• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.676-677
• /
• 2006

Synthesis of zinc oxide nanorods, sheets and flower like structure were done by the sol-gel method using zinc acetate dihydrate and sodium hydroxide at $80^{\circ}C$ with 12 hours refluxing time nanorods, in case of as synthesized powder, with diameter of 20-60nm. Annealing at higher temperature (300 and $500^{\circ}C$,) in air ambient changes the morphology to sheet and flower like structure. The standard peak of zinc oxide was observed in IR at $523cm^{-1}$. The UV-VIS spectroscopy of zinc oxide shows a characteristic peak at 375nm.

• Bulletin of the Korean Chemical Society
• /
• 제35권4호
• /
• pp.1091-1097
• /
• 2014

Tageteserecta flower like zinc oxide nanostructures composed of hexagonal nanorods were synthesized via sonochemical method at room temperature. The synthesized nanomaterials exhibited wurtzite hexagonal phase structure with the single crystalline nature. The diameter of the individual nanorods that constitute the flower shaped zinc oxide structures is in the range of 120-160 nm. The sonication time effectively determined the morphological properties of the prepared materials. The catalytic activity of prepared zinc oxide nanostructures towards N-formylation reactions were evaluated without any surface modification and the nanostructures exhibited good reaction yield with the prompt recyclability behavior.

• 한국포장학회지
• /
• 제22권3호
• /
• pp.85-93
• /
• 2016

본 연구에서는 초음파합성법을 이용하여 항균성과 자외선 차단성이 있는 삼차원 꽃 모양의 구조를 가진 FZnO를 제조하였다. 제조한 FZnO 분말은 E. coli와 S. aureus에 대해 99.9%와 97.8%의 항균력을 나타내었다. 제조한 LDPE/FZnO 복합필름에 대한 FTIR 분석과 SEM 분석결과 LDPE/FZnO 복합필름이 성공적으로 만들어졌지만, LDPE 매트릭스와 FZnO 분말과의 상호작용은 약한 것으로 확인되었다. FZnO 함량이 증가할수록 자외선 차단성이 증가하는 것을 확인할 수 있었다. 또한, FZnO함량이 증가할수록 E. coli와 S. aureus에 대한 항균성이 증가하는 것을 확인하였다. 하지만, 복합필름 내 물성 극대화 및 포장소재로 적용을 위해서는 FZnO 분말과 고분자와의 혼화성 향상에 대한 추가적인 연구가 필요하다는 것을 확인하였다.

• 센서학회지
• /
• 제19권5호
• /
• pp.356-360
• /
• 2010

Due to the high surface-to-volume ratio, the 3-dimensional(3D) nanostructures of metal oxides are regarded as the best candidate materials for the chemical gas sensors. Here we have synthesised flower-like 3D zinc oxide nanostructures through a simple hydrothermal route. Specific surface area of the 3D zinc oxide nanostructures synthesised in different pH values from 9.0 to 12.0 were evaluated by using a BET analyzer and the results were compared with that of a zinc oxide thin film fabricated by rf sputtering. Using interdigitated electrodes, superior CO gas sensing properties of the 3D zinc oxide nanostructures on the ZnO thin film to those of the ZnO thin film were demonstrated.

• 한국응용과학기술학회지
• /
• 제33권1호
• /
• pp.23-29
• /
• 2016

육방정계 우르자이츠형의 산화아연은 n형 반도체로써 3.37 eV의 넓은 밴드갭 에너지와 60 meV의 큰 엑시톤 바인딩 에너지를 가진 물질이다. 가스센서, 발광 다이오드, 염료 감응 태양 전지, 염료오염의 분해 등의 넓은 범위에서 활용이 가능하다. 합성 시 마이크로파 수열합성법을 사용하게 되면 높은 수율, 빠른 반응속도, 에너지 절약의 장점이 있다. 아민첨가제는 수산이온 생성 및 킬레이트 효과로 인해 산화아연 입자 형상을 조정하는 역할을 한다. 본 논문에서는 전구체로는 질산아연육수화물을 사용하였고, 형상조정제로는 에탄올아민, 에틸렌디아민, 디에틸렌트리아민, 헥사메틸렌테트라민을 사용하였다. 수산화소듐을 사용하여 용액을 pH 11로 조정하였다. 합성된 산화아연은 별모양, 막대형, 꽃모양, 원추형의 다양한 형상을 확인할 수 있었다. 아민첨가제에 의한 물리 화학적 특성과 광학적 특성을 분석하기 위해 XRD, SEM, EDS, FT-IR, UV-vis 스펙트럼, PL 스펙트럼을 사용하였다.

• 대한화학회지
• /
• 제60권1호
• /
• pp.34-38
• /
• 2016

본 연구는 zinc acetate dihydrate와 sodium hydroxide를 사용하여 ZnO nanoparticles (ZnO NPs)을 합성하였다. 실험에 사용된 방법은 초음파 방법이다. 같은 농도의 각각 zinc acetate dihydrate와 sodium hydroxide를 de-ionized water에 넣고 30분간 교반 하였다. 이 과정에서 생성된 백색의 생성물은 교반 하면서 ultrasonic processor을 사용하여 각각 60분, 120분, 180분, 240분, 360분 처리하였다. 생성물들은 원심분리 후 남은 이온들을 제거하기 위하여 에탄올을 사용하여 여러 번 세척하고, 50 ℃에서 24시간 동안 건조하였다. 합성된 물질들의 결정성과 구조적 특성을 확인하기 위하여 X-ray diffraction spectroscopy(XRD)와 Field emission scanning electron microscopy(FE-SEM)을 사용하였다. 광 촉매 효과는 오염물질 대신 Rhodamin-B를 사용하여 UV 조사하에 암실에서 실험하였다. 광 촉매 효과는 UV-vis spectrometer를 이용하여 확인하였다. XRD 결과 순수한 ZnO가 합성된 것을 확인 하였다. FE-SEM을 통하여 시간이 지남에 따라 구 형태에서 막대형태를 지나 꽃 형태로 변하는 것을 확인 할 수 있었다. 광촉매 특성 결과 꽃 형태를 가진 ZnO NPs가 광 촉매 특성이 가장 우수한 것으로 확인 되었다.