• Economic and Environmental Geology
• /
• v.30 no.1
• /
• pp.35-49
• /
• 1997

The coal formation of the Deokpyeong area are interbedded along metapelites of the Ogcheon Supergroup, which are composed mainly of graphite, quartz, muscovite and associated with small amounts of biotite, chlorite, pyrite and barite. The ratios of $SiO_2/Al_2O_3$, $Al_2O_3/Na_2O$ and $K_2O/Na_2O$ of the coaly metapelite are variable and wide range from 1.80 to 10.21, from 27.8 to 388.8 and from 7.6 to 61.8, respectively. These coal formation were deposited in basin of marine environments, and the REE of these rocks are not influenced with metamorphism and hydrothermal alterations on the basis of $Al_2O_3$ versus La, La against Ce, the ratios of La/Ce (0.19 to 0.99) and Th/U (0.02 to 4.75). These rocks also show much variation in $La_N/Yb_N$ (1.19 to 22.89), Th/Yb (0.14 to 21.43) and La/Th (0.44 to 13.67), and their origin is explained by derivation from a mixture of sedimentary and igneous rocks. The wide range in trace and REE element characteristics as Co/Th (0.12 to 2.78), La/Sc (0.33 to 10.18), Sc/Th (0.57 to 5.73), V/Ni (8 to 2347), Cr/V (0.02 to 0.67) and Ni/Co (1.56 to 32.95) of these coaly metapelites argues for inefficient mixing of the various source lithologies during sedimentation. Deep to pale green barium-vanadium muscovites (vanadium-oellacherite) have been found in this coal formations. Modes of occurrence and grain size of muscovite are heterogeneous, but most of the barium and vanadium-bearing muscovites occur along the boundaries between graphite and quartz grains, ranging from 200 to $350{\mu}m$ in length and from 40 to $60{\mu}m$ in width. Results of X-ray diffraction data of the minerals characterized to be monoclinic system with $a=5.249{\AA}$, $b=8.939{\AA}$, $c=20.924{\AA}$ and ${\beta}=95.894^{\circ}$. Representative chemical formula of the muscovite was $(Na_{0.09}K_{1.44}Ba_{0.46})(Al_{2.75}Ti_{0.07}V_{0.56}Fe_{0.08}Mg_{0.50})(Si_{6.12}Al_{1.88})O_{22}$. The V possibly substitute octahedral Al, and the Ba is coupled substitution of $K^+Si^{4+}=Ba^{2+}Na^+Ca^{2+}$, which compositional ranges of V and Ba are from 0.42 to 0.69 and from 0.34 to 0.56 based on $O_{22}$, respectively. Formation mechanism of the barium-vanadium muscovites in the coaly metapelite is shown that the formed by high pressure and temperature from regional metamorphism origanated during diagenesis at the interface between a basinal brine and organic matter.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.463-463
• /
• 2014

