• Journal of the Korean Ceramic Society
• /
• v.34 no.3
• /
• pp.303-313
• /
• 1997

To enhance the strength and formability of MCFC matrixes, alumina/${\gamma}$-LiAlO2 fiber-reinforced ${\gamma}$-LiAlO2 ma-trixes have been investigated. The MCFC matrixes with the thickness of 500~600 ${\mu}{\textrm}{m}$ were prepared by tape-casting of the slurry containing 10~30wt% fibers, followed by heat-treating up to $650^{\circ}C$. The porosity of fi-ber-reinforced matrixes decreased with the content of fibers, while the appropriate porosity(50~60%) for MCFC matrixes could be attained by adding larger ${\gamma}$-LiAlO2 particles with the diameter of about 50${\mu}{\textrm}{m}$ up to 50 wt%. The optimum length and content of the alumina fiber, both in the alignment of fibers and the enhancement of the strength, were found to be below 250${\mu}{\textrm}{m}$ and 20 wt%, respectively. On the other hand, the strength(156 gf/$\textrm{mm}^2$) of the ${\gamma}$-LiAlO2 matrix reinforced with ${\gamma}$-LiAlO2 fibers prepared in this study was improved by 20~40% in comparison with the alumina-fiber-reinforced matrix. It was also found that the alu-mina-fiber-reinforced matrix was completely corroded in molten carbonates but the ${\gamma}$-LiAlO2 was not.

• Journal of the Korean Ceramic Society
• /
• v.36 no.2
• /
• pp.107-115
• /
• 1999

Microstructural variation and strengthening effects with lamination methods of alumina fiber-reinforced ${\gamma}$-LiAlO2 matrixes for Molten Carbonate Fuel Cell(MCFC) were studied. The porosities of all matrix laminated by hot-pressing of two green sheets under 1 kg/$\textrm{cm}^2$ at 45$^{\circ}C$ for 1 min and by double-casting which the second layer cast on the first green sheet dried for 3.5h were more than 50%. The strength of the Al2O3 fiber-reinforced matrix prepared by lamination was enhanced by 70% in comparison with the non-laminated matrix (115 gf/$\textrm{mm}^2$) and the strength-directionality due to fiber-orientation also could be removed. The strength of matrixes laminated by triple-casting was higher than that of the double-cast matrix, but triple-cast matrix showed the directionality with the casting direction, and furthermore its porosity was less than 50%. Although the strength of matrixes laminated by double-casting (195 gf/$\textrm{mm}^2$) is slightly less than that of matrixes laminated by hot-pressing (212 gf/$\textrm{mm}^2$), the double-casting method was evaluated to be more efficient laminating process in MCFC matrix processing.