• Journal of Magnetics
• /
• v.16 no.3
• /
• pp.318-321
• /
• 2011

A new Fe-based amorphous compound powder was prepared from Fe-Si-B amorphous powder by crushing amorphous ribbons as the first magnetic component and Fe-Cr-Mo metallic glassy powder by water atomization as the second magnetic component. Subsequently by adding organic and inorganic binders to the compound powder and cold pressing, the new Fe-based amorphous compound powder cores were fabricated. This new Fe-based amorphous compound powder cores combine the superior DC-Bias properties and the excellent core loss. The core loss of 500 kW/$m^3$ at $B_m$ = 0.1T and f = 100 kHz was obtained When the mass ratio of FeSiB/FeCrMo equals 3:2, and meanwhile the DC-bias properties of the new Fe-based amorphous compound powder cores just decreased by 10% compared with that of the FeSiB powder cores. In addition, with the increasing of the content of the FeCrMo metallic glassy powder, the core loss tends to decrease.

• Advances in materials Research
• /
• v.6 no.4
• /
• pp.343-348
• /
• 2017

High-pressure gas atomization was employed to prepare the Fe-based $Fe_{50}Cr_{24}Mo_{21}Si_2B_3$ alloy powder. The effect of flow rate of atomizing gas on the median powder diameter was studied. The results show that the powder size decreased with increasing the flow rate of atomizing gas. Fe-based alloy coatings with amorphous phase fraction was then prepared by high velocity oxygen fuel spraying (HVOF) of gas atomized $Fe_{50}Cr_{24}Mo_{21}Si_2B_3$ powder. Microstructural studies show that the coatings present dense layered structure and low porosity of 0.17% in about $200{\mu}m$ thickness. The Fe-based alloy coating exhibits an average hardness of about 1230 HV. Our results show that the HVOF process results in dense and well-bonded coatings, making it attractive for protective coatings applications.

• Journal of Powder Materials
• /
• v.14 no.1 s.60
• /
• pp.63-69
• /
• 2007

The present study was focused on the synthesis of a zirconium-based alloyed nanopowder by the plasma arc discharge process. The chemical composition, phase structure, particle size and hydrogen sorption property of the synthesized powders under various synthesis conditions were analyzed using XRF, XRD, SEM, XPS and the ASTM-F798 method. The chemical composition of the synthesized Zr-V-Fe-based powders approached that of the raw material with an increasing hydrogen fraction in the powder synthesis atmosphere. The synthesized $Zr_{55}V_{29}Fe_{16}$ powder consist of a mixed phase structure of the $Zr,\;ZrH_2,\;FeV\;and\;Zr(V_{1-x}Fe_{x})_2$ phases. This powder has an average particle size of about 20 nm. The synthesized $Zr_{55}V_{29}Fe_{16}$ nanopowder showed getter characteristics, even though it had a lower hydrogen sorption speed than the $Zr_{57}\;V{36}\;Fe_7$ getter powder. However, the synthesized Zr nanopowder with an average particle size of 20 nm showed higher hydrogen sorption speed than the $Zr_{57}\;V{36}\;Fe_7$ getter powder.

• Journal of Powder Materials
• /
• v.19 no.2
• /
• pp.122-126
• /
• 2012

The Fe-based self-fluxing alloy powders and TiC particles were ball-milled and subsequently compacted and sintered at various temperatures, resulting in the TiC particle-reinforced Fe self-fluxing alloy hybrid composite, and the microstructure and micro-hardness were investigated. The initial Fe-based self-fluxing alloy powders and TiC particles showed the spherical shape with a mean size of approximately 80 ${\mu}m$ and the irregular shape of less than 5 ${\mu}m$, respectively. After ball-milling at 800 rpm for 5 h, the powder mixture of Fe-based self-fluxing alloy powders and TiC particles formed into the agglomerated powders with the size of approximately 10 ${\mu}m$ that was composed of the nanosized TiC particles and nano-sized alloy particles. The TiC particle-reinforced Fe-based self-fluxing alloy hybrid composite sintered at 1173 K revealed a much denser microstructure and higher micro-hardness than that sintered at 1073 K and 1273 K.