Dye-sensitized solar cells (DSSCs) have generated a strong interest in the development of solid-state devices owing to their low cost and simple preparation procedures. Effort has been devoted to the study of electrolytes that allow light-to-electrical power conversion for DSSC applications. Several attempts have been made to substitute the liquid electrolyte in the original solar cells by using (2,2',7,7'-tetrakis (N,N-di-p-methoxyphenylamine)-9-9'-spirobi-fluorene (spiro-OMeTAD) that act as hole conductor [1]. Although efficiencies above 3% have been reached by several groups, here the major challenging is limited photoelectrode thickness ($2{\mu}m$), which is very low due to electron diffusion length (Ln) for spiro-OMeTAD ($4.4{\mu}m$) [2]. In principle, the $TiO_2$ layer can be thicker than had been thought previously. This has important implications for the design of high-efficiency solid-state DSSCs. In the present study, we have fabricated 3-D Transparent Conducting Oxide (TCO) by growing tin-doped indium oxide (ITO) nanowire (NWs) arrays via a vapor transport method [3] and mesoporous $TiO_2$ nanoparticle (NP)-based photoelectrodes were prepared using doctor blade method. Finally optimized light-harvesting solid-state DSSCs is made using 3-D TCO where electron life time is controlled the recombination rate through fast charge collection and also ITO NWs length can be controlled in the range of over $2{\mu}m$ and has been characterized using field emission scanning electron microscopy (FE-SEM). Structural analyses by high-resolution transmission electron microscopy (HRTEM) and X-Ray diffraction (XRD) results reveal that the ITO NWs formed single crystal oriented [100] direction. Also to compare the charge collection properties of conventional NPs based solid-state DSSCs with ITO NWs based solid-state DSSCs, we have studied intensity modulated photovoltage spectroscopy (IMVS), intensity modulated photocurrent spectroscopy (IMPS) and transient open circuit voltages. As a result, above $4{\mu}m$ thick ITO NWs based photoelectrodes with Z907 dye shown the best performing device, exhibiting a short-circuit current density of 7.21 mA cm-2 under simulated solar emission of 100 mW cm-2 associated with an overall power conversion efficiency of 2.80 %. Finally, we achieved the efficiency of 7.5% by applying a CH3NH3PbI3 perovskite sensitizer.

• Korean Journal of Food Science and Technology
• /
• v.45 no.3
• /
• pp.274-278
• /
• 2013

The aim of our study was to investigate the chemical composition of the Asian ginseng seed (Panax ginseng C.A. Meyer) and the American ginseng seed (Panax quinquifolium L.) grown in Korea (3 years, KGS3; 4 years, KGS4), China (4 years, CGS4), and USA (4 years, AGS4). AGS had the heaviest 100-seed weight ($4.21{\pm}0.31g$). The approximate compositions of the ginseng seeds were 13.66-17.00% crude protein, 2.21-8.65% crude ash, 19.06-24.06% crude lipid, and 43.21-47.49% crude fiber. The mineral contents of the ginseng seeds were greater in order of K>P>Ca>Mg>Fe>Na>Zn >Cu. The unsaturated fatty acid content was 96.71-96.94%, and the major fatty acids oleic acid and linoleic acid were present. Total sugar content was 15.00-26.17 mg glucose/g. The acidic polysaccharide content was 0.56-0.80 mg ${\beta}$-Dgalacturonic acid/g. These results showed the differences in the physicochemical characteristics of ginseng seeds with respect to cultivation location, cultivation year, and species.

• Korean Journal of Food Science and Technology
• /
• v.48 no.6
• /
• pp.574-581
• /
• 2016

Glasswort (Salicornia herbacea L.) is an edible halophyte that grows in salt marshes. In the present study, anti- and pro-oxidant activities and cytotoxic properties of glasswort were investigated. Solvent fractions, including fractions of hexane, ethylether (Fr.E), ethylacetate (Fr.EA), butanol and water, were prepared from a 70% methanol extract of glasswort aerial parts. Fr.EA contained the highest levels of total polyphenols and flavonoids, showing the strongest scavenging activities against DPPH and ABTS radicals, and nitrite. In addition Fr.EA showed the most potent cytotoxic effects on HCT-116 colon cancer cells and INT-407 normal intestinal cells, followed by Fr.E. Most fractions also decreased the level of reactive oxygen species in the treated cells, but generated $H_2O_2$ in the medium. The cytotoxic activity of Fr.EA was more pronounced in the presence of ascorbic acid or N-acetylcysteine. These results indicate that the fractions from aerial parts of glasswort exhibit both anti- and pro-oxidant activities, and these activities modulate cytotoxic properties.

