• 한국세라믹학회지
• /
• 제46권3호
• /
• pp.253-262
• /
• 2009

The purpose of this study is to find out optimum conditions for zinc crystalline glaze under variables of firing: maximum firing temperature, crystal growth temperature, temperature increasing speed, annealing speed, holding time at maximum temperature and holding time at crystal growth temperature. Ferro Frit3110, ZnO and Quartz were used as starting materials and tested by three component system. The best result of test was selected and extended to its vicinity as five glaze formulas. And then the specimens were experimented by variable firing conditions and analyzed by crystal appearance observation, XRD, FT-IR and Raman spectroscopy. In result, main crystal was willemite in the zinc glazes. Some gahnite was detected in specimens which were fired at $1230^{\circ}C$, $1250^{\circ}C$ and $1270^{\circ}C$, however gahnite was not identified at $1300^{\circ}C$. Optimum zinc crystalline glaze was gained by following firing condition: temperature increasing speed $5^{\circ}C$/min, holding 1 h at $1270^{\circ}C$, annealing speed $3^{\circ}C$/min till $1170^{\circ}C$, holding 2 h at $1170^{\circ}C$ then naturally annealed.

• 한국광물학회지
• /
• 제17권4호
• /
• pp.309-325
• /
• 2004

연구는 호주 퀸즈랜드 주 북서부에 위치하는 은-납-아연 캔닝턴 광상은 호상편마암, 미그마타이트, 규선석-석류석 편암 그리고 각섬암으로 구성된 모암 주변부에서 발달해 있다. 모암에서 산출되는 규선석의 세 가지 다른 결정형태, 규선석을 포획광물로 함유한 아연-첨정석과 석류석 반상변정은 모암의 변성작용과 아연과 관련된 광화작용에 대한 지질학적 지시자로 사용되었다. 변성작용과 아연 광화작용과의 관계는 프로그램 THERMOCALC를 이용하여 KFMASH (K$_2$O-FeO-MgO-A1$_2$O$_3$-SiO$_2$- $H_2O$), KFMASHTO (K$_2$O-FeO-MgO-A1$_2$O$_3$-SiO$_2$-$H_2O$-TiO$_2$-Fe$_2$O$_3$), NCKFMASH ($Na_2$O-CaO-K$_2$O-FeO-MgO-Al$_2$O$_3$-SiO$_2$-$H_2O$) 그리고 MnNCKFMASH (MnO-$Na_2$O-CaO-K$_2$O-FeO-MgO-Al$_2$O$_3$-SiO$_2$-$H_2O$) 화학계에서 이들 세 가지 광물의 공생관계와 규선석-석류석-부분용융의 상평형 관계를 이용하여 결정하였다. MnNCKFMASH와 NCKFMASH계에서 부분 용융은 KFMASH와 KFMASHTO계에서 보다 낮은 온도에서 일어나며, MnNCKFMASH 계에서 용융 온도는 암석 화학 성분의 Na+Ca+K)의 비가 증가함에 따라 감소하는 경향을 보인다. 캔닝턴 광상의 모암은 MnNCKFMASH계의 경우 최고 온도와 압력 환경에서(634$\pm$62$^{\circ}C$, 4.8$\pm$1.3 kbar) 약 15% 용융되지만, KFMASHTO계하에서는 부분 용융이 일어나지 않는다. 규선석의 등변성도선과 모드 비의 변화를 근거로, 주상과 능면형의 규선석과 주상의 규선석을 포획하는 아연-첨정석 반상변정은 부분 용융을 포함하는 온도와 압력의 증가(약 550～$600^{\circ}C$, 2.0～3.0 kbar에서 700～75$0^{\circ}C$, 5.0～7.0 kbar)로 인한 것으로 생각된다. 또한 이와 같은 변성작용 동안의 최대 수축 변형 방향은 남-북 그 다음 동서 방향으로 주로 D$_1$과 D$_2$ 변형작용 동안에 형성되어졌다. 결론적으로 아연-첨정석의 성장과 관련된 아연 광화 작용은 D$_2$ 동안에 일어났고 그 후 부분 용융과 후기 변형/변성작용에 의해 재배치 또는 재농집 되어진 것으로 생각된다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2006년도 하계학술대회 논문집 Vol.7
• /
• pp.272-273
• /
• 2006

