• Journal of the Korean Chemical Society
• /
• v.17 no.5
• /
• pp.346-352
• /
• 1973

The quantitative separations of a mixture containing equal amounts of each cation such as Mn(Ⅱ), Cr(Ⅲ), V(Ⅴ), Cu(Ⅱ), Ni(Ⅱ), Co(Ⅱ), and Fe(Ⅲ) are carried out by the elution through $35cm{\times}3.14cm^2$ column of cation exchange resin, $Dowex 50w{\times}12$. The eluents are a mixture of 0.6 M sodium chloride and 0.1 M sodium tartrate (pH = 2.00 and 4.50) for Fe(Ⅲ), V(Ⅴ), Cu(Ⅱ), Ni(Ⅱ) and Co(Ⅱ), and a mixture of 3 M sodium chloride and 0.1 M sodium tartrate (pH = 4.50) or a mixture of 0.7 M sodium chloride and 0.5 M sodium oxalate (pH = 4.50 and 5.00) for Mn(Ⅱ) and Cr(Ⅲ). The subsidiary cations in a standard iron mixture such as V(Ⅴ), Cu(Ⅱ), Ni(Ⅱ), Mn(Ⅱ) and Cr(Ⅲ) are separated together from the large amount of Fe(Ⅲ) through $15cm{\times}3.14cm^2$ column of the resin, $Dowex 1{\times}8$, by elution with the eluent of 4.0 M hydrochloric acid. A small amount of Fe(Ⅲ), however, is eluted together with Cu(Ⅱ). V(Ⅴ), Ni(Ⅱ), Mn(Ⅱ) and Cr(Ⅲ) eluted together are separated quantitatively through $10cm{\times}3.14cm^2$ column of the resin,$Dowex 50w{\times}12$. Cu (Ⅱ) and a small amount of Fe(Ⅲ) are separated quantitatively through $10cm{\times}3.14cm^2$ column of the resin, $Dowex 50w{\times}12$, by the elution with a mixture of 0.6 M sodium chloride and 0.1 M sodium tartrate (pH = 2.00 and 4.50) as an eluent. By the conditions obtained in the separations of the standard iron mixture, Fe(Ⅲ) and all of the subsidiary cations in steel are quantitatively separated.

• Journal of the Korean Magnetics Society
• /
• v.5 no.3
• /
• pp.210-215
• /
• 1995

$Glass\Cr_{40\AA}\{[Cr_{10\AA}\NiFe_{50\AA}]}_N$ multilayers (number of layer N = 1, 2, 3, 4, 5, 6, 10) were made by dc magnetron sputtering under magnetic anisotropy of 200 G. Magnetoresistance curve MR(xx), MR(xy) were measured for the parallel and perpendicular current direction to external magnetic field. MR(xx) curves for the number of layer N=1, 5, 10 were almost became about zero percent, however the curves of other numbers appeared the phenomena of "positive magnetoresistance" that the resistance increased to external magnetic field, and the irregular and reversed curves in the vicinity of H=0 Oe.

• Journal of the Korean institute of surface engineering
• /
• v.51 no.6
• /
• pp.354-359
• /
• 2018

NaCl-induced hot corrosion behavior of ASTM T22 (Fe-2.25Cr-1Mo), T91 (Fe-9Cr-1Mo), T92 (Fe-9Cr-1.8W-0.5Mo), 347HFG (Fe-18-Cr-11Ni), and 310H (Fe-25Cr-19Ni) steels was studied after spraying NaCl on the surface. During corrosion at $600-800^{\circ}C$ for 50-100 h, thick, non-adherent, fragile, somewhat porous oxide scales formed. All the alloys corroded fast with large weight gains owing to fast scaling and destruction of protective oxide scales. Corrosion rates increased progressively as the corrosion temperature and time increased. Corrosion resistance increased in the order of T22, T91, T92, 347HFG, and 310H, suggesting that the alloying elements of Cr, Ni, and W beneficially improved the corrosion resistance of steels. Basically, Fe oxidized to $Fe_2O_3$, and Cr oxidized to $Cr_2O_3$, some of which further reacted with FeO to form $FeCr_2O_4$ or with NiO to form $NiCr_2O_4$.