• Restorative Dentistry and Endodontics
• /
• v.34 no.1
• /
• pp.69-79
• /
• 2009

The purpose of this study was to evaluate the influence of elastic modulus of restorative materials and the number of interfaces of post and core systems on the stress distribution of three differently restored endodontically treated maxillary second premolars using 3D FE analysis. Model 1, 2 was restored with a stainless steel or glass fiber post and direct composite resin. A PFG or a sintered alumina crown was considered. Model 3 was restored by EndoCrown. An oblique 500 N was applied on the buccal (Load A) and palatal (Load B) cusp. The von Mises stresses in the coronal and root structure of each model were analyzed using ANSYS. The elastic modulus of the definitive restorations rather than the type of post and core system was the primary factor that influenced the stress distribution of endodontically treated maxillary premolars. The stress concentration at the coronal structure could be lowered through the use of definitive restoration of high elastic modulus. The stress concentration at the root structure could be lowered through the use of definitive restoration of low elastic modulus.

• Korean Journal of Community Nutrition
• /
• v.17 no.6
• /
• pp.689-706
• /
• 2012

The purpose of this study was to evaluate effects of a nutrition education focused on Food Exchange System for the higher grades elementary children. Nutrition education lessons (40 min/lesson, 4 times), '5 major nutrients and functions', '6 food groups', 'daily needed energy and food exchange units', 'good choice of snacks and balanced exercise' were provided to elementary students (5th grade students). This research was based on the data from two groups of elementary school children in the 'education' group (n = 31) and 'non-education' group (n = 31). We assessed the changes in dietary attitude, food habit and nutrition knowledge using questionnaire and nutrient intake using 24hr recall method by nutrition education using the developed pamphlet. After education, there was a significant difference in the dietary attitude score only in attitude of 'balanced meal' (p < 0.001) in the education group compared to the non-education group. In food habit, there were significant positive changes in the type of breakfast and in the priority of choosing snack in the educated group. In nutrition knowledge, there were significant increases in scores of 'function of carbohydrate' (p < 0.05), 'function of fat' (p < 0.01), 'function of vitamin' (p < 0.01), 'foods of carbohydrate' (p < 0.01), and 'foods of vitamin' (p < 0.01) in the educated group. After education, carbohydrate: protein: fat (CPF) ratio was significantly different between the two groups (education group, 59 : 16 : 26 vs. non-education group, 63 : 15 : 23). In evaluation of nutrient intake by Dietary Reference Intakes for Koreans (KDRIs), there were significant positive effects in energy (p < 0.05), thiamin (p < 0.05), riboflavin (p < 0.05), vitamin C (p < 0.05), phosphorus (p < 0.01), Fe (p < 0.01) and zinc (p < 0.01) in the education group compared to the non-education group. In conclusion, the developed 4 times' nutritional education pamphlet focused on individual daily energy requirements and food exchange units using food exchange system for higher grades' elementary student may positively change nutrition knowledge and dietary intakes.

• Applied Chemistry for Engineering
• /
• v.1 no.1
• /
• pp.83-90
• /
• 1990

The semiconducting $(Pb_1\;_xSn_x)_1$ $_yTe_y$, one of the low - temperature thermoelectric materials, has been prepared and its chemical composition and nonstoichiometry has been analyzed. The content of Pb in the specimens was determined by the complexometric back - titration method with EDTA and Pb(II) standard solutions. Te - content was analyzed with the redox titration method. The electrical conductivity and the thermoelectric power have also been measured by the DC 4 - probe and the heat-pulse technique, respectively. All of the specimens showed a nonstoichiometric behavior in their chemical compositions (Te excess), thus gave rise to a p - type semiconducting property, and the nonstoichoimetry became bigger as the Sn - content increased. The thermoelectric power vs. temperature results have been analyzed upon the basis of the Fermi level vs. temperature profiles in the saturation regime. The specimen of x=0.1 evolved a transition from p - to n - type property at about 670K, which has been explained by the fact that the mobility of electrons is bigger than that of holes in the temperature range of the intrinsic regime.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.29 no.8
• /
• pp.489-493
• /
• 2016