• Journal of Powder Materials
• /
• v.18 no.2
• /
• pp.112-121
• /
• 2011

This study investigated the effect of solvent on the fabrication of Ni-free Fe-based alloy nano powders by employing the PWE (pulsed wire evaporation) in liquid and compared the alloy particles fabricated by three different methods (PWE in liquid, PWE in Ar, plasma arc discharge), for high temperature oxidation-resistant metallic porous body for high temperature soot filter system. Three different solvents (ethanol, acetone, distilled water) of liquid were adapted in PWE in liquid process, while X-ray diffraction (XRD), field emission scanning microscope (FE-SEM), and transmission electron microscope (TEM) were used to investigate the characteristics of the Fe-Cr-Al nano powders. The alloy powder synthesized by PWE in ethanol has good particle size and no surface oxidation compared to that of distilled water. Since the Fe-based alloy powders, which were fabricated by PWE in Ar and PAD process, showed surface oxidation by TEM analysis, the PWE in ethanol is the best way to fabricate Fe-based alloy nano powder.

• Journal of Powder Materials
• /
• v.27 no.4
• /
• pp.300-304
• /
• 2020

In this paper, a durability study is presented to enhance the mechanical properties of an Fe-Si-Al powder-based magnetic core, through the addition of graphite. The compressive properties of Fe-Si-Al-graphite powder mixtures are explored using discrete element method (DEM), and a powder compaction experiment is performed under identical conditions to verify the reliability of the DEM analysis. Important parameters for powder compaction of Fe-Si-Al-graphite powder mixtures are identified. The compressibility of the powders is observed to increase as the amount of graphite mixture increases and as the size of the graphite powders decreases. In addition, the compaction properties of the Fe-Si-Al-graphite powder mixtures are further explored by analyzing the transmissibility of stress between the top and bottom punches as well as the distribution of the compressive force. The application of graphite powders is confirmed to result in improved stress transmission and compressive force distribution, by 24% and 51%, respectively.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2000.04a
• /
• pp.32-32
• /
• 2000

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.118-119
• /
• 2006

The development of Fe-based metal matrix composites (MMCs) with high content of hard phase has been approached by combining the use of advanced powder metallurgy techniques like high-energy milling (HEM), cold isostatic pressing (CIP) and vacuum sinterings. A 30% vol. of NbC particles was mixed with Fe powder by HEM in a planetary mill during 10h, characteristing the powder by the observation of morphology and microstructure by scanning electron microscopy (SEM). After of sintering process the variation of density, hardness,carbon content and the microstructural changes observed, permits to find the optimal conditions of processing. Afterwards, a heat treatment study was performed to study the hardenability of the composite.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2009.05a
• /
• pp.282-285
• /
• 2009

Selective laser sintering (SLS) is a fast growing process of rapid production fur metallic based parts. To restore damaged mold surface using SLS, single layer experiments of $20{\mu}m$ Fe-Cr powder was performed under various heat input. Process window of $20{\mu}m$ Fe-Cr powder provided feasible process parameters for the smooth regular surface. To estimate coherence between melted powder and basematal, tendency of hardness distribution has been observed. Hardness of melted zone and remelted zone was diversified from 5GPa to 6.5GPa. It is over 2 times compared of hardness of basemetal. Average surface roughness of each direction on surface of melted powder was measured. Experimental results show that the mold restoring process using SLS can be successfully applied in the mold repair industry.

• Journal of Powder Materials
• /
• v.9 no.3
• /
• pp.161-166
• /
• 2002

Processing and properties of $Al_2O_3$ composites with Ni-Fe content of 10 and 15 wt% were investigated. Homogeneous powder mixtures of $Al_2O_3$/Ni-Fe alloy were prepared by the solution-chemistry route using $Al_2O_3$, $Ni(NO_3)_2{\cdot}6H_2O$ and $Fe(NO_3)_3{\cdot}9H_2O$ powders. Microstructural observation of composite powder revealed that Ni-Fe alloy particles with a size of 20nm were homogeneously dispersed on $Al_2O_3$ powder surfaces. Hot-pressed composites showed enhanced fracture toughness and magnetic response. The properties are discussed based on the observed microstructural characteristics.