• Transactions of the Korean hydrogen and new energy society
• /
• v.29 no.5
• /
• pp.419-426
• /
• 2018

$Ni-La_2O_3-Ce_{0.8}Zr_{0.2}O_2$ catalysts with various $La_2O_3$ loading were investigated for hydrogen production from steam reforming of methane (SRM). The $La_2O_3$ loading influenced the physicochemical properties of $Ni-La_2O_3-Ce_{0.8}Zr_{0.2}O_2$ catalysts such as BET surface area, Ni dispersion, Ni size and reducibility. Among the prepared catalysts, $Ni-70La_2O_3-Ce_{0.8}Zr_{0.2}O_2$ catalyst showed the highest activity and stability at a very high gas hourly space velocity (GHSV) of $932,556h^{-1}$. This is mainly due to high Ni dispersion, small Ni size and high reducibility.

• Transactions of the Korean hydrogen and new energy society
• /
• v.26 no.5
• /
• pp.477-483
• /
• 2015

LFG (Land-Fill Gas) includes components of $CH_4$, $CO_2$, $O_2$, $N_2$, and water. The preparation of synthesis gas from LFG as a DME (Dimethyl Ether) feedstock was studied by methane reforming of $CO_2$, $O_2$ and steam over $NiO-MgO-CeO_2/Al_2O_3$ catalyst. Our experiments were performed to investigate the effects of methane conversion and syngas yield on the amount of LFG components over $NiO-MgO-CeO_2/Al_2O_3$ catalyst. Results were obtained through the methan reforming experiments at the temperature of $900^{\circ}C$ and GHSV of 8,800. The results were as following; it has generally shown that syngas yield increase with the increase of oxygen and steam amounts and then decrease. Highly methane conversion of above 98% and syngas yield of approximately 60% were obtained in the feed of gas composition flow-rate of 243ml/min of $CH_4$, 241ml/min of $CO_2$, 195ml/min of $O_2$, 48ml/min of $N_2$, and 450ml/min of steam, respectively, under reactor pressure of 1 bar for 200 hrs of reaction time. Also, it was shown that catalyst deactivation by coke formation was reduced by excessively adding oxygen and steam as an oxidizer of the methane reforming.

• Transactions of the Korean hydrogen and new energy society
• /
• v.30 no.2
• /
• pp.95-102
• /
• 2019

In order to investigate the effect of water treatment on activity of WGS catalyst, $Cu/ZnO/MgO/Al_2O_3$ (CZMA) catalysts were synthesized by co-precipitation method. The prepared catalysts were water-treated at two different temperature (250, $350^{\circ}C$). Synthesized catalysts were characterized by using BET, SEM, $N_2O$ chemisorption, XRD, $H_2-TPR$ and XPS analysis. The catalytic activity tests were carried out at a GHSV of $28,000h^{-1}$ and a temperature range of $180-320^{\circ}C$. The reduction temperature decreased with water treatment and CZMA_250 catalyst showed the lowest reduction temperature and retained a large amount of $Cu^+$. Water-treated catalysts showed increased reactivity compared to untreated catalyst and the CZMA_250 catalyst showed higher catalytic activity on WGS reaction.

• Clean Technology
• /
• v.29 no.1
• /
• pp.39-45
• /
• 2023

To investigate the effects of Mg addition at different aging times and temperatures, Cu/MgO/Al₂O₃ catalysts were synthesized for the low-temperature water gas shift (LT-WGS) reaction. The co-precipitation method was employed to prepare the catalysts with a fixed Cu amount of 30 mol% and varied amounts of Mg/Al. Synthesized catalysts were characterized using XRD, BET, and H₂-TPR analysis. Among the prepared catalysts, the highest CO conversion was achieved by the Cu/MgO/Al₂O₃ catalyst (30/40/30 mol%) with a 60 ℃ aging temperature and a 24 h aging time under a CO₂-rich feed gas. Due to it having the lowest reduction temperature and a good dispersion of CuO, the catalyst exhibited around 65% CO conversion with a gas hourly space velocity (GHSV) of 14,089 h-1 at 300 ℃. However, it has been noted that aging temperatures greater or less than 60 ℃ and aging times longer than 24 h had an adverse impact, resulting in a lower surface area and a higher reduction temperature bulk-CuO phase, leading to lower catalytic activity. The main findings of this study confirmed that one of the main factors determining catalytic activity is the ease of reducibility in the absence of bulk-like CuO species. Finally, the long-term test revealed that the catalytic activity and stability remained constant under a high concentration of CO₂ in the feed gas for 19 h with an average CO conversion of 61.83%.

