• Journal of Welding and Joining
• /
• v.19 no.5
• /
• pp.512-519
• /
• 2001

Sink roll has been used in molten Zn-0.2%Al alloy bath of continuous galvanizing line in sinking and stabilizing process of the steel strip in molten metal bath. In this process, although the scraper scraps off the sink roll surface, the dross compounds is builded up on the sink roll surface and the life time of the sink roll is shorten by the dross compounds. The present study was investigated the application of the spray coating layer on sink roll body for improving durability In molten Zn-0.2%Al alloy. Through the durability tests in molten Zn-0.2%Al alloy with various ceramic and cermet coating layer, the optimum bond and top coating material was obtained. As the results, the system of STS430F base metal, WC-l7Co bond and $ZrO_2-SiO_2$ top coating was clarified to be the best quality of durability in molten Zn-0.2%Al alloy.

• Journal of the Korean institute of surface engineering
• /
• v.34 no.4
• /
• pp.313-320
• /
• 2001

It is well known that the amount of hot-dip Zn coated sheet steels used for automotive is rapidly increasing. As hot-dip steel sheets show good corrosion resistance and excellent formability, the demand for outer panel of automotive has been increased in order to satisfy with the requirement of high surface qualify. There are many kinds of factors influencing on the surface quality and the dross control in the galvanising bath is regarded as one of the most important thing. In this study the characteristic and growing behavior of dross in the galvanizing bath were investigated and the effect of dross on the surface defect of GA was surveyed. The dross defects on the GA sheet steels result from bottom dross whose diameter are larger 50$\mu\textrm{m}$ in the Zn pot. Dross-free state exist for about 30 hours from starting time of GA production.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 1998.05a
• /
• pp.53-53
• /
• 1998

• Journal of Advanced Marine Engineering and Technology
• /
• v.31 no.2
• /
• pp.173-181
• /
• 2007

Recently, galvanizing method is predominantly being used not only a economical point of view but also due to it s stability and long life. For example, guard rail of high way, all kinds of structures for ship etc. were protected with galvanizing and demand of galvanized structural materials was being increased with more and more. However, galvanized structures were inevitably being deteriorated with time eventually because they were corroded with solution of galvanizing film and exfoliation of it s film in the present severe corrosive environment. Therefore, it is necessary to improve the corrosion resistance of the galvanizing film through various methods such as variation of chemical composition of galvanizing bath, chromate treatment and coating treatment. In this study, three test specimens such as pure galvanizing, galvarium, and chromate treatment were submerged at tap water with inhibitor addition. And the effect of their corrosion resistance improvement was comparatively investigated with electrochemical method. Corrosion current density of the galvanized steel was the largest among three specimens, however, the galvarium steel showed the lowest corrosion current density. Futhermore, these three kinds of test specimens indicated considerably excellent corrosion resistance by dipped at tap water with inhibitor addition. Especially, the galvanized steel showed the best effect of corrosion resistance improvement than other test specimens.

• Corrosion Science and Technology
• /
• v.10 no.1
• /
• pp.6-12
• /
• 2011

The selective surface oxidation of a transformation-induced-plasticity (TRIP) steel containing 1.6 wt.% Mn and 1.5 wt.% Si during annealing at $800^{\circ}C$ was investigated for its influence on the formation of an inhibition layer during hot-dip galvanizing. The selective oxidation of the alloying elements and the oxide morphology were significantly influenced by the annealing atmosphere. The pure $N_{2}$ atmosphere with a dew point $-40^{\circ}C$ promoted the selective oxidation of Mn as a crystalline $Mn_{2}SiO_{4}$ phase, whereas the $N_{2}$ + 10% $H_{2}$ atmosphere with the same dew point $-40^{\circ}C$ promoted the selective oxidation of Si as an amorphous Si-rich oxide phase. During hot-dip galvanizing, the $Mn_{2}SiO_{4}$ phase was reduced more readily by Al in the Zn bath than the Si-rich oxide phase. Consequently, the pure $N_{2}$ atmosphere resulted in a higher formation rate of $Fe_{2}Al_{5}$ particles at the Zn/steel interface and better galvanizability than the $N_{2}$ + 10% $H_{2}$ atmosphere.

