• Proceedings of the KSME Conference
• /
• 2004.04a
• /
• pp.186-191
• /
• 2004

we can say that the increasing range of the value of GMT Sheet's tensile strength in the direction of fiber orientation is getting wider as the fiber content increases. It shows that the value of GMT Sheet's tensile strength in the direction of fiber orientation 90 is similar with the value of pp's intensity when fiber orientation function is J= 0.7, regardless of the fiber content. Tensile strength of GMT Sheet is affected by the fiber orientation distribution more than by the fiber content.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.29 no.8
• /
• pp.489-493
• /
• 2016

In this study, the effect of vanadium oxide ($V_2O_5$) content and pre-sintering atmosphere on sealing property of glass frit that consisted of $V_2O_5-BaO-ZnO-P_2O_5-TeO_2-CuO-Fe_2O_3-SeO_2$ was investigated by XPS (X-ray photoelectron spectroscopy). The content of V2O5 was changed to 15, 30, and 45 mol%, and the pre-sintering was carried out in air and $N_2$ condition, respectively. XPS analysis conducted before and after laser irradiation with identical sample. Before laser treatment, glass frits that were pre-sintered at air condition showed both $V^{4+}$ and $V^{5+}$, but the valence state was changed to $V^{5+}$ after laser irradiation when the glass frits contained 30 and 45 mol% $V_2O_5$; this change led to non-adhesive property. On the other hand, glass frits that were pre-sintered at $N_2$ condition exhibited only $V^{4+}$ and it showed fine adhesion irrespective of the $V_2O_5$ content. As a result, the existence of $V^{4+}$ seems to be a major factor for controlling the adhesive property of glass frit for laser sealing.

• Proceedings of KOSOMES biannual meeting
• /
• 2017.11a
• /
• pp.206-206
• /
• 2017

• Proceedings of the Korea Concrete Institute Conference
• /
• 2001.11a
• /
• pp.93-98
• /
• 2001

Using waste glass in concrete can cause crack and strength loss by the expansion of alkali-silica reaction(ASR). In this study, ASR expansion and properties of strength were analyzed in terms of clear waste glass grading, and by-products(fly ash, blast-furnace slag) and by-products content for reduction ASR expansion due to waste glass. In this accelerated ASTM C 1260 test of waste glass, pessimum grading can be found. Also, when the by-products are used with waste glass, there is an effect on reduction of expansion and strength loss due to ASR between the alkali in the cement paste and the silica in the waste glass.

• Journal of the Korean Ceramic Society
• /
• v.29 no.1
• /
• pp.35-40
• /
• 1992

Porous glass in the ZrO2-SiO2 system containing up to 30 mol% zirconia were prepared from the mixed solutions of Zr(O.nC3H7)4 and partially prehydrolyzed TEOS by the sol-gel method. Pore characteristics, physical properties and alkali resistance were investigated. The gels converted into the porous glass by heating at $700^{\circ}C$, it was found that the glass like skeleton was already made up in lower temperature regions. The specific surface area of the porous glass was 227 $m^2$/g, average mean pore size was about 19$\AA$ and porosity was 19.2%, pore characteristics and physical properties depended on heating temperature. Alkali resistance of the porous glass increased as the zirconia content increased, because of the appearance of Zr-enriched layer at glass surface.

• Advances in concrete construction
• /
• v.8 no.1
• /
• pp.1-7
• /
• 2019

The possibility of using recycled coarse glass aggregates as a substitute for natural crushed stone are relatively limited. In order to promote it for engineering application, this paper reports the effect of coarse glass aggregate on mechanical behavior of concrete. The coarse aggregates are substituted for coarse glass aggregate (CGA) as 0%,20%,40%,60%,80% and 100%.The results show that increasing the coarse glass aggregate content cause decrease in compressive strength, the elastic modulus, the splitting tensile strength, the flexural strength. An equation is presented to generate the relationship between cube compressive strength and prism compressive strength, the relationship between cube compressive strength and elastic modulus, the relationship between cube compressive strength and splitting tensile strength, the relationship between cube compressive strength and flexural strength of coarse glass concrete.

