• Journal of the korean academy of Pediatric Dentistry
• /
• v.30 no.3
• /
• pp.530-539
• /
• 2003

The aim of this study was to evaluate the resistance to degradation of four commercial composite resins in an alkaline solution. The brands studied were Charisma, Filtek P 60, Palpique Estelite, and Spectrum. Preweighed discs of each brand were exposed to 0.1N NaOH solution at $60^{\circ}C$. After 2 weeks they were removed, neutralized with HCl, washed with water and dried. Resistance to degradation was evaluated on the basis of following parameters: (a) mass loss(%) - determined from pre-and post-exposed specimen weights; (b) Si loss(ppm) - obtained from ICP-AE analysis of solution exposed to specimens; and (c) degradation depth(${\mu}m$) - measured SEM and CLSM from polished circular sections of exposed specimens. The results were as follows: 1. The sequence of mass loss was in descending order by Palpique Estelite, Filtek P 60, Charisma, and Spectrum. 2. The sequence of the degree of degradation layer depth was in descending order by Filtek P 60, Charisma, Palpique Estelita, and Spectrum. 3. The sequence of the Si loss was in descending order by Chrisma, Spectrum, Palpique Estelite, and Filtek P 60. 4. The correlation coefficient between mass loss and degradation layer depth was relatively high(r=0.704, p<0.05). 5. When observed with SEM, destruction of bonding was observed between resin matrix and filler. 6. When observed with CLSM, degradation layer depth of composite resin surface was observed.

• The Journal of Korean Academy of Prosthodontics
• /
• v.40 no.1
• /
• pp.79-87
• /
• 2002

The purpose of this study was to investigate the color stability of composite resins used widely as esthetic restorative material. Surefil(Dentsply, U.S.A.), Esthet X(Dentsply, U.S.A.), Filtek P60(3M, U.S.A.) , Filtek Z250(3M, U.S.A.), Synergy Compact(Coltene, Switzerland), and Synergy Duo(Coltene, Switzerland) were chosen for this study. Thirty six specimens($7mm{\times}2mm$) of each composite resin were fabricated and polished after polymerization. Treatment conditions designed for this study were thermocycling, methylene blue staining, and filtered coffee staining. The color changes before and after treatment were measured by colorimeter(colorimeter, Model Tc-6Fx, Tokyo Denshoku Co.) and analyzed. The followings were drawn from this study: 1. The color changes of Filtek Z250, Surefil, Filtek P60 and Esthet X after thermocycling for 3 weeks were greater than those of the others. 2. The color changes of Surefil and Esthet X after methylene blue stainig and those of Surefil, Filtek Z250 and Filtek P60 after coffee staining were great. 3. The color changes or Synergy Duo and Synergy Compact after thermocycling and coffee staining were relatively lesser than those of other composite resins.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.31 no.4
• /
• pp.685-695
• /
• 2004

The aim of this study was to evaluate the resistance to degradation and to compare the wear resistance characteristics of four composite resins in an alkaline solution. The resistance to degradation was evaluated on the basis of mass loss(%), degradation depth(${\mu}m$), Si loss(ppm) and wear depth. The brands studied were Heliomolar flow, Filtek supreme, Point4, Tetric flow. The results were as follows: 1. The sequence of the mass loss was in descending order by Heliomolar flow, Filtek supreme, Point4, Tetric flow. There was significant differences among the materials except Heliomolar flow and Filtek supreme. 2. The sequence of the degree of degradation layer depth was in descending order by Filtek supreme, Heliomolar flow, Tetric flow, Point4. There were significant differences among the materials except Heliomolar flow and Tetric flow. 3. The sequence of Si loss was in descending order by Filtek supreme, Heliomolar flow, Point4, Tetric flow. There were significant differences among the materials except Point 4 and Tetric flow. 4. The sequence of maximum wear depth was in descending order by Heliomolar flow, Point4, Fillet supreme, Tetric flow and there was increasing wear depth on soaking in 0.1N NaOH solution. 5. When observed with SEM, destruction of bonding between matrix and filler was observed and when observed with CLSM, the depth of degradation layer of specimen surface was observed. There results indicate that wear and hydrolytic degradation could be considered to be evaluation factors of composite resins.

