• 한국분말재료학회지
• /
• 제2권3호
• /
• pp.223-230
• /
• 1995

The effects of Mn and Co additions up to 0.6 and 2.0 wt% respectively and the amount of cold-rolled reduction on the thermal expansion coefficient (TEC) of powder rolled Fe-Ni Invar strips were investigated. The compacted strips were sintered, homogenized and cold-rolled to the final thickness of 0.8 mm, 0.65 mm and 0.4 mm. All the strips reached full density except the case of 0.8 mm sample which has a very few porosities. The interstitials which are well known to increase TEC were minimized to the level of 10 rpm C,5 and N,0 by the processing. TEC was found to decrease by increasing the cold reduction. The Mn content had little effect on the TEC. But in Fe-Ni-Co system, TEC decreased with Co content up to 0.4 wt% and then increased, yielding the minimum value of $0.2 {\times} 10-6/^{\circ}C$ at 0.4 wt% Co. This value is much lower than that of commercial Invar product. Such effect of Co is considered to be related with the maxiumum spontaneous- magnetostriction effect.

• 한국표면공학회지
• /
• 제28권6호
• /
• pp.352-360
• /
• 1995

The effect of electrolysis conditions on the composition, the magnetic properties and the preferred orientation of Ni-Fe-Co alloy deposits was investigated using the sulfate-chloride bath paddle agitated. Cathode current efficiency increases with the current density, showing the different tendency of the variation from that of the Ni-Fe electrodeposits. The Co content of the deposits decreases with increasing current density, while the content of Ni and Fe is shown to be minimum or maximum at 3A/$dm^2$ respectively. The Ni/Fe ratio of the alloy deposits is lower than that of Ni-Fe deposits. The coercive force($H_c$) of the deposits increases with the Co content in deposit, showing the relatively low value in the range of 1.8~5.0Wt.% Co. The anisotropy field ($H_k$) of the deposits is higher than that of Ni-Fe alloy deposits, The preferred orientation of the deposits is generally (200), but the orientation factor(R) changes with both the increase of current density and the magnetic field applied during deposition.

• 한국표면공학회지
• /
• 제29권3호
• /
• pp.195-202
• /
• 1996

The composition, the microstructure and the magnetic properties(HC and Hk) of Fe-Co-Ni alloy electrodeposits were investigated according to the electrolysis conditions using sulfate bath paddle agitated. The current efficiency of the alloys electrodeposition was considerably low in the range of 16∼50%. The Fe content(wt.%) of the alloy increased from 20% to 57% with current density, while Ni content of them decreased in the range of 70∼24% respectively, and Co content was nearly constant. As a result, Fe/Ni ratio of the alloy increased from 0.3 to 2.0 showing the anomalous codeposition. The structure of the alloy changed from fcc to the mixed one of fcc+bcc with the increase of Fe/Ni ratio. The preferred orientation of the alloy with fcc and bcc structure were (220) and (110) respectively. The alloy with Fe/Ni ratio(0.3∼l.2) had the lowest coercivity of 0.4∼0.8 Oe.

