• Advanced Composite Materials
• /
• v.18 no.4
• /
• pp.339-350
• /
• 2009

Al-Fe-V-Si alloys reinforced with SiC particles were prepared by multi-layer spray deposition technique. Both microstructures and mechanical properties including hardness and tensile properties development during hot exposure process of Al-8.5Fe-1.3V-1.7Si, Al-8.5Fe-1.3V-1.7Si/15 vol% $SiC_P$ and Al-10.0Fe-1.3V-2Si/15 vol% $SiC_P$ were investigated. The experimental results showed that an amorphous interface of about 3 nm in thickness formed between SiC particles and the matrix. SiC particles injected silicon into the matrix; thus an elevated silicon concentration was found around $\alpha-Al_{12}(Fe,\;V)_3Si$ dispersoids, which subsequently inhibited the coarsening and decomposition of $\alpha-Al_{12}(Fe,\;V)_3Si$ dispersoids and enhanced the thermostability of the alloy matrix. Moreover, the thermostability of microstructure and mechanical properties of Al-10.0Fe-1.3V-2Si/15 vol% $SiC_P$ are of higher quality than those of Al-8.5Fe-1.3V-1.7Si/15 vol% $SiC_P$.

• Resources Recycling
• /
• v.20 no.5
• /
• pp.34-39
• /
• 2011

Metallurgical grade silicon(MG-Si) was melted with Ca at 1500$^{\circ}C$ under Ar atmosphere. The sample was cooled at 10 $^{\circ}C$/min to room temperature and leached in aqua regia. In the present study, the effect of Ca addition and conditions of acid leaching on removal of Fe and P in MG-Si were investigated. CaSi$_2$ phase was formed at the grain boundary of MG-Si melting with Ca. Also FeSi$_2$ phase was precipitated in CaSi$_2$ phase. By the formation of CaSi$_2$ phase, 97% of Fe and 66 % of P were removed from Ca added MG-Si with the particle size of 600~850${\mu}m$ by aqua regia(more than 30%) leaching.

• Journal of Korea Foundry Society
• /
• v.23 no.2
• /
• pp.77-85
• /
• 2003

Some alloying elements such as Cr, B, Ti and Si were added individually or as a mixture to Fe-30 at.%Al alloys. The alloys were melted using an arc furnace and then heat-treated for homogenization at 1000$^{\circ}C$ for 7 days and followed by rolling at 1000$^{\circ}C$. The alloying elements on rolling characteristics were investigated by the microstructures and fracture mode before and after rolling. The microstructures before rolling showed that all of the alloys had equiaxed grains. On the other hand, the microstructures of rolling plane as well as its perpendicular plane became elongated after rolling. The alloys such as Fe-30Al, Fe-30Al-3Ti, Fe-30Al-0.5B, Fe-30Al-5Cr and Fe-30Al-3Ti-0.5B revealed better rolling behaviour from the point that intergranular and cleavage fractures were not fundamentally occurred. But the addition of 5Ti or 3Si to Fe-Al alloys had detrimental effects. The Ti-added alloy system such as Fe-30Al-5Ti, Fe-30Al-5Ti-5Cr, Fe-30Al-3Ti-5Cr and Fe-30Al-5Ti-0.5B were cracked through grain and showed cleavage fracture. The Si-added alloy system such as Fe-30Al-5Si, Fe-27Al-3Si and Fe-27Al-5Cr-3Si were cracked along the grain boundary and showed intergranular fracture. $DO_3{\leftrightarrow}B_2$ transition temperature of Fe-30at.%Al alloy was 520$^{\circ}C$, whereas the addition of 3Ti and 3Ti+0.5B comparably increased the temperature to 797 and 773$^{\circ}C$, respectively.

• Proceedings of the Korean Magnestics Society Conference
• /
• 2001.10a
• /
• pp.48-49
• /
• 2001

• Journal of the Korean Chemical Society
• /
• v.54 no.5
• /
• pp.579-581
• /
• 2010

Solid silica supported ferric chloride ($SiO_2-FeCl_3$) catalyzed one-step synthesis of various benzimidazoles from o-phenylenediamine and aldehydes using $H_2O_2$ as the oxidant. The salient features of this method are simple and convenient procedure, easy purification and shorter reaction times.

