• The Journal of Advanced Prosthodontics
• /
• v.10 no.5
• /
• pp.361-366
• /
• 2018

PURPOSE. The aim of this study was to evaluate the effects of relining materials on the flexural strength of relined thermoplastic denture base resins (TDBRs). MATERIALS AND METHODS. For shear bond strength testing, 120 specimens were fabricated using four TDBRs (EstheShot-Bright, Acrytone, Valplast, Weldenz) that were bonded with three autopolymerizing denture relining resins (ADRRs: Vertex Self-Curing, Tokuyama Rebase, Ufi Gel Hard) with a bond area of 6.0 mm in diameter and were assigned to each group (n=10). For flexural strength testing, 120 specimens measuring $64.0{\times}10.0{\times}3.3mm$ (ISO-1567:1999) were fabricated using four TDBRs and three ADRRs and were assigned to each group (n=10). The thickness of the specimens measured 2.0 mm of TDBR and 1.3 mm of ADRR. Forty specimens using four TDBRs and 30 specimens using ADRRs served as the control. All specimens were tested on a universal testing machine. For statistical analysis, Analysis of variance (ANOVA) with Tukey's test as post hoc and Spearman's correlation coefficient analysis (P=.05) were performed. RESULTS. Acry-Tone showed the highest shear bond strength, while Weldenz demonstrated the lowest bond strength between TDBR and ADRRs compared to other groups. EstheShot-Bright exhibited the highest flexural strength, while Weldenz showed the lowest flexural strength. Relined EstheShot-Bright demonstrated the highest flexural strength and relined Weldenz exhibited the lowest flexural strength (P<.05). Flexural strength of TDBRs (P=.001) and shear bond strength (P=.013) exhibited a positive correlation with the flexural strength of relined TDBRs. CONCLUSION. The flexural strength of relined TDBRs was affected by the flexural strength of the original denture base resins and bond strength between denture base resins and relining materials.

• Steel and Composite Structures
• /
• v.45 no.1
• /
• pp.133-145
• /
• 2022

Steel fiber composite bar (SFCB) is a novel type of reinforcement, which has good ductility and durability performance. Due to the unique pseudo strain hardening tensile behavior of SFCB, different flexural behavior is expected of SFCB reinforced concrete (SFCB-RC) beams from traditional steel bar reinforced concrete (S-RC) beams and FRP bar reinforced concrete (F-RC) beams. To investigate the flexural behavior of SFCB-RC beam, four points bending tests were carried out and different flexural behaviors between S/F/SFCB-RC beams were discussed. An flexural analytical model of SFCB-RC beams is proposed and proved by the current and existing experimental results. Based on the proposed model, the influence of the fiber volume ratio R of the SFCB on the flexural behavior of SFCB-RC beams is discussed. The results show that the proposed model is effective for all S/F/SFCB-RC flexural members. Fiber volume ratio R is a key parameter affecting the flexural behavior of SFCB-RC. By controlling the fiber volume ratio of SFCB reinforcements, the flexural behavior of the SFCB-RC flexural members such as bearing capacity, bending stiffness, ductility and repairability of SFCB-RC structures can be designed.

• Carbon letters
• /
• v.12 no.3
• /
• pp.177-179
• /
• 2011

The use of carbon nanotubes (CNTs) as a reinforcing material in a polymer matrix has increased in various industries. In this study, the flexural behavior of CNT-modified epoxy/basalt (CNT/epoxy/basalt) composites is investigated. The effects of CNT modification with silane on the flexural properties of CNT/epoxy/basalt composites were also examined. Flexural tests were performed using epoxy/basalt, oxidized CNT/epoxy/basalt, and silanized CNT/epoxy/basalt multi-scale composites. After the flexural tests, the fracture surfaces of the specimens were examined via scanning electron microscopy (SEM) to investigate the fracture mechanisms of the CNT/epoxy/basalt multi-scale composites with respect to the CNT modification process. The flexural properties of the epoxy/basalt composites were improved by the addition of CNTs. The flexural modulus and strength of the silane-treated CNT/epoxy/basalt multi-scale composites increased by approximately 54% and 34%, respectively, compared to those of epoxy/basalt composites. A SEM examination of the fracture surfaces revealed that the improvement in the flexural properties of the silane-treated CNT/epoxy/basalt multi-scale composites could be attributed to the improved dispersion of the CNTs in the epoxy.

