• 한국강구조학회 논문집
• /
• 제19권2호
• /
• pp.171-179
• /
• 2007

본 논문은 유전자 알고리즘을 근거한 이산최적설계 알고리즘에 의한 온실구조용 최적설계 프로그램을 개발하였다. 최적기법은 이산화 최적기법에 효과적인 유전자알고리즘을 근거로 하였다.본 연구에서 목적함수는 온실 구조물의 중량이고, 제약조건식은 한계상태설계기준에 대한 설계 제한식이다. 설계변수는 KSD 3760 농업용 아연도강관이다. 온실구조의 경제적인 구조설계나 안정성평가에 대한 기준을 제시하고자 하였다. 또한 온실구조자재의 표준화 및 규격화연구에 기여하고자 하였다. 본 연구의 유전자 알고리즘에 의한 온실구조용 이산화 최적설계 프로그램의 적용을 위해 설계 예를 들었다.

• 한국표면공학회지
• /
• 제31권6호
• /
• pp.379-388
• /
• 1998

The iron-zinc interfacial reaction and corrosin properties in galvanizing bath containning Ni have been intestigated. The substrate steel plates were galvanized in Zn or Zn-0.018Al baths with various Ni contents. The corrosion resistance of galvanized specimens was also evaluated by $60^{\circ}$bending test for galvannealing speaaimens. The corrosion resistance was improved with Ni addition in pure Zn bath, while deteriorated with Ni addition in Zn-0.18Al bath. The anti-powdering property, on thhe otherhand, was improved with Ni addition in Zn-0.18Al bath, while deteriorated with Ni addition in pure Zn. It was found that the anti-powdering property was improved with increasing $\xi$ phase ratio in reaction layer.

• 한국표면공학회지
• /
• 제30권5호
• /
• pp.320-332
• /
• 1997

The development of colored surface on zinc coating by the oxidation of a melten alloy of zinc with a minor amount of oxygen-avid additive such as tianium has been studied. Using a galvanizing Zinc alloy containing 0.1 to 0.3wt%Ti, gold, purple or blue color was developed clearly and stably, depending upon the extent of oxidation, by air cooling after hot dipping in a bath at temperature of $550^{\circ}C$ to $600^{\circ}C$. The source of the color is light interference with surface oxide layer. THe final color depends on the thickness of the color depends on the thickness of $TiO_2$, played So compositing, temperature and time at elevated temperature after are all controlling variables. Since oxidation film such as $TiO_2$ played role of passivation film, the corrosion resistance in a colored galvanized steel sheet. It is also thought that surface oxide layer of $TiO_2$ inhibited dissolution of the coating layer.

• Structural Engineering and Mechanics
• /
• 제35권3호
• /
• pp.301-314
• /
• 2010

The paper presents the results and conclusions of dynamic load tests that were conducted on a road bridge over the Mokrzyca river in Wroclaw (Poland) made of galvanized corrugated steel plates (CSP). The critical speed magnitudes, velocity vibration, vibration frequency were determined in the paper. The dynamic analysis is extremely important, because such studies of soil-steel bridges in the range of dynamic loads are relatively seldom conducted. Conclusions drawn from the tests can be most helpful in the assessment of behaviour of this type of corrugated plate bridge with soil. In consideration of application of this type of structure in the case of small-to-medium span bridges, the conclusions from the research will not be yet generalized to all types of such solutions. The detailed reference to all type of such bridge structures would be requiring additional analysis (field tests and calculations) on the other types of soil-steel bridges.

• Corrosion Science and Technology
• /
• 제10권6호
• /
• pp.199-204
• /
• 2011

Hot dip metallic coated steels like as galvanized (GI), zinc-aluminium (GL) and aluminium coated steels are mostly used where corrosion resistance is needed. There are two kinds (type 1 and type 2) of aluminium coated steel being commercially used among them. Type 1 aluminium coated steel is coated with an Al-5~11 wt%Si alloy and Type 2 aluminium coated steel consists of commercially pure aluminium. Type 1 Al coated steel is generally used in automotive components and electrical appliances while type 2 aluminium coated steel is mainly used in construction applications such as building cladding panels, air conditioning and ventilation system. In this study, Type 1 aluminium coated steels have tested by accelerated conditions (salt spray or corrosive gas) and outdoor exposure condition in order to understand their corrosion behaviour. Due to the distinct corrosion mechanism of Al which exposes to the severe chloric condition, Salt Spray Test cannot predict the ordinary atmospheric corrosion of Al based coated materials. In addition, the test results and their corrosion feature of Al coated steel sheets will be discussed comparing with other metallic coated steel sheets of GI and GL.

• Corrosion Science and Technology
• /
• 제23권3호
• /
• pp.221-227
• /
• 2024

During hot stamping of hot-dip zinc-coated steel sheets such as hot-dip galvanized steel sheets and hot-dip galvannealed steel sheets, an oxide mainly composed of ZnO is formed on the sheet surface. However, excessive formation of ZnO can lead to a decrease in the amount of metal Zn in the coating layer, decreasing the corrosion resistance of hot-stamped members. Therefore, it is important to suppress excessive formation of ZnO. While the formation of Al oxides and Mn oxides along with ZnO layer during the hot stamping of hot-dip zinc-coated steel sheets can affect ZnO formation, crystal structures of such oxides have not been elucidated clearly. Thus, this study aimed to analyze structures of oxides formed during hot stamping of hot-dip galvannealed steel sheets using transmission electron microscopy. Results indicated the formation of an oxide layer comprising ZnAl₂O₄ at the interface between ZnO and the coating layer with Mn₃O₄ at the outermost of an oxide layer.

