Statement of problem : Fracture of composite resin core will be occulted by progress of crack. Bonding interface of different materials has large possibility of starting point of crack line. Therefore, the bond strength of glass fiber post to composite resin core is important for prevention of fracture. Purpose: This in vitro study tried to find out how to get the higher strength of glass fiber post to composite resin core through surveying the maximum load that fractures the post and cote complex. Materials and methods: 40 specimens made with glass fiber Posts(Style $post^{(R)}$, Metalor, Swiss) and composite resin core ($Z-100^{(R)}$, 3M, USA) were prepared and loaded to failure with push-out type shear-bond strength test in a universal test machine. The maximum fracture load and fracture mode were investigated in the specimens that were restored with four different surface treatments. With the data. ANOVA test was used to validate the significance between the test groups, and Bonferroni method was used to check if there is any significant statistical difference between each test group. Evely analysis was approved with 95% reliance. Results: On measuring the maximum fracture load of specimens, both the treatments of sandblasted and acid-etched one statistically showed the strength increase rather than the control group (p<0.005). The scanning electric microscope revealed that sand blasting made more micro-retention form not only on the resin matrix but on the glass fiber, and acid-etching contributed to increase in surface retention form, eliminated the inorganic particles in resin matrix. Specimen fracture modes investigation represented that sand blasted groups showed lower bonding failure than no-sand blasted groups. Conclusion: Referring to the values of maximum fracture load of specimens, the bonding strength was increased by sand blasting and acid-etching.
Turker, Sebnem Begum;Alkumru, Hasan Necdet;Akalin, Buket
The Journal of Advanced Prosthodontics
/
제8권2호
/
pp.158-166
/
2016
PURPOSE. The aim of this study was to determine the fracture resistance and the mode of fracture of endodontically treated teeth restored with different fiber posts and all-ceramic crowns. MATERIALS AND METHODS. Two glass fiber reinforced post systems in two different sizes and polyethylene fiber ribbon in two different thicknesses (n=10) were used. The specimens, restored with all-ceramic crowns, were subjected to a compressive load (in N) delivered at a 130-degree angle to the long axis until a fracture could be noted. The results were analyzed statistically with a One-Way ANOVA test (P<.05). RESULTS. Statistically significant differences were observed between the mean fracture resistance values of Postec, Snowlight, and Kerr Connect thin specimens (P<.0095). The Postec results (395.70 N) were found to be significantly higher than the others. No statistical difference was observed among the thick specimens (P<.2657). The mean fracture resistance values of the Snowlight thick samples were found to be higher than those of the Snowlight thin samples. The specimens were always fractured around the cemento-enamel junction at the palatinal side. No post fracture was observed for the thin Snowlight and Kerr Connect specimens or for the thick Postec and Kerr Connect specimens. Among the common failure types of the specimens, the worst was observed to be the root fracture failure. The highest post dislodgement failure result (80%) was obtained from the thin Kerr Connect specimen. CONCLUSION. In terms of optimizing fracture resistance, the fiber post size selection should be done according to the forces applied to the restored teeth.
Kim, Hyun-Dong;Lee, Joo-Hee;Ahn, Kang-Min;Kim, Hee-Sun;Cha, Hyun-Suk
The Journal of Advanced Prosthodontics
/
제5권2호
/
pp.104-109
/
2013
PURPOSE. Among the surface treatment methods suggested to enhance the adhesion of resin cement to fiberreinforced composite posts, conflicting results have been obtained with silanization. In this study, the effects of silanization, heat activation after silanization, on the bond strength between fiber-reinforced composite post and resin cement were determined. MATERIALS AND METHODS. Six groups (n=7) were established to evaluate two types of fiber post (FRC Postec Plus, D.T. Light Post) and three surface treatments (no treatment; air drying; drying at $38^{\circ}C$). Every specimen were bonded with dual-curing resin cement (Variolink N) and stored in distilled water for 24 hours at $37^{\circ}C$. Shear-bond strength (MPa) between the fiber post and the resin cement were measured using universal testing device. The data were analyzed with 1-way ANOVA and by multiple comparisons according to Tukey's HSD (${\alpha}$=0.05). The effect of surface treatment, fiber post type, and the interactions between these two factors were analyzed using 2-way ANOVA and independent sample T-tests. RESULTS. Silanization of the FRC Postec Plus significantly increased bond strength compared with the respective non-treated control, whereas no effect was determined for the D.T. Light Post. Heat drying the silane coupling agent on to the fiberreinforced post did not significantly improve bond strength compared to air-syringe drying. CONCLUSION. The bond strength between the fiber-reinforced post and the resin cement was significantly increased with silanization in regards to the FRC Postec Plus post. Bond strength was not significantly improved by heat activation of the silane coupling agent.
