• 한국주조공학회지
• /
• 제38권6호
• /
• pp.111-120
• /
• 2018

In this study, the effects of two different casting methods (gravity casting and, diecasting) and various solid-solution conditions on the mechanical properties of ASC (Al-10.5wt%Si-1.75wt%Cu) and ALDC12 (Al-10.3wt%Si-1.72wt%Cu-0.76wt%Fe-0.28wt% Mn-0.32wt%Mg-0.9wt%Zn) alloys were investigated. A thermodynamic solidification analysis program (PANDAT) was used to predict the liquidus, solidus, and phases of the used alloys. In the results of an XRD analysis, ${\beta}$-AlFeSi peaks were observed only in the ALDC12 alloy regardless of the casting method or SST (solid-solution treatment) conditions. However, according to the results of a FE-SEM observation, both ${\theta}(Al_2Cu)$ and ${\beta}$-AlFeSi were found to exist besides ${\alpha}$-Al and eutectic Si in the gravity-casted ASC alloy at $500^{\circ}C$ after a SST of 120min. The ${\alpha}$-AlFeSi and ${\beta}$-AlFeSi phases including the eutectic phases were also found to exist in the ALDC12 alloy. The results of a microstructural observation and analyses by XRD, FE-SEM and EDS were in good agreement with the PANDAT results. The gravity-casted ALDC12 and ASC specimens showed the highest Y.S. and UTS values after aging for three hours at $180^{\circ}C$ after a SST at $500^{\circ}C$ for 30min. At longer solid-solution treatment times at $500^{\circ}C$ in the gravity-casted ALDC12 and ASC specimens, the elongations of the ASC alloys increased, whereas they decreased slightly in the ALDC12 alloys.

• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 2000년도 International Symposium on Magnetics The 2000 Fall Conference
• /
• pp.584-584
• /
• 2000

Electronic structures of ordered Fe$_3X (X = Al, Si), and their derivative ternary alloys of Fe_2TX (T = 3d transition metal) have been investigated by using the linearized muffin-tin orbital (LMTO) band method. The role of the coupling between substituted transition metal and its neighbors is investigated by calculating the magnetic moments and local density of states (LDOS). It is shown that it is essential to include the coupling beyond nearest neighbors in obtaining the magnetic moment of Fe alloy. The preferential sites of T impurities in Fe_3X are determined from the total energy calculations. The derivative ternary alloys of Fe_2TX have characteristic electronic structures of semi-metal for Fe_2VAI and (nearly) half-metal for Fe_2TAI (T = Cr, Mn) and Fe_2TSi (T = V, Cr, Mn)

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 1995년도 추계학술강연 및 발표대회 강연 및 발표논문 초록집
• /
• pp.14-14
• /
• 1995

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.1000-1001
• /
• 2006

Two atomized alloy powders were pre-compacted by cold and subsequently hot forged at temperatures ranging from 653K to 845K. The addition of Cu and Mg causes a decrease in the eutectic reaction temperature of Al-10Si-5Fe-1Zr alloy from 841K to 786K and results in a decrease of flow stress at the given forging temperature. TEM observation revealed that in addition to Al-Fe based intermetallics, $Al_2Cu$ and $Al_2CuMg$ intermetallics appeared. The volume fraction of intermetallic dispersoids increased by the addition of Cu and Mg. Compressive strength of the present alloys was closely related to the volume fraction of intermetallic dispersoids.

• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 2003년도 하계학술연구발표회 및 한.일 공동심포지엄
• /
• pp.38-39
• /
• 2003

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2013년도 춘계학술대회 논문집
• /
• pp.112-113
• /
• 2013

Thin CrAlMgSiN films, whose composition were 30.6Cr-11.1Al-7.3Mg-1.2Si-49.8N (at.%), were deposited on steel substrates in a cathodic arc plasma deposition system. They consisted of alternating crystalline Cr-N and AlMgSiN nanolayers. After oxidation at $800^{\circ}C$ for 200 h in air, a thin oxide layer formed by outward diffusion of Cr, Mg, Al, Fe, and N, and inward diffusion of O ions. Silicon ions were relatively immobile at $800^{\circ}C$. After oxidation at $900^{\circ}C$ for 10 h in air, a thin $Cr_2O_3$ layer containing dissolved ions of Al, Mg, Si, and Fe formed. Silicon ions became mobile at $900^{\circ}C$. After oxidation at $900^{\circ}C$ for 50 h in air, a thin $SiO_2-rich$ layer formed underneath the thin $Cr_2O_3$ layer. The film displayed good oxidation resistance. The main factor that decreased the oxidation resistance of the film was the outward diffusion and subsequent oxidation of Fe at the sample surface, particularly along the coated sample edge.

