• Journal of the Korean Magnetics Society
• /
• v.6 no.2
• /
• pp.112-116
• /
• 1996

스퍼터링법으로 제조한 NiFeCo/Cu/NiFeCo/FeMn 스핀밸브 자성 다층막의 자기적 성질과 자기저항에 대해 연구하였다. Cu 사잇층 두께가 15 .angs. 인 경우 약 6%의 자기저항을 얻을 수 있었다. NiFeCo/FeMn에서 교환이방성 자계는 약 20 Oe 정도였는데, 이는 NiFe/FeMn 계 스핀밸브 구조에서 보고된 값(100 Oe 이상) 보다 현저히 작은 것이다. 3 mTorr에서 제조한 NiFeCo 박막은 약 10 Oe 정도의 큰 보자력을 보임으로써 비슷한 조건에서 제조한 NiFe 박막의 경우(약 2 Oe)보다 상당히 큰 값을 갖는 것으로 관찰되었다. 작은 교환이방성 자계와 큰 보자력으로 인해 음 .rarw. 양 방향과 양 .rarw. 음 방향의 자화거동에 있어서 비대칭적인 자기저항 이력곡선 거동을 보이는 것으로 나타났다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.05a
• /
• pp.55-58
• /
• 2003

FeMn based spin valves often consist of a NiFe/FeMn/NiFe trilayer structure. We have investigated the evolution of exchange bias at the bottom and top interfaces in the NiFe(5nm)/FeMn(x)/NiFe(5nm) trilayer structure as a function of FeMn thickness in the range 3 nm to 30 nm. The XRD results indicate (111) textured growth for NiFe and FeMn layers. The magnetization studies using VSM show two hysteresis loops corresponding to the bottom NiFe seed layer and top NiFe layers with greater bias for the bottom NiFe layer, for FeMn thickness equal to and above 5 nm. The larger exchange bias for the bottom seed layer is confirmed by the surface sensitive MOKE hysteresis loop measurements which show gradual weakening of the MOKE hysteresis loop for the bottom NiFe layer with increasing FeMn thickness. The observed large exchange bias in a spin valve structure is usually attributed to the pinning NiFe layer on top of the FeMn layer, even when a NiFe seed layer of a few nm thickness is present, whereas, in reality it may be arising from the bottom seed layer, as shown by the present study.

• Journal of the Korean Magnetics Society
• /
• v.9 no.4
• /
• pp.196-202
• /
• 1999

The magnetic properties and the microstructures of the Mn-Ir/Ni-Fe multilayers with various stacking structures and buffer layer materials have been investigated. The (111) texture of Mn-Ir/Ni-Fe was observed in the top structures with Ta, Zr, or Ti buffer materials. However, all Mn-Ir/Ni-Fe multilayers with top structures exhibit high $H_{ex}$, regardless of the (111) preferred orientation of Mn-Ir film. The samples whose high $H_{ex}$ observed grain-to-grain epitaxial tendency and the large grain of Mn-Ir film at the interface. It can be explained that the $H_{ex}$ does not depend on the (111) texture of the Mn-Ir film and the interface roughness, but depends on the grain size of the Mn-Ir film and the morphology of the interface between the Mn-Ir and the Ni-Fe grains, and the $H_c$ depends on the interface roughness between the Mn-Ir and the Ni-Fe films.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.9 no.5
• /
• pp.486-492
• /
• 1999

The purpose of this research was to find out what is the dominant factor determining the $H_{ex}$ and the $H_C$ of Mn-Ir/Ni-Fe multilayers with different buffer layers. Regardless of (111) texture of Mn-Ir layer, all samples showed over the $H_{ex}$ of 155 Oe. We found out the $H_{ex}$ and the $H_C$ of Mn-Ir/Ni-Fe multilayers depend on interface morphology and grain size of Mn-Ir layer at the interface between Mn-Ir and Ni-Fe layers. The dependence of magnetroesistance ratio and coupling field on the thickness of ferromagnetic layer, thickness of Cu layer and different buffer layers have been studied. Maximum magnetoresistance ratio appeared for the sample Ta(5 nm)/Mn-Ir(10 nm)/Ni-Fe(7.5 nm)/Cu(2 nm)/Ni-Fe(6 nm)/Ta(5 nm)/Si. Magnetoresistance ratio may be related to grain of ferromagnetic layer. Coupling field may be related to the roughness and the grain size of ferromagnetic layer in the spin-valve multilayers.