• Journal of the Korean Society of Hazard Mitigation
• /
• v.7 no.5
• /
• pp.11-18
• /
• 2007

A laboratory investigation was conducted to characterize the flexural fatigue behavior of high performance fiber reinforced cement mortar. Five specimens for statics flexural test and fourteen specimens for the flexural fatigue test were made based on the fiber mixing ratio. Static flexural tests were firstly performed to obtain magnitudes of static failure loads and stress levels before flexural fatigue tests. The flexural fatigue behaviors were investigated based on the stress level and fiber mixing ratio. Also, the equations for the interrelation of the flexural fatigue stress levels with the number at loading cycle were proposed.

• Structural Engineering and Mechanics
• /
• v.19 no.2
• /
• pp.185-198
• /
• 2005

In the design of reinforced concrete beams, it is a standard practice to use the yield stress of the steel reinforcement for the evaluation of the flexural strength. However, because of strain hardening, the tensile strength of the steel reinforcement is often substantially higher than the yield stress. Thus, it is a common belief that the actual flexural strength should be higher than the theoretical flexural strength evaluated with strain hardening ignored. The possible increase in flexural strength due to strain hardening is a two-edge sword. In some cases, it may be treated as strength reserve contributing to extra safety. In other cases, it could lead to greater shear demand causing brittle shear failure of the beam or unexpected greater capacity of the beam causing violation of the strong column-weak beam design philosophy. Strain hardening may also have certain effect on the flexural ductility. In this paper, the effects of strain hardening on the post-peak flexural behaviour, particularly the flexural strength and ductility, of reinforced normal- and high-strength concrete beams are studied. The results reveal that the effects of strain hardening could be quite significant when the tension steel ratio is relatively small.

• Journal of the Architectural Institute of Korea Structure & Construction
• /
• v.35 no.8
• /
• pp.131-138
• /
• 2019

Since concrete has a low tensile strength compared to the compressive strength, reinforced concrete flexural members represent easy crack occurance under a small load. In order to overcome this problem, steel fiber reinforced concrete has been developed to compensate the tensile strength and brittleness of members. However, in the design formula of the domestic building code, it is not specified in the design formula reflecting the material characteristics. Therefore, the field application of the steel fiber reinforced concrete have had many restrictions. In this study, a flexural tensile strength model of steel fiber reinforced concrete is proposed by collecting and analyzing the material properties of material test results conducted by various researchers, and verified by the test results of cracking and stiffness evaluation of flexural members based on the proposed model. As a result of this study, the flexural tensile strength model of steel fiber reinforced concrete which can reflect the mixing ratio and aspect ratio of the steel fiber was proposed and the validity of the proposed material model equation was evaluated from the load-deflection relationship in the flexural test of the slab member.

• Journal of the Architectural Institute of Korea Structure & Construction
• /
• v.36 no.4
• /
• pp.123-133
• /
• 2020

The purpose of this study is to analyze the method of retrofitting flexural strength and the flexural performance of retrofitted shear walls. There are various ways to reinforce the flexural strength of reinforced concrete shear wall structural systems that have already been built, in the case of that, the external force is increased, and the internal force is insufficient. However, there are various problems, such as excessive flexural stiffness after reinforcement and increasing the thickness and length of the wall. We have developed a retrofit method to solve these problems. The wall end is excavated to place the required vertical rebars, and concrete is poured after placing rebars. This is the same concept as creating wall end boundary elements later on. We also studied the anchorage method of reinforcement and the interaction method between the retrofitting end and the existing wall. The flexural test results for the reinforced concrete shear wall using the studied retrofit method can be predicted according to the sectional analysis and FEM analysis, and there are differences in the plastic hinge length, crack propagation, stiffness degradation and energy dissipation due to the bending depending on the vertical rebar ratio of wall end.

