• Korean Journal of Materials Research
• /
• v.24 no.12
• /
• pp.710-714
• /
• 2014

The effect of titanium dioxide ($TiO_2$) on the properties of color conversion glasses was examined for glasses based on $BaO-ZnO-B_2O_3-SiO_2$. One glass sample, containing 25 mol% of each component, was used as a reference; the other three glass samples contained 1, 3, and 5 mol% $TiO_2$, respectively. The four color conversion glass samples were prepared by sintering a mixture of glass frits and a $YAG:Ce^+$ phosphor. The characteristics of the color conversion glass samples, such as luminous efficacy, luminance, CIE (Commission International de I'Eclairage) chromaticity, CCT (Correlated Color Temperature), and CRI (Color Rendering Index) were analyzed according to the PL spectrum. The refractive index of the glass samples was found to increase with the titanium dioxide content. In conclusion, luminous efficacy of color conversion glasses increased as the content of $TiO_2$ was raised in the glass matrix.

• Journal of the Korean Ceramic Society
• /
• v.48 no.1
• /
• pp.74-79
• /
• 2011

The pore generation technology using GHM (Glass Hollow Microsphere) was studied in order to reduce the weights of porcelain. In this study, we verify the property of modified slurry by adding GHM. The modified slurry was prepared by adding 1.0~2.5 wt%(K1), 1.0~6.0 wt%(K37) of GHM to the slurry for porcelain. The slurry viscosity were stable inside a content range of 1.0~2.5 wt%(K1), 1.0~6.0 wt%(K37). However, the viscosity of modified slurry increased more than 3.0 wt%(K1) and 6.5 wt%(K37). The formed specimen by slip casting was fired at $1229^{\circ}C$, $1254^{\circ}C$. As the amount of GHM content increased, the weight decreased and the addition of 1.0~2.5 wt%(K1), 1.0~6.0 wt%(K37) of GHM resulted in a weight drop of 30%(K1) and 25(K37). However, when the GHM content increased, the strength decreases over 70%. This is caused by the presence of a large volume of surface defects (pores) and defects from the agglomeration of GHM.

• Journal of Korean Ophthalmic Optics Society
• /
• v.18 no.4
• /
• pp.365-371
• /
• 2013

Purpose: In this study, we evaluated the physical and thermal properties of the compositions made by blending glass fiber (GF) of different contents into glass fiber polyamide-66, and investigated if the compositions applying to the glasses frame to replace the TR-90, which is polyamide-12 resin used as an injection-type spectacle frame material. Methods: To investigate the characteristics change of polyamide-66 (PA-66) compositions with the change of the content of glass fibers, we produced a composition of the content by using a twin-screw extruder. The mechanical strength of the composition production was measured and coating properties as well as cutting processability were evaluated. We evaluated the applicability of the glasses frame by comparison the results of new compositions with characterizations of traditional TR. Results: For the results of the characterization of Polyamide-66/GF composition, we found that the higher increase of content of the glass fiber, the less mold shrinkage rate, and the mechanical strength was increased. Tensile strength increased from $498kg/cm^2$ for 0 wt% of the content of the glass fibers to $849kg/cm^2$ for 30 wt% of the content of the glass fibers. As a result of a coating evaluation, the strength of coating was 4B in the GF 5wt% and 5B, which was extremely good coating characteristics, in the over than GF 5 wt%. Conclusions: In case that 30 wt% of the glass fiber was blended, the mechanical strength was greatly improved, the hardness was increased, injection temperature increased due to increase of the viscosity, and the flow mark of the product may occur. The paint coating of PA-66 blended with glass fiber was all excellent. With general evaluating physical properties and workability properties it was determined that around 10 wt% of the content of the glass fibers was possible to apply a spectacle frame.

• Journal of the Korean Ceramic Society
• /
• v.36 no.12
• /
• pp.1350-1355
• /
• 1999

Sintering characteristics and dielectric properties of low temperature sinterable Glass/Ceramic dielectric materials were investigated. The dielectric materials which were developed for microwave frequency applications consist of SiO2-TiO2-Bi2O3-RO system(RO:BaO-CaO-SrO) crystallizable glass and Al2O3 as a ceramic filler. Sintering experiments showed that no more densification occurred above 80$0^{\circ}C$ and bulk density and shrinkage depended on Al2O3 content only. Results of dielectric measurements showed that $\varepsilon$r Q$\times$f and $\tau$f of the material containing 30wt% Al2O3 were 17.3, 600 and +23 ppm respectively. Those values for 45 and 60wt% Al2O3 samples were 11.6, 1400, +0.7 ppm and 7.2, 2000, -8.5 ppm, repectively. The results clearly showed that the Glas/Ceramic materials of present experiment decreased in $\varepsilon$r and increased in $\times$f value and changed from positive to negative value in $\tau$f value with the increasement of Al2O3 content.

• The Journal of the Korea Contents Association
• /
• v.13 no.7
• /
• pp.141-149
• /
• 2013

Recently, the time in which children moves by car become frequent, they stay longer in the car because leisure life including camping and etc. increased. Children whose physical activities are active were subject to restriction because of the limited car boarding visual space and on security. Because of limited space in cars, domestic and foreign automotive companies show the different glass roof applied in cars that exhibited wide clear view in order to remove tedious and stuffy of children while they stay for a long time inside the car. In addition, the potential probability in which the Smart Car that the IT technology is grafted research and research that it utilizes the door window glass as the display is progressed and which the glass roof can be used as the screen can be sufficient. In this study, the in-vehicle display application case and Smart Devices constellation application were benchmarked. The car glass roof application method of the constellation studying content which performed the user survey for the child by the car with the parents whose movement is frequent and considers the child and fundamental interaction way tried to be drawn and we try to propose.