본 연구의 목적은 수종의 섬유 강화 레진 포스트의 방사선 불투과도와 식별도를 비교하고자 하는 것이다. 이번 실험을 위해 1) FRC Postec Plus (Ivoclar Vivadent AG, Schaan, Liechtenstein) 2) Snowlight (Carbotech, Lewis center, OH, USA) 3) Dentin Post (Komet Brasseler, Lamgo, Germany) 4) Rely-X Fiber Post (3M ESPE, St.paul, MN, USA) 5) D.T.-Light Post (BISCO, Schaumburg, IL,USA ) 6) Luxapost (DMG, Hamburg, Germany) 등 6종의 섬유 강화 레진 포스트를 사용하였다. 각 포스트를 참고 기준으로 사용한 1 mm, 2 mm 간격의 알루미늄 step-wedge와 함께 디지털센서를 사용하여 방사선 촬영하였다. 방사선 불투과도는 각 포스트의 다섯 지점에서 $10{\times}10$ 화소의 평균 회색조 값으로 계산하였고 동일 두께의 알루미늄 당량으로 비교하였다. 치아 시편으로 비슷한 방사선 불투과도를 보이는 상악 전치 6개에 포스트를 식립 후 건조 하악골의 설측에 위치시켜 방사선 사진을 촬영하였다. 포스트만을 촬영한 사진과 치아 시편의 방사선 사진들을 구강악안면방사선과 전공자 3명, 치과보존과 전공자 3명, 일반 치과 의사 3명에게 보여주고 설문지를 작성하도록 요청하였다. 설문지는 포스트와 포스트가 식립된 치아 시편 사진에서 방사선 불투과도가 가장 높은 포스트와 낮은 포스트를 고르는 문항, 치근단과 치관부 끝에서 인접 상아질과 가장 식별이 잘되는 포스트를 고르는 문항을 포함하였다. 실험의 결과는 다음과 같았다. 1. 각 FRC-Post는 다양한 방사선 불투과도를 보였다. 2. 가장 높은 방사선 불투과도와 가장 낮은 방사선 불투과도를 가지는 포스트를 고르는 질문에서 포스트만 나열한 경우 실험군 모두 100%의 정답률을 보였으나 포스트를 치아에 넣고 치조골을 중첩시킨 경우 정답률의 변화를 보였다. 3. 포스트 주변 상아질과 구분되는 정도를 묻는 질문에 대해 시편의 조합 순서를 바꾸자 일관된 식별 결과를 보이지 않았다. 이에 본 연구에 사용한 포스트는 다양한 방사선 불투과도를 보이나 식별 능력에 영향을 미칠 정도의 방사선 불투과도 차이를 보이지 않는 것으로 사료된다.