• Resources Recycling
• /
• v.16 no.6
• /
• pp.3-9
• /
• 2007

Although the ferrous material was separated by the magnetic separation before the incineration process, the municipal solid waste incineration bottom ash generated during incinerator in metropolitan area consists of many iron products which account for about $3{\sim}11%$ as well as ceramics and glasses. The formation of $NiFe_2O_4$ and $FeCr_2O_4$ with a $Fe_3O_4-Fe_2O_3$ (similar to pure Fe) on the surface of iron product was found during air-annealing in the incinerator at $1000^{\circ}C$, because Ni and Cr has a chemical attraction about iron is using to coat with Ni and Cr metals for poish or to prevent corrosion. Therefore, Fe-Ni Cr oxide can be formed on durface of the iron product and it can be separated from bottom ash through the magnetic separation. So, in this study, the separation ratio of heavy metals as magnetic separation and mineralogical formation of Fe-ion(heavy metal) in ferrous metals corroded were investigated. As the result, the separation ratio of Ni and Cr based on particle sizes accounted for about $45{\sim}50%$, and Cu and Pb accounted for below 20%. Also, the leaching concentration of Ni and Cr in bottom ash separated by magnetic separation was lower than that in fresh bottom ash.

• Advances in materials Research
• /
• v.6 no.4
• /
• pp.343-348
• /
• 2017

High-pressure gas atomization was employed to prepare the Fe-based $Fe_{50}Cr_{24}Mo_{21}Si_2B_3$ alloy powder. The effect of flow rate of atomizing gas on the median powder diameter was studied. The results show that the powder size decreased with increasing the flow rate of atomizing gas. Fe-based alloy coatings with amorphous phase fraction was then prepared by high velocity oxygen fuel spraying (HVOF) of gas atomized $Fe_{50}Cr_{24}Mo_{21}Si_2B_3$ powder. Microstructural studies show that the coatings present dense layered structure and low porosity of 0.17% in about $200{\mu}m$ thickness. The Fe-based alloy coating exhibits an average hardness of about 1230 HV. Our results show that the HVOF process results in dense and well-bonded coatings, making it attractive for protective coatings applications.

• Analytical Science and Technology
• /
• v.14 no.2
• /
• pp.173-179
• /
• 2001

The study was carried out to analyze the pollutant Fe, Cu, Cr, Zn, Cd for sediments collected from lake in K river basin. Three analytical methods currently used in Korea, Japan, U.S.A, were compared. Pretreatment using microwave digestion showed higher analytical results for Fe, Cu, Cr, Zn, Cd than Korean Official Method(KOM) and American Toxicity Characteristic Leaching Procedure(TCLP) Method. Also, analytical results using microwave digestion, TCLP and KOM were as follows: 38.1-48.0 mgFe/kg, 10.2-15.9 mgFe/kg AND 3.5-12.6 mgFe/kg, 37.0-50.1 mgCu/kg, 0.06-0.24 mgCu/kg and 0.01-0.03 mgCu/kg, 137.0-152.0 mgZn/kg, 0.67-0.82 mgZn/kg and 0.3-0.5 mgZn/kg, respectively. From this result, a new analytical method for the determination of heavy metal in sediment should be developed for the accurate estimation of pollution degree in sediment.

• Journal of Powder Materials
• /
• v.12 no.1
• /
• pp.43-50
• /
• 2005

Mechanical alloying using high-energy ball mill and subsequent spark plasma sintering (SPS) process was applied to Al-Fe-Cr and Al-Fe-Mo powder mixture to investigate effects of Cr and Mo addition on thermal stability of Al-Fe, and thereby to enhance its thermal stability up to $500^{\circC}$. Various analytical techniques including micro-Vickers hardness test, SEM, TEM, X-ray diffractometry and corrosion test were carried out. It was found that addition of Cr and Mo to Al-Fe system played a role of grain growth inhibitor of matrix Al and some precipitates such as $Al_3Fe$ during SPS and subsequent heat treatment. The inhibition of grain growth resulted in increased Vickers hardness and thermal stability up to $500^{\circC}$ comparing to those of Al-Fe alloy system.