In this study, the effect of vanadium oxide ($V_2O_5$) content and pre-sintering atmosphere on sealing property of glass frit that consisted of $V_2O_5-BaO-ZnO-P_2O_5-TeO_2-CuO-Fe_2O_3-SeO_2$ was investigated by XPS (X-ray photoelectron spectroscopy). The content of V2O5 was changed to 15, 30, and 45 mol%, and the pre-sintering was carried out in air and $N_2$ condition, respectively. XPS analysis conducted before and after laser irradiation with identical sample. Before laser treatment, glass frits that were pre-sintered at air condition showed both $V^{4+}$ and $V^{5+}$, but the valence state was changed to $V^{5+}$ after laser irradiation when the glass frits contained 30 and 45 mol% $V_2O_5$; this change led to non-adhesive property. On the other hand, glass frits that were pre-sintered at $N_2$ condition exhibited only $V^{4+}$ and it showed fine adhesion irrespective of the $V_2O_5$ content. As a result, the existence of $V^{4+}$ seems to be a major factor for controlling the adhesive property of glass frit for laser sealing.

• Journal of the Optical Society of Korea
• /
• v.19 no.6
• /
• pp.705-710
• /
• 2015

The fabrication process of thin boron-doped nanocrystalline diamond (B-NCD) microelectrodes on fused silica single mode optical fiber cladding has been investigated. The B-NCD films were deposited on the fibers using Microwave Plasma Assisted Chemical Vapor Deposition (MW PA CVD) at glass substrate temperature of 475 ℃. We have obtained homogenous, continuous and polycrystalline surface morphology with high sp³ content in B-NCD films and mean grain size in the range of 100-250 nm. The films deposited on the glass reference samples exhibit high refractive index (n=2.05 at λ=550 nm) and low extinction coefficient. Furthermore, cyclic voltammograms (CV) were recorded to determine the electrochemical window and reaction reversibility at the B-NCD fiber-based electrode. CV measurements in aqueous media consisting of 5 mM K₃[Fe(CN)₆] in 0.5 M Na₂SO₄ demonstrated a width of the electrochemical window up to 1.03 V and relatively fast kinetics expressed by a redox peak splitting below 500 mV. Moreover, thanks to high-n B-NCD overlay, the coated fibers can be also used for enhancing the sensitivity of long-period gratings (LPGs) induced in the fiber. The LPG is capable of measuring variations in refractive index of the surrounding liquid by tracing the shift in resonance appearing in the transmitted spectrum. Possible combined CV and LPG-based measurements are discussed in this work.

• Korean Journal of Materials Research
• /
• v.22 no.11
• /
• pp.569-574
• /
• 2012

Large single grain $Gd_{1.5}Ba_2Cu_3O_{7-y}$ (Gd1.5) bulk superconductors were fabricated by a top-seeded melt growth (TSMG) process using an $NdBa_2Cu_3O_{7-y}$ seed. The seeded Gd1.5 powder compacts with a diameter of 50 mm were subjected to the heating cycles of a TSMG process. After the TSMG process, the diameter of the single grain Gd1.5 compact was reduced to 43 mm owing to the volume contraction during the heat treatment. The superconducting transition temperature ($T_c$) of the top surface of the single grain Gd1.5 sample was as high as 93.5 K. The critical current densities ($J_cs$) at 77 K and 1T and 1.5 T were in ranges of 25,200-43,900 $A/cm^2$ and 10,000-23,000 $A/cm^2$, respectively. The maximum attractive force at 77 K of the sample field-cooled using an Nd-B-Fe permanent magnet (surface magnetic field of 0. 527 T) was 108.3 N; the maximum repulsive force of the zero field-cooled sample was 262 N. The magnetic flux density of the sample field-cooled at 77 K was 0.311T, which is approximately 85% of the applied magnetic field of 0.375 T. Microstructure investigation showed that many $Gd_2BaCuO_5$ (Gd211) particles of a few ${\mu}m$ in size, which are flux pinning sites of Gd123, were trapped within the $GdBa_2Cu_3O_{7-y}$ (Gd123) grain; unreacted $Ba_3Cu_5O_8$ liquid and Gd211 particles were present near the edge regions of the single grain Gd1.5 bulk compact.