LTCC(low temperature co-fired ceramics)용 glass/ceramic 복합체를 제조하기 위해 4 종류의 borosilicate계 glass를 선정하고 filler로 $Al_2O_3$ ceramics를 filler 사용하여 30~50 vol% glass frit에 따른 소결 및 유전 특성에 대하여 조사하였다. Glass frit은 $SiO_2$와 $B_2O_3$ 함량비를 고정한 후 R(CaO, BaO, ZnO, $Bi_2O_3$)에 따라 유리 연화온도(Ts)와 함량이 소결에 미치는 영향 및 유전 특성 변화를 고찰한 결과, CaO-$B_2O_3-SiO_2$ glass의 경우 다량의 2 차상이 형성되었고, 이에 $900^{\circ}C$ 이하에서 완전 소결이 이루어지지 않았으며, BaO-$B_2O_3-SiO_2$ glass는 celsian($BaAl_2Si_2O_8$) 결정이 형성되면서 소결성의 저하를 갖고 왔으며, ZnO-$B_2O_3-SiO_2$ glass는 소결이 진행됨에 따라 주상이 $Al_2O_3$에서 gahnite($ZnAl_2O_4$) 결정이 형성되면서 품질계수가 크게 증가하였으며, $Bi_2O_3-B_2O_3-SiO_2$ glass는 45 vol%일 때 $900^{\circ}C$에서부터 일정한 선수축율 특성을 나타내었지만, 다량의 액상으로 인하여 유전 특성의 저하를 나타내었다.

• E2M - 전기 전자와 첨단 소재
• /
• 제8권1호
• /
• pp.95-101
• /
• 1995

Crystallizable glasses with precipitation of celsian, anorthite, wollastonite and gahnite were prepared for the purpose of insulating dielectric layers in devices such as integrated circuit substrates. The starting glasses were prepared by melting the batches for 1 hour at 1450.deg. C and then Quenching to a distilled water. And crystallization behavior of these glasses were studied by DTA, TMA, XRD analysis and by the measurement of dielectric properties. The overall composition of the glass-ceramic consists in weight percent of 30-35% A1$_{2}$O$_{3}$, 13-26% BaO, 5-21% CaO, 10-24% ZnO, 4.5-9.0% TiO$_{2}$ and 4-8% B$_{2}$O$_{3}$. As a result, in barium-rich glasses only celsian phase was developed in the range of 850-900.deg. C. Also, the thermal expansion coefficient, dielectric constant and quality factor of these glass-ceramics were 68*10$^{-7}$ /.deg. C, about 9 and more than 1000, respectively.

• 한국세라믹학회지
• /
• 제12권1호
• /
• pp.23-28
• /
• 1975

The object of this study is to find the optimum conditions for crystal growth and kinds of crystal in ZnO-Al2O3-SiO2 glass composition. At first, the base glass composed of ZnO (44.7%), Al2O3(14.0%) and SiO2(41.3%) was melted in propane gas furnace at 1450-150$0^{\circ}C$ for an hour, and then it was poured into the stainless steel mould heated previously at $600^{\circ}C$ to obtain the thin glass test piece. Four crystal forms from base glass such as stuffed keatite, zinc orthosilicate, zinc aluminosilicate, and cristobalite were crystallized during heat treatment between 80$0^{\circ}C$ and 110$0^{\circ}C$. For the investigation of crystal growth, X-ray diffractometer and thermal differential analysis were used and the growth rate of the four crystal forms were obtained by the method of Archimedes specific gravity and intensity comparison of X-ray diffraction peak. The results obtained were as follows. 1) Stuffed keatite peaks which started to appear after two hours at 80$0^{\circ}C$ were maximum after 11 hours and this crystal breaks down to willemite irreversibly at about 100$0^{\circ}C$. 2) Development of gahnite started at 85$0^{\circ}C$ and increased with temperature growth. 3) Stuffed keatite which had been transformed slowly into willemite at 100$0^{\circ}C$ was decreased with time and willemite increased until four hours. 4) Cristobalite began to be developed after treatment of 110$0^{\circ}C$.