• Journal of the Korean Chemical Society
• /
• v.56 no.4
• /
• pp.448-458
• /
• 2012

In order to develop alloy resistance in aggressive sulphat ion, the corrosion behavior of metallic glasses $Ni_{92{\cdot}3}Si_{4.5}B_{32}$, $Ni_{82,3}Cr_7Fe_3Si_{4.5}B_{3.2}$ and $Ni_{75.5}Cr_{13}Fe_{4.2}Si_{4.5}B_{2.8}$ (at %) at different concentrations of $H_2SO_4$ solutions was examined by electrochemical methods and Scanning Electron Microscope (SEM) and X-ray Photoelectron Microscopy (XPS) analyses. The corrosion kinetics and passivation behavior was studied. A direct proportion was observed between the corrosion rate and acid concentration in the case of $Ni_{92{\cdot}3}Si_{4.5}B_{32}$ and $Ni_{75.5}Cr_{13}Fe_{4.2}Si_{4.5}B_{2.8}$ alloys. Critical concentration was observed in the case of $Ni_{82,3}Cr_7Fe_3Si_{4.5}B_{3.2}$ alloy. The influence of the alloying element is reflected in the increasing resistance of the protective film. XPS analysis confirms that the protection film on the $Ni_{92{\cdot}3}Si_{4.5}B_{32}$ alloy was NiS which is less protective than that formed on Cr containing alloys. The corrosion rate of $Ni_{82,3}Cr_7Fe_3Si_{4.5}B_{3.2}$ and $Ni_{75.5}Cr_{13}Fe_{4.2}Si_{4.5}B_{2.8}$. alloys containing 7% and 13% Cr are $7.90-26.1{\times}10^{-3}$ mm/y which is lower about 43-54 times of the alloy $Ni_{92{\cdot}3}Si_{4.5}B_{32}$ (free of Cr). The high resistance of $Ni_{75.5}Cr_{13}Fe_{4.2}Si_{4.5}B_{2.8}$ alloy at the very aggressive media may due to thicker passive film of $Cr_2O_3$ which hydrated to hydrated chromium oxyhydroxide.

• Journal of Powder Materials
• /
• v.22 no.2
• /
• pp.100-104
• /
• 2015

The porous metals are known as relatively excellent characteristic such as large surface area, light, lower heat capacity, high toughness and permeability. The Fe-Cr-Al alloys have high corrosion resistance, heat resistance and chemical stability for high temperature applications. And then many researches are developed the Fe-Cr-Al porous metals for exhaust gas filter, hydrogen reformer catalyst support and chemical filter. In this study, the Fe-Cr-Al porous metals are developed with Fe-22Cr-6Al(wt) powder using powder compaction method. The mean size of Fe-22Cr-6Al(wt) powders is about $42.69{\mu}m$. In order to control pore size and porosity, Fe-Cr-Al powders are sintered at $1200{\sim}1450^{\circ}C$ and different sintering maintenance as 1~4 hours. The powders are pressed on disk shapes of 3 mm thickness using uniaxial press machine and sintered in high vacuum condition. The pore properties are evaluated using capillary flow porometer. As sintering temperature increased, relative density is increased from 73% to 96% and porosity, pore size are decreased from 27 to 3.3%, from 3.1 to $1.8{\mu}m$ respectively. When the sintering time is increased, the relative density is also increased from 76.5% to 84.7% and porosity, pore size are decreased from 23.5% to 15.3%, from 2.7 to $2.08{\mu}m$ respectively.

• Journal of the Korean Magnetics Society
• /
• v.17 no.1
• /
• pp.47-50
• /
• 2007

[ $ZnCr_2O_4$ ] shows geometrically frustrated magnet. Recently, $CoCr_2O_4$ has been investigated for multiferroic property and dielectric anomalies by spin-current model. Polycrystalline $CoCr_2O_4$ and $CoCrFeO_4$ compounds was prepared by wet-chemical process. Crystallographic and magnetic properties of $CoCr_2O_4$ and $CoCrFeO_4$ were investigate by using the x-ray diffractometer(XRD), vibrating sample magnetometer(VSM), superconducting quantum interference device magnetometer(SQUID), and $M\"{o}ssbauer$ spectroscopy. The crystal structure was found to be single-phase cubic spinel with space group of Fd3m. The lattice constants of $CoCr_2O_4$ and $CoCrFeO_4$ $a_0$ were determined to be 8.340 and 8.377 ${\AA}$, respectively. The ferrimagnetic transition temperature for the both samples were observed at 97 K and 320 K. The $M\"{o}ssbauer$ absorption spectra at 4.2 K show that the well developed two sextets are superposed with small difference of hyperfine field($H_{hf1}=507\;and\;H_{hf2}=492\;kOe$). Isomer shift values($\delta$) of the two sextets are found to be 0.33 and 0.34 mm/s relative to the Fe metal, respectively, which are consistent with the high spin $Fe^{3+}$ charge state.