• Korean Journal of Materials Research
• /
• v.10 no.2
• /
• pp.144-147
• /
• 2000

10%C-5%Mo-5%W-10%Cr 및 10%C-5%Mo-5%W-10%V 백주철의 응고거동을 열분석을 통하여 연구하였다. 15Kg 용량의 고주파 유도옹해로에 선철, 고철, Fe-Mo, Fe-W, Fe-Cr, Fe-V 등을 장입시켜 용해시킨 후 슬래그를 제거시키고 $1550^{\circ}C$에서 Y블럭의 펩 주형에 주입하였다. 응고거동을 조사하기 위하여 50g을 Y블럭에서 채취한 뒤 알루미나 도가니에 넣어 재용해시킨 후 1$0^{\circ}C$/min의 냉각속도로 냉각시키면서 여섯 종류의 다른 온도에서 도중에 급냉시켜 응고조직을 광학현미경으로 관찰하였다. 10%C-5%Mo-5%W-10%Cr 백주철의 경우 초정 오스테나이트, 오스테나이트와 M(sub)7C(sob)3의 공정, 오스테나이트와 M(sub)6C의 공정으로, 10%C-5%Mo-5%W-10%V 백주철의 경우 초정 MC, 오스테나이트와 MC의 공정, 오스테나이트와 M(sub)2C의 공정으로 각각 순차적으로 정출하였다. 정출하였다.

• Journal of Powder Materials
• /
• v.24 no.2
• /
• pp.133-140
• /
• 2017

This study investigates the oxidation properties of Fe-14Cr ferritic oxide-dispersion-strengthened (ODS) steel at various high temperatures (900, 1000, and $1100^{\circ}C$ for 24 h). The initial microstructure shows that no clear structural change occurs even under high-temperature heat treatment, and the average measured grain size is 0.4 and $1.1{\mu}m$ for the as-fabricated and heat-treated specimens, respectively. Y-Ti-O nanoclusters 10-50 nm in size are observed. High-temperature oxidation results show that the weight increases by 0.27 and $0.29mg/cm^2$ for the as-fabricated and heat-treated ($900^{\circ}C$) specimens, and by 0.47 and $0.50mg/cm^2$ for the as-fabricated and heat-treated ($1000^{\circ}C$) specimens, respectively. Further, after 24 h oxidation tests, the weight increases by 56.50 and $100.60mg/cm^2$ for the as-fabricated and heat-treated ($1100^{\circ}C$) specimens, respectively; the latter increase is approximately 100 times higher than that at $1000^{\circ}C$. Observation of the surface after the oxidation test shows that $Cr_2O_3$ is the main oxide on a specimen tested at $1000^{\circ}C$, whereas $Fe_2O_3$ and $Fe_3O_4$ phases also form on a specimen tested at $1100^{\circ}C$, where the weight increases rapidly. The high-temperature oxidation behavior of Fe-14Cr ODS steel is confirmed to be dominated by changes in the $Cr_2O_3$ layer and generation of Fe-based oxides through evaporation.

• Journal of Magnetics
• /
• v.16 no.2
• /
• pp.173-176
• /
• 2011

Fe-Cr alloys with different Cr contents were prepared by an arc melting technique. The alloys were isochronally aged in the range from $400^{\circ}C$ to $900^{\circ}C$ with $50^{\circ}C$ steps with a holding time of 100 hours. The ageing produced embrittlement in the alloys due to either the formation of a Cr-rich ${\alpha}'$ phase or a $\sigma$ phase at high temperatures. Magnetic Hysteresis Loop (MHL) and Micro-Vickers hardness were measured at each step to correlate the magnetic and mechanical properties. Coercivity and hardness of the alloys were increased and remanence decreased up to 500-$550^{\circ}C$ due to formation of a Cr-rich ${\alpha}'$ phase. Beyond 500-$550^{\circ}C$ range, the coercivity and hardness decreased and remanence increased due to the coarsening or dissolution of the Cr-rich ${\alpha}'$ phase. In the Fe-48% Cr alloy, formation of the $\sigma$ phase at $700^{\circ}C$ reduced the maximum induction of the alloy significantly.