• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.30 no.6
• /
• pp.232-236
• /
• 2020

In this study, the optical properties of CaF2-Al2O3-B2O3-TiO2 (CABT) system glass doped with rare earth ion, that is used in various light devices due to its excellent luminous properties, were analyzed as a function of kind of crystal phases formed and size of crystals generated in the glass matrix. TiO2 was added to control nucleation and crystallization, and Eu2O3 was added to enhance the luminescence characteristics. DTA analysis was performed to confirm the heat treatment condition of crystal generation, and XRD and SEM anal ysis were carried out for the crystal phase change of nanometer size. As a result of the analysis, the luminous properties of oxy-fluoride-based glass were improved duo to crystallization of nanometer size, but was rather degraded when excessively large crystals were generated.

• Journal of the Optical Society of Korea
• /
• v.7 no.3
• /
• pp.156-159
• /
• 2003

Permanent structure of photoinduced singlemode waveguide in optical fluoride glasses was demonstrated using the self-channeled plasma filament excited by a femtosecond (110 fs) Ti:sapphire laser ($λ_p$ = 800 nm). The photoinduced refractive index modification in ZBLAN glasses reached a length of approximately 10 - 15 mm from the input surface of the optical glass with the diameters ranging from 5 to 8 ${\mu}{\textrm}{m}$ at input intensities more than l.0 ${\times}$ $10^{12}$ W/$\textrm{cm}^2$. The graded refractive index profiles were fabricated to be a symmetric form from the center of an optical fluoride glass and a maximum value of refractive index change (ㅿn) was measured to be l.3${\times}$$10^{-2}$. The beam profile of the output beam transmitted through the modified region showed that the photoinduced refractive index modification produced a permanent structure of singlemode waveguide.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.31 no.2
• /
• pp.84-88
• /
• 2021

The change of the photoluminescence properties of La2O3-CaF2-Al2O3-SiO2 glass-ceramics doped with rare earth material, that is used as laser and optical sensors, was analyzed according to heat treatment temperature. The heat treatment conditions for fabricating glass-ceramics were obtained through non-isothermal thermal analysis, and X-ray diffraction analysis was performed to determine the degree of crystal growth and kinds of crystal phases generated according to the heat treatment temperature. Using Scherrer's equation, it was predicted that crystals with a size of 25~40 nm would be generated inside the glass-ceramics. Photoluminescence (PL) analysis showed that the specimens heat-treated at 660℃ to 670℃ for 1 hour had the highest PL intensity. Also, from the CIE color coordinate analysis, all glass-ceramics specimens emitted red-orange light regardless of the heat treatment condition.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.34 no.3
• /
• pp.408-419
• /
• 2007

In the child, it is very important that he/she will have the ability to suppress aesthetic restorative materials of secondary caries. With the representative preventive material against caries, the importance of fluoride is more emphasized. This study examined the differences in fluoride release and re-uptake among some restorative materials, following a treatment of APF gel and fluoride varnish. The surface roughness was observed under scanning electron microscope. Studying this will provide for the research to find effective restorative materials and fluoride type in tooth caries prevention. It is applied from presence at a clinic that restorative materials are resin, flowable resin, compomer and glass ionomer. Fluoride release was measured at 24-hour intervals for 7 days, 3-day intervals from 8th to 38th day using an ion-selective electrode and analyzer. Then, the materials were treated with the fluoride gel and fluoride varnish respectively, fluoride release was measured and specimens were evaluated under scanning electron microscope for 4 weeks. It was concluded that 1. Fluoride was released for 38 days from restorative materials under 1 ppm in case of flowable resin, 1-2 ppm in compomer and 2-8 ppm in glass ionomer, a few of fluoride was released after 45 days 2. Fluoride has more releasing after application of APF gel than fluoride varnish. Fluoride re-uptake was observed under 0.6-0.2 ppm in fluoride varnish and 0.6-2.6 ppm in APF gel after starting the procedure one day(p<0.05). For the remaining 4 weeks, they demonstrated a similar release. 3. Specimens were evaluated under scanning electron microscope. Applied fluoride in the experimental group surface was rougher than the control group that did not receive fluoride application. Fluoride varnish group had a smoother surface than both the APF gel group and the varnish APF gel group that received a fluoride application.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.29 no.1
• /
• pp.1-10
• /
• 2002

The purpose of this study was to evaluate the fluoride release and anticariogenic effect of two compomers which is known to have been developed to improve the weak properties of glass ionomer cement and composite resin. Z-100 as composite resin(Group I), Dyract AP(Group II) and F-2000(Group III) as compomer, and Fuji II LC as glass ionomer cement(Group IV) were used as test materials and evaluations were peformed by pH/ISE meter far analyses of fluoride and polarizing microscope for analyses of anticariogenicity. The results can be summarized as follows: 1. The amount of fluoride release in compoite resin and compomer groups showed general pattern of decline during test period. Z-100 showed no fluoride release during test period. Fuji II LC showed the highest fluoride release among test groups and then F-2000 were followed. 2. The least resistance to dimineralization was observed microscopically in Z-100 group which has no fluoride in it. The best resistance to dimineralization was observed microscopically in Fuji II LC group and then compomer groups were followed. 3. Significant difference in lesion area was found between Fuji II LC group and another groups. Significant difference in lesion area was found between compomer groups and Z-100 group. No significant difference in lesion area was found between Dyract AP group and F-2000 cup. 4. Two compomers showed continual fluoride release and anticariogenic effect around filling materials. therefore, compomer was evaluated very attractive restorative material in pediatric dentistry.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.35 no.2
• /
• pp.81-89
• /
• 2019

