The photodegradation efficiency of formic acid on $TiO_2$ photocatalytic membranes was investigated. A new titania membrane reactors for purification of water combining microfiltration with photocatalytic degradation of organic compounds were developed. Titania membrane tubes(average pore size of $0.2\mu m$) were prepared by the slip casting, and porous thin films of $TiO_2$ were formed on the tube surface by the sol-gel process to increase the surface area, and consequently to increase photodegradation efficiency of organic compounds. The UV light with the wavelength of 365 nm was used as a light source for photocatalytic reactions. The photodegradation efficiency of the organic compounds was strongly dependent on the flux of the solution, the microstructure of the membrane (sol pH), and the amount of $O_2$ supplied. The effects of the primary oxidant such as $H_2O_2$ and dopants such as $Nb_2O_5$ on the photodegradation efficiency were also investigated. The results showed that more than 80% of formic acid could be degraded using membrane coated with a $TiO_2$ sol of pH 1.45. The photodegradation efficiency could be improved by about 20% when adding $H_2O_2$ in feed solution or doping $TiO_2$ membranes with $Fe_2O_3$.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.18 no.1
• /
• pp.50-55
• /
• 2008

AI-doped ZnO(AZO) thin films have been fabricated on glass substrate by sol-gel method, and the effect of Al precursors and post-annealing temperature on the characteristics of AZO thin films was investigated. The sol was prepared with zinc acetate, EtOH, MEA and Al precursors. In order to dope Al in ZnO, two types of aluminum nitrate and aluminum chloride were used as Al precursor. Zinc concentration was 0.5 mol/l and the content of Al precursor was 1 at% of Zn in the sol. The sol was spin-coated on glass substrate, and the coated films were annealed at 550ue for 2 hand were post-annealed at temperature ranges of $300{\sim}500^{\circ}C$ for 2 h in reducing atmosphere ($N_2/H_2$= 9/1). Structural, electrical and optical propertis of the fabricated AZO thin films were analyzed by XRD, FE-SEM, AFM, hall effect measurement system and UV-visible spectroscopy. Optical and electrical properties of AZO thin films prepared with aluminum nitrate as Al precursor were better than those of films prepared with aluminum chloride. The electrical resistivity and the optical transmittance of films decreased with increasing post-annealing temperatures. The minimum electrical resistivity of $2{\times}10^{-3}$ and the maximum optical transmittance of 91% were obtained for the AZO thin films post-annealed at $550^{\circ}C\;and\;300^{\circ}C$, respectively.

• Journal of the Korean Electrochemical Society
• /
• v.11 no.3
• /
• pp.197-210
• /
• 2008

The cathode materials for lithium ion battery have been developed in accordance with the battery performance. $LiCoO_2$ initially adapted at lithium ion battery is going to be useful even at the charging voltage of 4.3 V by surface treatment or doping which drastically improved the performance of $LiCoO_2$. On the other hand, the complicate and multiple functions of recent electronic equipments required higher operational voltage and higher capacity than ever, which is going to be driving force for developing new cathode materials. Some of them are $LiNi_{1-x}{M_xO_2}$, $Li[Ni_{x}Mn_{y}Co_{z}]O_{2}$, $Li[{Ni}_{1/2}{Mn}_{1/2}]O_{2}$. Other new type of cathode materials having high safety is also developed to apply for HEV (hybrid electrical vehicle) and power tool applications. ${LiMn}_{2}{O}_{4}$ and $LiFePO_4$ are famous for highly stable material, which are expected to give contribution to make safer battery. In near future, the various materials having both capacity and safety will be developed by new technology, such as solid solution composite.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.15 no.11
• /
• pp.6952-6957
• /
• 2014

In photocatalysis, the addition of metal matter to $TiO_2$ can alter the surface properties. As such, the metal can increase the rate of the photodegradation reaction. In this study, a range of modified $TiO_2$ photocatalysts were prepared and tested to improve the activity of photodegradation at a batch-typed photoreactor. To obtain a good sol solution of the $TiO_2$ photocatalyst, several types of dispersion agents and stabilizers were investigated. The photocatalyst solutions were modified with isoproply alcohol as the dispersion agent and sodium silicate as the stabilizer. The effects of various metallic elements on enhancing the photocatalytic activity of $TiO_2$ on the degradation of toluene were examined. Palladium-added $TiO_2$ was found to be the best, whereas copper or tungsten-added also showed good results. In the case of palladium addition, the increase in removal efficiency was 25%. On the other hand, Fe-added $TiO_2$ showed a notable decrease in photocatalytic degradation. Additional doping of copper or tungsten on the $Pd/TiO_2$ had no positive effect on the photodegradation activity.

