• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1209-1210
• /
• 2006

A novel sintering process is proposed for bonding of $BaTiO_3$ and $Al_2O_3$ layers. Common commercial glass was used and infilterated among filler particles. As the kind of commercial glass, the phenomenon of the infilteration is different. Although Sud-1140 glass forms a glass/filler composite, it is not completely infilterated into the filler particles at $900^{\circ}C$. However as the increase of sintering temperature the infilteration of glass was improved. In this study, GA-1 and GA-12 glasses were infilterated the more than Sud-1140 glass. However, they are reacted by $BaTiO_3$ layer. The results of the experiment show that constrained sintering and the co-firing of the different materials were possible for glass infilteration using Sud-1140 glass at $1000^{\circ}C$.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1218-1219
• /
• 2006

The shrinkage variation of Low Temperature Cofired Ceramics(LTCC) limits the size of the substrates that impose limitations on embedded passive components. This paper focuses on the method of minimizing or controlling planar shrinkage and reducing distortion during firing. The laminated sheets of alumina and glass were sintered at varying temperature, and depending on the amount of the glass ceramics. When the sintered of multi-layer structure with $Al_2O_3/Glass/Al_2O_3$, the glass infiltrated entirely into $Al_2O_3$ layer at the temperature of about $950^{\circ}C$ or higher.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.298-299
• /
• 2006

공통의 glass를 이용한 LTCC 이종소재의 무수축 접합 가능성을 확인하기 위하여 2종의 상용 glass를 이용하여 소결온도를 변화시키면서 미세구조 및 결정구조, x-y축 방향의 수축율을 관찰하였다. 실험 결과 GA-12 glass는 강유전체 $BaTiO_3$와 glass의 composite개념을 이용한 접합에 적절하지 않은 것으로 판단되었으며, GA-1 glass의 경우는 $750^{\circ}C$와 $800^{\circ}C$ 사이에서 glass의 충분한 침투조건이 확인되며, 결정구조 에서도 glass/$BaTiO_3$ composite이 형성되므로 layer 간의 delamination은 발견되지만 x-y축 방향의 무수축 접합의 가능성이 확인되었다.