• Bulletin of the Korean Chemical Society
• /
• 제19권5호
• /
• pp.533-539
• /
• 1998

A magnetic film was deposited on a slide glass substrate from aqueous solutions of $FeCl_2$ and $NaNO_2$ at 363 K. XRD analysis showed that the film was polycrystalline magnetite $(Fe_{3(1-{\sigma})}O_4)$ without impurity phase. The lattice constant was 0.8390 nm. Mossbauer spectrum of the film could be deconvoluted by the following parameters: isomer shifts for tetrahedral $(T_d)$ and octahedral $(O_h)$ sites are 0.28 and 0.68 mm/s, respectively, and corresponding magnetic hyperfine fields are 490 and 458 kOe, respectively. The estimated chemical formula of the film by the peak intensity of Mossbauer spectrum was $Fe_{2.95}O_4$. Low temperature transition of the magnetite (Verwey transition) was not detected in resistivity measurement of the film. Properties of the film were discussed with those of pressed pellet and single crystal of synthetic magnetites. On the surface of the film, magnetite particles of about 0.2 μm in diameter were identified by noncontact atomic force microscopy (NAFM) and magnetic force microscopy (MFM).

• Proceedings of the KIEE Conference
• /
• 대한전기학회 1997년도 추계학술대회 논문집 학회본부
• /
• pp.294-295
• /
• 1997

CO-Cr 수직자기기록 매체의 우수한 하지층을 개발하기 위하여, 스피넬 결점막$(Fe,M)_3O_4$ (M=Ni,Zn)이 스핀스프레이 페라이트 플레이팅 방법으로 유리 기판 위에 제작되었다. 반응액과 산화액은 기판이 회전하는 반응용기로 분사되었다. 반응은 기판의 회전소독, 반응온도, 반응액과 산화액의 유속 그리고 반응액과 산화액의 농도에 의해 영향받았다. 반응액과 산화액의 유속은 60(ml/min)으로 하고, 반응온도는 90[$^{\circ}C$] 그리고 기판의 회전속도는 150[rpm]의 조건하에서, 페라이트 플레이팅 반응에 미치는 반응액과 산화액 농도의 영향이 화학적 조성, 결정학적 및 자기적 특성의 관점에서 연구되었다. $Ni_{0.34}Zn_{0.66}Fe_2O_4$의 조성에서, 우리는 가장 안정한 결정학적 및 자기적 특성을 얻었다.