• Restorative Dentistry and Endodontics
• /
• v.27 no.5
• /
• pp.502-514
• /
• 2002

The aim of this study was to evaluate the marginal adaptation of direct class II sandwich restoration with packable composites(P-60), resin modified glass ionomer cement(Fuji-II LC), flowable compomer(Dyract Flow), flowable composites(Filtek Flow) in comparison with total bond restorations. In addition, for sandwich restorations, influence of different sandwich techniques was also evaluated. Large butt-joint box typed class II cavites with cervical margins 1mm below the cemento-enamel junction were cut into 70 extracted human molars. The cavities(7 groups, n=10) were filled using a closed/open sandwich restoration or total bond restoration technique with materials according to the manufacturer's recommandation using the single-component bonding agent for each system. Teeth were thermocycled 500 times between 5$^{\circ}C$ and 55$^{\circ}C$ with 30-second dwell time. The teeth were then coated with nail polish 1mm short of the restoration, placed in a 2% methylene blue for 24 hours, and sectioned with diamond wheel. Sections were examined with a stereoscope to determine the extent of microleakage. Dentine /Cementum margins were analyzed for microleakage on scale of 0(no leakage) to 4(entire axial wall) and interface between materials, on scale of 0(no leakage) to 3(axial wall). Results were evaluated with Kruskal Wallis Test, corrected for ties, to determine whether there were statistically significant differences among the seven groups. Pairs of groups were analyzed using the Student-Newman-Keuls Method and Dunn s Method. The results were as follows : 1. All groups showed some micoleakage in cervical portion. But there were no microleakage in interface between materials. 2. Closed sandwich restorations with Fuji-II LC and Filtek Flow had significantly lower leakage rating than total restorations with only P-60. However, open sandwich restorations with Dyract Flow showed significantly higher (P<0.05) 3. Closed sandwich restorations had significantly lower leakage rating than total restorations. However open sandwich restoration s showed significantly higher (P<0.05). 4. Sandwich restorations with Fuji-II LC were iou$.$or leakage than only P-60. Filtek Flow, Dyract Flow. But there were no statistically differences among the materials. From the results above, it could be concluded, closed sandwich restorations was effective in reducing microleakage of class II restorations. The best results showing the least microleakage were for the closed sandwich technique with Fuji-II LC and Filtek Flow.

• Journal of Korean society of Dental Hygiene
• /
• v.12 no.3
• /
• pp.533-541
• /
• 2012

Objectives : The purpose of this study was to evaluate the effects of tooth bleaching agent contained 35% hydrogen peroxide on the color, microhardness and surface roughness of tooth-colored restorative materials. Methods : Four types of tooth-colored restorative materials, including a composite resin(Filtek Z350 ; Z350), a flowable composite resin(Filtek P60 : P60), a compomer(Dyract$^{(R)}$ AP ; DY), and a glass-ionomer cement(KetacTM Molar Easymix ; KM) were used in the study. The specimens($8mm{\times}5mm$) were made by using a customized acrylic mold. Each material was divided into two groups equally(n=40) : experimental group(35% HP) and control group(distilled water). 35% HP group was treated 30 mim/5 days for 15 days. Each 30 minute treatment session consisted of two 15 minute cycles of gel application with 20 second light exposure. The authors measured the color, microhardness, and roughness of the specimens before and after bleaching. The data were analyzed with ANOVA and T-test. Results : 35% HP group showed an apparent color change(${\Delta}E^*$) than control group. In particular, DY and KM showed a noticeable color change and statistically significant differences(p<0.05). 35% HP group showed a reduction in microhardness. Z350 and P60 does not have a statistically significant difference(p>0.05), DY and KM showed a statistically significant difference(p<0.05). Percentage microhardness loss(PML) of control group was 0.6 to 5.5% in the group, 35% HP group was 6.6 to 34.6%. Roughness was increased in 35% HP group after bleaching. Especially DY and KM were significantly increased(p<0.05). Conclusions : Bleaching agents may affect the surface of existing restorations; therefore, they should not be used indiscriminately when tooth-colored restorations are present.