PURPOSE. To investigate the void parameters within the resin cements used for fiber post cementation by micro-CT (${\mu}CT$) and regional push-out bonding strength. MATERIALS AND METHODS. Twenty-one, single and round shaped roots were enlarged with a low-speed drill following by endodontic treatment. The roots were divided into three groups (n=7) and fiber posts were cemented with Maxcem Elite, Multilink N and Superbond C&B resin cements. Specimens were scanned using ${\mu}CT$ scanner at resolution of $13.7{\mu}m$. The number, area, and volume of voids between dentin and post were evaluated. A method of analysis based on the post segmentation was used, and coronal, middle and apical thirds considered separately. After the ${\mu}CT$ analysis, roots were embedded in epoxy resin and sectioned into 2 mm thick slices (63 sections in total). Push-out testing was performed with universal testing device at 0.5 mm/min cross-head speed. Data were analyzed with Kruskal-Wallis and Mann-Whitney U tests (${\alpha}=.05$). RESULTS. Overall, significant differences between the resin cements and the post level were observed in the void number, area, and volume (P<.05). Super-Bond C&B showed the most void formation ($44.86{\pm}22.71$). Multilink N showed the least void surface ($3.51{\pm}2.24mm^2$) and volume ($0.01{\pm}0.01mm^3$). Regional push-out bond strength of the cements was not different (P>.05). CONCLUSION. ${\mu}CT$ proved to be a powerful non-destructive 3D analysis tool for visualizing the void parameters. Multilink N had the lowest void parameters. When efficiency of all cements was evaluated, direct relationship between the post region and push-out bonding strength was not observed.
Statement of problem. Glass fiber post is one of recent developments to accommodate esthetic restoration for endodontically treated teeth. This has many advantages over conventional post system in physical properties, esthetic factor, risk of root and restoration fracture, adhesion to core, radiopacity, removal and retrievabilty, biocompatibility and chemical stability. Purpose. This in vitro study was to evaluate the most suitable type of resin core for the glass fiber post through surveying the fracture modes and the maximum load that fractures the tooth. Material and methods. 50 sound maxillary premolars restored with glass fiber posts($ParaPost^{(R)}$ Fiber White) and different types of resin cores(ParaCore, $Z100^{TM}$, $Rebilda^{(R)}$ and $Admira^{(R)}$) were prepared and loaded to faiure in a universal test machine. The maximum fracture load and fracture mode were investigated in the specimens that were restored with resin and those of metal cast and core. With the data, Wilcoxon rank sum test was used to validate the significance between the test groups, and Tukey' s studentized range test was used to check if there is any significant statistical difference between each test group. Every analysis was approved with 95% reliance. Results. On measuring the maximum fracture load of teeth specimens, there was a significant difference between the maximum fracture loads of the tooth specimens. ParaCore showed the highest mean maximum fracture load followed by $Z100^{TM}$. And, the distribution of fracture mode of tooth specimens showed generally Type D, the three parted fracture of the core around the post was mostly seen(62.5%), and specifically, ParaCore showed 90% and $Z100^{TM}$ showed 100% Type D fracture. Conclusion. Referring to the values of maximum fracture load and mean compressive fracture load, ParaCore and $Z100^{TM}$ had high values and are recommended as tooth colored resin core material for glass fiber post. CLINICAL IMPLICATIONS. This study was carried out intending to be of aid in selecting the appropriate resin core for the glass fiber post. The dual cure type composite resin ParaCore and light cure type composite resin $Z100^{TM}$ have good properties and are recommended as tooth colored resin core material for glass fiber post.
