• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2004년도 추계학술대회 논문집 Vol.17
• /
• pp.539-542
• /
• 2004

The $ZnGa_2O_4$ phosphor target is synthesized through solid-state reactions at the calcine temperature of $700^{\circ}C$ and sintering temperature of $1300^{\circ}C$ in order to deposit $ZnGa_2O_4$ phosphor thin film by rf magnetron sputtering system. The $ZnGa_2O_4$ phosphor thin film is deposited on Si(100) substrate and prepared $ZnGa_2O_4$ phosphor thin film is annealed by rapid thermal processor(RTP) at $700^{\circ}C$, 15sec. The x-ray diffraction patterns of $ZnGa_2O_4$ phosphor target and thin film show the position of (311) main peak. The cathodoluminescenre(CL) spectrums of $ZnGa_2O_4$ phosphor thin film show main peak of 420nm and maximum intensity at the substrate temperature of $500^{\circ}C$ and annealing temperature of $700^{\circ}C$ 15sec.

• 한국진공학회지
• /
• 제22권3호
• /
• pp.119-125
• /
• 2013

In-line magnetron sputtering system을 사용하여 대면적($60{\times}60cm^2$) 소다라임 유리기판위에 투명전도성 ZnO(Al)와 ZnO(AlGa) 박막을 500 nm에서 1,450 nm까지 두께별로 증착하여 전기적, 광학적 특성을 연구하였다. XRD를 통해 c-축 방향성(002)을 가지고 성장된 것을 확인 하였다. Hall 특성 분석을 통해 이동도 및 캐리어 농도의 특성을 확인 하였으며, 그에 따른 ZnO(AlGa)의 비저항이 $9.03{\times}10^{-4}{\Omega}{\cdot}cm$에서 $7.83{\times}10^{-4}{\Omega}{\cdot}cm$으로 ZnO(Al) 보다 높게 나타났으며, 가시광선 영역에서 투과율은 87.6%에서 84.3%으로 나타났다. 따라서 ZnO(AlGa)는 전기적 특성이 우수하고 높은 투과율로 대면적용 투명전도성 재료로의 활용에 적합한 특성을 지닌 것을 확인 할 수 있었다.

• 한국재료학회지
• /
• 제23권3호
• /
• pp.161-167
• /
• 2013

The ZnO thin films were grown on GaN template substrates by RF magnetron sputtering at different RF powers and n-ZnO/p-GaN heterojunction LEDs were fabricated to investigate the effect of the RF power on the characteristics of the n-ZnO/p-GaN LEDs. For the growth of the ZnO thin films, the substrate temperature was kept constant at $200^{\circ}C$ and the RF power was varied within the range of 200 to 500W at different growth times to deposit films of 100 nm thick. The electrical, optical and structural properties of ZnO thin films were investigated by ellipsometry, X-ray diffraction (XRD), atomic force microscopy (AFM), photoluminescence (PL) and by assessing the Hall effect. The characteristics of the n-ZnO/p-GaN LEDs were evaluated by current-voltage (I-V) and electroluminescence (EL) measurements. ZnO thin films were grown with a preferred c-axis orientation along the (0002) plane. The XRD peaks shifted to low angles and the surface roughness became non-uniform with an increase in the RF power. Also, the PL emission peak was red-shifted. The carrier density and the mobility decreased with the RF power. For the n-ZnO/p-GaN LED, the forward current at 20 V decreased and the threshold voltage increased with the RF power. The EL emission peak was observed at approximately 435 nm and the luminescence intensity decreased. Consequently, the crystallinity of the ZnO thin films grown with RF sputtering powers were improved. However, excess Zn affected the structural, electrical and optical properties of the ZnO thin films when the optimal RF power was exceeded. This excess RF power will degrade the characteristics of light emitting devices.

