• 한국환경과학회:학술대회논문집
• /
• 한국환경과학회 2001년도 정기총회 및 봄 학술발표회 초록집
• /
• pp.236-237
• /
• 2001

In this study, experiments were carried out to measure the variations in the corrosion potential and current density of polarization curves with amorphous $Fe_{70}Cr_5Si_{10}B_{15}$ and $Co_{70}Cr_5Si_{10}B_{15}$ alloy ribbon. The results were particularly examined to identify the influences of corrosion potential including various conditions such as hydrochloric acid, temperature, salt, pH, and oxygen. The optimum conditions were established with variations including temperature, salt, pH, oxygen, corrosion rate, and resistance of corrosion potential. The mass tranfer coefficient(${\alpha}$) value was determined with the Tafel's slope for the anodic dissolution based on the polarization effect with optimum conditions. The second anodic current density peak and maximum passive current density were designated as the critical corrosion sensitivity($I_{r}/I_{f}$).

• 한국재료학회지
• /
• 제5권1호
• /
• pp.112-122
• /
• 1995

Metal hydride alloys of TiFe based system have been produced by mechanical alloying(MA) method and their electrochemical characteristics have been evaluated for application for Ni/MH battery electrode. These alloys became amorphous after 36hrs ball milling and easily activated electrochemically. All MA amorphous alloys reached at the first charge/discharge cycle the maximum capacity which was 2-3 times higher than the crystalline state. But their cyclic lives were much inferior to the crystalline state. Alloying elements such as Ni, Co, Cr, Mo substituting Fe greatly improved the capacity and 180 mAh/g capacity was obtained in an alloy of TiFe_{0.6}Ni_{0.1}Co_{0.1}Cr_{0.1}Mo_{0.1}$.

• 한국재료학회지
• /
• 제19권6호
• /
• pp.319-324
• /
• 2009

The deposition behavior and structural and magnetic properties of electroless Co-B and Co-Fe-B deposits, as well as the amorphous ribbon substrates, were investigated. These Co-based alloy deposits exhibited characteristic polycrystalline structures and surface morphology and magnetic properties that were dependent on the type of amorphous substrates. The catalytic activity sequence of the amorphous ribbon electrodes for anodic oxidation of DMAB was estimated from the current density-potential curve in the anodic partial electrolytic bath that did not contain the metal ions. Both the deposition rate and potential in the initial region were obtained in order of the catalytic activity, depending on the alloy compositions of the substrates. The deposition rate linearly varied against the deposition time. The initial deposition potential may have also determined the structural and magnetic properties of the deposit based on the thickness of ${\mu}m$ order. Furthermore, a basic study of the electroless deposition processes on an amorphous ribbon substrate has been carried out in connection with the structural and magnetic properties of the deposits.

• Journal of Electrochemical Science and Technology
• /
• 제10권1호
• /
• pp.82-88
• /
• 2019

Here, we report on nanocrystalline Si-Al-M (M = Fe, Cu, Ni, Zr) alloys for use as an anode for lithium-ion batteries, which were fabricated via a melt-spinning method. Based on the XRD and TEM analyses, it was found that the Si-Al-M alloys consist of nanocrystalline Si grains surrounded by an amorphous matrix phase. Among the Si-Al-M alloys with different metal composition, Ni-incorporated Si-Al-M alloy electrode retained the high discharge capacity of 2492 mAh/g and exhibited improved cyclability. The superior $Li^+$ storage performance of Si-Al-M alloy with Ni component is mainly responsible for the incorporated Ni, which induces the formation of ductile and conductive inactive matrix with crystalline Al phase, in addition to the grain size reduction of active Si phase.

• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 2008년도 Asian Magnetics Conference
• /
• pp.161.1-161.1
• /
• 2008

• Bulletin of the Korean Chemical Society
• /
• 제17권7호
• /
• pp.621-625
• /
• 1996

A variety of metal oxides were coated by sol-gel process from their metal alkoxides on the ribbons of Co-based and Fe-based amorphous alloys, and the effects of surface oxide coating on the magnetic properties of the alloy are investigated. The core loss is found to be reduced significantly by the oxide coating, the loss reduction becoming more prominent at higher frequencies. The shape of the hystersis loop is also dependent upon the kind of the coated metal oxide. The coatings of MgO, SiO2, MgO·SiO2 and MgO·Al2O3 induce tensile stress into the Fe-based ribbon whereas those of BaO, Al2O3, CaO·Al2O3, SrO·Al2O3 and BaO·Al2O3 induce compressive stress. These results may be explained by the modification of domain structures via magnetoelastic interactions with the shrinkage stress induced by the sol-gel coating.