• Restorative Dentistry and Endodontics
• /
• v.47 no.4
• /
• pp.43.1-43.13
• /
• 2022

Objectives: This study compared the surface gloss (SG), gloss retention (GR), and color stability (CS) of 2 universal resin composites after chemical (CA) and mechanical (MA) aging. Materials and Methods: Twenty disc-shaped samples of G-ænial A'Chord (GC-Europe) and Filtek Universal (3M-ESPE) were polished with sequential abrasive papers. For CA, specimens were stored in 1 mL of 75% ethanol for 15 days at 37℃, and readings (SG, GR, and CS) were obtained at baseline and 5, 10, and 15 days. For MA, specimens were subjected to 10,750 simulated brushing cycles. SG and CS were evaluated after every 3,583 cycles. SG was measured with a glossmeter (geometrical configuration: 60°), and values were expressed in gloss units. Color was measured with a spectrophotometer using the CIE-L^*a^*b^* color system. The Student's t-test, 1-way analysis of variance, and Scheffé test were used for statistical analysis (α = 0.05). Results: G-ænial presented significantly higher SG values than Filtek (p = 0.02), with GR reductions of 5.2% (CA) and 5.3% (MA) for G-ænial and 7.6% (CA) and 7.2% (MA) for Filtek. The aging protocol had no statistically significant effect on SG or GR (p = 0.25) from baseline to the final readings. G-ænial-MA presented the lowest color difference (ΔE = 1.8), and G-ænial-CA and Filtek-CA had the largest changes (ΔE = 8.6 and ΔE = 11.8, respectively). Conclusion: G-ænial presented higher SG values and better CS. Both restorative materials demonstrated acceptable GR and CS. Aging protocols impacted these properties negatively.

• Imaging Science in Dentistry
• /
• v.42 no.2
• /
• pp.89-93
• /
• 2012

Purpose : Clinicians commonly encounter cases in which it is difficult to determine whether adjacent radiopacities are normal or pathologic. The ideal radiopacity of composite resin is equal to or higher than that of the same thickness of aluminum. We aimed to investigate the possible effects of different curing times on the post-24-hour radiopacity of composite resins on digital radiographs. Materials and Methods : One mm thick samples of Filtek P60 and Clearfil resin composites were prepared and cured with three regimens of continuous 400 mW/$cm^2$ irradiance for 10, 20 and 30 seconds. Along with a 12-step aluminum step wedge, digital radiographs were captured and the radiopacities were transformed to the equivalent aluminum thicknesses. Data were compared by a general linear model and repeated-measures of ANOVA. Results : Overall, the calculated equivalent aluminum thicknesses of composite resins were increased significantly by doubling and tripling the curing times (F(2,8)=8.94, p=0.002). Notably, Bonferroni post-hoc tests confirmed that the radiopacity of the cured Filtek P60 was significantly higher at 30 seconds compared with 10 seconds (p=0.04). Although the higher radiopacity was observed by increasing the time, other comparisons showed no statistical significance (p>0.05). Conclusion : These results supported the hypothesis that the radiopacity of resin composites might be related to the duration of light curing. In addition to the current standards for radiopacity of digital images, defining a standard protocol for curing of dental materials should be considered, and it is suggested that they should be added to the current requirements for dental material.

• The Journal of Korean Academy of Prosthodontics
• /
• v.44 no.1
• /
• pp.1-9
• /
• 2006

