• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2000년도 춘계학술대회논문집A
• /
• pp.200-205
• /
• 2000

Fatigue failure modes of load-carrying cruciform weld joints are dependent on the characteristics of the fatigue crack initiation and propagation from the weld toe or the weld root. In this study, constant amplitude fatigue tests on load-carrying fillet welded specimen carried out, and fatigue strengths were evaluated. Also, an attempt is made to develop a new analytical model with more accuracy to predict the fatigue crack propagation life of fillet welded cruciform joints of SWS 490B steels containing lack of penetration defects. From the result of this study, fatigue crack growth characteristics of load-carrying fillet welded cruciform joints, containing lack of penetration defects are found to be affected by the weld geometry, stress range and microstructures of the weld zone.

• Journal of Welding and Joining
• /
• 제32권2호
• /
• pp.37-42
• /
• 2014

In this study, non-load-carrying fillet welded joints fabricated using EH grade-steel are evaluated with the structural stress approach. The thickness effect was investigated by a study on welded steel joints with thickness ranging from 25 to 80mm. As-welded joint for main plate thickness of 25 to 80mm, the fatigue strength is reduced gradually. On the other hand, in case of main plate thickness of 25 to 80mm, the structural stress concentration factor increases gradually. As a result, for structural stress approach, thickness effect is not required for correction. Based on these results, a new evaluation fillet welded joint for fatigue design purposes has been proposed FAT 125.

• Journal of Welding and Joining
• /
• 제26권6호
• /
• pp.97-102
• /
• 2008

It is well known that there exist two typical fatigue crack initiation locations in ship structures: one is the weld toe and the other is the weld root where partial penetration weld is performed. In particular, it is important for fillet weldments to avoid weld root cracking in order to prevent catastrophic failure particularly in ship structures. Therefore detail considerations are required for cruciform joints with partial penetration when there is a possibility of weld root crack initiation. For these reasons, fatigue tests on welded joints were performed in this study. Concept of stress intensity factor(SIF) by means of fracture mechanics is applied for predicting fatigue life of fillet welded joints.

• 한국안전학회지
• /
• 제25권6호
• /
• pp.161-168
• /
• 2010

A series of fatigue tests have been performed on the non-load carrying fillet welded joints in order to quantitatively assess the fatigue characteristics due to the grindings and TIG(Tungsten Inert Gas) welding treatments. From the results of fatigue tests, it has been shown that the fatigue strengths at $2{\times}106$ load cycles were improved in the case of the grinding sand TIG welding treatments, and we could know that it is satisfying fatigue strength prescribed in fatigue design standard in general. Besides, from the results of fracture mechanics approaches, the geometric shape correction factors were the most dominant factors in the initial fatigue crack growth, but as the fatigue crack develops, the finite plate correction factor were became the most dominant factor, and the fatigue life on non-load carrying fillet welded joints could be relatively exactly estimated by using the relations between fatigue crack growth rate and stress intensity factor obtained from finite element analysis and existing proposed formulae.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2006년 추계학술발표대회 개요집
• /
• pp.29-31
• /
• 2006

Stainless steel sheets are widely used as the structural material for the railroad cars and the commercial vehicles. These kinds structures used stainless steel sheets are commonly fabricated by using the gas welding. For fatigue design of gas welded joints such as fillet and plug type joint, it is necessary to obtain design information on stress distribution at the weldment as well as fatigue strength of gas welded joints. And also, the influence of the geometrical parameters of gas welded joints on stress distribution and fatigue strength must be evaluated. the ${\Delta}P-N_f$ curves were obtained by fatigue tests. Using these results, ${\Delta}P-N_f$ curves were rearranged in the ${\sigma}-N_f$ relation with the maximum stress at the edge of fillet welded joint.

• 한국기계가공학회지
• /
• 제6권1호
• /
• pp.20-26
• /
• 2007

In this study, fatigue strength of load-carrying cruciform fillet welded joints were evaluated using a new method proposed by Yamada, for geometric or structural stress in welded joint, that is, one-millimeter stress below the surface in the direction corresponding to the expected crack path. Validity of the method is verified by analyzing fatigue test results for load-carrying cruciform welded specimens has different size of weld toe radius, leg length and plate thickness reported in literature. Structural stress concentration factor for 1mm below the surface was calculated by finite element analysis for each specimen respectively. When compared to the basic fatigue resistance curve offered by BS7608, the one-millimeter stress method shows conservative evaluation for load-carrying cruciform fillet welded joints.