• Journal of the Korean Ceramic Society
• /
• v.28 no.4
• /
• pp.324-328
• /
• 1991

Monolithic silica gel and glass were prepared from TMOS solution with high concentration of HCl. Appearance of the dried gels and gelation time varied with content of HCl and H2O were observed in the TMOS-CH3OH-HCl-H2O system. The conversion from gel to glass during heat treatment stage was investigated using TG-DTA, XRD, IR and SEM and characteristics of the gel were examined by measuring bulk density, linear shrinkage and Vicker's hardness. A transparent silica glass was prepared from the gel after heat treatment at 1050℃.

• Journal of Conservation Science
• /
• v.29 no.3
• /
• pp.279-286
• /
• 2013

It is characterized and classified as the type of red brown glass beads to compare the chemical composition and manufacturing technique on the 141 samples in 12 sites of the Three Kingdom Period analyzed until now. It can be divided into three types according to the chemical composition of stabilizers(CaO & $Al_2O_3$) and soda raw materials(MgO & $K_2O$) on the red brown glass beads except one sample. Type I of high alumina glass is identified as the most common types that is 78.6 % of the distribution ratio at analytical samples and is excavated the most from ruin sites. In contrast, type II, 13.6 % of distribution ratio at analytical samples, is about 5 % CaO and $Al_2O_3$, MgO and $K_2O$ at around 1.5 % is similar to the composition of plant ash glass. Type III is that the content of CaO is higher than $Al_2O_3$ and the content of MgO and $K_2O$ is below 1.5 %. It is the same as the composition of natron glass and its share is the lowest as 7.9 %. Of these, type III is divided into two types according to the content of MgO and $K_2O$. It is identified that manufacturing technique of type I and II is drawing and type III is casting method with microscopic investigations. Type II and III is estimated that raw materials is different because is confirmed in the majority of ruins in spite of the fact that distribution ratio is very low. So, red brown glass beads distributed in Korea Peninsula are divided into three types of glass culture.

• Applied Chemistry for Engineering
• /
• v.29 no.1
• /
• pp.112-116
• /
• 2018

In this study, the mixing characteristics of water glass and additives (Si, alkali metal), which are one of the main raw materials of silicate based binder used in the production of molds during casting process, were examined. Molecular structures of water glass, additives and mixtures were analyzed FT-IR and viscosity measurements and their correlation were compared. The addition of Si source to the water glass accelerated the Si networking in the material and increased the viscosity. When the alkali metal was added, the viscosity of the water glass decreased by suppressing the Si networking of the water glass. Viscosities of the water glass and lithium silicate (LS) mixtures increased when the content of LS was less than 20 wt% and gradually decreased when the content was more than 20 wt%. By adding KOH to the water glass, the viscosity could be lowered and it could be used effectively to mix with colloidal silica (CS) or potassium methyl siliconate (PMS).

• Journal of the Korean Ceramic Society
• /
• v.25 no.5
• /
• pp.431-436
• /
• 1988

The properties of scid-resistance to boiling HCl, thermal expansion coefficient and softening temperature of mother glass and glass-ceramic of LAS systems were investigated at the contents of SiO2 varing from 57 to 67wt%. The nucleation and growth of crystalline phase of LAS compositions were carried out at 50$0^{\circ}C$ and $700^{\circ}C$. The crystalline phase jconsists of lithium alumino silicate, lithum meta silicate, lithium disilicate, $\alpha$-crystobalite and $\alpha$-quartz. Lithium alumino silicate(virgilite) is the major crystalline phase in the glass ceramics. The degree of acid resistant property was increased in proportion with the silica content for both glass and ceramics. Glass-ceramic gives lower acid-resistance and thermal expansion coefficient while softening temperature shows higher for glass-ceramic than for mother glass.

• International Journal of Concrete Structures and Materials
• /
• v.18 no.2E
• /
• pp.125-132
• /
• 2006

Waste glass has been increasingly used in industrial applications. One shortcoming in the utilization of waste glass for concrete production is that it can cause the concrete to be weakened and cracked due to its expansion by alkali-silica reaction(ASR). This study analyzed the ASR expansion and strength properties of concrete in terms of waste glass color(amber and emerald-green), and industrial by-products(ground granulated blast-furnace slag, fly ash). Specifically, the role of industrial by-products content in reducing the ASR expansion caused by waste glass was analyzed in detail. In addition, the feasibility of using ground glass for its pozzolanic property was also analyzed. The research result revealed that the pessimum size for waste glass was $2.5{\sim}1.2mm$ regardless of the color of waste glass. Moreover, it was found that the smaller the waste glass is than the size of $2.5{\sim}1.2mm$, the less expansion of ASR was. Additionally, the use of waste glass in combination with industrial by-products had an effect of reducing the expansion and strength loss caused by ASR between the alkali in the cement paste and the silica in the waste glass. Finally, ground glass less than 0.075 mm was deemed to be applicable as a pozzolanic material.