• 한국재료학회지
• /
• 제1권4호
• /
• pp.198-205
• /
• 1991

$Fe_2O_3,\;Al_2O_3,\;TiO_2$ 및 Si분말을 사용하여 고상반응법으로 써어미스터 소결체를 합성하였다. 합성된 소결체의 조식특성을 SEM으로 조사하고, 액체항온조에서 $-50~+50^{\circ}C$ 온도영역에서의 측정 결과 $\beta$상수가 972~4005K의 값을 갖는 써어미스터 소결체를 얻었다. 이 소결체는 고공기온측정을 위한 라디오존데용 온도센서로 사용될 수 있다.

• 암석학회지
• /
• 제2권2호
• /
• pp.63-73
• /
• 1993

The assemblage epidote and grandite garnet occurs in low-to medium-grade metabasites and calc schists of various geotectonic settings and in hydrothermally altered calcareous rocks in skarn deposits. The compositions of sixteen epidote-garnet paris have been analysed by means of electron microprobe. Al-Fe partitioning between coexisting grandite garnet and epidote is considered and measured at the grain boundaries on the supposition that the surface equilibrium was maintained in the following exchange reaction: 2$Ca_2Al_3Si_3O_12$(OH)+$Ca_3Fe_2Si_3O_12$=2$Ca_2A_l2FeSi_3O_12$(OH)+$Ca_3Al_2Si_3O_12$ Partition coefficients confirms the differences in thermal conditions between low-grade and medium-grade metamorphic rocks. $K_D$ values ($X_{$CO_2$}$=($Fe^{+3}$/Al)$^{Ep}$/($Fe^{+3}$/Al)$^{Gr}$, where Fe=$Fe^{+3}$) from greenschist facies rocks of the estimated metamorphic temperatures, 330~$390^{\circ}C$, range approximately between 0.02 and 0.17. Epidote-amphibolite facies rocks and calcareous skarns of the estimated temperatures, 400~$550^{\circ}C$, have $K_D$ values between 0.24 and 0.37. $K_D$ values from the rocks of the temperatures, 640~$700^{\circ}C$, range nearly between 0.58 and 0.75. The diagrams in Figs. 2 and 3 can serve as a mineralogic thermometer for relatively shallow rocks, assuming that the pressure dependence of partition coefficients for the iron-exchange reaction in the two minerals can be neglected.

• 한국자기학회지
• /
• 제11권5호
• /
• pp.196-201
• /
• 2001

Si(100)/Ta(50 )/NiFe(60 )/FeMn(250 )/NiFe(70 )/Al$_2$O$_3$/NiFe(150 )/Ta(50 )구조를 가진 자기터널접합의 자기저항비 향상에 관해서 연구하였다. 자성층과 절연층 사이 계면에 CoFe을 삽입하여 5.75%에서 13.7%까지 향상시켰다. 그리고 절연층은 16 의 Al을 순수한 산소 및 산소/아르곤 혼합 분위기에서 프라즈마 산화법으로 형성하였다. 순수한 산소 분위기에서는 최적 산화시간 30초에서 13.7%의 자기저항비를 얻었지만,산소/아르곤의 혼합기체를 사용하면 최적 산화시간 40초에서 15.3%의 자기저항비를 얻었다.

• 한국재료학회지
• /
• 제15권3호
• /
• pp.166-171
• /
• 2005

Fe-6Al-9Si(N) alloy powders were synthesized by hybrid process of chemical nitrification and mechanical milling. The nitriding treatment on Fe-6Al-9Si alloy powders formed $\gamma'-Fe_4N$ phase on the powders surface. The nitriding-treated powders were pulverized by horizontal high-energy ball milling machine. The longer ball milling time tended to reduce the size of alloy powders. In ball milling for 36h, extremely fine powders with about $7\~9wt\%$ nitrogen were obtained. Through X-ray diffraction analysis on the powders, it was found out that the longer milling time caused a disappearance of the crystallinity of $\alpha-Fe$ in the powders. TEM study confirmed that the powders is comprised of a few tens nano-meter sized crystals, including $\alpha-Fe$ phase with partially $\gamma'-Fe_4N$ phase. Hysteresis curves of the synthesized powders measured by VSM revealed lower saturation magnetization and higher coercivity, which seemed to be attributed to nitrogen-impregnation and severe residual stress developed during the high energy milling. Microstructure observation on the powder annealed at 873 K for 1 h showed 10 to 20 nm sized $\alpha-Fe$ crystal. Such a enhanced crystallinity significantly increased the magnetization and decreased the coercivity, which was attributed to not only the crystallinity but also residual stress relaxation.