• Journal of Welding and Joining
• /
• v.18 no.3
• /
• pp.51-59
• /
• 2000

Sink roll has been used in molten 55%Al-Zn alloy bath of continuous galvanizing line for sinking and stabilizing working steel strip in molten metal bath. In the process, the sink roll body inevitably build up dross compounds and pitting on the sink roll surface during 55%Al-Zn alloy coated strip production, and the life time of the sink roll is shorten by build up dross compounds and pitting. The present study examined the application of thermally sprayed ceramic coatings method on sink roll body for improving erosion resistance at molten 55% Al-Zn pool. In this experiment, the stainless steels such as STS 316L and STS 430F were used as the substrate materials. The CoNiCr and WE-Co powder were selected as bond coating materials. Moreover $Al_2O_3-ZrO_2-SiO_2 and ZrO_2-SiO_2$ powders selected as the top coating materials. Appearances of the specimens before and after dipping to molten 55%Al-Zn pool were compared and analyzed. As a result of this study, STS430F of substrate, WC-Co of bond spray coatings, $ZrO_2-SiO_2$ power of top spray coatings is the best quality in erosion resistance test at molten 55%Al-Zn pool

• Proceedings of the KWS Conference
• /
• 2009.11a
• /
• pp.95-95
• /
• 2009

Zinc coatings provide the most effective and economical way of protecting steel against corrosion. There are three types of galvanizing lines typically used in production line in galvanizing industries,Galvanize (GI) coating (Zn-0.1-0.3%Al), Galfan coating (Zn-5%Al), Galvalume(GL) coating (45%Zn-Al). In continuous Galvanizing lines, the immersed bath hardware (e.g. bearings, sink, stabilizer, and corrector rolls, and also support roll arms and snout tip) are subjected to corrosion and wear failure. Understanding the reaction of these materials with the molten Zn alloy is becomes scientific and commercial interest. To investigate the reaction with molten Zn alloys, static immersion test performed for 4, 8, 16, and 24 Hr. Two different baths used for the static immersion, which are molten Zn and molten Zn-55%Al. Microstructures characterization of each of the materials and intermetallic layer formed in the reaction zone was performed using optical microscope, SEM and EDS. The thickness of the reaction layer is examined using image analysis to determine the kinetics of the reaction. The phase dominated by two distinct phase which are eutectic carbide and matrix. The morphology of the intermetallic phase formed by molten Zn is discrete phase showing high dissolution of the material, and the intermetallic phase formed by Zn-55wt%Al is continuous. Aluminum reacts readily with the materials compare to Zinc, forming iron aluminide intermetallic layer ($Fe_2Al_5$) at the interface and leaving zinc behind.

• Journal of the Korean Electrochemical Society
• /
• v.3 no.4
• /
• pp.204-210
• /
• 2000

The control of dissolved aluminum concentration in the hot dip zinc galvanizing bath is greatly important in producing galvannealed steel sheets. The purpose of present study is to provide basic data for measurement of the aluminum concentration in site in hot dip zinc bath at the temperature of $460^{\circ}C\~500^{\circ}C$ using $CaF_2$ solid electrolyte sensor with three kinds of reference electrode. Good workability and stability of the sensor were confirmed with the $Bi+BiF_3$ reference electrode from the emf measurement. In order to measure the aluminum concentration in Zn-Al bath, the galvanic cell of fluorine ion was constructed with $CaF_2$ solid electrolyte as follows; $$(-)W|Zn-Al,\;AlF_3|CaF_2|Bi,BiF_3|W(+)$$. The emf measurement was made at the temperature of $460\pm10^{\circ}C$ in the Zn-Al bath. The following correlationship between aluminum concentration and emf was obtained by the least square regression analysis; $$E/mV=56.795log[\%Al]+1881.7\;R=0.9704$$,$$0.026wt\%{\leq}[\%Al]{\leq}0.984wt\%$$

