This study presents analysis of fire hazard of electrical heating pad. In order to analyze fire hazard fire experimental and flammability experiment is conducted. The fire experiment is conducted to simulate normal condition and abnormal condition such as breakdown of thermostat. Vertical burning test(UL 94) is conducted for the fire retardant experiment. Kinds of electric heating pad used for experiment are electric mat, fabric pad, vinyl pad. The results show that fire hazard is high in case of breakdown of thermostat with the rating voltage supply. And Material of electric heating pad has not fire retardant performance.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.32 no.3
• /
• pp.213-218
• /
• 2019

In this study, a high-temperature vulcanizing (HTV) method was used to achieve a shore a hardness of 70. The basic base was composed of 60% silicon gum (GUM) which is a high-viscosity polymer, 30% fumed silica (FS), and 5% of plasticizer. The GUM and FS were mixed well with less than 1% silane to improve rubber strength. Expanded vermiculite was added as a filler at 10%, 15%, and 20%. The curing conditions were $170^{\circ}C$ for 10 min and a molding method was applied. We report herein, the results of inorganic analysis and flame-retardant and tracking tests on the expanded vermiculite. The flame retardance and tracking test outcomes for a shore a hardness of 70 were found to be optimal when the expanded vermiculite content was 10%.

• Fire Science and Engineering
• /
• v.33 no.3
• /
• pp.21-28
• /
• 2019

To examine the mechanical and combustion characteristics of FRTP, either polycarbonate or nylon were used as a matrix, and either glass fiber or carbon fiber were used as the fiber reinforcement. The fiber reinforcement content was differentiated at 0~40 wt%. The tensile strength and heat distortion temperature increased with increasing reinforcement content. When the fiber reinforcement content was above 30 wt%, the flammability rating showed V-0. As the fiber reinforcement content increased from 0 to 40 wt%, the peak heat release rate of polycarbonate decreased by approximately 51% and that of nylon decreased by approximately 24%. The rate of CO generation decreased for a period of time, and then increased. This appears to have resulted from incomplete combustion. The rate of CO₂ generation shows a similar tendency with the heat release rate. As fiber reinforcement content levels increased from 0 to 40 wt%, the CO₂ peak rate of polycarbonate generation decreased by approximately 50% and that of nylon decreased by 28%.