• Structural Engineering and Mechanics
• /
• v.50 no.6
• /
• pp.817-834
• /
• 2014

An experimental program was designed in the current work to examine the structural behavior of ferrocement beams reinforced with composite materials under three point loadings up to failure. The experimental program comprised casting and testing of twelve ferrocement beams having the dimensions of 120 mm width, 200 mm depth and 1600 mm length. The twelve beams were different in the type of reinforcements; steel bars, traditional wire meshes (welded and expanded wire meshes) and composite materials (fiberglass wire meshes and polypropylene wire meshes). The flexural performances of the all tested beams in terms of strength, ductility, cracking behavior and energy absorption were investigated. Also all the tested beams were simulated using ANSYS program. The results of the experimental tests concluded that the beam with fiber glass meshes gives the lowest first crack load and ultimate load. The ferrocement beam reinforced with four layers of welded wire meshes has better structural behavior than those beams reinforced with other types of wire meshes. Also the beams reinforced with metal wire meshes give smaller cracks width in comparing with those reinforced with non-metal wire meshes. Also the Finite Element (FE) simulations gave good results comparing with the experimental results.

• Journal of the Korean Society for Heat Treatment
• /
• v.26 no.2
• /
• pp.66-71
• /
• 2013

The purpose of this study is to prepare a high-strength Fiberglass Reinforced Metal (FRM). Aluminum covering over carbon fibers (CF) was made to increase their wettability to molten aluminum. A cylindrical sputtering apparatus was used for the covering. One tow of carbon fibers was placed along the central axis of the cylindrical target. Aluminum was uniformly coated around the carbon fiber tow. But in case of CF without sizing treatment, aluminum spread into the inside of the tow. Preforms of carbon fiber/aluminum composite were made by impregnating carbon fiber with molten aluminum. Contact angle of molten aluminum to the aluminum-coated carbon fiber was about $30^{\circ}$. The fractured section of preform was observed by SEM, which showed that molten aluminum wetted the outer part of the tow well but had not penetrated into the center, and that adhesion between CF and aluminum matrix was in good condition.

• Journal of the Korean Society for Heat Treatment
• /
• v.25 no.1
• /
• pp.1-5
• /
• 2012

The purpose of this study is to prepare a high strength fiberglass reinforced metal. Aluminum covering was carried out over carbon materials such as carbon fiber in order to increase their wettability to molten metals such as aluminum. A sputtering apparatus with a cylindrical target was fabricated to carry out the covering. Sputtering was caused by glow discharge between the target and the two anode plates attached to its top and bottom. As the substrate for preliminary test, a thin carbon wire was used instead of carbon fiber, and the wire was placed at the central axis of the target. Aluminium coating was formed on the whole surface of the substrate. The formation rate and structure of coating were varied by controlling the electrical potential of substrate. When the substrate was electrically isolated, coating with columnar structure was formed with a formation rate of $15{\mu}m/hr$. In case of grounded substrate, coating with amorphous structure was formed with a formation rate of $7{\mu}m/hr$.