목적: 이번 연구의 목적은 FRC-포스트와 코어가 색상차이에 따라 구별되는 정도를 비교하는 것이다. 연구 재료 및 방법: 실험을 위해 유사한 크기(${\pm}0.5 mm$)와 길이(${\pm}0.5 mm$)의 발치 한 하악 소구치 9개를 근관 형성하고 충전하였다. 3개의 치근을 체온을 재현하기 위해 $37^{\circ}C$ 물이 흐르는 가는 실리콘 튜브로 감은 후 cold mounting resin에 매몰하여 각 3개의 치근이 매몰된 총 3개의 시편을 제작하였다. 개개의 시편 치근에는 3종류의 $Snowpost^{(R)}$, MACRO-$LOCK^{TM}$ POST $ILLUSION^{TM}$$XRO^{(R)}$, FRC $Postec^{(R)}$ Plus post를 이용하여 각각의 포스트에 맞게 공간을 형성하고 포스트를 접착하였다. 3개의 시편 별로 $Luxacore^{(R)}$ Dual Blue, $Luxacore^{(R)}$ Dual A3 및 $Filtek^{TM}$ Z350 XT A1E로 코어를 축조, 시편 별로 다른 코어를 사용하였다. 각 시편에 대해 온도를 낮추기 위한 압축공기를 불 때와 안 불 때로 나누어 디지털 이미지를 촬영하였다. 치과의사 50명과 치과대학 대학생 50명 총 100명에게 어떤 포스트가 코어와 가장 구별이 잘되는 지를 설문조사 하였다. 결과: $Luxacore^{(R)}$ Dual Blue에서는 $Snowpost^{(R)}$가, $Luxacore^{(R)}$ Dual A3에서는 $Snowpost^{(R)}$가, $Filtek^{TM}$ Z350 A1E에서는 MACRO-$LOCK^{TM}$ POST $ILLUSION^{TM}$$XRO^{(R)}$가 구별이 가장 잘되었다. 압축공기를 불어 온도를 내리면 나타나는 MACRO-$LOCK^{TM}$$ILLUSION^{TM}$$XRO^{(R)}$의 색은 포스트와 코어의 구별을 더 용이하게 하였다. 결론: FRC-포스트와 복합레진 코어가 구별되는 정도는 색상차이에 따라 다름을 알 수 있었다.
Paula Pontes Garcia ;Aline Cappoani ;Ricardo Susin Schelbauer ;Gisele Maria Correr ;Carla Castiglia Gonzaga
Restorative Dentistry and Endodontics
/
제45권4호
/
pp.49.1-49.11
/
2020
Objectives: The aim of this study was to perform a clinical and radiographic analysis of endodontically treated teeth (ETT) restored with cast metal posts (CMPs) or prefabricated glass fiber posts (GFPs) and crowns. Materials and Methods: Fifty ETT were restored with 25 CMPs and 25 GFPs at a private dental clinic between 2001 and 2016. The restorations consisted of 12 all-ceramic crowns, 31 metal-ceramic crowns, and 7 composite resin crowns. Demographic data, type of teeth, type of post-and-core system, time of placement, crown restorations, the number of proximal contacts, the type of antagonist, and reports of any complications after post-and-core placement were recorded for each patient. Assessments were performed at baseline (radiographic) and follow-up (radiographic and clinical). Data were analyzed by the McNemar test, the Pearson χ2 test, and Kaplan-Meier survival curves (α = 0.05). The mean follow-up was 67.6 months. Results: No significant difference was observed for any of the radiographic parameters when the baseline and final radiographs were compared. In the clinical evaluation, anatomical form (p = 0.009) and occlusion (p = 0.001) showed significant differences according to the type of crown restoration; specifically, metal-ceramic and all-ceramic crowns outperformed composite resin crowns. Conclusions: CMPs and GFPs showed favorable results for restoring ETT after 6 years of follow-up. All-ceramic and metal-ceramic crowns showed higher survival rates and better clinical outcomes.
Makade, Chetana S.;Meshram, Ganesh K.;Warhadpande, Manjusha;Patil, Pravinkumar G.
