• International Journal of Concrete Structures and Materials
• /
• 제4권2호
• /
• pp.119-125
• /
• 2010

In this study, the effects of the fineness modulus of reactive aggregate on ASR expansion and ASR products have been investigated. The reactive aggregate used was metamorphic aggregate originated from Korea. ASR tests were conducted according to accelerated mortar bar test. The morphology and chemical composition of products formed in mortar bars, 5 years after the mortar bar test had been performed, were studied by scanning electron microscopy equipped with energy dispersive spectroscopy. Test results indicated that ASR expansion of mortar bars decrease in linear proportion to the fineness modulus of reactive aggregate. SEM images indicated that mortar bars showed reactive products formed in cement paste, within air voids and within cracks through particles except for the mortar bar with the fineness modulus of 3.25. The EDS analysis of the reactive products showed presence of silica, calcium and sodium, typical of ASR product composition.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2003년도 가을 학술발표회 논문집
• /
• pp.102-105
• /
• 2003

The purpose of this study is to examine the influence of the flowability and the compressive strength of concrete after the improving of grain shape of the coarse aggregate and fine aggregate fineness modulus. According to the experimental results, the coarse aggregate after improvement of grain shape it lead to be down by 6% fine aggregate ratio, from 47% to 41%. The 0.5% increase of fine aggregate fineness modulus lead to 3% increase of concrete slump, and 1% reduction of concrete air content. While compressive strength on fine aggregate fineness modulus, it was increased until fineness modulus 3.0, but after it reached by 3.5 it was decreased. The compressive strength of the coarse aggregate after improving the grain shape was decreased by 6% due to loss of the adhesion of cement paste.

• 콘크리트학회논문집
• /
• 제17권5호
• /
• pp.785-792
• /
• 2005

본 연구는 굵은골재의 입형불량과 잔골재의 조립률 저하가 초유동콘크리트의 특성에 미치는 영향을 검토한 것이다. 이론 위해 잔골재 조립률을 2.0, 2.5, 3.0, 3.5로 변화시키고 굵은골재는 입형개선전$\cdot$후 골재를 사용하여 초유동콘크리트의 유동검 및 충전성능을 검토하였다. 또한 골재입자의 분산거리를 상대비교 함으로써 잔골재의 조립률 및 굵은골재의 입형이 골재입자의 분산거리에 미치는 영향을 검토하였다. 실험 결과 굵은골재와 잔골재 혼합시의 최소공극률은 골재 입형개선 유무에 관계없이 잔골재 조립률 3.0, 2.5, 2.0, 3.5 순으로 나타나 조립률 KS 규정 값 $2.3\~3.1$보다 작거나 클 경우 공극률을 증가시키는 것으로 나타났으며, 굵은골재의 입형은 구형율 0.69의 원반상에서 구형율 0.78의 구상으로 개선할 경우 최소공극률을 나타내는 잔골재율을 $47\%$에서 $41\%$로 $6\%$ 감소시키는 것으로 나타났다. 잔골재 조립률에 따른 28일 압축강도 특성은 조립률 2.0에서 2.5, 3.0으로 증가할수록 약 3MPa씩 증가하였으나, 조립률 3.5에서는 3.0에 비해 약 9MPa 정도 감소하였다. 또한 굵은골재의 입형개선과 잔골재 조립률의 증가는 유동성, 충전성 및 V로드 상대유하시간을 향상시키는 것으로 나타났으며, 잔골재 조립률은 KS 규정 값 $2.3\~3.1$을 만족하는 범위내에서 높은 값을 사용하는 것이 페이스트 용적비를 증가시키는 것으로 나타났다.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2003년도 가을 학술발표회 논문집
• /
• pp.106-111
• /
• 2003

This paper is to investigate the characteristics of a concrete in which river sand is partially substituted with crushed sand. Since river sand has a relatively small fineness modulus, there is a need to increase the fineness modulus of sand used in the manufacture of concrete. In an experiment, it was observed that when river sand had a fineness modulus of 2.0~2.4 and crushed sand had a fineness modulus of 2.8~3.5, the substitution rate of the crushed sand was preferably within the range of 25~50%. The experimental results also revealed that as the substitution rate of the crushed sand increased, the flowability of the concrete tended to increase. However, when the substitution rate of the crushed sand reached 75% or more, the workability of the concrete was considerably poor. Further, as the substitution rate of the crushed sand increased, the air content and the bleeding rate of the concrete were low.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2004년도 춘계 학술발표회 제16권1호
• /
• pp.388-391
• /
• 2004

This research investigates how the fineness modulus of fine aggregates and the grain shape of coarse aggregates affects flow characteristics, packing characteristics and compressive strength characteristic. The experimental results, show that increase of the fine aggregate's fineness modulus improved concrete flow, but filling ability was high at over KS regulation extent due to segregation phenomena. It is considered that the improvement of 0.1 spherical rate was effective to concrete fluidity elevation by reducing about $6\%$ of fine aggregate ratio displays which the smallest gap rate of aggregate. Compressive strength was increased to about 0.6MPa everytime F.M. 0.1 of fine aggregate fineness is increased. However, it was decreased to about 9MPa at F.M. 3.5 compared to F.M. 3.0.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2008년도 춘계 학술발표회 제20권1호
• /
• pp.725-728
• /
• 2008

