• Nuclear Engineering and Technology
• /
• v.56 no.7
• /
• pp.2740-2747
• /
• 2024

The sintering process acquired ferromagnetic copper ferrite ceramic material with a small concentration of Ni ion at 1100 ℃ for 1 h. Previously, copper ferrite with Ni proportions powder was acquired by the wet chemical process according to the relation CuFe_2-xNi_xO₄ where x takes values 0.0, 0.015, 0.03, 0.04, and 0.05. The role of Ni ion in the copper ferrite structure was investigated by X-ray analysis, Scanning electron microscope, EDX analysis, and density measurements. The gamma-ray shielding properties for the fabricated CuFeNiO ceramics samples were evaluated using the Monte Carlo simulation method. The obtained results show an enhancement in the linear attenuation coefficient for the fabricated ceramics with increasing the insertions of Ni ions within the fabricated samples, where increasing the Ni ions concentration between 0 and 1.19 wt% increases the linear attenuation by between 1.581 and 1.771 cm^-1 (at 0.103 MeV), 0.304-0.338 cm^-1 (at 0.662 MeV), and 0.160-0.178 cm^-1 (at 2.506 MeV), respectively. Simultaneously, the radiation protection efficiency for a 1 cm thickness of the fabricated samples increased between 14.8 and 16.3% with increasing the Ni ions between 0 and 1.19 wt%. Although the Ni doping concentration does not exceed 1.5 wt% of the total composition of the fabricated ceramics, the shielding capacity of the fabricated ceramics was enhanced by more than 11%, along the studied energy interval. Therefore, the fabricated samples can be used in gamma-ray shielding applications.

• Resources Recycling
• /
• v.9 no.2
• /
• pp.11-17
• /
• 2000

Consumption of nickel is continuously increasing and the wastes of secondary battery, ferrite and catalyst containing Ni are also generated periodically. Among those wastes, the aim of this research is the recovery of nickel from used Ni-Cd recharge battery. Battery consisted of Ni 24 wt%, Fe 30 wt% and Cd 18.5 wt%. Metal was recovered by solvent extraction after leaching. Cadmium was leached completely in 1N-HCl and Ni was recovered above 70%. 30 vol% MSP-8 separated Cd and Ni completely from acidic leaching solution. In addition $NH_4NO_3$ as one of ammonium salt type leachants showed an excellent leaching selectivity to Ni and Cd. Ni in leached solution was recovered completely by LIX-extractant and more than 70% of Cd in raffinate was by D2EHPA.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.633-634
• /
• 2006

The aim of present work is to link geometrical parameter of maximum area of structural defect $\sqrt{area}\;_{max}$ (proposed by Y. Murakami, 1983) with surface fatigue mechanisms. Determined relations allow making predictions of surface fatigue properties of cemented carbides (WC-Co hardmetal - H15 - 85wt% WC and 15wt %Co, TiC-based cermets - T60/8 - 60wt %TiC and Fe/8wt% Ni and T70/14 - 70wt %TiC and Fe/14wt% Ni) in conditions of rolling contact and impact cycling loading. Pores considered being equivalent to small defects. Three comparative defects conditions are distinguished: surface pore, just below free surface and interior pores. The Vickers hardness of binder (as main responsible for the fracture mechanism of hardmetal and cermets) assumed to be the basis of such assumption. The estimate of this prediction has been done by analyzing the pore sizes using the statistics of extremes. The lower bound of fatigue properties can be correctly predicted by considering the maximum occurring pore size.

• Journal of the Korean Society of Safety
• /
• v.30 no.4
• /
• pp.8-13
• /
• 2015

The magnetic shape memory alloys have recently received a lot of attention due to the considerable progress achieved in understanding the particular importance and the development of the factors. Among these alloys, the ferromagnetic Co-Ni- alloys have been concerned specially because of the thermoelastic character of the fcc (g) - bct (a) martensitic transformation which exhibits under the action of the temperature (shape memory effect), the stress (superelasticity) and the magnetic field (magnetoelasticity). The morphological, the crystallographical, and the thermal characteristics of thermally induced martensite in Co-35.3Ni-11.3Al(wt.%) and Co-28.1Ni-47.4Fe-3.3Ti (wt.%) alloy have been investigated by the scanning electron microscope (SEM), the X-ray Diffraction (XRD), and the differential scanning calorimeter (DSC).

• Journal of Korean Society of Environmental Engineers
• /
• v.33 no.2
• /
• pp.93-102
• /
• 2011

In this study, experiments on total digestion and sequential extraction were conducted in order to understand total metal contents, and mobility, bioavaliability and toxicity of metals in marine dredged sediment from Busan New Port. The total concentrations of arsenic and heavy metals in the dredged sediment were relatively low as follows: Al (2.36~2.96 wt.%), As (1.6~3.3 mg/kg), Ba (30.0~33.8 mg/kg), Cd (0.12~0.18 mg/kg), Cr (27.5~35.0 mg/kg), Cu (11.3~15.0 mg/kg), Fe (2.91~3.51 wt.%), Mn (324~408 mg/kg), Ni (18.8~23.8 mg/kg), Pb (23.8~31.3 mg/kg), and Zn (70.0~86.3 mg/kg). In addition, it was found that most of Al (87.5~95.9%), As (74.1~93.8%), Ba (71.8~77.6%), Cr (69.5~94.3%), Cu (50.0~78.7%), Fe (70.8~87.6%), Ni (64.5~75.3%), Pb (53.4~64.3%), and Zn (62.5~81.7%) existed in the residual fraction, meaning that those elements might come from natural sources. On the other hand, Cd and Mn were present mainly in the non-residual fraction. Due to low concentrations of toxic heavy metals and high percentage of residual fraction, it could be possible to reuse the dredged sediment for bricks, pavement base material, etc.

