 1-monolayer LB film which has a higher melting temperature than the 3-monolayer film due to the strong interaction with the silver substrate.

• Journal of Periodontal and Implant Science
• /
• v.40 no.3
• /
• pp.125-131
• /
• 2010

Purpose: Among available biomaterials, bioceramics have drawn special interest due to their bioactivity and the possibility of tailoring their composition. The degradation rate and formulation of bioceramics can be altered to mimic the compositions of the mineral phase of bone. The aim of this study was to investigate the bone formation effect of amorphous calcium phosphate glass cement (CPGC) synthesized by a melting and quenching process. Methods: In five male beagle dogs, $4{\times}4$ mm 1-wall intrabony defects were created bilaterally at the mesial or distal aspect of the mandibular second and fourth premolars. Each of the four defects was divided according to graft materials: CPGC with collagen membrane (CM), biphasic calcium phosphate (BCP) with CM, CM alone, or a surgical flap operation only. The dogs were sacrificed 8 weeks post-surgery, and block sections of the defects were collected for histologic and histometric analysis. Results: There were significant differences in bone formation and cementum regeneration between the experimental and control groups. In particular, the CPGC and BCP groups showed greater bone formation than the CM and control groups. Conclusions: In conclusion, CPGC was replaced rapidly with an abundant volume of new bone; CPGC also contributed slightly to regeneration of the periodontal apparatus.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.36 no.6
• /
• pp.591-598
• /
• 2012

In this study, the cutting characteristics of bulk metallic glass (BMG) cut using a computer numerically controlled (CNC) lathe were investigated for different insert tool materials and cutting speeds. The surface roughness, chip morphology, cutting forces, and tool wear during turning of $Zr_{50}Cu_{40}Al_{10}$ BMG alloy were examined. Four kinds of tool materials were used to cut an 8-mm-diameter BMG. The examination of the surface roughnesses of the BMG specimens machined at each cutting speed showed that the surface roughness became better as the cutting speed increased, and the tool materials also influenced the surface roughness. The chip morphology investigations showed that the unoxidized BMG chips had serrated curled chips with adiabatic shear bands, while the oxidized chips exhibited local melting and tangling rather than the usual spiral-shaped chips. The cutting force induced during machining of the Zr-based BMG was the largest for the TiN-WC tool, followed by the polycrystalline diamond (PCD) tool. The cermet tool exerted the smallest cutting force.