• 한국자기학회지
• /
• 제25권3호
• /
• pp.67-73
• /
• 2015

본 연구는 철기(Fe based) $Fe_{73.5}Si_{13.5}B_9Nb_3Cu_1$ 나노결정 합금의 분말코어(powder core)의 연자기적 특성 향상을 위한 기초연구로서, 절연 코팅제의 첨가량 및 분말입도에 따른 투자율, 코어손실 및 DC 바이어스 특성을 주로 조사하였다. 우선 합금조성을 PFC 장치를 이용하여 비정질 합금리본을 제조한 후, 열처리, 미분쇄 및 분급하여 얻어진 합금분말에 절연 코팅제(PEI)의 첨가량을 0.5, 1.0, 2.0, 2.5 wt%로 변화시켜 $16ton/cm^2$으로 압축성형 및 결정화 열처리하여 제조한 토로이달 나노결정 분말코어($OD12.7mm{\times}ID7.62mm{\times}H4.75mm$)는 절연 코팅제 함량이 증가할수록 투자율은 감소하였지만, 코어손실 및 DC 바이어스 특성은 향상됨을 확인하였다. 이러한 이유는 합금분말 절연 코팅제 첨가량이 증가할수록 비정질 합금분말 입자가 적어져 분말코어의 성형밀도가 낮아지기 때문으로 추정되었으며, 절연 코팅제의 함량은 1 wt%가 가장 적합한 것으로 판단되었다. 또한 절연 코팅제 함량을 1 wt%로 고정하고, 합금분말의 입도에 따라 제조한 분말코어의 경우, 실효투자율 및 코어손실은 입도가 클수록 우수하였지만, DC 바이어스 특성은 인가자장이 증가함에 따라 더욱 나빠짐을 확인하였다. 그 이유는 합금분말 표면의 코팅층 두께 차이에 의한 절연효과, 잔류기공 혹은 분말코어의 성형밀도 차이 등에 기인하는 것으로 추정되었다.

• 한국분말재료학회지
• /
• 제23권5호
• /
• pp.391-396
• /
• 2016

In this study, ultra-fine soft-magnetic micro-powders are prepared by high-pressure gas atomization of an Fe-based alloy, Fe-Hf-B-Nb-P-C. Spherical powders are successfully obtained by disintegration of the alloy melts under high-pressure He or $N_2$ gas. The mean particle diameter of the obtained powders is $25.7{\mu}m$ and $42.1{\mu}m$ for He and $N_2$ gas, respectively. Their crystallographic structure is confirmed to be amorphous throughout the interior when the particle diameter is less than $45{\mu}m$. The prepared powders show excellent soft magnetic properties with a saturation magnetization of 164.5 emu/g and a coercivity of 9.0 Oe. Finally, a toroidal core is fabricated for measuring the magnetic permeability, and a ${\mu}_r$ of up to 78.5 is obtained. It is strongly believed that soft magnetic powders prepared by gas atomization will be beneficial in the fabrication of high-performance devices, including inductors and motors.

• Journal of Magnetics
• /
• 제1권1호
• /
• pp.24-30
• /
• 1996

The relationship between effective permeability and the remanence ratio of an Fe-based amorphous alloy (Metglas 2605S3A) is investigated over a wide frequency range, in an effort to understand magnetization behavior of the alloy. In the frequency range from 1 to 200 kHz, the permeability is maximum at the remanence ratio of 0.4-0.5 and, at frequencies over 500 kHz, the correlation with negative coefficients emerges indicating that the permeability decreases with the remanent ratio, except for the ribbon coated with an insulating layer of MgO which exhibits both high values of the effective permeability and remanence ratio. It is considered from the correlation results that the boundary at which the dominant magnetization mechanism changes from domain wall motion to spin rotation is near 500 kHz. The core loss is also investigated as a function of annealing time when the samples are annealed at a fixed temperature of $435^{\circ}C$. The core loss in most cases decreases with the annealing time, the degree of the loss may consist of the hysteresis loss and anomalous eddy current loss. The two loss components are considered to be of similar magnitudes at low frequencies while, at high frequencies, the dominant contribution to the total loss is the anomalous loss.

• 한국자기학회지
• /
• 제12권1호
• /
• pp.30-33
• /
• 2002

초미세결정렵 Nd-Fe-B-Mo-Cu합금에서 Co 치환이 미세조직과 자기특성에 미치는 영향을 조사 하였다. 급속응고법으로 제조된 비정질 Nd-(Fe, Co)-B-Mo-Cu합금은 결정화에 의하여 $\alpha$-Fe기 초미세결정립 Nd-(Fe, Co)-B-Mo-Cu합금이 제조되었다. Co로의 Fe치환은 결정립 미세화에 기여하며, 이로 인하여 경자기특성이 개선되었다. 최적열처리된 초미세결정립 N $d_4$(F $e_{0.85}$ $Co_{0.15}$)$_{82}$ $B_{10}$M $o_3$Cul합금의 잔류자화, Curie온도는 Co가 치환되지 않은 합금에 비하여 개선된 우수한 특성을 나타내었다. 64$0^{\circ}C$, 10분 열처리된 초미세결정립 N $d_4$(F $e_{0.85}$ $Co_{0.15}$)$_{82}$ $B_{10}$M $o_3$Cu 합금의 평균결정립 크기는 약 15 nm이며, 이때 보자력, 잔류자화 및 최대에너지적은 각각 239kA/m, 1.4 T 및 103.5 kJ/ $m^3$이었다.