The Journal of Advanced Prosthodontics
/
제3권2호
/
pp.90-95
/
2011
PURPOSE. To compare the fracture resistance and the mode of failure of endodontically treated teeth restored with different post-core systems. MATERIALS AND METHODS. Root canal treatment was performed on 40 maxillary incisors and the samples were divided into four groups of 10 each. For three experimental groups post space preparation was done and teeth were restored with cast post-core (Group B), stainless steel post with composite core (Group C) and glass fiber post with composite core using adhesive resin cement (Group D). Control group (A) samples were selected with intact coronal structure. All the samples were prepared for ideal abutment preparation. All the samples were subjected to a load of 0.5 mm/min at $130^{circ}$.until fracture occurred using the universal testing machine. The fracture resistance was measured and the data were analyzed statistically. The fracture above the embedded resin was considered to be favorable and the fracture below the level was considered as unfavorable. The statistical analysis of fracture resistance between different groups was carried out with t-test. For the mode of failure the statistical analysis was carried out by Kruskal-Wallis test and Chi-Square test. RESULTS. For experimental group Vs control group the fracture resistance values showed significant differences (P<.05). For the mode of failure the chi-square value is 16.1610, which means highly significant (P=.0009) statistically. CONCLUSION. Endodontically treated teeth without post core system showed the least fracture resistance demonstrating the need to reinforce the tooth. Stainless steel post with composite core showed the highest fracture resistance among all the experimental groups. Teeth restored with the Glass fiber post showed the most favorable fractures making them more amenable to the re-treatment.
목적: 본 연구에서는 자가-접착 레진 시멘트의 접착 강도에 포스트의 표면 처리와 접착 시스템이 미치는 영향을 조사하고자 하였다. 재료 및 방법: 비슷한 치근 길이를 가진 48개의 사람 상악 단근치를 사용하여 160개의 시편을 제작하고 접착 시스템에 따라 4개의 군으로 분류하였다(no adhesive, Adper Single Bond 2, Clearfil SE Bond, Clearfil S3). 각 군은 포스트 표면 처리 방식에 따라 다시 4개의 군으로 세분하였다(no treatment, sandblast, silane, sandblast and silane). 포스트를(Parapost Fiber White) Rely X Unicem을 사용하여 접착하였다. 치아를 장축에 수직으로 1 mm 두께로 절단 하였다. Push-out test를 0.5 mm/분의 crosshead speed로 시행하였다. 2-way ANOVA, 1-way ANOVA 검정을 시행하였고 Tukey test를 통한 사후 검정을 시행하였다(${\alpha}=0.05$). 결과: Tukey test를 통한 사후 검정에서 접착 시스템에 따른 차이가 나타났다. Clearfil SE Bond가 가장 높은 접착 강도를 나타내었다. 결론: 상아질에 Clearfil SE bond를 사용하고 포스트를 실란 처리시 가장 높은 접착 강도를 나타내었다.
본 웹사이트에 게시된 이메일 주소가 전자우편 수집 프로그램이나
그 밖의 기술적 장치를 이용하여 무단으로 수집되는 것을 거부하며,
이를 위반시 정보통신망법에 의해 형사 처벌됨을 유념하시기 바랍니다.
[게시일 2004년 10월 1일]
이용약관
제 1 장 총칙
제 1 조 (목적)
이 이용약관은 KoreaScience 홈페이지(이하 “당 사이트”)에서 제공하는 인터넷 서비스(이하 '서비스')의 가입조건 및 이용에 관한 제반 사항과 기타 필요한 사항을 구체적으로 규정함을 목적으로 합니다.
제 2 조 (용어의 정의)
① "이용자"라 함은 당 사이트에 접속하여 이 약관에 따라 당 사이트가 제공하는 서비스를 받는 회원 및 비회원을
말합니다.
② "회원"이라 함은 서비스를 이용하기 위하여 당 사이트에 개인정보를 제공하여 아이디(ID)와 비밀번호를 부여
받은 자를 말합니다.
③ "회원 아이디(ID)"라 함은 회원의 식별 및 서비스 이용을 위하여 자신이 선정한 문자 및 숫자의 조합을
말합니다.
④ "비밀번호(패스워드)"라 함은 회원이 자신의 비밀보호를 위하여 선정한 문자 및 숫자의 조합을 말합니다.
제 3 조 (이용약관의 효력 및 변경)
① 이 약관은 당 사이트에 게시하거나 기타의 방법으로 회원에게 공지함으로써 효력이 발생합니다.