• 대한기계학회논문집A
• /
• 제34권4호
• /
• pp.467-474
• /
• 2010

용접이음부의 신뢰성 확보는 구조물의 건전성과 내구성에 직접적인 영향을 미치기 때문에 가스용접 이음재의 피로설계기준(fatigue design criterion)을 정하기 위해서는 피로시험을 수행하여 ${\Delta}P$-Nf 관계를 이용하는 것이 일반적이다. 그러나 피로데이터를 장시간 획득하는 과정에서 여러 가지 변동인자에 의해서 피로데이터가 영향을 받기 때문에 피로데이터의 신뢰도가 떨어진다. 또한, 이음재의 재질 및 접합형태가 달라질 때마다, 각각의 경우에 대해서 새로운 피로시험이 요구됨으로 많은 시간과 비용이 소모된다. 따라서 이러한 문제점들을 개선하고 신뢰성 있는 설계를 하기 위해서 필렛 가스용접 이음재를 적용, 반복피로시험을 통한 데이터를 통계적으로 분석하여, 다양한 가스용접 이음재의 피로수명을 예측함과 동시에 실제 피로시험데이터와 비교 분석하여 예측된 수명의 신뢰도(reliability)와 신뢰구간(confidence interval)을 추정함으로서 새로운 피로설계기준 방법을 제시하고자 하였다.

• 한국구조물진단유지관리공학회 논문집
• /
• 제17권3호
• /
• pp.48-55
• /
• 2013

본 연구에서는 피로 손상된 용접이음의 피로수명 향상을 위한 방법으로 햄머피닝 처리법의 적용성을 검토하기 위하여 면외거셋 필렛 용접이음과 하중비전달형 리브 필렛 용접이음의 피로실험을 실시하였다. 본 실험에서는 면외거셋과 리브를 필렛 용접한 후 햄머피닝 처리를 하지 않은 용접그대로의 시험편, 용접후 햄머피닝 처리한 시험편, 그리고 용접그대로 시험편의 피로수명의 50% 시점에 햄머피닝 처리를 한 시험편의 피로실험을 실시하였다. 그리고 햄머피닝 처리에 의한 면외거셋과 리브 용접토우부의 형상 및 표면응력의 변화를 측정하였다. 그 결과, 햄머피닝처리에 의해 30~83MPa의 압축잔류응력이 도입 되었으며, 이로 인하여 강구조물의 제작시 용접후에 햄머피닝 처리를 실시하면 피로수명을 크게 향상 시킬 수 있을 뿐만 아니라, 이를 공용기간이 예상 피로수명의 50% 이하인 강구조물의 용접이음에 적용하여도 최소 1.3배 이상의 피로수명과 피로한계 향상효과를 기대할 수 있음을 제시하였다.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 1996년도 추계학술대회 논문집
• /
• pp.1058-1062
• /
• 1996

The assessments of weld defects by fracture mechanics are performed for design of welded Joints. In general, butt, T-type, and L-type welded joint are useful for welding structure. When linear weld defects are in welded joint, stress intensity factors for each joints are calculated by finite element method. Analysis results are shown for the fracture modes and characteristics of joint types. And they are founded for the weaken order of welded joints being T-type, butt, L-type.

• 한국철도학회:학술대회논문집
• /
• 한국철도학회 2004년도 추계학술대회 논문집
• /
• pp.222-227
• /
• 2004

Under cyclic loading, the fatigue failures of welded joints occur at weld toes which induce stress concentration by weld shape. So we need to obtain the peak stress and the S-N curve to assess the fatigue strength of welded joints. However the measurement of peak stress is of high uncertainty and low reproducibility, so we use nominal stress instead in fatigue tests of welded joints. In this study, fatigue tests to obtain S-N curves and FE analyses to obtain stress concentration factors were conducted for the two types of cruciform fillet welded joints, that is, load-carrying and non load-carrying types. Then we changed the obtained S-N curves to that based on peak stress using the hot-spot stress concept. From the analyses of the S-N curves obtained, we have concluded that there is a need to develop a new method to evaluate the fatigue life.