• Journal of the Korean Magnetics Society
• /
• v.5 no.5
• /
• pp.570-574
• /
• 1995

Magnetoresistance of NiFeCo/Cu/NiFeCo/FeMn uncoupled exchange biased sandwiches has been studied. The magnetoresistance change ratio, ${\Delta}R/R_{s}$ showed 4.1 % at a saturation field as low as 11 Oe in $Si/Ti(50\;{\AA})/NiFeCo(70\;{\AA})/Cu(23\;{\AA})/NiFeCo(70\;{\AA})/FeMn(150\;{\AA})/Cu(50\;{\AA})$ spin valve structure. In this system, the magnetoresistance was affected by interlayer material and thickness. When Ti and Cu were used as the interlayer material in this structure, maximum magnetoresistance change ratio were 0.32 % and 4.1 %, respectively. 6.1 % MR ratio was obtained in $Si/Ti(50\;{\AA})/NiFeCo(70\;{\AA})/Cu(15\;{\AA})/NiFeCo(70\;{\AA})/FeMn(150\;{\AA})/Cu(50\;{\AA})$ spin valve structure. The magnetoresistance change ratio decreased monotonically as the interlayer thickness increased. It was found that the exchange bias field exerted by FeMn layer to the adjacent NiFeCo layer was ~25 Oe, far smaller than that reported in NiFe/Cu/NiFe/FeMn spin valve structure(Dieny et. al., ~400 Oe). The relationship between the film texture and exchange anisotropy ha been examined for spin valve structures with Ti, Cu, or non-buffer layer.

• Proceedings of the Korean Magnestics Society Conference
• /
• 1997.11a
• /
• pp.30-31
• /
• 1997

• Proceedings of the Korean Magnestics Society Conference
• /
• 2002.12a
• /
• pp.190-191
• /
• 2002

Granular feromagnets는 non-magnetic maxtrix 안에 nanometer-sized의 ferromagnetic grain들 구성된다. Co-Cu,Co-Ag, Fe-Ag, NiFe-Ag $^1$을 포함하는 이미 알려진 다른 Granular 금속 합금들의 giant magnetoresistance 에 관계하여 Granular feromagnets 에 대해 조사하였다. Bulk상태의 NiFe와 Mn 혼화되기 쉽다.$^2$ 그리고 Mn은 열처리된 다층박막의 NiFe의 lattice에 쉽게 수용되어진다.$^3$ 이번 실험에서는 metastable한 fcc solid solution NiFe-Mn 박막이 열처리 하에서 NiFe과 Mn으로 분리되었다. (중략)

• Journal of the Korean Magnetics Society
• /
• v.10 no.6
• /
• pp.274-279
• /
• 2000

The microstructure and thermal properties of the Mn-IriNi-Fe exchange biased multi-layers with various buffer layers and stacking structures have been investigated. The H$_{e{\chi}}$ and the T$_{b}$ depend on the Mn-Ir grain size at the interface between the Mn-Ir layer and the Ni-Fe layer, The (111) preferred orientation of Mn-Ir/Ni-Fe on the Ta buffer layer may promote the values of J$_{k}$ and H$_{e{\chi}}$. The samples which produce the Hex have the epitaxial relationship at the interface between the Mn-Ir layer and the Ni-Fe layer due to the generation of misfit dislocation.

• Journal of the Korean Magnetics Society
• /
• v.9 no.3
• /
• pp.166-172
• /
• 1999

The magnetic properties between Mn-Ir antiferromagnetic layer and Ni-Fe ferromagnetic layer have been investigated in Mn-Ir/Ni-Fe/Zr on Si wafer formed by magnetron sputtering. Mn-Ir was sputtered from Ir chips and Mn target using D.C. power, Ni-Fe and Zr were deposited from Ni-Fe and Zr targets using D.C. power under Ar atmosphere. We studied the dependence of the magnetic properties on Ir content of Mn-Ir layer for Mn-Ir/Ni-Fe bilayer, and obtained the highest $H_ex$ of 219 Oe and the low $H_c$ of 30 Oe. And then focused on the effect of base pressure for Mn-Ir containing multilayers. Our experimental data showed that if the base pressure is higher than $3.0{\times}10^{-6}\;Torr$, the exchange anisotropy of Mn-Ir/Ni-Fe/Zr disappeared probably due to the grain refining of Mn-Ir film. In addition we have studied the dependence of Zr buffer on magnetic properties of Mn-Ir/Ni-Fe/Zr multilayers, and observed that Zr buffer about (111) texture and lower $H_c$ of Mn-Ir/Ni-Fe/Zr multilayer.

• Applied Microscopy
• /
• v.45 no.1
• /
• pp.9-15
• /
• 2015

In the present study, microstructural evolution in CuCrFeNi, CuCrFeNiMn, and CuCrFeNiMnAl alloys has been investigated. The as-cast CuCrFeNi alloy consists of a single fcc phase with the lattice parameter of 0.358 nm, while the as-cast CuCrFeNiMn alloy consists of (bcc+fcc1+fcc2) phases with lattice parameters of 0.287 nm, 0.366 nm, and 0.361 nm. The heat treatment of the cast CuCrFeNiMn alloy results in the different type of microstructure depending on the heat treatment temperature. At $900^{\circ}C$ a new thermodynamically stable phase appears instead of the bcc solid solution phase, while at $1,000^{\circ}C$, the heat treated microstructure is almost same as that in the as-cast state. The addition of Al in CuCrFeNiMn alloy changes the constituent phases from (fcc1+fcc2+bcc) to (bcc1+bcc2).