• Journal of the Korean Ceramic Society
• /
• v.51 no.5
• /
• pp.505-510
• /
• 2014

The properties of black ceramic pigments including thermal and glaze stability were systematically investigated so that these pigments could be used to decorate porcelain products. Various compositions of $(Ni,Mn)(Fe,Cr,Mn)_2O_4$ and $Co(Fe,Cr)_2O_4$ powders were synthesised using a solid state reaction method. The obtained $Co(Fe,Cr)_2O_4$ and $(Ni,Mn)(Fe,Cr,Mn)_2O_4$ powders showed single phases of spinel structure after calcination processes at $1000^{\circ}C$ and $1200^{\circ}C$, respectively. CIE $L^*a^*b^*$ colourimetric parameters of glazed $Co(Fe,Cr)_2O_4$ and $(Ni,Mn)(Fe,Cr,Mn)_2O_4$ pigments were analyzed according to the different amounts of Cr substitution. In addition, the amount of $Cr^{+6}$ remaining in the $Co(Fe,Cr)_2O_4$ and $(Ni,Mn)(Fe,Cr,Mn)_2O_4$ pigments was also measured.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2012.05a
• /
• pp.170-171
• /
• 2012

$Fe_2O_3$, Al, Cr과 Si 분말을 고 에너지 볼 밀링해서 나노분말을 제조한 후 고주파유도 가열 활성 연소합성 장치로 1분 이내의 짧은 시간에 합성 및 소결한 $Al_2O_3+4.65(Fe_{0.43}Cr_{0.17}Al_{0.323}Si_{0.077})$, $Al_2O_3$ + 5.33 ($Fe_{0.375}Cr_{0.11}Al_{0.3}Si_{0.075}$), $Al_2O_3$ + 6.15 ($Fe_{0.325}Cr_{0.155}Al_{0.448}Si_{0.072}$), $Al_2O_3$ + 3.3 ($Fe_{0.6}Cr_{0.3}Al_{0.6}$) 소결체 시편을 $700^{\circ}C$의 온도에서 100시간 동안 공기 중에서 산화 및 $N_2-H_20-H_2S$ 혼합 가스 내에서 황화 부식을 실시하였다. 그 결과 산화 및 황화 부식 후에 ${\alpha}-Al_2O_3$가 표면에 생성되어 보호 피막으로 작용하여 우수한 내식성을 보였다.

• 연구논문집
• /
• s.29
• /
• pp.141-149
• /
• 1999

Brazing of Fe-Cr-Al alloy was carried out at $1200^{\circ}C$ in vacuum furnace using nickel-based filler metals : BNi-5 powder(Ni-Cr-Si-Fe base alloy} and MBF-50 foil (Ni-Cr-Si-B). The effect of boron content on the stability of oxide scale on the brazed joint was investigated by means of cyclic oxidation test performed at $1050^{\circ}C$ and $1200^{\circ}C$. Apparently, the joints brazed with MBF-50 containing boron showed relatively stable oxidation rates compared to boron-free BNi-5 at both temperatures. However, it was considered that the slower weight loss of MBF-50 brazed specimen wasn’t resulted from the low oxidation rate but from the spallation of oxide layer. The oxide layer consisted of thick spinel oxide on the surface and $Al_2 O_3$ internal oxide layer along the interface between mother alloy and braze, the mother alloy was also eroded seriously by the formation of spinel oxides such as $FeCr_2 O_4$ and $NiCr_2 O_4$ on the surface, likely to be induced by the change of oxide forming mechanism due to diffusion of boron from the braze. On the contrary, the joint brazed with BNi-5 showed the good oxidation resistance during the cyclic oxidation test. It seems that the oxidation can be retarded by the formation of stable $Al_2 O_3$ layer at the surface.

