• Korean Journal of Materials Research
• /
• v.20 no.3
• /
• pp.148-154
• /
• 2010

It is necessary to develop new methods to prevent catastrophic failure of structural material in order to avoid accidents and conserve natural and energy resources. Design of intelligent materials with a self-diagnosing function to prevent fatal fracture of structural materials was achieved by smart composites consisting of carbon fiber tows or carbon powders with a small value of ultimate elongation and glass fiber tows with a large value of ultimate elongation. The changes in electrical resistance of CF-GFRP/GFRP (carbon fiber and glass fiber-reinforced plastics/glass fiber-reinforced plastics) composites increased abruptly with increasing strain, and a tremendous change was seen at the transition point where carbon fiber tows were broken. Therefore, the composites were not to monitor damage from the early stage. On the other hand, the change in electrical resistance of CP-GFRP/GFRP (carbon powder dispersed in glass fiber-reinforced plastics/glass fiber-reinforced plastics) composites increased almost linearly in proportion to strain. CP-GFRP/GFRP composites are superior to CF-GFRP/GFRP composites in terms of their capability to monitor damage by measuring change in electrical resistance from the early stage of damage. However, the former was inferior to the latter as an application because of the difficulties of mass production and high cost. A method based on monitoring damage by measuring changes in the electrical resistance of structural materials is promising for improved reliability of the material.

• Nuclear Engineering and Technology
• /
• v.56 no.2
• /
• pp.685-687
• /
• 2024

Fiber optic cables are used extensively for remote monitoring in applications under extreme conditions, such as at high temperatures or in ionizing radiation fields. When high temperature fiber optic cables were subjected to gamma irradiations, there was a significant loss in transmission at wavelengths < 350 nm after only 1 minute of irradiation. Negligible recovery of the fiber optic transmission with time was observed over 2 years, but the irradiation damage was almost completely reversed by high temperature annealing at 400 ℃.

• Journal of the Korean Society of Clothing and Textiles
• /
• v.22 no.2
• /
• pp.224-232
• /
• 1998

Protease is mixtured in detergent to remove protein-soil easily. It must not act on the any fiber except protein-soil during laundry. So the purpose of this study is to investigate how protease is affect the fiber, particulary the protein-fiber. For this purpose, silk, wool and nylon are selected as samples, and the extent of the damage was estimated as tensile strength and surface condition (that is fibrillation). The results are as follows. The tensile strength of fiber treated with protease were lowered at enzyme concentration 0.1%, temperature 4$0^{\circ}C$ , and, as washing time was longer, it was lowered more. And it was showed that the surface of fibers were fiblliated by protease during washing. From this results, it was found that protease damaged protein-fiber. The damage of silk was the largest of all, and wool was less damaged than silk, because it has the scale (cuticle) on the outside. Additionary, an influence of surfactant on damage of fiber was little about three fibers, but, the fibers were damaged more by the binary nonionic-surfactant and protease mixture than by protease only.

• Nuclear Engineering and Technology
• /
• v.55 no.6
• /
• pp.2053-2068
• /
• 2023

Following a loss of coolant accident (LOCA), prestressing concrete containment vessels (PCCVs) may experience high thermal load as well as internal pressure. The high temperature stress would increase the risk of premature damage to the containment, which reduces the safety margin during the increasing internal pressure. However, current investigations cannot clearly address the issues of thermal-pressure coupling effect on damage propagation and thus safety of the containment. Thus, this paper offers three simple and powerful damage parameters to differentiate the severity of damage of the containment. Moreover, despite of the temperature action severely threatening the pressure performance of the containment, the research regarding the improvement of the resistant performance of the containment is quite scarce. Therefore, in this paper, a comprehensive comparison of damage propagation and mechanism between conventional and fiber-reinforced concrete (FRC) containments is performed. The effects of fiber characteristics parameters on damage propagation of structures following the LOCA are also specifically revealed. It is found that the proposed damage indices can properly indicate state of damage in the containment body and the addition of fiber can be used to obviously mitigate the damage propagation in PCCV considering the thermal-pressure coupling.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2003.04a
• /
• pp.117-120
• /
• 2003

Electro-micromechanical techniques were applied using four-probe method for carbon nanotube (CNT) or nanofiber (CNF)/epoxy composites with their content. Carbon black (CB) was used to compare with CNT and CNF. The fracture of carbon fiber was detected by nondestructive acoustic emission (AE) relating to electrical resistivity for double-matrix composites test. Sensing for fiber tension was performed by electro-pullout test under uniform cyclic strain. The sensitivity for fiber damage such as fiber fracture and fiber tension was the highest for CNT/epoxy composites, and in CB case they were the lowest compared with CNT and CNF. Reinforcing effect of CNT obtained from apparent modulus measurement was the highest in the same content. The results obtained from sensing fiber damage were correlated with the morphological observation of nano-scale structure using FE-SEM. The information on fiber damage and matrix deformation and reinforcing effect of carbon nanocomposites could be obtained from electrical resistivity measurement as a new concept of nondestructive evaluation.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2001.05a
• /
• pp.89-92
• /
• 2001