• 한국지구과학회지
• /
• 제32권7호
• /
• pp.707-718
• /
• 2011

보성-화순지역 하상퇴적물에 대한 지질집단별 자연배경치와 지구화학적 특성에 대해 연구하였다. 이를 위해 1차 수계를 따라 하상퇴적물시료 186개를 채취하였고, 실험실에서 자연건조 시킨 후, XRF, ICP-AES, NAA분석을 실시하였다. 하상퇴적물의 지질집단별 자연배경치와 지구화학적 특성을 알기 위해, 시료를 화강암질편마암(GGn)지역과 반상변정질편마암(PGn)지역으로 분리하였다. 화강암질편마암지역의 주성분원소 함량은 $SiO_2$ 45.5-73.09 wt.%, $Al_2O_3$ 12-20.76 wt.%, $Fe_2O_3$(T) 3.72-8.85 wt.%, $K_2O$ 2.38-4.2 wt.%, MgO 0.75-2.77 wt.%, $Na_2O$ 0.78-1.88 wt.%, CaO 0.27-2.1 wt.%, $TiO_2$ 0.56-1.72 wt.%, $P_2O_5$ 0.06-0.73 wt.% and MnO 0.03-0.95 wt.%이고 반상변정질편마암지역의 주성분원소 함량은 $SiO_2$ 43.74-70.71 wt.%, $Al_2O_3$ 11.54-25.05 wt.%, $Fe_2O_3$(T) 3.44-13.46 wt.%, $K_2O$ 2.08-3.86 wt.%, MgO 0.65-2.99 wt.%, $Na_2O$ 0.63-1.7 wt.%, CaO 0.35-2.07 wt.%, $TiO_2$ 0.68-4.17wt.%, $P_2O_5$ 0.1-0.31 wt.% and MnO 0.07-0.33 wt.%이다. 화강암질편마암지역 하상퇴적물의 위해원소 함량은 크롬 41.7-242 ppm, 코발트 7.6-25.1 ppm, 니켈 12-61 ppm, 구리 10-47 ppm, 아연 48.5-412 ppm, 납 17-215 ppm이고 반상변정질편마암지역은 크롬 29.6-454 ppm, 코발트 5.9-53.7 ppm, 니켈 8.7-287 ppm, 구리 6.4-134 ppm, 아연 43.6-370 ppm, 납 15-37 ppm이다. 화강암질편마암지역에서 크롬은 MgO와 코발트는 $Al_2O_3$, $Fe_2O_3$(T), MgO와 니켈은 $Fe_2O_3$(T), CaO, MgO와 높은 상관성을 가지나, 구리, 아연, 납은 비교적 낮은 상관성을 보였다. 반상변정질편마암지역에서 일반적으로 크롬, 코발트, 니켈, 구리는 주성분원소와 대부분 높은 상관성을 보였으나, 아연과 납은 낮은 상관성을 보였다.

• 한국전기전자재료학회논문지
• /
• 제15권5호
• /
• pp.406-411
• /
• 2002

Ni-Zn ferrite is required to have predominant and stable characteristics in the range of high frequency for the power line communication, so that microstructures and magnetic properties such as power loss and initial permeability in $Ni_{0.8}Zn_{0.2}Fe_2O_4$ were investigated in terms of variable $Bi_2O_3,CaO$ and $V_2O_5$ contents. $Bi_2O_3$ and $V_2O_5$ liquid phase created during sintering process promoted sintering and grain growth but much of the closed pore existed in the grains. The grain size of the specimens with $V_2O_5$ of over 0.5 wt% decreased as the result of "pinning effect"and the resonance frequency increased with CaO of 0.3we%. The high initial permeability of 81.52%, resonance frequency of 17.05 MHz and low power loss of 17,858 kW/$\textrm{m}^3$ were obtained from the samples with $Bi_2O_3$ of 0.5, CaO of 0.3, and $V_2O_5$ of 0.7 wt%.

• 한국재료학회지
• /
• 제14권11호
• /
• pp.813-820
• /
• 2004

The electrolytic reduction of spent oxide fuel involves the liberation of oxygen in a molten LiCl electrolyte, which is a chemically aggressive environment that is very corrosive for typical structural materials. So, it is essential to choose the optimum material for the process equipment handling molten salt. In this study, corrosion behavior of Haynes 263, 75, and Inconel X-750, 718 in molten salt of $LiCl-Li_{2}O$ under oxidation atmosphere was investigated at $650^{\circ}C\;for\;72\sim360$ hours. At $3\;wt\%\;of\;Li_{2}O$, Haynes 263 alloy showed the highest corrosion resistance among the examined alloys, and up to $8\;wt\%\;of\;Li_{2}O$, Haynes 75 exhibited the highest corrosion resistance. Corrosion products were formed $Li(Ni,Co)O_2,\;LiNiO_2\;and\;LiTiO_2\;and\;Cr_{2}O_3$ on Haynes 263, $Cr_{2}O_3,\;NiFe_{2}O_4,\;LiNiO_2,\;Li_{2}NiFe_{2}O_4,\;Li_{2}Ni_{8}O_10$ and Ni on Haynes 75, $Cr_{2}O_3,\;(Al,Nb,Ti)O_2,\;NiFe_{2}O_4,\;and\;Li_{2}NiFe_{2}O_4$ on Inconel X-750 and $Cr_{2}O_3,\;NiFe_{2}O_4\;and\;CrNbO_4$ on Inconel 718, respectively. Haynes 263 showed local corrosion behavior and Haynes 75, Inconel X-750, 718 showed uniform corrosion behavior.