• 콘크리트학회논문집
• /
• 제24권5호
• /
• pp.613-621
• /
• 2012

철근부식은 콘크리트의 내구성 문제뿐 아니라 구조적인 안전성에 영향을 미치므로 매우 중요한 열화이다. 철근부식을 방지하기 위하여 콘크리트 구체의 내구성을 향상시키려는 연구가 진행되고 있으나 용융아연도금 철근과 같이 철근 표면을 코팅함으로서 부식을 방지하려는 연구도 진행되고 있다. 이 연구는 용융아연도금 철근의 내부식성능 및 구조성능을 정량적으로 평가하는 것이다. 이를 위하여 아연, 알루미늄, 아연 45% + 알루미늄 55% 등을 사용한 도금 철근에 대하여 예비실험을 수행하였다. 다양한 금속코팅재료의 부식거동을 평가하여 최적의 도금재료인 아연을 선정하였으며, 아연도금 철근의 전위변화를 촉진염수 분무실험 등을 통하여 평가하였다. 또한 용융아연 도금된 철근과 일반철근을 이용하여 철근의 인장강도 시험, 콘크리트와의 부착력 시험 등이 수행되었으며, 최종적으로 RC 보를 제작하여 균열패턴 및 구조거동을 평가하였다. 이 연구에서는 다양한 금속코팅재료의 부식거동, 노치를 가진 금속의 전위변화 등을 포함한 부식특성이 평가되었다. 또한 부착력, 인장강도, 하중에 따른 거동 등을 포함한 구조적 거동이 평가되었으며, 최종적으로 용융아연도금 철근의 사용에 대한 적용성이 검토되었다.

• 한국강구조학회 논문집
• /
• 제16권5호통권72호
• /
• pp.609-619
• /
• 2004

유럽을 중심으로 스틸스터드의 약점으로 지목 받고 있는 열교현상을 억제하기 위한 스터드 개선 연구가 활발히 진행되고 있다. 이 연구는 크게 마감재와 접촉 면적을 줄이는 방법, 웨브면에서 열전달 경로를 늘이는 방법, 열전도성이 낮은 소재를 사용하는 방법, 그리고 스터드를 피복하는 방법으로 구분할 수 있다. 비교적 저층의 주거용 건축물을 대상으로 하는 국외의 경우 에너지 소비에 초점이 맞춰져 있지만, 본 연구의 경우 중층화를 대비하여 구조적 성능도 고려하여 아연도금강판(SGC58)과 FRP를 에폭시로 부착하여 150SL 형태의 복합스터드를 개발하였다. 복합스터드의 소재로는 두께 1.0mm과 1.2mm 강판과 두께 4mm(4ply), 6mm(6ply)의 FRP를 적용하였고, 4가지의 접합 상세에 대한 제작 및 실험을 통해 최종적으로 우수한 결과를 보인 2가지를 선택하였다. 이와 같은 과정을 거쳐 개발된 복합스터드의 압축 성능을 확인하기 위해 2가지 접합 상세에 대해 단면 높이인 150mm에 대해 3, 6, 9, 12배 길이에 대해 압축 실험을 계획하였고, 기존 스틸 스터드와 비교하기 위하여 동일 형태의 비교 실험체도 제작하였다. 실험결과, 복합스터드의 최대하중은 강판 두께 1.0mm인 경우 동일 두께의 스틸 스터드보다 평균 1.62배, 1.2mm인 경우 평균 1.46배 증가하였으며, 가력 종료 시점에 이르기까지 일체 거동을 보여 구조적으로 우수함이 입증되었다.

• 대한기계학회논문집
• /
• 제13권2호
• /
• pp.229-235
• /
• 1989

본 연구에서는 편면도금 강판과 복합조직 고장력 강판간의 이종 용접재의 피로거동을 연구하고져 한다. 즉 유한요소법으로 응력분포를 조사하고 그 결과와 피로균열발생 위치를 비교 검토해 보고자 한다.

• 한국철도학회:학술대회논문집
• /
• 한국철도학회 2002년도 추계학술대회 논문집(II)
• /
• pp.981-986
• /
• 2002

ACSR of the catenary wires is corrosion degradation progressed by the effect of atmospheric pollution. ACSR which consists of galvanized steel stranded aluminum. The inside of Steel Reinforced is hot-dipped zinc coating steel wire and it takes charge of tension. If ACSR is exposed in atmosphere, the galvanic corrosion is occurred because it is contacted with aluminum. It is occurred the chemical reaction rapidly so that the local a defect is also occurred. If the catenary wires are exposed in atmosphere of pollution conditions, it may cause to reduce the mechanical strength by corrosion degradation and may cause to damage the wires by micro cracks. Accordingly, this study presents the effects of mechanical properties through the corrosion of ACSR.