• Journal of the Korean Ceramic Society
• /
• v.40 no.3
• /
• pp.229-233
• /
• 2003

By using an oxynitride glass as a sintering additive, the effects of BN content on microstructure and mechanical properties of the hot-pressed and subsequently annealed SiC-BN composites were investigated. The microstructures developed were analyzed by image analysis. The morphology of SiC grains was strongly dependent on BN content in the starting composition. The aspect ratio of SiC decreases with increasing BN content and the average diameter of SiC shows a maximum at 5 wt% BN and decreases with increasing BN content in the starting powder. The fracture toughness increased with increasing BN content while the strength decreased with increasing BN content. The strength and fracture toughness of SiC or SiC-TiC composites were strongly dependent on the morphology of SiC grains, but the strength and fracture toughness of SiC-BN composites were strongly dependent on BN content rather than morphology of SiC grains. These results suggest that fracture toughness of SiC ceramics can be tailored by manipulating BN content in the starting composition. Typical fracture toughness and strength of SiC-10 wt% BN composites were 8 MPa$.$m$\^$1/2/ and 445 MPa, respectively.

• Proceedings of the Korean Fiber Society Conference
• /
• 1996.10a
• /
• pp.468-472
• /
• 1996

A series of UV-curable polyurethane acrylate ionomer were synthesized from isophorone diisocyanate(IPDI), poly(tetramethylene ether glycol)(PTMG), 2,2-bis(hydroxymethyl)propionic acid (CMPA), triethylamine(TEA), 2-hydroxy ethyl acrylate (HEA), and dibutyl tin dilaurate (DBT) as a catalyst. 2,2-dimethoxy-2-phenyl acetophenone(DMPAP) was used as a photoinitiator. The films of UV-cured polyurethane acylate ionomer were prepared by casting the formulated materials onto a glass plate at room temperature and cured using a medium pressure mercury lamp (80 W/cm, max = 365nm). Effects of DMPA content, molecular weight of PTMG and degree of neutralization on the properties were invesigated. It is found that the storage modulus increased with increasing DMPA content. The glass transition temperature of sample A shifted to higher temperature as the content of DMPA was increased. Tensile modulus also increased with increasing DMPA content. Modulus and Tg decreased with increasing molecular weight of PTMG form 650 to 2000. With increasing the degree of nutralizaion, ionomers exhibited improved modulu.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.29 no.6
• /
• pp.298-307
• /
• 2019

Two types of CaO-Al₂O₃-SiO₂ (CAS) glass powder applied spray coating on the surface of sintered Al₂O₃ were researched for sintering behavior; (1) Si-rich, glass containing high content SiO₂, (2) Ca-rich, containing high content CaO. Foaming of bubbles remaining inside the Ca-rich glass was produced at a viscosity of approximately 10⁷~10⁹ poise, resulting in decreasing shrinkage (interfering with sintering) and increasing surface roughness. In case of Si-rich glass, there was no serious foaming bubbles phenomenon like Ca-rich below 1000℃, however cristobalite crystals with low density occurred at 1200℃ and then produced re-foaming of bubbles, resulting in abnormal sintering behavior. These phenomenon is considered to be a decrease in viscosity due to an increase in the Ca content of the glass according to the formation of low-density cristobalite crystals. Therefore, in case of CAS glass, it is necessary to consider the increase of surface roughness and the sintering interference because of foaming bubbles phenomenon at low temperature sintering. Especially, when containing high SiO₂ content, abnormal foaming phenomenon due to crystallization at high temperature should be predicted.

• Journal of Welding and Joining
• /
• v.21 no.1
• /
• pp.107-113
• /
• 2003

Joining of $Si_3N_4$ to $Si_3N_4$ with crystallized glass solder was studied. $SiO_2-Al_2O_3-MgO$ glass with $P_2O_5$ as a crystallizing reagent was used as a solder. To improve the hish temperature toughness of joined specimen, two stage heat treatment was applied to Joined sample for the crystallization of joined layer, Two factors, i.e. thickness of soldered layer and crystallization were taken and thier effects on joining strength were investigated by a SEM-EDX observation of joined interface and bending strength both at room and elevated temperatures. Obtained results are summarized as follows: (1) Nitrogen diffused from $Si_3N_4$ to solder during the Joining process. Average amount of nitrogen in soldered layer depended on the thickness of the soldered layer and increased with decrease of the thickness. (2) Joining strength of the specimen having a thinner soldered layer was stronger than that of thicker layer. This can be mainly attributed to the difference of the nitrogen content in the soldered layer. (3) Higher content of nitrogen in solder brought forth higher viscosity of the solder. Hence the crystallization of the solder become more difficult in thinner layer of the solder than thicker one. (4) Thus, the effect of crystallization was evaluated mostly by the thicker layer specimen. Crystallization of soldered layer improved markedly the fracure strength of joining at higher temperatures than the softening temperature of glass solder.