• The Journal of the Petrological Society of Korea
• /
• v.27 no.1
• /
• pp.37-47
• /
• 2018

Volcanic ash samples of historical eruptions from Mt. Baekdu were analyzed for major oxides, trace and rare earth elements by a variety of analytical techniques. The results indicate that the ashes consist of approximately 58.8~71.1 wt.% $SiO_2$, 9.6~16.8 wt.% $Al_2O_3$, 4.5~6.9 wt.% $Fe_2O_{3t}$, 0.1~1.7 wt.% MgO, 0.3~1.6 wt.% CaO, 5.2~6.3 wt.% $Na_2O$, 4.3~5.9 wt.% $K_2O$ and less than 1.2 wt.% $TiO_2$. Thirty two trace metals including Ba, Cu, Cr. Co, Ni, Sr, V, Zn, and Zr were analyzed. The ashes can be divided two groups: group A(1 ka Millennium pumice, 1668 and $190{\underline{3}}$ pumice) and group B(1702 pumice) according to the relative enrichment of HREEs. The abundances of heavy metals such as Cu, Co, Mn, and Zn were relatively low. As compared to the Sakurajima volcanic ash, Baekdusan volcanic ash has low concentrations of Y, Nb, Pb, U, Sc, V, Ni and Cu and high concentrations of Zr, Ba, Hf, Cr, Co, Zn and rare-earth (except Eu).

• Nuclear Engineering and Technology
• /
• v.53 no.6
• /
• pp.1887-1892
• /
• 2021

The effect of gadolinium and boron on the texture development and magnetic properties of the texture controlled 23Cr-10NiCu duplex stainless steels were studied to develop a high performance neutron and electromagnetic shielding material. The 23Cr-10NiCu base alloy is composed of 60% of austenite and 40% of ferrite, whereas, the 23Cr-10NiCu-0.5Gd-0.8B modified alloy is composed of 66% of austenite, 27% of ferrite and 7% of CrFeB intermetallic compounds. The gadolinium and boron addition to the 23Cr-10NiCu base alloy increased mechanical properties. Microstructure observation showed that the small addition of 0.5 wt% gadolinium and 0.8 wt% boron to the alloy retarded to form texture at the same hot rolling conditions, and improved the maximum magnetism, residual magnetism and coercive force about 3%, 122% and 120%, respectively.

• Journal of Powder Materials
• /
• v.1 no.1
• /
• pp.35-41
• /
• 1994

Mechanical alloying process of Al-8wt.% Ni powder was investigated for the various milling time in order to get the steady state powder. High temperature deformation behaviors of the sintered specimens were investigated by activation energy calculated after high temperature compression tests at the strain rates of 2.5$\times$10-3 s-1, 2.5$\times$10-2 s-1 and 2.5$\times$10-1 s-1 at the temperature range between $350^{\circ}C$ and $450^{\circ}C$. The steady state was obtained after 1000 minutes of milling with the PCA of 1.5 wt.% stearic acid under the condition of grinding media to powder weight ratio of 50 : 1 and impeller rotating speed of 300 rpm. True activation energy of Al-8wt.% Fe alloy was estimated to be 181 kJ/mole at the temperature range of 350~ $400^{\circ}C$ and 265 kJ/mole at the range of 400~$450^{\circ}C$.

• Economic and Environmental Geology
• /
• v.42 no.6
• /
• pp.549-559
• /
• 2009

The objectives of this study are to investigate the biomineralization of goethite and lepidocrocite formed on the twisted-stalk and the sheathed-filament structure that is suggest microbe origin, and heavy metal in the yellow Fe-hydroxide. On the ratio of Cl and the Cl/Br ratios that are a pollution and non-pollution of groundwaters, it is indicated that the groundwater in this areas were relatively contaminated by human activity. The composition of the yellow Fe-hydroxide consisted mainly of $Fe_2O_3$ and $SiO_2$. The content of $Fe_2O_3$ ranges from 58.57 wt.% to 75.7 3wt.%, and $SiO_2$ content ranges from 5.8 wt.% to 16.17 wt.%. Heavy metal elements such as Zn(max. 6,160 mg/kg), Pb(max. 377 mg/kg), U(max. 503 mg/kg), Cr(max. 203 mg/kg), Cu(max. 77 mg/kg), V(max. 162 mg/kg), Ni(max. 105 mg/kg) were observed to be rich in those yellow Fe-hydroxide. The lath and platy crystals and needle-shaped crystals were clearly observed on the twisted-stalks and sheathed-filaments structure. The goethite, gypsum, and lepidocrocite were identified in the yellow Fe-hydroxide by x-ray powder diffraction.

• Korean Journal of Materials Research
• /
• v.13 no.8
• /
• pp.531-536
• /
• 2003

The electromagnetic properties and microstructures of the ferrites based on ($Ni_{0.2}$ $Cu_{0.2}$ $Zn_{0.6}$)$_{1.085}$($Fe_2$$O_3$)$_{0.915}$ were investigated by changing the amount of additive SnO$_2$and CaO and the sintering temperatures. Addition of $SnO_2$caused pores in the specimen. There was no variation of grain size by changing the amount of additives. Total loss was reduced when ($Ni_{0.2} $Cu_{0.2}$ $Zn_{ 0.6}$)$_{1.085}$ ($Fe_2$$O_3$)$_{0.915}$ composition was sintered at $1150^{\circ}C$ rather than $1300^{\circ}C$. Addition of CaO was useful to reduce the total loss because it increased the sintering density. The lowest total loss was obtained when 0.06 wt% $SnO_2$and 0.4 wt% CaO were added at the same time.