• Applied Science and Convergence Technology
• /
• v.24 no.6
• /
• pp.289-292
• /
• 2015

The etching processes of glass in aqueous hydrofluoric acid (HF) solutions were used to improve the current density of solar cell. In this study, the textured glass substrate has been etched by solution and the $TiO_2$ thin films have been prepared on this textured glass. After the $TiO_2$ film deposition the surface has been etched by HF under different concentration and the etched $TiO_2$ thin films had a longer electron lifetime and higher haze ratio as well as light scattering, resulting in 1.7 times increment of dye-sensitized solar-cell(DSSC) efficiency. Increases in the surface root-mean-square roughness of glass substrates from 80 nm to 1774 nm enhanced haze ratio in above 300 nm wavelength. In particular, haze ratio of etched $TiO_2$ films on textured glass showed gradually increasing tendency at 550 nm wavelength by increasing of HF concentration up to 10M, suggesting a formation of crater with various sizes on its surface.

• Journal of IKEEE
• /
• v.25 no.1
• /
• pp.128-132
• /
• 2021

In this paper, the surface of electrodes used in solar cells was roughened using wet etching method among surface texturing method, and after surface treatment, dye sensitive solar cell using TiO2 oxide semiconductor was produced. The surface spectroscopic properties of surface treated electrodes were analyzed according to etching time, and by evaluating the electrical properties of TiO2 dye-sensitized solar cells produced according to etching time, the study on improving the efficiency of solar cells according to surface treatment was conducted. As a result, solar cells that etched the electrode surface for 10 minutes could see an improvement of about 27.46[%] over their existing efficiency.