• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.5 no.3
• /
• pp.233-239
• /
• 1995

$La_{1/3}NbO_3$ and $La_{1/3}TaO_3$ large single crystal was prepared by the infrared floating zone method and their crystal structure and dielectric properties were investigated from the viewpoint of A - site vacancy. In $La_{1/3}TaO_3$ crystal, the crystal symmetry and approximate lattice constants was tetragonal and a $\approx$ 0.397, b $\approx$ 0.397 and c $\approx$ 0.775 from the nonextinction and the reciprocal lattice point length seen on Weissenberg and Precession photographs. The jump of some $2/3La^{3+}$ ions leads to increase the moving paths due to the generation of new vacancies at middle empty sites and thus this result is confirmed to provoke the dielectric anomaly.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.5 no.3
• /
• pp.209-214
• /
• 1995

Abstract 0.2 wt % $Fe_2O_3$ doped $SrTiO_3$ single crystals were grown by floating zone method in air and Nz atmosphere, respectively. The growth rate was fixed at 5 mm/hr and rotation speed was maintained at 30 rpm. As - grown crystals were cut perpendicular to its growth direction and then, annealed at 900, 1000 and $1100^{\circ}C$ for 2 hours in Nz atmosphere. Resistivities of each samples were measured and then converted into conductivities. By using these conductivity values, the activation energies were calculated and by means of the calculated activation energies, mechanism which contribute to increasing the electrical conductivity were investigated.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.5 no.3
• /
• pp.240-249
• /
• 1995

Rutile type of $TiO_{2}$ single crystal was grown by floating zone method in order to obtain the highly transparent and contamination-free single crystal. The linear refractive index of perpendicular and parallel to c-axis was measured as a function o f wavelength from 500 to 1000nm. The optical energy band gap was estimated as 2.99 eV from the absorption spectrum. The theoretical $\chi^{(3)}$} value of $TiO_{2}$ was discussed in comparison with that of $SiO_{2}$ quartz single crystal on the basis of semiempirical model. On the other hand, the second-hyperpolarizability, ${\gamma}({Ti}^{4+})$ was calculated in order to describe the effect of $Ti_{4}$ ion on the third order nonlinear optical properties.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.6 no.3
• /
• pp.368-376
• /
• 1996

$LiNbO_{3}$ single crystals (undoped, 5 mol% MgO-doped and 5 mol% ZnO-doped) were grown by the floating zone method which has the characteristics of a compositional homogeneity and uniform distribution of the dopants. The optimum growth condition was established experimentally and the defect structures such as domain structure, dislocation structure, slip band, and microtwins were characterized using a microscopic method.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.24 no.12
• /
• pp.2909-2916
• /
• 2000

6.5wt% Si steel is widely known as an excellent magnetic material because its magnetostriction is nearly zero. The AX magnetic properties as magnetostriction of 6.5% Si steel were evaluated and compared with those of conventional 3% Si steel sheet. In this paper, the fracture behavior of the poly crystals and single crystals of Fe-6.5wt%Si alloy has been observed. Single crystals were prepared by Floating Zone(FZ) method, which melts the alloy by the use of high temperature electron beam in pure argon gas condition. And the single crystals were annealed at 500$^{\circ}C$ and 700$^{\circ}C$ respectively and tensile tested at room temperature. According to the result, B2 phase has more good elongation than DO$_3$ phase. It was also found that the fracture surfaces of the single crystals have hairline facets in same direction, and the facets change the direction according to the single crystal phase.