• Applied Chemistry for Engineering
• /
• v.21 no.6
• /
• pp.648-652
• /
• 2010

Catalytic activities of the partial oxidation of methane (POM) to hydrogen were investigated over Pd(5)/Ti-SPK and Pd(5)/Zr-SPK in a fixed bed flow reactor (FBFR) under atmosphere, and the catalysts were characterized by BET, XPS, XRD. The BET surface areas, pore volume and pore width of Horvath-Kawaze, micro pore area and volume of t-plot of Pd(5)/Ti-SPK and Pd(5)/Zr-SPK were $284m^2/g$, $0.233cm^3/g$, 3.9 nm, $30m^2/g$, $0.015cm^3/g$ and $396m^2/g$, $0.324cm^3/g$, 3.7nm, $119m^2/g$, $0.055cm^3/g$, repectively. The nitrogen adsorption isotherms were type IV with hysteresis. XPS showed that Si 2p and O 1s core electronlevels of Ti-SPK and Zr-SPK substituted Ti and Zr shifted to slightly lower binding energies than SPK. The oxidation states of Pd on the surface of catalysts were $Pd^0$ and $Pd^{+2}$. XRD patterns showed that crystal structures of fresh catalyst changed amorphous into crystal phase after reaction. The conversion and selectivity of POM to hydrogen over Pd(5)/Ti-SPK and Pd(5)/Zr-SPK were 77, 84% and 78, 72%, respectively, at 973 K, $CH_4/O_2$ = 2, GHSV = $8.4{\times}10^4mL/g_{cat}{\cdot}h$ and were kept constant even after 3 days in stream. These results confirm superior activity, thermal stability, and physicochemical properties of catalyst in POM to hydrogen.

• Applied Chemistry for Engineering
• /
• v.18 no.2
• /
• pp.155-161
• /
• 2007

In this study, the reactivity of a $SnO_2-ZrO_2$(Sn/Zr = 2/1) catalyst for $SO_2$ reduction by CO was investigated in order to optimize the various reaction conditions such as temperature, gas hourly space velocity (GHSV), and [CO]/[$SO_2$] molar ratio. The reaction temperature in the range of $300{\sim}550^{\circ}C$, space velocity in the range of $5000{\sim}30000cm^3/[g_{-cat}{\cdot}h]$ and [CO]/[$SO_2$] molar ratio in the range of 1.0~4.0 were employed. The optimum temperature, GHSV, and [CO]/[$SO_2$] molar ratio were determined to be $325^{\circ}C$, $10000cm^3/[g_{-cat}{\cdot}h]$, and 2.0, respectively; under these conditions, $SO_2$ conversion was over 99% and sulfur selectivity was over 95%. In addition, the effect of $H_2O$ content on the $SO_2$ reduction by CO was also investigated. As the $H_2O$ content increased from 2 vol% up to 6 vol%, the reactivity and sulfur selectivity decreased. In case of 2 vol% $H_2O$ content, the reaction temperature and [CO]/[$SO_2$] molar ratio were varied in the range of $300{\sim}400^{\circ}C$ and 1.0~3.0. The optimum temperature and [CO]/[$SO_2$] molar ratio were $340^{\circ}C$ and 2.0, respectively under which $SO_2$ conversion and sulfur selectivity were about 90% and 87%, respectively.

• Clean Technology
• /
• v.29 no.2
• /
• pp.126-134
• /
• 2023

Direct catalytic decomposition is a promising method for controlling the emission of nitrous oxide (N₂O) from the semiconductor and display industries. In this study, a γ-Al₂O₃ catalyst was developed to reduce N₂O emissions by a catalytic decomposition reaction. The γ-Al₂O₃ catalyst was prepared by an extrusion method using boehmite powder, and a N₂O decomposition test was performed using a catalyst reactor that was approximately 25.4 mm (1 in) in diameter packed with approximately 5 mm of catalysts. The N₂O decomposition tests were carried out with approximately 1% N₂O at 550 to 750 ℃, an ambient pressure, and a GHSV=1800-2000 h^-1. To confirm the N₂O decomposition properties and the effect of O₂ and steam on the N₂O decomposition, nitrogen, air, and air and steam were used as atmospheric gases. The catalytic decomposition tests showed that the 1% N₂O had almost completely disappeared at 700 ℃ in an N₂ atmosphere. However, air and steam decreased the conversion rate drastically. The long term stability test carried out under an N₂ atmosphere at 700 ℃ for 350 h showed that the N₂O conversion rate remained very stable, confirming no catalytic activity changes. From the results of the N₂O decomposition tests and long-term stability test, it is expected that the prepared γ-Al₂O₃ catalyst can be used to reduce N₂O emissions from several industries including the semiconductor, display, and nitric acid manufacturing industry.