Purpose: The purpose of this study was to evaluate the efficacy and substitute possibility of a newly developed flowable composite resins as a luting cement for translucent fiber post. Material & Method: Two kinds of 12 mm translucent fiber Post (D.T. Light-Post (Bisco, USA) and FRC Postec (Ivoclar vivadent, Liechtenstein) was inserted into the teflon mold (7 mm diameter, 9 mm long) and Filtek-Flow (3M ESPE. USA), a light activated flowable composite resin, was polymerized for 60 seconds through the post. Also, the post was cut from the tip to 9 mm, 6 mm, 3 mm, and Filtek-Flow was light cured according to each length. For comparison, 60 seconds light-cured and 24 hours self-cured two dual cured resin cement (Duo-cement (Bisco, USA) and 2 Panavia-F (Kuraray, Japan)) samples were prepared as control group. Also cavities (1 mm in width, 1 mm in depth and 12 mm in length) were prepared using acrylic plate and aluminum bar, and flowable composite resin was flied and light cured by the diffused light from the fiber post's side wall. The degree of polymerization was measured according to the distance from curing light using Vickers' hardness test. Result: Within the limitation of this study, the following conclusions were drawn: 1. Vickers' hardness of light cured dual cured resin cement and flowable composite resin decreased from Panavia-F, Filtek-Flow and Duo-cement accordingly (p<0.05). In the dual curing resin cement, light curing performed group showed higher surface hardness value than self cured only group (p<0.05). 2. Surface hardness ratio (light cured through fiber post /directly light cured) of D.T. Light-Post using Filtek-Flow showed about 70% in the 6 mm deep and about 50% in the 12 mm deep FRC Postec showed only 40% of surface hardness ratio. 3. Surface hardness ratio by diffused light from the post's side wall showed about 50% at 6 mm and 9 mm deep, and about 40% at 12 mm deep in D.T. Light-Post. However, FRC Postec showed about 40% at 6 mm deep, and almost no polymerization in 9 mm and 12 mm deep.

• Journal of Convergence for Information Technology
• /
• v.9 no.7
• /
• pp.159-167
• /
• 2019

This study aimed to evaluate the effects of oral rinsing solution on the color stability, surface microhardness and surface roughness change of composite resin. In this in-vitro study, 80 disc-shaped specimens were fabricated of Filtek P60 and Filtek Z250(A2 shade). The samples of each group were randomly divided into eight subgroups (n=10). The baseline color values ($L^*$, $a^*$, $b^*$) of each specimen were measured according to CIE LAB system using a colorimeter. After baseline color measurements, the control samples were immersed in distilled water and the test groups were immersed colorless, green and purple mouthrinses three times a day for thirty minutes. This process was repeated for two weeks. Green and purple oral rinsing solutions displayed color, microhardness and roughness change of all composite resin after immersion in the mouthrinses. Therefore, prescription of oral rinsing solution for a minimum of two weeks is a common practice, which may cause discoloration of aesthetic composite restorations of patients.

• Journal of Korean society of Dental Hygiene
• /
• v.13 no.2
• /
• pp.351-360
• /
• 2013

Objectives : The purpose of this study was to evaluate the effects of tooth bleaching agent contained 15% carbamide peroxide on the color, microhardness and surface roughness of tooth-colored restorative materials by using pH cycling model. Methods : Four types of tooth-colored restorative materials, including a composite resin(Filtek Z350 ; Z350), a flowable composite resin(Filtek P60 : P60), a compomer(Dyract$^{(R)}$ AP ; DY), and a glass-ionomer cement(KetacTM Molar Easymix ; KM). were used in the study. Eighty-eight specimens of each material were fabricated, randomly divided into two groups(n=44): experimental group(15% carbamide peroxide) and control group(distilled water). These groups were then divided into four subgroups(n=11). All groups were bleached 4 hours per day for 14 days using pH cycling model. The authors measured the color, microhardness, and roughness of the specimens before and after bleaching. The data were analyzed with ANOVA and T-test. Results : Z350 and P60 showed a slight color change(${\Delta}E^*$), whereas DY and KM showed significantly color change(p<0.05). Among them, the greatest color change was observed in DY. Percentage microhardness loss(PML) of the distilled water group was 1.8 to 5.1%, and 15% peroxide peroxide group was 5.0 to 25.2%. Microhardness of DY and KM showed a statistically significant decrease(p<0.05). Roughness was increased in all groups after bleaching. Z350 and P60 does not have a significant difference(p>0.05), however DY and KM significantly increased more than the 0.2 ${\mu}m$(p<0.05). Conclusions : The effects of bleaching on restorative materials were material dependent. It is necessary to consider the type of the material before starting the treatment.