본 연구에서는 고분말도 플라이애쉬를 사용한 콘크리트의 역학 및 수축특성을 분석하기 위하여 플라이애쉬의 분말도 4000, 6000, 8000급의 3수준과 치환율 30%로 설정 하였으며, 물-결합재비 40, 50%의 2수준으로 계획하였다. 또한, 고로슬래그 미분말 3종의 치환율 20%의 수준으로 3성분계의 조합조건을 설정하여 실험을 실시한 결과, 강도특성에서는 플라이애쉬의 분말도가 증가할수록 압축, 인장 및 휨 강도가 플레인 콘크리트와 동등하거나 상회하는 경향을 나타냄과 동시에 압축강도와 탄성계수의 관계에서도 플라이애쉬의 분말도가 증가할수록 탄성계수가 다소 증가하는 경향을 나타내었으며, 탄성계수는 장기재령으로 갈수록 확연히 증가하는 경향을 나타내었다. 또한, 건조수축에서는 플라이애쉬의 분말도에 대한 영향은 미미하였으나, 분말도가 증가할수록 감소하는 경향을 나타내었다.

• 콘크리트학회논문집
• /
• 제12권1호
• /
• pp.45-52
• /
• 2000

The quality of cement mortar products largely depends on various work conditions, specially on the grading and grade shape of aggregates. However, the effect of grading and grade shape on the quality is not considered by both KS codes and production processes, resulting in the increase of the possibility of quality degradation. The objective of this study was to investigate the effect of grading and grade shape on the strength and absorption characteristics of cement mortar products. Flexural and compressive strength increased with the increase of fineness modulus and W/C. The strength increase was measured larger with river sand than with crushed sand. Absorption tended to decrease with the increase of fineness modulus and W/C, but did not affected by the source of sand.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2021년도 가을 학술논문 발표대회
• /
• pp.50-51
• /
• 2021

Recently, as concrete is used in many construction works in Korea, the use of aggregates is also increasing. However, the depletion of aggregate resources is making it difficult to supply and demand high-quality aggregates, and the use of defective aggregates is causing problems such as poor performance such as the liquidity and strength of concrete pouring out in the field. As a result, quality tests such as sieve analysis test is conducted on their own, but this study was conducted to improve time and manpower by using the CNN-based Deep Learning Model for the fineness modulus.

• 한국터널지하공간학회 논문집
• /
• 제24권4호
• /
• pp.317-326
• /
• 2022

구조용 합성섬유는 작은 비중에 의한 반발률 감소, 지하수 및 해수에 의한 부식 발생의 우려가 없어 강섬유의 대체재로 구조용 합성섬유의 관심이 최근 높아지고 있다. 본 연구에서는 시멘트 복합체의 잔골재 조립률이 구조용 섬유의 인발강도 및 인발에너지에 미치는 영향을 평가하기 위한 실험연구를 수행하였다. 조립률 1.96, 2.69, 3.43인 잔골재로 시멘트 몰탈을 제작하였으며 구조용 합성섬유 1종(polypropylene), 강섬유 1종(hooked ends type)을 대상으로 단일섬유 dog bone shape 공시체를 제작하여 pull-out 실험을 수행하였다. 실험결과 구조용 합성섬유 공시체에서 시멘트 몰탈의 조립률이 증가할수록 인발강도 및 인발에너지가 증가함을 알 수 있었다. 구조용 합성섬유의 경우 시멘트 몰탈과 섬유 사이의 마찰력이 인발메커니즘의 중요인자로 시멘트 몰탈의 잔골재 조립률이 높아질수록 골재 입자가 크고 거칠어지며 섬유와 시멘트 몰탈 사이의 마찰력이 증가하여 섬유의 인발을 억제하기 때문으로 판단된다. 반면, 강섬유 공시체의 경우 시멘트 몰탈 조립률 증가에 따른 인발강도 및 인발에너지의 뚜렷한 경향성은 나타나지 않았다. 이는 강섬유 hooked ends 부분의 기계적 정착이 시멘트 복합체와 강섬유 사이의 마찰력과 비교하여 인발저항력에 미치는 영향이 더 크므로 시멘트 복합체의 잔골재 조립률 변화가 인발저항력에 상대적으로 적은 영향을 미치는 것으로 판단된다.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1998년도 봄 학술발표회논문집(II)
• /
• pp.661-664
• /
• 1998

In this paper, the properties of inter-lacking block by the kind of aggregate and fineness modulus are investigated. According to the experimental results, compressive strength and flexural strength increase and absorption ratio decrease with larger fineness modulus in the range of 2.15~4.20. Flexural strength with river sand is higher than that with crushed sand by about 19%, compressive strength with river sand, that with crushed sand by about 11% and absorption ratio with river sand is smaller than that with crushed sand by abort 2%.