② 당 사이트는 이 약관을 개정할 경우에 적용일자 및 개정사유를 명시하여 현행 약관과 함께 당 사이트의
초기화면에 그 적용일자 7일 이전부터 적용일자 전일까지 공지합니다. 다만, 회원에게 불리하게 약관내용을
변경하는 경우에는 최소한 30일 이상의 사전 유예기간을 두고 공지합니다. 이 경우 당 사이트는 개정 전
내용과 개정 후 내용을 명확하게 비교하여 이용자가 알기 쉽도록 표시합니다.
제 4 조(약관 외 준칙)
① 이 약관은 당 사이트가 제공하는 서비스에 관한 이용안내와 함께 적용됩니다.
② 이 약관에 명시되지 아니한 사항은 관계법령의 규정이 적용됩니다.
제 2 장 이용계약의 체결
제 5 조 (이용계약의 성립 등)
① 이용계약은 이용고객이 당 사이트가 정한 약관에 「동의합니다」를 선택하고, 당 사이트가 정한
온라인신청양식을 작성하여 서비스 이용을 신청한 후, 당 사이트가 이를 승낙함으로써 성립합니다.
② 제1항의 승낙은 당 사이트가 제공하는 과학기술정보검색, 맞춤정보, 서지정보 등 다른 서비스의 이용승낙을
포함합니다.
제 6 조 (회원가입)
서비스를 이용하고자 하는 고객은 당 사이트에서 정한 회원가입양식에 개인정보를 기재하여 가입을 하여야 합니다.
제 7 조 (개인정보의 보호 및 사용)
당 사이트는 관계법령이 정하는 바에 따라 회원 등록정보를 포함한 회원의 개인정보를 보호하기 위해 노력합니다. 회원 개인정보의 보호 및 사용에 대해서는 관련법령 및 당 사이트의 개인정보 보호정책이 적용됩니다.
제 8 조 (이용 신청의 승낙과 제한)
① 당 사이트는 제6조의 규정에 의한 이용신청고객에 대하여 서비스 이용을 승낙합니다.
② 당 사이트는 아래사항에 해당하는 경우에 대해서 승낙하지 아니 합니다.
- 이용계약 신청서의 내용을 허위로 기재한 경우
- 기타 규정한 제반사항을 위반하며 신청하는 경우
제 9 조 (회원 ID 부여 및 변경 등)
① 당 사이트는 이용고객에 대하여 약관에 정하는 바에 따라 자신이 선정한 회원 ID를 부여합니다.
② 회원 ID는 원칙적으로 변경이 불가하며 부득이한 사유로 인하여 변경 하고자 하는 경우에는 해당 ID를
해지하고 재가입해야 합니다.
③ 기타 회원 개인정보 관리 및 변경 등에 관한 사항은 서비스별 안내에 정하는 바에 의합니다.
제 3 장 계약 당사자의 의무
제 10 조 (KISTI의 의무)
① 당 사이트는 이용고객이 희망한 서비스 제공 개시일에 특별한 사정이 없는 한 서비스를 이용할 수 있도록
하여야 합니다.
② 당 사이트는 개인정보 보호를 위해 보안시스템을 구축하며 개인정보 보호정책을 공시하고 준수합니다.
③ 당 사이트는 회원으로부터 제기되는 의견이나 불만이 정당하다고 객관적으로 인정될 경우에는 적절한 절차를
거쳐 즉시 처리하여야 합니다. 다만, 즉시 처리가 곤란한 경우는 회원에게 그 사유와 처리일정을 통보하여야
합니다.
제 11 조 (회원의 의무)
① 이용자는 회원가입 신청 또는 회원정보 변경 시 실명으로 모든 사항을 사실에 근거하여 작성하여야 하며,
허위 또는 타인의 정보를 등록할 경우 일체의 권리를 주장할 수 없습니다.
② 당 사이트가 관계법령 및 개인정보 보호정책에 의거하여 그 책임을 지는 경우를 제외하고 회원에게 부여된
ID의 비밀번호 관리소홀, 부정사용에 의하여 발생하는 모든 결과에 대한 책임은 회원에게 있습니다.