• Journal of the Korean Magnetics Society
• /
• v.19 no.2
• /
• pp.62-66
• /
• 2009

The soft magnetic FeSiCr were processed the ball-mill for 30 hours and the shape of FeSiCr particles was changed from sphere to flake type, which was observed using scanning electron microscope. The complex permittivity and permeability spectra and reflection loss of FeSiCr-rubber composite was measured using Network Analyzer in order to investigate the relationship between the microwave absorption and the material constants. The matching frequency shifted toward lower frequency range with microwave absorber thickness, and microwave absorber with FeSiCr-rubber composite showed a maxium reflection loss of -8.3 dB at 1.86 GHz for a 1.3 mm thickness.

• Journal of Powder Materials
• /
• v.1 no.1
• /
• pp.66-71
• /
• 1994

Optical microstructures and mechanical properties of Na gas atomized Al-20Si-5Fe alloying powder and its hot extrudates were studied on 3 different types of powder size distribution. This powder showed the size distribution of 10~210 $\mu\textrm{m}$. Also the microstructures of $\alpha$-Al, primary and eutectic Si and needle shaped intermetallic compounds were observed by optical microscope. These needle shaped intermetallic compounds were identified as ${\delta}Al_4FeSi_2$- by XRD and EDX analysis. The ultimate tensile strength(UTS) of these alloy extrudates was increased from 324 to 390 MPa with decreasing powder size range from 120~210 $\mu\textrm{m}$ to 10~64 $\mu\textrm{m}$. A value of Micro-vic-kers hardness was simillar to the result of UTS. These extrudates showed better wear resistance than those of Al-20Si-2X(X : Ni, Cr, Zr), although they are insensitive to the size distribution. These results indicate that the presentation of ${\delta}Al_4FeSi_2$ intermetallic compounds contributed to the wear resistance improvement.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.10 no.1
• /
• pp.36-41
• /
• 2000

We studied the exchange anisotropy of Ni-Fe/Co-Fe/Mn-Ir/Cu/buffer/Si multilayers using D.C magnetron sputtering technique. Generally, Ni-Fe/Mn-Ir/buffer(Cu)/Si multilayers cannot pin the ferromagnetic layer for the lower exchange biased field. We got $H_{ex}$ ex/ increased by two times, after using Cu/Ta as buffer layer to get larger grain size of Mn-Ir layer and inserting very thin Co-Fe layer between the Ni-Fe layer and the Mn-Ir layer to get improved grain-to-grain epitaxy relation at the interface between Ni-Fe layer and Mn-Ir layer. The variation of $H_{ex}$ by thickness of Mn-Ir layer in ferromagnete/Mn-Ir/buffer/Si multilayers is different to that in Mn-Ir/ferromagnete/buffer/Si multilayers, because the volume distribution of grain size of Mn-Ir layer and the exchange energy at the interface between the Mn-Ir and the ferromagnetic layers is different for stacking sequence.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.27 no.7
• /
• pp.462-467
• /
• 2014

In this paper, we studied the magnetic composite sheets for electromagnetic wave noise absorber of quasi-microwave band by using soft magnetic FeSiCr and Fe50Ni flakes with the thickness of about $1{\mu}m$ and polymer. The magnetic hysteresis curve including saturation magnetization and residual magnetization and the complex permeability characteristics of the composite sheets were investigated to clarify the mixing effect on electromagnetic wave absorption properties. The saturation magnetization was decreased about 10% while the residual magnetization was increased about 15% and the real parts of complex permeability at below 500 MHz were increased 0.6~4 while those values at above 500 MHz were decreased 0.4~2.5 according to the change of contents of FeSiCr and Fe50Ni powders. As a result, the reflection loss can be moved to the lower frequency from 2~3 GHz to 1~1.5 GHz as the contents of Fe50Ni flaky powder into FeSiCr flaky powder was increased up to 50%.

• Korean Journal of Materials Research
• /
• v.33 no.9
• /
• pp.353-359
• /
• 2023

This study investigated the growth behavior and characteristics of compounds formed at the interface between a liquid Al-Si-Cu alloy and solid cast iron. Through microstructural analyses, it was observed that various AlFe and AlFeSi phases are formed at the interface, and the relative proportion of each phase changes when small amounts of strontium are added to the Al alloy. The results of the microstructural analysis indicate that the primary phases of the interfacial compounds in the Al-Si-Cu base alloy are Al₈Fe₂Si and Al_4.5FeSi. However, in the Sr-added alloys, significant amounts of binary AlFe intermetallic compounds such as Al₅Fe₂ and Al₁₃Fe₄ formed, in addition to the AlFeSi phases. The inclusion of Sr has a slight diminishing effect on the rate at which the interfacial compounds layer thickens during the time the liquid Al alloy is in contact with the cast iron. The study also discusses the nano-indentation hardness and micro-hardness of the interfacial phases.