• Journal of the Korean Society for Marine Environment & Energy
• /
• v.19 no.3
• /
• pp.203-210
• /
• 2016

In this study, nine heavy metals were analyzed in seaweeds collected from market and laver culture farm of Korea and a food safety assessment were also carried out for these heavy metals. The level of heavy metal concentrations in seaweeds was in the following order: Fe>As>Zn>Cu>Cd>Pb>Cr>Ni>Hg. Except for zinc and cadmium, seven heavy metals were significantly higher in cultured laver than in processed laver. Significant correlation was observed Cr-Fe in cultured laver and Cu-Zn, Cd-Cu, Cd-Zn and Pb-Ni in processed laver and Cu-Cr, Cu-Zn, Cd-Cr and Ni-Fe in sea tangle and Zn-Fe, Cr-Fe, Cr-Zn, Cd-Ni, Cu-Cd and Cu-Pb in processed sea mustard. Considering differences in heavy metal concentration between processed laver and cultured laver and in correlation among heavy metals, removal efficiency of heavy metals may be attributed to seaweed treatment process. The average weekly intakes of Cu, Cd, Zn, Fe and Hg via seaweeds consumption were about 0.1~7.6% of PTWI (Provisional Tolerable Weekly Intakes). Therefore, it was found that heavy metals in the seaweeds were very safe for consumption.

• Journal of the Korean institute of surface engineering
• /
• v.49 no.4
• /
• pp.339-343
• /
• 2016

ASTM T23 steel with a composition of Fe-2.25%Cr-1.6%W corroded at 600 and $700^{\circ}C$ for 5-70 h in $N_2$/(0.5, 2.5)%$H_2S$-mixed gas at 1 atm. It corroded rapidly, forming the outer FeS scale and the inner (FeS, $FeCr_2O_4$)-mixed scale. The ensuing outward diffusion of $Fe^{2+}$ ions during corrosion led to the protrusion of FeS platelets over the outer FeS scale. The formation of FeS at the surface facilitated the oxidation of Cr to $FeCr_2O_4$ in the inner scale. Since the nonprotective FeS scale existed over the whole scale, T23 steel displayed poor corrosion resistance in the $H_2S$-containing atmosphere.

• Proceedings of the Korean Society of Soil and Groundwater Environment Conference
• /
• 2002.04a
• /
• pp.233-236
• /
• 2002

다양한 산업활동에 의하여 발생하는 6가 크롬 (Cr(Ⅵ))은 대표적인 토양 및 지하수 오염물질이다. Cr(Ⅵ)은 3가크롬(Cr(III))로의 환원에 의한 침전반응으로 이동성이 저하된다고 알려져 있다. 본 연구에서는 기존의 고형화/안정화 공정에 환원.분해 반응을 추가한 2가철 기반 분해성 고형화/안정화(Degradative Solidification/Stabilization)공정에 의한 Cr(Ⅵ) 처리 특성을 고찰하였다. 회분식 실험결과 cemen/Fe(II) system내에 Cr(Ⅵ)은 환원반응 뿐만 아니라 cement에 의한 침전에 의해서도 제거됨이 밝혀졌다. Cr(Ⅵ)의 제거속도는 Fe(II)의 반응당량에 비례하는 것으로 보여진 반면, cement/solution ratio에 따른 Cr(Ⅵ) 제거동역학의 차이는 그다지 크지 않았다

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.20 no.3
• /
• pp.141-146
• /
• 2010

$LiFePO_4$ doped with Cr showed improved electrochemical properties as a cathode material of lithium-ion batteries compared to the undoped. The improvement was thought that the doping would raise the electronic conductivity of the compounds. The electrical conductivity of $LiFe_{0.965}Cr_{0.03}B_{0.005}PO_4$ and $LiFe_{0.965}Cr_{0.03}Al_{0.005}PO_4$ powder was measured in the temperature range from 30 to $80^{\circ}C$. The doped powders were synthesized via mechanochemical milling and subsequent heat treatment at 675~$750^{\circ}C$ for 5~10h. The doping enhanced grain growth and electrical conductivity. The electrical conductivity of the $LiFe_{0.965}Cr_{0.03}Al_{0.005}PO_4$ powder at $30^{\circ}C$ was $1{\times}10^{-8}S/cm$, which was higher two orders of magnitude than that of the undoped.