• Transactions of Materials Processing
• /
• v.18 no.4
• /
• pp.329-335
• /
• 2009

In order to better predict the springback for friction stir welded DP590 steel sheet, the combined isotropic-kinematic hardening was formulated with considering the permanent softening behavior during reverse loading. As for yield function, the non-quadratic anisotropic yield function, Yld2000-2d, was used under plane stress condition. For the verification purposes, comparisons of simulation and experiments were performed here for the unconstrained cylindrical bending, the 2-D draw bending tests. For two applications, simulations showed good agreements with experiments.

• Journal of Welding and Joining
• /
• v.12 no.1
• /
• pp.80-93
• /
• 1994

The microstructure and fractography of the friction welded joint of Al to Cu have been investigated in order to understand the formation of intermetallic compounds and their effects on the failure in tensile test of the joint. The variation of welding pressure did not affect significantly the tensile strength of joint. However, the tensile strength of joint decreaed as welding time increased. The thickness of reaction layers of welded joints was several micro-meters and mainly composed of intermetallic compounds of $CuAl_2$, $Cu_9Al_4$ and Al+$CuAl_2$. The thickness of $CuAl_2$, $Cu_9Al_4$ was increased with welding time. However, $CuAl_2$ was gradually changed to $Cu_9Al_4$ which caused the decrease of tensile strength . Even though the morphology of fractured surfaces depended upon the welding time, the failure occurred along $CuAl_2$ intermetallic compound itself or between $CuAl_2$ and $Cu_9Al_4$ in most cases.

• Journal of Welding and Joining
• /
• v.31 no.2
• /
• pp.21-25
• /
• 2013

Aluminum alloys have been considered for substantial use in these industries. This ensues from their attractive strength to weight ratio, superb formability, apposite weldability and acceptable corrosion resistance. Depending on the specific application, corrosion behavior is a significant factor of a welded joint. In this study, recent researches in the view of corrosion resistance of friction stir welded aluminum alloys are briefly reviewed.

• Journal of Welding and Joining
• /
• v.15 no.4
• /
• pp.90-98
• /
• 1997

A copper-tungsten sintered alloy(Cu-W) has been friction welded to a tough pitch copper in order to investigate the effect of friction pressure on bonding strength and a charicteristic of fracture. The tensile strength of the friction welded joint was increased up to 90% of the Cu base metal under the condition of friction time 1.2 sec, friction pressure 4.5kgf/$\textrm{mm}^2$ and upset pressure 10kgf/$\textrm{mm}^2$. From the results of fracture surface analysis, the increase of friction pressure could remarkably decrease the force and the time to be normally acted on weld interface. The W particles which were included in the plastic zone of Cu side could induce fracture adjacent to the weld interface because their existance in Cu induces a decrease in available section area and an increase in notch effect. Therefore, the tensile strength was decreased at high friction pressure (6kgf/$\textrm{mm}^2$) because the destruction of W was increased by an increase in mechanical force and crack was formed at weld interface.

• Proceedings of the KWS Conference
• /
• 2001.05a
• /
• pp.120-121
• /
• 2001

• Journal of Ocean Engineering and Technology
• /
• v.10 no.3
• /
• pp.24-33
• /
• 1996

Up to now, most of studies on mechanical properties in friction welded components are about tensile and bending strength. However the fatigue studies on the friction-welded components subjected to repeated stress are not available. The purposes of this study are the development of fundamental design and the development of in-process real-time weld quality evaluation technique by acoustic emission for the bar-to-bar dissimilar friction welding of hydraulic valve spool steels.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.7 no.2
• /
• pp.47-53
• /
• 1998

In this study, behavior of deformation and mechanical properties under static tensile load in friction welded dissimilar materials. and necking phenomenon occuring at yeilding point are shown. Behavior of Hv(Micro Vickers Hardness) is observed that the maximum value is occured near by the interface. and the minimum value is arised at the heat affected zone. Fracture occured at the minimu value of Hv of the heat affected zone is observed. The position of fracture surface is subjected to behavior of Hv. Yielding strength subjected to friction welding conditions, specially to upset pressure is shown.

• Journal of Welding and Joining
• /
• v.17 no.5
• /
• pp.69-76
• /
• 1999

A copper-tungsten sintered alloy(Cu-W) has been friction welded to a tough pitch copper in order to investigate the effect of upset pressure on friction weldability. Under the condition of friction time 0.8sec, upset pressure 150MPa, the tensile strength and Charpy impact value of the friction welded joint were 336MPa, $400KJ/m^2$ respectively. And highest temperature of the weld measured was below $800^{circ}K$ which is very lower than melting point of Cu($1356^{circ}K$). Under the same conditions, W grains picked up in Cu matrix from Cu-W profitably affected on these mechanical fracture, and were dispersed in Cu by plastic flow during brake time.

• Journal of Welding and Joining
• /
• v.15 no.6
• /
• pp.78-84
• /
• 1997

Friction welding technique was studied to weld the turbine wheel and shaft of a turbocharger. The welding parameters were selected to investigate the effects of variables on welding quality of Inconel 713C and SCM 440. Experimental results showed that the turbine wheel and shaft could be successfully welded by friction welding. The heat affected zone was identified to be 2 mm from the weld seam. After welding, the hardness profile was found to have sudden increase and decrease for inconel 713C and SCM 440 respectively. Tensile strength of welded specimens was higher than the required strength for all of the studied welding parameters. The central portion of fracture surfaces by bending had no defects such as crack.

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2002.10a
• /
• pp.283-288
• /
• 2002

This study accompanied with the friction welding of a spheroidal graphite cast iron bar and 2024 Aluminium alloy bar with A1050 insert metal and investigated between conditions of friction welding faces and welded joint strength. This principal results of the experimental investigation could be summarized as follows: If the optimum friction welding is selected, the aspect of the spheroidal graphite cast iron and 2024 Aluminium could be welded with a pure Aluminium insert metal.