• Journal of Environmental Science International
• /
• v.16 no.1
• /
• pp.121-128
• /
• 2007

This study performed in order to evaluate the effects of pipe materials on corrosion and bacteria regrowth using a laboratory scale batch test. Two varieties of feed water with different microbial conditions were selected: tap water, surface river water (Han River water), and five pipe materials; carbon steel, copper, galvanized iron, stainless steel, and PVC, Carbon steel and galvanized iron pipes showed higher corrosion rates than other materials. In terms of attached bacterial growth, pipes with PVC and stainless steel showed higher bacteria concentration compared to other materials. Pseudomonas vesicularis was the predominant bacteria found on biofilm. The behavior of bacterial growth in the pipes was observed using a scanning electron microscope.

• Corrosion Science and Technology
• /
• v.3 no.2
• /
• pp.67-71
• /
• 2004

Galvanized Steel pipes have been widely used in industries and apartments, Unexpected early leakage has been found in an apartment. Tunneling corrosion or penetration was found in the water supply pipes. The chemical compositions of the pipes and properties of coating layer were evaluated. The pipes met the specification of KS D 3507. The cause of early failure was analyzed through the examination of macrostructures and microstructures, It was found that the pipes were failed by grooving corrosion, which resulted from galvanic corrosion of weld bead and matrix.

• Journal of Korean Society of Water and Wastewater
• /
• v.13 no.2
• /
• pp.82-88
• /
• 1999

This study was to evaluate disinfection efficiency of chlorine and chloramine as secondary disinfectants in the distribution systems. Indicator organism, HPC in the suspended and attached were measured for copper, galvanized steel, PVC, and carbon steel pipes. For suspended microorganism, the PVC pipe was markedly dense among the assessed pipe materials. The attached microorganism was markedly equivalent roughness of pipe materials. In copper and galvanized pipes, chloramine was more effective that free chlorine to disinfect suspended microorganism in the contact time of 2 hours. The contact time for the 99% inactivation of suspended microorganism by chloramine was longer than that of free chlorine. Regardless of pipe materials, chloramine was effective on both disinfection efficiency and 99% inactivation time for attached microorganism. In conclusion, chloramine which is good disinfectant for long contact time was recommended as secondary disinfectant in distribution system.

• Journal of the Korean institute of surface engineering
• /
• v.24 no.1
• /
• pp.18-24
• /
• 1991

In the present work the adhesion failure of a hot-dip galvanized coating has been studied as a function gas composition temperature of strip and of atmospheric gas in furnace. The adhesion failure of the hot-dip galvani-zed coating is classified as three mechanisms : carbon deposition, oxide film formation and alloy layer formation. The adhesion failure due to oxide film formation decreased markedly by increasing the gases temperature of direct fired furnace(DFF) in order to improve the reducing ability of steel strip. Optimum conditions of operating and manufacturing facilities for improving the coating adherence are suggested by analyzing the interface between steel substrate and coating layer.

• Journal of the Korean institute of surface engineering
• /
• v.27 no.3
• /
• pp.149-157
• /
• 1994

The formation of spangles on a hot dip galvanized sheet steel by spray cooling the molten zinc coating with air, water and 2.0wt% $NH_4H_2PO_4$ solution has been studied performing laboratory experiments, and their coating properties have been evaluated. Minimized spangles were easily formed by mist spraying the solution for 1 second at the low nozzle spray pressure onto the molten zinc at 420~$422^{\circ}C$ because the solute $NH_4H_2PO_4$ in the sprayed solution imparted a highly rapid cooling effect to the coating through its endothermic de-composition reactions and because the decomposed products acted as numerous nucleation sites for the mini-mized spangles on the coating. Good surface appearances sand sound coating properties were obtained on this coating. Only regular spangles were formed on the coating by the forced convective air cooling. At the high nozzle spray pressure, zero spangles were formed on the coating by the pure water spray cooling. However, the coating had a dull and rough surface with craters sand cracks.

• Journal of Welding and Joining
• /
• v.12 no.2
• /
• pp.76-86
• /
• 1994

Spot welding behavior of galvanized steel has been studied using both numerical and experimental techniques. The model that used to calculate temperature distribution within weldment is two-dimensional axis-symmetric finite difference method, and nugget sizes of specimen welded in condition of welding current and time has been estimated by experiment Results have shown that nugget sizes are increased in proportion to welding current and time, but the growth rate of nugget is decreased. Shear-tensile strength tests have shown interface fracture when welding current is 7, 9KA, welding time is 8-14cycle and 11KA, 8-10cycle respectively, but above 7, 9KA fracture shows button type. In button fracture, shear-tensile strengths have been proportional to nugget sizes.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.5 no.4
• /
• pp.38-46
• /
• 1996

This paper discusses the feasibility of Ultrasonic Nondestructive Evaluation (UNDE) technique for sport weld quality. Ultrasonic c-scan image assisted by image processing technique was used for Nondestructive Evaluation(NDE) of spot weld quality. Ultrasonic testing results obtained were confirmed and compared by Optical Microscope and SAM(Scanning Acoustic Mircroscope) observation of the spot-weld cross section, The results show that the nugget dinameter can be successfully measured with the accuracy of 0.5mm. It was ascertained that ultrasonic c-scan technique is very effective method for the sake of the approach to the quantitative measurement of nugget diameter and the discrimination of the corona bond from nugget. Additional support for the above conclusions is provided by the results for galvanized steel. The ultrasonic results for galvanized welds generally correspond to the results for uncoated steel. Finally, it was found that the above-mentioned technique can be sufficiently applied to NDE method for securing the Quality Assurance(QA) of spot welded products in production line.

• Journal of The Korean Digital Architecture Interior Association
• /
• v.8 no.1
• /
• pp.57-64
• /
• 2008

There are many problems in present truss-deck slab system for example welding defect, segregation, water leakage, rust and tarnish etc. These problems may be caused by spot welding thin galvanized steel plate and lattice bar. The TOX Joining Systems is to join metal sheets of different material and thickness with and without coating or painting without adding heat or a joining part. Newly developed TOX-deck slab system using non-welding joint is free from above mentioned problems. The objects of this study are suggestion of design strength of TOX joint by experimental and statistical analyses and development of window based program to design the TOX-deck slab system.

• Proceedings of the KWS Conference
• /
• 1992.10a
• /
• pp.91-95
• /
• 1992

The resistance spot welding process has been extensively used for joining of sheet metals, which are subject to variation of many process variables. Many qualitive analyses of sampled process variables have been attempted to predict nugget size. In this paper, dynamic resistance and electrode movement signal which is a good indicative of the nugget size was examined by introducing an artificial neural network estimator. An artificial neural feedforward network with back-propagation of error was applied for the estimation of the nugget size. The prediction by the neural network is in good agreement with the actual nugget size for resistance spot welding of galvanized steel. The results are quite promising in that the quantitative estimation of the invisible nugget size can be achieved without conventional destructive testing of welds.

• Proceedings of the KWS Conference
• /
• 2003.11a
• /
• pp.123-125
• /
• 2003