• The Korean Journal of Ceramics
• /
• v.4 no.3
• /
• pp.249-253
• /
• 1998

The influence of PbO additive on dielectric properties and sintering behavior of $(Pb_{0.46}Ca_{0.55})$ {$(Fe__1/2}Nb_{1/2}){0.9}Sn_{{0.1}$}$O_3$ ceramics has been investigated. The incorporation of a limited excess PbO ($\leq$2.0 wt. %) in the starting materials is quite beneficial for densification in the temperature range of 1150~$1175^{\circ}C$ in air. At a small doping level (0.8 wt. %) the ceramics prepared from powders calcined at $900^{\circ}C$ showed the best dielectric properties. The dielectric constants ($\varepsilon_r$) and Q.f were found to be 85.8~85.6 and 8530~8600 GHz, respectively. The temperature coefficient of resonant frequency ($\tau_f$) varied in the range of -2~4 $ppm/^{\circ}C$. Examination of the microstructure as well as analysis of the second phases in these materials revealed the presence of the pyrochlore-type phase which is detrimental to the dielectrics.

• Applied Chemistry for Engineering
• /
• v.24 no.6
• /
• pp.611-615
• /
• 2013

Vanadium oxide ($VO_2$) and tungsten-doped vanadium oxide (W-$VO_2$) powder, well known as thermochromic materials, were prepared from vanadium pentoxide ($V_2O_5$) and oxalic acid dihydrate by hydrothermal and calcination process. The crystal structure and thermochromic property of samples were analyzed using FE-SEM, XRD, XPS, DSC, and UV-Vis-NIR spectroscopy. With increasing the doping amount of W, the phase transition temperature of W-$VO_2$ sample decreased from $70^{\circ}C$ to $42^{\circ}C$. When heating W-$VO_2$ sample above the phase transition temperature, the UV-Vis-NIR spectrum was not changed in the visible range and shifted towards a low transparency in the full name (NIR) region.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.18 no.6
• /
• pp.253-257
• /
• 2008

To enhance the luminescence properties, the red phosphor composed of $(Y,\;Zn)_2O_3$:$Eu^{3+}$ as doping concentration of Zn ion is synthesized at $1200^{\circ}C$ for 6 hrs in air atmosphere by conventional solid reaction method. As a result of the red phosphor $(Y,\;Zn)_2O_3$:$Eu^{3+}$ is measured X-ray diffraction (XRD), The main peak is nearly corresponded to the same as JCPDS card (No. 41-1105). When the doping concentration of Zn ion is more than 5 mol%, However, the ZnO peak is showed by XRD analysis. Therefore, when the doping concentration of Zn ion is less than 5 mol%, the Zn ion is well mixed in $Y_2O_3$ structure without the impurity phases. The photoluminescence (PL) properties is shown as this phosphor is excited in 254 nm region and the highest emission spectra of $(Y,\;Zn)_2O_3$:$Eu^{3+}$ has shown in 612 nm region because of a typical energy transition ($^5D_0{\rightarrow}^7F_2$) of $Eu^{3+}$ ion. As the doping concentration of Zn ion is more than 10 mol%, the emission peak is suddenly decreased. when the highest emission peak as doping concentration of Zn ion is shown, the composition of this phosphor is $(Y_{0.95},\;Zn_{0.05})_2O_3$:$Eu^{3+}_{0.075}$ and the particle size analyzed by FE-SEM is confirmed from 0.4 to $3{\mu}m$.