• 한국결정성장학회지
• /
• 제26권3호
• /
• pp.109-114
• /
• 2016

용매열합성법과 하소 과정으로 이루어진 두 단계 공정을 통해 단분산된 마이크로 크기의 구형 $ZnGa_2O_4$ 입자를 합성하였다. 합성된 3차원 구조의 구형 $ZnGa_2O_4$ 입자는 핵 생성과정에서 발생된 $ZnGa_2O_4$ 핵들이 자기 조립에 의해 형성된다. 이렇게 3차원 구조의 입자를 형성하는 원리인 '핵 성성'과 '자기 조립' 과정은 계면활성제인 PEG(polyethylene glycol)의 영향을 받는다. 그 이유는 계면활성제인 PEG의 농도가 임계응집농도(critical aggregation concentration)를 결정짓기 때문이다. 그리고 $ZnGa_2O_4$ 단상 합성을 위해 원료인 zinc acetate의 양을 조절했으며, 최적의 하소 조건을 결정하고자 TG-DTA를 통해 열적 거동을 확인했다. 또한 열처리 전 모체와 $900^{\circ}C$에서 1시간의 열처리 과정을 거친 산화물을 구성하는 작용기의 변화를 규명하기 위해 FT-IR을 측정하였다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2005년도 추계학술대회 논문집 Vol.18
• /
• pp.301-302
• /
• 2005

The $ZnGa_2O_4$:Cr phosphor was synthesized through solid-state reactions at the various molar ratio of Cr from 0.002 % to 0.01 %. The XRD patterns show that the Cr-doped $ZnGa_2O_4$ has a (311) main peak and a spinel phase. Also the emission wavelength shills from 510 to 705 nm in comparison with $ZnGa_2O_4$:Mn when Cr is doped in $ZnGa_2O_4$. These results indicate that $ZnGa_2O_4$ phosphors hold promise for potential applications in field-emission display devices with high brightness operating in full color regions.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2014년도 제46회 동계 정기학술대회 초록집
• /
• pp.322.2-322.2
• /
• 2014

Lighting emitting diodes of n-ZnO/MQW/p-GaN structure are fabricated and investigated. To realize this LED structure, n-ZnO/MQW/p-GaN are grown by MOCVD. At several bias voltages, blue-green light is emitted from the ZnO mesa edge. However, the emission is restricted near the mesa edge. It is seen that the hole current does not spread well. It is because conductivity of p-GaN is extremely small. The break down voltage of the device is small compared to conventional InGaN/GaN LEDs. It is seen that ZnO columnar grain boundaries act as leakage current paths and non-radiative recombination center.

• 반도체디스플레이기술학회지
• /
• 제13권1호
• /
• pp.91-95
• /
• 2014

(F,Ga) co-doped ZnO thin film on glass substrate was fabricated via a simple non-alkoxide sol-gel spin-coating. Contrary to the F single doped ZnO thin film, the (F,Ga) co-doped thin film showed a significant reduce in electrical resistivity after a second post-heat-treatment in reducing environment. The resulting decrease in electrical resistivity with Ga co-doping is considered to be resulted from the increases both carrier density and mobility. The optical transmittance of the (F,Ga) co-doped thin film in the visible range showed higher transmittance with Ga co-doping compared with F single doped ZnO thin film.

• Transactions on Electrical and Electronic Materials
• /
• 제12권1호
• /
• pp.11-15
• /
• 2011

In this study, $ZnGa_2O_4$ phosphors in its application to field emission displays and electroluminescence were synthesized through the precipitation method and $Mn^{2+}$ ions. A green luminescence activator, $Cr^{3+}$ ions, and a red luminescence activator were separately doped into $ZnGa_2O_4$, which was then screen printed to an indium tin oxide substrate. The thick films of the $ZnGa_2O_4$ were deposited with the various thicknesses using nano-sized powder. The best luminescence characteristics were shown at a thickness of 60 ${\mu}m$. Additionally, green-emission $ZnGa_2O_4:Mn^{2+}$ and red-emission $ZnGa_2O_4:Cr^{3+}$ phosphor thick films, which have superior characteristics, were manufactured through the screen-printing method. These results indicate that $ZnGa_2O_4$ phosphors prepared through the precipitation method have wide application as phosphor of the full color emission.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2010년도 제39회 하계학술대회 초록집
• /
• pp.165-165
• /
• 2010