• Journal of the Korea Concrete Institute
• /
• v.28 no.1
• /
• pp.95-104
• /
• 2016

Flexural strength of concrete ground slab reinforced with steel fiber is evaluated using the equivalent flexural strength ratio of steel fiber reinforced concrete based on the yield line theory. Recently, the European standard specifies that the tensile performance of the steel fiber reinforced concrete be evaluated directly from the residual flexural strength after the cracking of concrete. Thus, in the study, an experiment was carried out to evaluate the conventional equivalent flexural strength ratio and the residual flexural strength of the steel fiber reinforced concrete. Then the design flexural strength was investigated according to the location of a point load, based on the ratio of the radius of contact area of the load to the radius of relative stiffness. Design flexural capacity obtained from ACI 360R-10 was smaller than that from TR 34 (2003 & 2013). In addition, TR 34 (2013), which evaluates the design flexural capacity based on the residual flexural strength, showed slightly smaller value than TR 34 (2003).

• Korean Journal of Materials Research
• /
• v.30 no.1
• /
• pp.38-43
• /
• 2020

Sand casting 3D printing uses a binder jetting method to produce a mold having complicated shape by spraying a binder on sand coated with activator. Appropriate heat treatment process in sand mold fabrication can increase the degree of polymerization to improve flexural strength. However, long heat treatment of over 24 hours decreases flexural strength and reliability due to chemical bond decomposition through thermal degradation. The main role of the activator is to control the reaction rate between the polymer chains. As a result, when the activator composition is increased from 0.15 wt% to 0.25 wt%, the flexural strength is increased by 218 N/㎠. However, excess activator (0.40 wt%) has been shown to decrease reliability without increasing flexural strength. The main role of the binder is to control the flexural strength of the specimen. As the binder composition is increased from 2.00 wt% to 4.00 wt%, the flexural strength increases to about 255 N/㎠, indicating the maximum flexural strength increase. Finally, the reliability of the flexural strength of the fabricated specimens is evaluated by a Weibull plot. Weibull modulus calculations are used to evaluate the flexural strength reliability of the specimens, and maximum reliability value of 11.7 is obtained at 0.20 wt% activator composition. Therefore, it is confirmed that this composition has maximum flexural strength reliability.

• Magazine of the Korea Concrete Institute
• /
• v.8 no.5
• /
• pp.163-170
• /
• 1996

Cellulose fibers, being fairly strong and stiff as well as cheap and plentiful with low energy demand during manufacture, are strong contenders for the reinforcement of cement-based materials. Cellulose fiber-cement composites, generally manufactured by slurry-dewatering procedure, can find applications in the production of flat and corrugated cement sheets and many other thin-sheet cement products. This paper presents the results of an experimental study concerned with the effects of fiber content and moisture conditions on the flexural performance of these composites. An effort was also made to study the effect of pozzolanic admixtures on the flexural performance in different moisture conditions. The test results obtained were analyzed statistically using the analysis of variance in order to derive reliable conclusions. The results generated in this study were indicative of significant effects of fiber content and moisture condition of flexural performance. There is a tendency in flexural strength to increase in increase in fiber content up to 8%: flexural toughness values continue to increase even at higher fiber contents. Moisture content has a significant effect on the flexural performance. There is a tendency in flexural strength to decrease and flexural toughness to increase with increasing moisture content Composites incorporating pozzolans showed an increase in the flexural strength while slightly reducing the flexural toughness and were sensitive to variations in moisture content.