• Journal of Welding and Joining
• /
• 제33권2호
• /
• pp.8-13
• /
• 2015

This study was carried out to evaluate mechanical properties of the jointed Al6061/HT590 alloys by friction stir welding (FSW). FSW was conducted under the conditions with tool rotating speed of 500 RPM and traveling speed of 300 mm/min., where Ar gas was introduced to prevent the materials from corrosion during the welding process. Electron back-scattering diffraction (EBSD) was used to characterize microstructures such as grain size, misorientation angle and crystal orientation. Evolution of intermetallic compounds in Al6061 during the process were examined in terms of morphology, size and aspect ratio at three distinct zones Al base material, heat affected zone and stir zone, where transmission electron microscope (TEM) was used. It was revealed that FSW gave rise to refinement of grains as well as growth of intermetallic compounds in Al6061. The morphological changes of intermetallic compounds exerted an influence on mechanical properties, resulting in occurrence of fracture in the part of the base material instead of the jointed parts (heat affected zone and stir zone). This study systematically evaluated the microstructural evolutions during the FSW for joining Al6061 with HT590 and their effect on mechanical properties.

• 동력기계공학회지
• /
• 제21권5호
• /
• pp.86-91
• /
• 2017

Friction Stir Welding (FSW) is useful technique to join aluminum alloy with energy efficient and environment friendly. In this paper, the design of experiment with three-way factorial design was adopted for optimum conditions of welding variables in the FSW of Al 6061 alloy. Tools of shoulder diameter of 9, 12, 15 mm and pin length of 1.5 mm were used. Also the material's dimension for welding were $2{\times}100{\times}150mm$, and the tensile specimens were worked by water-jet technique. Welding variables were shoulder diameter, rotating speed and travel speed of tool. From the results of this work, the welding factor influenced on yield strength most was travel speed and the optimum condition for FSW was predicted as the shoulder diameter of 15 mm, welding speed of 500 mm/min and rotating speed of 2,000 rpm. Also the presumption range of yield strength at optimal condition of reliability 99% was estimated to $207.19{\pm}9.91MPa$.

• International journal of advanced smart convergence
• /
• 제4권1호
• /
• pp.145-153
• /
• 2015

Friction Stir Welding (FSW) is a solid state welding that could successfully weld the difficult-to-weldmaterials such as an aluminum alloy. In this welding process, the stirrer of the welding tool is one of the important factors for producing the perfect sound joint that indicates the higher joint strength. So, this report aims to apply the friction stir welding using various stirrer geometries to weld the AA6063-T1 aluminum alloy butt joint, investigates the mechanical properties of the joint and then compares the mechanical properties with the microstructure of the joint. An experiment was started by applying the friction stir welding process to weld a 6.3 mm thickness of AA6063-T1 aluminum alloy butt joint. A study of the stirrer geometries effect such as a cylindrical geometry, a cone geometry, a left screw geometry and a right screw geometry at a rotational speed of 2000 rpm and a welding speed of 50-200 mm/min was performed. The mechanical properties such as a tensile strength and a hardness of the joint were also investigated and compared with the microstructure of the joint. The results are as follows. A variation of FSW Stirrer shape directly affected the quality AA6063-T1 aluminum alloy butt joint. A cylindrical stirrer shape and a cone stirrer shape produced the void defect at the bottom part of the weld metal and initiated the failure of the joint when the joint was subjected to the load during the tensile test. Left and right screw stirrer shapes gave the sound joint with no void defect in the weld metal and affected to increase the joint strength that was higher than that of the aluminum base metal.

• 융합정보논문지
• /
• 제9권7호
• /
• pp.94-99
• /
• 2019

마찰교반용접법(Friction Stir Welding, FSW)은 1991년에 영국 용접연구소 TWI(The Welding Institute)에서 최초 개발된 후 여러 산업분야에 걸쳐 적용연구가 활발히 진행되고 있다. 본 연구에서는 철도차량 차체의 주요 구성 소재인 알루미늄 합금 (Al-6005-T6) 평판 압출재에 대한 마찰교반접합 적용 기초연구를 수행하였다. 접합속도를 500 mm/min으로 고정한 채 회전공구의 회전속도를 600-1600 rpm으로 변화될 때 미세구조와 기계적 물성 변화에 미치는 영향에 대해 평가하였다. 경도 측정 결과 nugget부는 모재의 70% 수준의 경도값을 가지며 설정된 범위 내의 공구 회전속도와 연관성은 관찰되지 않았으며 용접계면에서 약 5 mm 벗어나게 되면 모재의 경도값을 가지는 것으로 확인되었다. 인장시험 결과 회전속도가 올라갈수록 항복강도와 인장강도가 소폭 하락하는 경향을 보였으며 연신률의 변화는 관찰되지 않았다.