• Bulletin of the Korean Chemical Society
• /
• v.34 no.1
• /
• pp.89-94
• /
• 2013

Layered $Li_{1+x}(Mn_{0.4}Ni_{0.4}Fe_{0.2})_{1-x}O_2$ (0 < x < 0.3) solid solutions were synthesized using solgel method with adipic acid as chelating agent. Structural and electrochemical properties of the prepared powders were examined by means of X-ray diffraction, Scanning electron microscopy and galvanostatic charge/discharge cycling. All powders had a phase-pure layered structure with $R\bar{3}m$ space group. The morphological studies confirmed that the size of the particles increased at higher x content. The charge-discharge profiles of the solid solution against lithium using 1 M $LiPF_6$ in EC/DMC as electrolyte revealed that the discharge capacity increases with increasing lithium content at the 3a sites. Among the cells, $Li_{1.2}(Mn_{0.32}Ni_{0.32}Fe_{0.16})O_2$ (x = 0.2)/$Li^+$ exhibits a good electrochemical property with maximum initial capacity of 160 $mAhg^{-1}$ between 2-4.5 V at 0.1 $mAcm^{-2}$ current density and the capacity retention after 25 cycles was 92%. Whereas, the cell fabricated with x = 0.3 sample showed continuous capacity fading due to the formation of spinel like structure during the subsequent cycling. The preparation of solid solutions based on $LiNiO_2-LiFeO_2-Li_2MnO_3$ has improved the properties of its end members.

• Journal of the Korean Magnetics Society
• /
• v.18 no.4
• /
• pp.136-141
• /
• 2008

In this study, the magnetic(static and high-frequency) and microwave absorbing properties have been investigated in Ru-Co substituted M-hexaferrites($BaFe_{12-2x}Ru_xCo_xO_{19}$). The powders and sintered specimens were prepared by conventional ceramic processing technique. With the calcined powders, the composite specimens were prepared using the silicone rubber as a matrix material. The substitution ratio of Ru-Co to obtain in-plane magnetic anisotropy, thus having the minimum coercivity, is much smaller (about x=0.3) than the previously reported Ti-Co substituted specimen. Owing to this low substitution, the specimen has a large value of saturation magnetization($M_s$=65 emu/g). Ferromagnetic resonance behavior and microwave absorbing frequency band is strongly influnced by the coercvity which can be controlled by Ru-Co substitution ratio. It is found that the M-hexaferrites with planar magnetic anisotropy by doping Ru-Co in both sintered and composite form have superior microwave absorbing properties in GHz frequency range.

• Applied Chemistry for Engineering
• /
• v.19 no.5
• /
• pp.477-483
• /
• 2008

$La_{0.7}Sr_{0.3}Co_{0.2}Fe_{0.8}O_{3-{\delta}$ oxide was synthesized by a citrate method and a typical dense membrane of perovskite oxide has been prepared using as-prepared powder by pressing and sintering at $1300^{\circ}C$. Precursor of $La_{0.7}Sr_{0.3}Co_{0.2}Fe_{0.8}O_{3-{\delta}$ prepared by citrate method was investigated by TGA and XRD. Metal-citrate complex in precursor was decomposed into perovskite oxide in the temperature range of $260{\sim}410^{\circ}C$ but XRD results showed $SrCO_3$ existed as impurity at less than $900^{\circ}C$. Electrical conductivity of membrane increased with increasing temperature but then decreased over $700^{\circ}C$ in air atmosphere ($Po_2=0.2atm$) and $600^{\circ}C$ in He atmosphere ($Po_2=0.01atm$) respectively due to oxygen loss from the crystal lattice. The oxygen permeation flux increased with increasing temperature and maximum oxygen permeation flux of $La_{0.7}Sr_{0.3}Co_{0.2}Fe_{0.8}O_{3-{\delta}$ membrane with 1.6 mm thickness was about $0.31cm^3/cm^2{\cdot}min$ at $950^{\circ}C$. The activation energy for oxygen permeation was 88.4 kJ/mol in the temperature range of $750{\sim}950^{\circ}C$. Perovskite structure of membrane was not changed after permeation test of 40 h and the membrane was stable without secondary phase change with 0.3 mol Sr addition.