• Korean Journal of Materials Research
• /
• v.27 no.7
• /
• pp.369-373
• /
• 2017

Unidirectionally solidified TiAl alloys were prepared by optically-heated floating zone method at growth rates of 10 to 70 mm/h in flowing argon. The microstructures and tensile properties of these crystal bars were found to depend strongly on the growth rate and alloy composition. TiAl alloys with composition of 47 and 50 at.%Al grown under the condition of 10 mm/h showed $Ti_3Al({\alpha}_2)/TiAl({\gamma})$ layer structures similar to single crystals. As the growth rate increased, the alloys with 47 and 50 at.%Al compositions showed columnar-grain structures. However, the alloys fabricated under the condition of 10 mm/h had a layered structure, but the alloy with increased growth rate consisted of ${\gamma}$ single phase grains. The alloy with a 53 at.%Al composition showed a ${\gamma}$ single phase regardless of the growth rate. Room-temperature tensile tests of these alloys revealed that the columnar-grained material consisting of the layered structure showed a tensile ductility of larger than 4 % and relatively high strength. The high strength is caused by stress concentration at the grain boundaries; this enhances the secondary slip or deformation twinning across the layered structure in the vicinity of the grain boundaries, resulting in the appreciable ductility.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.859-860
• /
• 2006

TiC-$TiB_2$-SiC system was a ternary eutectic, whose eutectic composition was 34TiC-$22TiB_2$-44SiC (mol%). TiC-$TiB_2$-SiC ternary eutectic composite were synthesized by a floating zone method using TiC, $TiB_2$ and SiC powders as starting materials. The TiC-$TiB_2$-SiC eutectic composite showed a lamellar texture. TiC(022), $TiB_2(010)$ and SiC(111) of the eutectic composite were perpendicular to the growth direction. TiC-$TiB_2$-SiC ternary eutectic composite had specific relationship among the crystal planes: TiC[011]//$TiB_2[010]$//SiC[112], TiC(200)//$TiB_2$(001)//SiC(402) and $TiC(1\bar{1}1)$//$TiB_2(101)$//SiC(220).

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.10 no.4
• /
• pp.279-285
• /
• 2000

High quality crystals of $YMnO_3$, which is interested in non-volatile memory device application, were grown by the floating zone method. Optimum condition for powder synthesis was established to be $1200^{\circ}C$ for 10 hrs and optimum condition for sintering of $YMnO_3$feed-rod was established to be $1500^{\circ}C$ for 10hrs respectively. It was found from non-seeded growth experiment that $YMnO_3$crystal was grown preferentially to the [1010] orientation. The $YMnO_3$single crystal, which was grown to the direction of perpendicular to C-axis, was typically 5mm in diameter, 50 mm in length and showed dark-blue color.

• Korean Journal of Crystallography
• /
• v.13 no.1
• /
• pp.41-47
• /
• 2002

La/sub 1-x/Ca/sub x/MnO₃ manganese oxide were grown using the floating zone image furnace with halogen lamps as heat source. The growth condition was 4∼6 mm/hr growth rate in air atmosphere, 45∼50 rpm and 20∼25 rpm of rotation rate of feedrod and growing crystal, respectively. Characterization analyses of the crystal were carried out using XRD, SEM, and EPMA. Orientation of crystal was determined using EBSD. The electromagnetic properties were measured with Quantum Design PPMS by 4 point probe method and resulted MR value of 462% at 215 K.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.25 no.7
• /
• pp.1073-1081
• /
• 2001

Many researches have published numerous papers about the high-strain-rate obtained from Split Hopkinson Pressure Bar(SHPB) tests. And 6.5wt%Si steel is widely known as an excellent magnetic material because its magnetostriction is nearly zero. Single crystals are prepared by the Floating Zone(FZ) method, which melts the alloy by the use of a high temperature electron beam in a pure argon gas condition. In this paper, the fracture behavior of the poly crystals and single crystals (DO$_3$phase) of Fe-6.5wt%Si alloy by SHPB test is observed. The comparison of high-strain-rate results with static results was done. Obtained main results are as follows: (1) Fe-6.5wt%Si alloy has higher strength at high-strain-rate tensile. SHPB results of polycrystal are twice as high as static results. (2) From the fractography, the cleavage steps are remarkably reduced in the SHPB test compared with the static test.