• Journal of Welding and Joining
• /
• 제19권6호
• /
• pp.584-590
• /
• 2001

• 한국마린엔지니어링학회:학술대회논문집
• /
• 한국마린엔지니어링학회 2002년도 춘계학술대회논문집
• /
• pp.153-160
• /
• 2002

This paper shows the possibility of performing Lap joint using the friction stir welding and the determination of tool's dimensions for FSW in Milling machine. This research also is reported on obtaining the tensile-shear strength, 9.319 ( kgf/mm$^{2}$) and the energy absorption, 2,682 (kgf-mm) under this experiment. The optimal tool's dimensions and method for Lap joint in 2tmm aluminum alloy plate using FSW is as follows; The diameter of shoulder and pin are 9 $\phi$mm and 3$\phi$mm, the length of pin is 3.6mm. The conditions of shoulder of tool is not pressed into original base metal.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2005년도 춘계학술발표대회 개요집
• /
• pp.171-173
• /
• 2005

To evaluate the applicability of dissimilar metal friction stir welding in automobile manufacturing process, friction stir welding trials were carried out for typical 5000 and 6000 series aluminum alloy sheets with 2mm thickness. The sound joints of A15052 and A16061-T6 alloys were successfully formed under a wide range of welding condition. Excellent weld ability has been obtained at a condition of rotating speed 2000rpm and travel speed 100mm/min, while a radiographic test also confirmed defect free joint for this condition. Through the Erichsen cup test, the plastic formability of the FSWelded joints was found to be about 83% of base metal.

• 한국공작기계학회논문집
• /
• 제17권4호
• /
• pp.22-28
• /
• 2008

Friction stir welding(FSW) is an relatively new solid state joining process. A1606l-T6 aluminium alloy has gathered wide acceptance in the fabrication of light weight structures requiring a high strength to weight ratio and good corrosion resistance. This friction stir process(FSP) uses a non-consumable tool to generate frictional heat in the abutting surfaces. The welding parameters such as tool rotational speed, welding speed, etc., and tool pin profile playa major role in deciding FSP zone formation in A16061-T6 aluminium alloy. Tow different tool pin profiles have been used to fabricate the joints. The formation of friction stir processed zone has been analysed macroscopically. Tensile properties of the joints have been evaluated and correlated with the friction stir processed zone formation.

• 한국분말재료학회지
• /
• 제22권3호
• /
• pp.181-186
• /
• 2015

In this study, the effect of the friction stir welding (FSW) was compared with that of the gas tungsten arc welding (GTAW) on the microstructure and microhardness of Cu-Ni alloy weldment. The weldment of 10 mm thickness was fabricated by FSW and GTAW, respectively. Both weldments were compared with each other by optical microstructure, microhardness test and grain size measurement. Results of this study suggest that the microhardness decreased from the base metal (BM) to the heat affected zone (HAZ) and increased at fusion zone (FZ) of GTAW and stir zone (SZ) of FSW. the minimum Hv value of both weldment was obtained at HAZ, respectively, which represents the softening zone, whereas Hv value of FSW weldment was little higher than that of GTAW weldment. These phenomena can be explained by the grain size difference between HAZs of each weldment. Grain size was increased at the HAZ during FSW and GTAW. Because FSW is a solid-state joining process obtaining the lower heat-input generated by rotating shoulder than heat generated in the arc of GTAW.

• Journal of Welding and Joining
• /
• 제27권5호
• /
• pp.81-87
• /
• 2009

Recently, extruded aluminium-alloy panels have been used in the car bodies for the purpose of the light-weight of railway vehicles and FSW(Friction Stir Welding), which is superior to the arc weldings, has been applied in the railway vehicles. This paper presents the optimum design of the FSW process on A6005 extruded alloy for railway vehicles to improve its mechanical properties. Rotational speed, welding speed and tilting angle of the tool tip were chosen as design parameters. Three objective functions were determined; maximizing the tensile strength, minimizing the hardness and maximizing the difference between the normalized tensile strength and hardness. The tensile tests and the hardness tests for fifteen FSW experiments were carried out according to the central composite design table. Recursive model functions on three characteristic values, such as the tensile strength, the hardness difference(${\Delta}Hv$) and the difference of normalized tensile strength and ${\Delta}Hv$, were estimated according to the classical response surface analysis methodology. The reliability of each recursive function was verified by F-test using the analysis of variance table. Sensitivity analysis on each characteristic value was done. Finally, the optimum values of three design parameters were found using Sequential Quadratic Programming algorithm.