GaInZnO는 투명 비정질 산화물 반도체로서 태양전지, 평판 액정 디스플레이, 잡음방지 코팅, 터치 디스플레이 패널, 히터, 광학 코팅 등 여러 응용에 쓰인다. 이 논문에서는 투명전자소자로 관심을 모으고 있는 GaInZnO의 전자적 그리고 전기적 특성을 측정하였다. GaInZnO 박막은 $SiO_2$ (100)/Si 기판위에 RF 마그네트론 스퍼터링 증착법으로 $Ga_2O_3:In_2O_3:ZnO$의 조성이 2:2:1로 된 타겟을 가지고 박막을 성장시켰다. 성장한 후에 RTP를 이용하여 30분간 열처리 하였다. GaInZnO의 전자적 특성을 나타내는 띠틈 및 실리콘 기판과의 원자가 띠 오프셋 값을 측정하였으며, 이 값들을 통해 GaInZnO박막과 실리콘 기판과의 띠 정렬도 수행하였다. 띠틈은 반사 전자 에너지 손실 분광법(REELS)을 이용하여 측정하였고, 원자가 띠 오프셋은 광전자 분광법(XPS)을 이용하여 측정하였다. 열처리 온도가 $400^{\circ}C$까지는 띠틈의 변화 및 XPS 결합에너지의 변화가 없는 것으로 보아 열적안정성이 우수함을 알 수 있다. 반면 $450^{\circ}C$에서의 띠틈이 감소하는 것으로 보아 $450^{\circ}C$에서는 열적안정성이 깨지는 것을 알 수 있다. GaInZnO 박막을 채널 층으로 하고 전극은 알루미늄(Al)으로 된 TFT를 제작하여 전기적 특성을 조사하였다. TFT 특성 결과 이동도가 약, subthreshold swing(S.S)이 약 1.5 V/decade, 점멸비가 약 $10^7$으로 측정되었다. 유리 위에 증착시킨 GaInZnO 박막의 투과율을 측정해본 결과 모든 시료가 가시광선 영역에서 80%이상의 투과율을 갖는 것으로 보아 투명전극소자로 응용이 가능하다는 것을 알 수 있었다.

• 한국결정성장학회지
• /
• 제31권2호
• /
• pp.73-77
• /
• 2021

RF 마그네트론 스퍼터링 공정에 의해 Ga-doped ZnO 박막이 O2 및 Ar 분위기 하에서 증착 조건에 따라 합성되었으며, N2 분위기에서, 600℃에서 급속열처리(RTA)를 실시하였다. 증착된 ZnO : Ga 박막에 대해 두께를 측정하였고, XRD 패턴 분석에 의해 결정상을 조사하였으며, FE-SEM, AFM 이미지에 의해 박막의 미세구조를 관찰하였다. O2 및 Ar 분위기 기체 종류별로 형성된 박막들의 증착 조건에 따라 X-선 회절 패턴의 (002)면의 세기는 상당한 차이를 나타냈다. O2 조건에서는 Ga doping이 이루어진 단일 박막의 경우에서는 강한 세기의 회절피크가 관찰되었다. O2 및 Ar 조건에서는 Ga doping이 이루어진 다층박막의 경우에서는 다소 약한 세기의 (002) 면의 피크만을 나타내었다. FE-SEM image에서는 박막의 표면입자의 크기는 두께가 증가함에 따라 입자크기가 다소 증가하는 것으로 관찰되었다. O2 및 Ar 분위기 조건 하에서, Ga doping이 이루어진 다층박막의 경우에서는, 비저항은 6.4 × 10-4Ω·cm을 나타냈고, O2 분위기 조건하에서, Ga doping이 이루어진 단일 박막의 경우에서는 저항값이 감소하였고, Ga-doped ZnO 박막의 두께가 2 ㎛로 증가하면서 저항이 감소하였으며, 1.0 × 10-3 Ω·cm의 비교적 낮은 비저항 값을 나타내었다.