Drop weight impact tests were performed to investigate the impact behavior of carbon fiber/epoxy composite laminates reinforced by short fibers and other interleaving materials. Characterization techniques, such as cross-sectional fractography and scanning acoustic microscopy, were employed quantitatively to assess the internal damage of some composite laminates. Scanning electron microscopy was used to observe impact damage and fracture modes on specimen fracture surfaces. The results show that composite laminates experience various types of fracture; delamination, intra-ply cracking, matrix cracking and fiber breakage depending on the interlayer materials. Among the composite laminates tested in this study, the composites reinforced by Zylon fibers showed very good impact damage resistance with medium level of damage, while the composites interleaved by poly(ethylene-co-acrylic acid) (PEEA) film is expected to deteriorate the bulk strength due to the reduction of fiber volume fraction, even though the damaged area is significantly reduced.

• Journal of Ocean Engineering and Technology
• /
• v.16 no.4
• /
• pp.48-53
• /
• 2002

Fiber-reinforced composites are extensively used in electronic, ship and aerospace applications due to their high strength and high toughess. In these applications, they are often subjected to localized heat damage due to various sources. In order to ensure their reliability, it is important to predict their residual properties using nondestructive evaluation thchniques. Fabric fiber composite specimens were manufactured with six layers of the glass-fiber prepreg and the carbon-fiber prepreg, respectively. The specimens were subjected to a localized heat damage using a heated copper tip with a diameter of 10mm at 35$0^{\circ}C$(CFRP) and 30$0^{\circ}C$(GFRP), respectively. The specimens were then subjected to tension tests while acoustic emission (AE) activities of specimens were collected. The AE activity of all specimens showed three types of distinct frequency regions. Those are matrix cracking, failure of the fiber/matrix interface and fiber breakage.

• Textile Coloration and Finishing
• /
• v.33 no.4
• /
• pp.309-316
• /
• 2021

Due to the rigid nature of the silicon carbide fiber(SiC), fiber damage occurs from the friction during the carding process. This damage not only lowers the spun yarn yield, but also lowers the heat resistance of the spun yarn, so that ultra-high heat resistant yarn cannot be manufactured. Therefore, in the carding process where the most friction between fiber and machine(wire, etc.) occurs, some factors were modified and tested, and as a result of measuring the change in physical properties, fiber damage decreased due to the wire angle or wire density, resulting in improved yield. The test method used to measure the yield of SiC fiber was the carbonization method, and the content of SiC fibers was calculated using the remaining amount after carbonization. Carbonization test was performed at air condition, 700℃, and for 2 hours. Analysis by SEM-EDX showed that the carbide was consistent with the composition of the SiC fiber.

• Proceedings of the KSME Conference
• /
• 2001.11a
• /
• pp.204-209
• /
• 2001

In this research, the effects of fiber stacking sequence on damage behaviors of FML(Fiber Metal Laminates) subject to indentation loading. SOP (Singly Oriented Ply) FML and angle ply FML were fabricated to study fiber orientation effects and angle ply effects. FML were fabricated by using 1050 aluminum laminate and carbon/epoxy prepreg. To increase adhesive bonding strength, Al laminate was etched using FPL methods. The static indentation test were conducted by using UTM(5ton, Shimadzu) under the 2side clamped conditions. During the tests, load and displacement curve and crack initiation and propagation behaviors were investigated. As fiber orientation angle increases, the crack initiation load of SOP FML increases because the stiffness induced by fiber orientation is increased. The penetration load of SOP FML is influenced by the deformation tendency and boundary conditions. However, the macro-crack of angle ply FML was initiated by fiber breakage of lower ply because angle plies in Angle ply FML prevents the crack growth and consolidation. The Angle ply FML has a critical cross-angle which prevent crack growth and consolidation. Damage behavior of Angle ply FML is changed around the critical cross-angle.

• Advances in concrete construction
• /
• v.16 no.3
• /
• pp.141-153
• /
• 2023

In order to develop and take full advantage of pasture fiber and waste concrete, this article studied how different amounts of pasture fiber influenced the toughness and pore structure of concrete with different replacement rates of recycled fine aggregate. Pasture fiber recycled concrete constitutive equations were established under idealized stiffness and toughness damage rate, based on fracture energy and damage mechanics theories. The relationship between pore structure and toughness was studied utilizing nuclear magnetic resonance and fractal theory. The toughness of text groups (0% (JZ), 10% (ZS10), 20% (ZS20)) first increased and then decreased with increasing amounts of pasture fiber, based on the damage rate of toughness. The toughness of concrete samples with recycled fine aggregate and pasture fiber is negatively correlated to the fractal dimension of small and medium-sized pores with a pore size of 0-500 nm. At a replacement rate of 10% of the recycled fine aggregate, the fractal dimension of the air voids (r: 500-9000 nm, i.e., Lg(r) ∈ [2.7, 3.9]) shows a gradual decrease with the increase of grass fiber dosage, indicating that with such a replacement rate of the recycled fine aggregate, the increase of pasture fiber can reduce the complexity of the pore structure of the air voids (500-9000 nm).