• The Journal of Korean Academy of Prosthodontics
• /
• v.50 no.1
• /
• pp.53-60
• /
• 2012

Purpose: The purpose of this study was to compare Ni-Cr alloy property of gas-oxygen torch soldering and infrared welding using optical microscope and Electron Probe Micro Analyzer (EPMA). Materials and methods: Ni-Cr alloys were casted for specimens. Specimens had 3.0 mm diameter, 30.0 mm length and were divided into two groups. Each group had 4 specimens. One group was for gas-oxygen torch soldering and the other was infrared welding. Specimens were cut with low-speed disc and soldered each other with gas-oxygen torch and infrared machine. After soldering and polishing, specimens were observed at 3 points (soldering point, 5 mm distance point, 10 mm distance point) with optical microscope and analyzed 3 points (soldering point, 5 mm distance point, 10 mm distance point with EPMA. Results: The results of this study were as follows: 1. The observation of gas-oxygen torch soldering at 10 mm distance point under the optical microscope was not founded any specific surface properties, but some crack lines were observed at 5 mm distance and soldering point. 2. There were no crack lines were founded at the observation of infrared welding at 10 mm distance and 5 mm distance points under the optical microscope. However, at the 5 mm distance, the surface was not smooth enough compared with at 10 mm distance point. Some crack lines were observed at the welding point as well. 3. In the EPMA analysis of the gas-oxygen torch soldering, the component of Ni was increased by 4.5%, Cr was increased by 7.5% than that of the Ni-Cr alloy at the 10.0 mm distance. At the 5 mm distance, the component of Ni was decreased by 6.1%, Mo was increased by 9.0% than that of the Ni-Cr alloy but Cr was equally shown at the 5.0 mm distance. Only Ni was shown at the soldering point. 4. In the EPMA analysis of the infrared welding, the component of Ni was increased by 9.1%, Cr was increased by 0.4% than that of the Ni-Cr alloy but Al was equal at the 10.0 mm distance. At the 5 mm distance, the component of Ni was increased by 4.7%, Cr was increased by 4.7% and Al was increased by 0.1% than that of the Ni-Cr alloy. At the welding point, the component of Ni was increased by 8.8%, Cr was increased by 8.2% than that of the Ni-Cr alloy. Conclusion: From these results, at the 5 mm distance from the soldering point, the surface of the infrared welding was more smoother than that of the gas-oxygen torch soldering. On the EPMA analysis, the component of the specimens with infrared welding was more similar than that of the gas-oxygen torch soldering compared with the component of the Ni-Cr alloy.

• The Journal of Advanced Prosthodontics
• /
• v.2 no.4
• /
• pp.117-121
• /
• 2010

PURPOSE. The present study was intended to evaluate the effect of soldering techniques with infrared ray and gas torch under different gap distances (0.3 mm and 0.5 mm) on the tensile strength and surface porosity formation in Ni-Cr base metal alloy. MATERIALS AND METHODS. Thirty five dumbbell shaped Ni-Cr alloy specimens were prepared and assigned to 5 groups according to the soldering method and the gap distance. For the soldering methods, gas torch (G group) and infrared ray (IR group) were compared and each group was subdivided by corresponding gap distance (0.3 mm: G3 and IR3, 0.5 mm: G5, IR5). Specimens of the experimental groups were sectioned in the middle with a diamond disk and embedded in solder blocks according to the predetermined distance. As a control group, 7 specimens were prepared without sectioning or soldering. After the soldering procedure, a tensile strength test was performed using universal testing machine at a crosshead speed 1 mm/min. The proportions of porosity on the fractured surface were calculated on the images acquired through the scanning electronic microscope. RESULTS. Every specimen of G3, G5, IR3 and IR5 was fractured on the solder joint area. However, there was no significant difference between the test groups (P > .05). There was a negative correlation between porosity formation and tensile strength in all the specimens in the test groups (P < .05). CONCLUSION. There was no significant difference in ultimate tensile strength of joints and porosity formations between the gas-oxygen torch soldering and infrared ray soldering technique or between the gap distance of 0.3 mm and 0.5 mm.

• The Journal of Korean Academy of Prosthodontics
• /
• v.34 no.1
• /
• pp.143-150
• /
• 1996

The purpose of this study was to evaluate the tensile strength of solder joint between gold alloy and nickel-chromium alloy. The specimens were made with type III gold alloys and Ni-Cr-Be alloy and Degular Lot 2 solder. Eighteen paired specimens were made, and subdivided into three groups. Group I specimens were gold alloy-gold alloy combination, Group II specimens were gold alloy-Ni-Cr alloy combination, Group III specimens were Ni-Cr alloy-Ni-Cr alloy combination. Solder block were made with solder investment(Degussa A,G, Germany) and stored in room temperature for 24 hours. To reduce the formation of metallic oxide and increase wetting properties, flux was used before preheating and soldering procedure. The specimens were preheated at $650^{\circ}C$ and flux were applied again and gas-oxygen torch was used to solder the specimen. All soldered specimens were subjected to a tensile force in the Instron universal testing machine : the crosshead speed was 1 mm/mim. Tensile strength values of three soldered joint groups were 1. Gold alloy-Gold alloy solder joint : $$48.8kg/mm^2$$ 2. Gold alloy-Ni-Cr alloy solder joint : $$30.9kg/mm^2$$ 3. Ni-Cr alloy-Ni-Cr alloy solder joint : $$31.8kg/mm^2$$ The microscopic examination of fracture site showed cohesive and combination fracture modes in gold alloy specimens, but showed all adhesive fracture modes in Ni-Cr alloy containing specimens.