Purpose: This study aimed to investigate the correlation between the solubility and the amount of fluoride release when a resin surface coating agent is applied to RMGIC. Materials and Methods: To measure the fluoride release and solubility, Fuji II $LC^{(R)}$and $Filtek^{TM}$ Z350XT without a surface coating, Fuji II $LC^{(R)}$ with G coat $plus^{TM}$ and Fuji II $LC^{(R)}$ with $Permaseal^{(R)}$ were prepared. And the amount of fluoride release and solubility were measured. Results: There was no significant difference in the daily fluoride release between the surface coating agents. The cumulative fluoride release was significantly different between the groups using RMGIC at 56 days (P < 0.05). In the solubility measurement, RMGIC without surface coating was significantly different only on the 7th day compared to the other three groups (P < 0.05). Conclusion: Surface coating agents can prevent the degradation of properties by the initial solvent in RMGIC. Therefore, fluoride is preserved inside the restorative material and the effect of surface coating after the addition is reduced, so that the effect on fluoride release and storage is also reduced.

• Restorative Dentistry and Endodontics
• /
• v.44 no.3
• /
• pp.24.1-24.1
• /
• 2019

• The korean journal of orthodontics
• /
• v.43 no.1
• /
• pp.29-34
• /
• 2013

Objective: To examine the prophylactic potential of 3 orthodontic bonding adhesives: Fuji Ortho SC, Illuminate, and Resilience. Methods: Thirty-six Wistar Wag rats were randomly divided into 4 groups consisting of 9 rats each. One of the groups received no treatment and was used as a control. In the other groups, individual bands coated with one of the 3 adhesives were cemented to the lower incisors. Enamel samples were obtained after 6 and 12 weeks and analyzed using scanning electron microscopy in combination with energy dispersive spectrometry. Results: Six weeks after band cementation, no fluoride was found in the enamel of the lower incisors. After 12 weeks, there was no fluoride in the enamel of teeth coated with the Resilience composite. However, in the case of the Illuminate composite and the resin-modified glass ionomer Fuji Ortho SC cement, the depth of fluoride penetration reached $2{\mu}m$ and $4.8-5.7{\mu}m$, respectively. Conclusions: Fluoride ions from orthodontic adhesives can be incorporated into the surface layer of the enamel. Orthodontists may apply orthodontic adhesives, such as the Fuji Ortho SC, to reduce the occurrence of caries during orthodontic treatment with fixed appliances.

• Restorative Dentistry and Endodontics
• /
• v.21 no.2
• /
• pp.635-641
• /
• 1996

This study was designed to evaluate the anti cariogenic effect of F in primers, bonding agents, composite resins or glass ionomer cements in enamel. Twenty-five extracted teeth were selected and a cavity was prepared on either the buccal or the lingual surface of each tooth. After pumicing and etching, the samples were divided into 5 groups. In group A, the samples were primed, bonded and filled with ART bond and Brilliant Enamel (Coltene, Switzerland). Group B composed of Optibond and Herculited XRV (Kerr, USA), group C composed of Syntac and Tetric(Vivadent, Lichtenstein), and group D composed of Scotch-bond Multipurpose and Z 100 (3M, YSA). In group E, the samples were filled with glass ionomer cement (Fuji II LC, Japan), All surfaces except the 2mm beyond the cavosurface margin of the sample were protected, and samples were then put into an acid buffer for 3 days to develop the initial caries. The samples were then sectioned through the filling body into thin wafers and then examined with a polarizing microscope under water imbibition. The fluoride in primer, bonding agent, or composite filling material did not prevent the initial caries in the enamel area adjacent to the filling body whereas the fluoride in the glass ionomer did prevent the initial stage caries.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.35 no.3
• /
• pp.469-476
• /
• 2008

This study was performed to compare the fluoride release pattern and compressive strength of recently developed resin-modified glass ionomers($Ketac^{TM}$ N 100 and Fuji Fil LC) with those of conventional glass ionomer restorative material(Fuji II LC). Fifteen sample discs(6 mm diameter and 1 mm height) were prepared for each tested material. The fluoride release was measured by pH/ISE meter(750P, Istek, Korea) for 31 days. For compressive strength experiment, fifteen cylindrical specimens were prepared for each tested material. Each specimen was submitted to compressive strength testing in an universal testing machine(Kyung-sung Testing Machine Co., Korea) at crosshead speed of 5.0mm/min until failure. The results can be summarized as follows; 1. Fuji Fil LC released the highest amount of fluoride, followed by Fuji II LC and $Ketac^{TM}$ N 100(p<0.05). 2. The compressive strength of Fuji Fil LC was the lowest(p<0.05). However, no significant difference was found from Fuji II LC and $Ketac^{TM}$ N 100(p>0.05). By considering the above results, careful case selection and accurate clinical application is recommended when using $Ketac^{TM}$ N 100 and Fuji Fil LC.