• 한국수소및신에너지학회논문집
• /
• 제23권2호
• /
• pp.117-124
• /
• 2012

Alkaline electrolysis needs the electrode having a low overvoltage and good corrosion resistance in alkaline solution such as KOH and NaOH, for the oxygen and hydrogen production. The commercial materials such as SUS(stainless steel)-316, Ni and NiFe were evaluated for the electrode in alkaline electrolysis. The test solution for the alkaline electrolysis used 1~9M NaOH and 1~9M KOH. The voltage increased with an increase of current density in each solution. As for the 15wt.% (about 5M) NaOH, the voltage of the tested electrode under the current density of 1.8A/$cm^2$ showed the almost same value. The voltage over the current density of 1.8A/$cm^2$ deceased in the order: Ni${\fallingdotseq}$NiFe$cm^2$ showed the almost same value. The voltage over the current density of 1.8A/$cm^2$ deceased in the order: NiFe${\fallingdotseq}$SUS-316. From the results, it was estimated that NiFe and Ni was suitable as the electrode for the alkaline water electrolysis using NaOH and KOH electrolyte.

• 한국자기학회지
• /
• 제13권6호
• /
• pp.246-250
• /
• 2003

고주파 대역에서 전자기적 특성이 안정적으로 유지되는 Ni-Zn 페라이트를 제조하기 위해 Ni$_{0.8}$Zn$_{0.2}$Fe$_2$O$_4$를 기본조성으로 Bi$_2$O$_3$와 CaO를 첨가하였다. Bi$_2$O$_3$의 첨가량이 0.3 wt%까지는 손실이 증가하였고 그 이상의 첨가량에서는 감소하였으며, 투자율은 Bi$_2$O$_3$ 첨가량이 증가할수록 증가하였다. Bi$_2$O$_3$와 CaO는 고용체를 형성하여 입계에 편석 됨으로서 비저항층을 형성하여 각각 0.7 wt%, CaO 0.3 wt% 첨가할 경우 가장 낮은 손실과 높은 공명주파수를 나타내었다.

• 대한금속재료학회지
• /
• 제50권6호
• /
• pp.419-425
• /
• 2012

The purpose of this research was to develop a low Ni austenitic cast iron through replacing Ni by Cu and Mn because they are cheaper than Ni. The effect of the Cu content (6-12 wt%) on the microstructure characteristics was investigated in Fe-3%C-16%(Ni+Cu+Mn) cast iron. Contrary to general effect of the Cu on cast iron, the result of the microstructure analysis indicated that bainite and cementite were formed in high Cu content (>8 wt%Cu). A crystallized Cu-solution (Cu-Mn) phase and MnS in the Cu-solution were formed. The quantity of those phases increased as the Cu content increased. Consequently, the high Cu content in the composition ratio (Ni+Cu+Mn=16%) caused the formation of Cu-Mn/MnS and those phases decreased the effect of Cu and Mn on austenite formation. For this reason, bainite and cementite were formed in high Cu content.

• 한국레이저가공학회지
• /
• 제2권2호
• /
• pp.27-33
• /
• 1999

Electron beam was applied on the low carbon steel in order to fabricate Metal/Metal GBM(Graded Boundary Material). Ni sheet was placed on the steel substrate. The electron beam was irradiated on the surface and produced a homogeous alloyed layer. Sequential repetition of electron beam treatments for 4 times resulted in 8mm thick graded layer. To determine each layers property, optical microscopy, XRD, microhardness tester and EDS were used. The residual stress was measured by the low angle x-ray diffraction method. The graded boundary layer was stepwise profile, but Ni content incresed up to 80 wt% and Fe content decreased 20 wt% near surface. Each layers microstructure and hardness varied by different Fe/Ni composition. The compressive residual stress was induced by martensite transformation in the 1st and End layers and the shrinkage cracks were formed in graded layer by rapid cooling.