• Corrosion Science and Technology
• /
• v.11 no.1
• /
• pp.9-14
• /
• 2012

The formation of the Fe-Al inhibition layer in hot-dip galvanizing is a confusing issue for a long time. This study presents a characterization result on the inhibition layer formed on C-Mn-Cr and C-Mn-Si dual-phase steels after a short time galvanizing. The samples were annealed at $800^{\circ}C$ for 60 s in $N_{2}$-10% $H_{2}$ atmosphere with a dew point of $-30^{\circ}C$, and were then galvanized in a bath containing 0.2 %Al. X-ray photoelectron spectroscopy (XPS) and transmission electron microscopy (TEM) was employed for characterization. The TEM electron diffraction shows that only $Fe_{2}Al_{5}$ intermetallic phase was formed. No orientation relationship between the $Fe_{2}Al_{5}$ phase and the steel substrate could be identified. Two peaks of Al 2p photoelectrons, one from metallic aluminum and the other from $Al^{3+}$ ions, were detected in the inhibition layer, indicating that the layer is in fact a mixture of $Fe_{2}Al_{5}$ and $Al_{2}O_{3}$. TEM/EDS analysis verifies the existence of $Al_{2}O_{3}$ in the boundaries of $Fe_{2}Al_{5}$ grains. The nucleation of $Fe_{2}Al_{5}$ and the reduction of the surface oxide probably proceeded concurrently on galvanizing, and the residual oxides prohibited the heteroepitaxial growth of $Fe_{2}Al_{5}$.

• Corrosion Science and Technology
• /
• v.11 no.1
• /
• pp.1-8
• /
• 2012

The development of martensitic grades which can be processed in continuous galvanizing lines requires the reduction of the oxides formed on the steel during the hot dip process. This reduction mechanism was investigated in detail by means of High Resolution Transmission Electron Microscopy (HR-TEM) of cross-sectional samples. Annealing of a martensitic steel in a 10% $H_2+N_2$ atmosphere with the dew point of $-35^{\circ}C$ resulted in the formation of a thin $_{C-X}MnO.SiO_{2}$ (x>1) oxide film and amorphous $_{a-X}MnO.SiO_{2}$ oxide particles on the surface. During the hot dip galvanizing in Zn-0.13%Al, the thin $_{C-X}MnO.SiO_{2}$ (x>1) oxide film was reduced by the Al. The $_{a-X}MnO.SiO_{2}$ (x<0.9) and $a-SiO_{2}$ oxides however remained embedded in the Zn coating close to the steel/coating interface. No $Fe_{2}Al_{5-X}Zn_{X}$ inhibition layer formation was observed. During hot dip galvanizing in Zn-0.20%Al, the $_{C-X}MnO.SiO_{2}$ (x>1) oxide film was also reduced and the amorphous $_{a-X}MnO.SiO_{2}$ and $a-SiO_{2}$ particles were embedded in the $Fe_{2}Al_{5-X}Zn_{X}$ inhibition layer formed at the steel/coating interface during hot dipping. The results clearly show that Al in the liquid Zn bath can reduce the crystalline $_{C-X}MnO.SiO_{2}$ (x>1) oxides but not the amorphous $_{a-X}MnO.SiO_{2}$ (x<0.9) and $a-SiO_{2}$ oxides. These oxides remain embedded in the Zn layer or in the inhibition layer, making it possible to apply a Zn or Zn-alloy coating on martensitic steel by hot dipping. The hot dipping process was also found to deteriorate the mechanical properties, independently of the Zn bath composition.