• Transactions of the Korean hydrogen and new energy society
• /
• v.25 no.6
• /
• pp.577-585
• /
• 2014

Nanorod and particle shape $CeO_2$ were synthesized via hydrothermal process and precipitation method, respectively, and used as supports of Pt catalyst for water gas shift (WGS) reaction. Three different durations (12, 48, and 96h) for hydrothermal process were applied for the preparation of nanorod type $CeO_2$. 1.0 wt% of Pt was loaded on the prepared supports with incipient wetness method prior to the catalytic activity tests that were carried out at a GHSV of $95,541h^{-1}$, and a temperature range of 200 to $360^{\circ}C$. Varying duration of hydrothermal process led to the difference in physical characteristics of $CeO_2$ nanorods, such as aspect ratio, BET surface area, pore diameter, and pore volume. Consequently, the catalytic activities of Pt/$CeO_2$ nanorods were affected by the physical characteristics of the supports and appeared to be in the order of Pt/$CeO_2$(12) > Pt/$CeO_2$(48) > Pt/$CeO_2$(96). The comparison of the catalytic activities and results of the analysis (XPS, XRD, SEM, BET and TPR) for the supports revealed that the activity of the catalysts depends on chemical states of the Pt and the support materials in the temperature range that is lower than $280^{\circ}C$. However, the activity is rather dependent on the physical characteristic of the supports because the increased gas velocity limits the mass transfer of reactants in micropores of the supports.

• Transactions of the Korean hydrogen and new energy society
• /
• v.28 no.1
• /
• pp.1-8
• /
• 2017

Cu/Mn/Ce catalysts for water gas shift (WGS) reaction were synthesized by urea-nitrate combustion method with the fixed molar ratio of Cu/Mn as 1:4 and 1:1 with the doping concentration of Ce from 0.3 to 0.8 mol%. The prepared catalysts were characterized with SEM, BET, XRD, XPS, $H_2$-TPR, $CO_2$ TPD, $N_2O$ chemisorption analysis. The catalytic activity tests were carried out at a GHSV of $28,000h^{-1}$ and a temperature range of 200 to $400^{\circ}C$. The Cu/Mn(CM) catalysts formed Cu-Mn mixed oxide of spinel structure ($Cu_{1.5}Mn_{1.5}O_4$) and manganese oxides ($MnO_x$). However, when a small amount of Ce was doped, the growth of $Cu_{1.5}Mn_{1.5}O_4$ was inhibited and the degree of Cu dispersion were increased. Also, the doping of Ce on the CM catalyst reduced the reduction temperature and the base site to induce the active site of the catalyst to be exposed on the catalyst surface. From the XPS analysis, it was confirmed that maintaining the oxidation state of Cu appropriately was a main factor in the WGS reaction. Consequently, Ce as support and dopant in the water gas shift reaction catalysts exhibited the enhanced catalytic activities on CM catalysts. We found that proper amount of Ce by preparing catalysts with different Cu/Mn ratios.

• Applied Chemistry for Engineering
• /
• v.26 no.2
• /
• pp.154-158
• /
• 2015

In this study, the catalytic activity of ${\gamma}-Al_2O_3$ was investigated for the decomposition of $NF_3$. Reactions for $NF_3$ decomposition were carried out in the range of reaction temperature of $330{\sim}730^{\circ}C$ and GHSV of $3,000{\sim}15,000mL/g-cat{\cdot}h$ in a fixed-bed catalytic reactor system. Thermal decomposition of $NF_3$ was also performed in order to compare with the catalytic decomposition of $NF_3$. The conversion of $NF_3$ by the catalytic decomposition at $400^{\circ}C$ was four times higher than that of the thermal decomposition. It was confirmed that the reaction behavior of $NF_3$ over ${\gamma}-Al_2O_3$ exhibited two reaction pathways in the presence of steam. Fluorine in $NF_3$ over ${\gamma}-Al_2O_3$ was chemically absorbed to $AlF_3$ by the gas-solid reaction in the absence of steam. The catalytic decomposition of $NF_3$ occurred by hydrolysis with steam. It was also confirmed by FT-IR analysis that $NF_3$ was completely decomposed to NOx and HF above $500^{\circ}C$.