③ 회원은 당 사이트 및 제 3자의 지적 재산권을 침해해서는 안 됩니다.
제 4 장 서비스의 이용
제 12 조 (서비스 이용 시간)
① 서비스 이용은 당 사이트의 업무상 또는 기술상 특별한 지장이 없는 한 연중무휴, 1일 24시간 운영을
원칙으로 합니다. 단, 당 사이트는 시스템 정기점검, 증설 및 교체를 위해 당 사이트가 정한 날이나 시간에
서비스를 일시 중단할 수 있으며, 예정되어 있는 작업으로 인한 서비스 일시중단은 당 사이트 홈페이지를
통해 사전에 공지합니다.
② 당 사이트는 서비스를 특정범위로 분할하여 각 범위별로 이용가능시간을 별도로 지정할 수 있습니다. 다만
이 경우 그 내용을 공지합니다.
제 13 조 (홈페이지 저작권)
① NDSL에서 제공하는 모든 저작물의 저작권은 원저작자에게 있으며, KISTI는 복제/배포/전송권을 확보하고
있습니다.
② NDSL에서 제공하는 콘텐츠를 상업적 및 기타 영리목적으로 복제/배포/전송할 경우 사전에 KISTI의 허락을
받아야 합니다.
③ NDSL에서 제공하는 콘텐츠를 보도, 비평, 교육, 연구 등을 위하여 정당한 범위 안에서 공정한 관행에
합치되게 인용할 수 있습니다.
④ NDSL에서 제공하는 콘텐츠를 무단 복제, 전송, 배포 기타 저작권법에 위반되는 방법으로 이용할 경우
저작권법 제136조에 따라 5년 이하의 징역 또는 5천만 원 이하의 벌금에 처해질 수 있습니다.
제 14 조 (유료서비스)
① 당 사이트 및 협력기관이 정한 유료서비스(원문복사 등)는 별도로 정해진 바에 따르며, 변경사항은 시행 전에
당 사이트 홈페이지를 통하여 회원에게 공지합니다.
② 유료서비스를 이용하려는 회원은 정해진 요금체계에 따라 요금을 납부해야 합니다.
제 5 장 계약 해지 및 이용 제한
제 15 조 (계약 해지)
회원이 이용계약을 해지하고자 하는 때에는 [가입해지] 메뉴를 이용해 직접 해지해야 합니다.
제 16 조 (서비스 이용제한)
① 당 사이트는 회원이 서비스 이용내용에 있어서 본 약관 제 11조 내용을 위반하거나, 다음 각 호에 해당하는
경우 서비스 이용을 제한할 수 있습니다.
- 2년 이상 서비스를 이용한 적이 없는 경우
- 기타 정상적인 서비스 운영에 방해가 될 경우
② 상기 이용제한 규정에 따라 서비스를 이용하는 회원에게 서비스 이용에 대하여 별도 공지 없이 서비스 이용의
일시정지, 이용계약 해지 할 수 있습니다.
제 17 조 (전자우편주소 수집 금지)
회원은 전자우편주소 추출기 등을 이용하여 전자우편주소를 수집 또는 제3자에게 제공할 수 없습니다.
제 6 장 손해배상 및 기타사항
제 18 조 (손해배상)
당 사이트는 무료로 제공되는 서비스와 관련하여 회원에게 어떠한 손해가 발생하더라도 당 사이트가 고의 또는 과실로 인한 손해발생을 제외하고는 이에 대하여 책임을 부담하지 아니합니다.
제 19 조 (관할 법원)
서비스 이용으로 발생한 분쟁에 대해 소송이 제기되는 경우 민사 소송법상의 관할 법원에 제기합니다.
[부 칙]
1. (시행일) 이 약관은 2016년 9월 5일부터 적용되며, 종전 약관은 본 약관으로 대체되며, 개정된 약관의 적용일 이전 가입자도 개정된 약관의 적용을 받습니다.