• Journal of Korea Foundry Society
• /
• v.33 no.6
• /
• pp.233-241
• /
• 2013

Effect of Fe and Mn contents on the castability of Al-9wt%Si-xMg-yFe-zMn alloy has been studied. The alloy was composed of ${\alpha}$-Al phase, Al+eutectic Si phase, ${\beta}$-Al5FeSi compound and chinese script ${\alpha}$-$Al_{15}(Mn,Fe)_3Si_2$ compound. ${\beta}$-$Al_5FeSi$ and ${\alpha}$-$Al_{15}(Mn,Fe)_3Si_2$ compounds assumed to effect the fluidity and shrinkage behaviors of the alloy during solidification due to the crystallization of ${\alpha}$-$Al_{15}(Fe,Mn)_3Si_2$ and ${\beta}$-$Al_5FeSi$ compounds above eutectic temperature. As Fe and Mn contents of Al-9wt%Si-0.3wt%Mg system alloy increased from 0.15wt% to 0.6wt% and from 0.3wt% to 0.7wt%, fluidity of the alloy decreased by 5.7% and 3.3%, respectively. And as Mg content of Al-9wt%Si-0.45wt%Fe-0.5wt%Mn system alloy increased from 0.3wt% to 0.4wt%, fluidity of the alloy decreased by 8.6%. When Fe content of the alloy increased from 0.15wt% to 0.6wt%, macro shrinkage ratio decreased from 6.1% to 4.1%, and micro shrinkage ratio increased from 0.04% to 0.24%. Similarly, Mn content of the alloy increased from 0.3wt% to 0.7wt%, macro shrinkage ratio decreased from 6.0% to 4.5% and micro shrinkage ratio increased from 0.12% to 0.18%. Judging from the castability of the alloy, Al-9wt%Si-0.3wt%Mg alloy with low content of Fe and Mn, 0.1wt% Fe and 0.3wt% Mn, is recommendable.

• Journal of the Korean Magnetics Society
• /
• v.18 no.5
• /
• pp.195-199
• /
• 2008

Composites of $Fe_{93.5}Si_{6.5}$ powder and epoxy were prepared using a thermal curing process. Scanning electron microscope (SEM), vibrating sample magnetometer (VSM) and network analyzer were used to analyze the structure, electromagnetic properties and microwave absorption of the composites. Results show that the saturation magnetization depends on the fraction of the $Fe_{93.5}Si_{6.5}$ powder in the composite, which affects initial permeability. It is believed that the eddy current loss is a dominant factor over 1 GHz and that the resonance frequency of the composite decreases with increasing fractions of $Fe_{93.5}Si_{6.5}$ powder. Finally, reflection loss was calculated from the permeability and permittivity of these composites. Composite with 50 wt.% $Fe_{93.5}Si_{6.5}$ powder fractions and 5 mm thickness showed reflection loss below -20 dB from 3.66 GHz to 4.16 GHz. Therefore, it is believed that thin Fe-Si/epoxy composites may be a good candidate for microwave absorption application.

• Journal of Korea Foundry Society
• /
• v.15 no.4
• /
• pp.397-407
• /
• 1995

The objectives of this study are first, to expand our understanding of relationship between magnetic properties and microstructural features such as grain size and texture, and second to reduce core loss of Fe-6.5%Si strip through optimizing heat treatment conditions. A rapid solidification technique, planar flow casting(PFC), was adopted to produce Fe-6.5%Si strips. The strips were heat treated under various conditions. The results show that heat treatment conditions can change not only grain size but also (200) texture formation on the strip surface. Variation in magnetic properties of Fe-6.5%Si strip is analyzed in terms of the change in grain size as well as (200) texture on the strip surface. The heat treatment conditions of $1100^{\circ}C$ over 2 hr or $1150^{\circ}C$ $1{\sim}2hr$ in $N_2+5%H_2$ appear to minimize core loss of Fe-6.5%Si strips.

• Journal of the Korean Magnetics Society
• /
• v.20 no.1
• /
• pp.13-17
• /
• 2010

Fe-3, 4.2 and 6.8% Si compressed cores were fabricated, and then electrical resistivity, AC and DC magnetic properties, microhardness, and other properties were analyzed in order to know whether best soft magnetic properties could be also obtained in an Fe-Si compressed core with the well-known composition of Fe-6.5% Si. With increasing the silicon content, eddy current loss and hysteresis loss decreased and increased, respectively, so that a minimum total loss was not obtained in the well-known Fe-6.8 % Si cores, but obtained in the Fe-4.2 % Si cores. Also electrical resistivity of the cores and hardness of the particles increased monotonously with silicon content so that compaction ratio of the cores decreased. B2 and $DO_3$ ordered phase could be observed only in Fe-6.8% Si powder. A minimum loss and highest permeability of the Fe-4.2 % Si cores can be explained by the ratio of specific electrical resistivity of insulator to that of magnetic particles, micro-hardness, compaction ratio and demagnetization coefficient of the Fe-Si powder particles with silicon content.

• Journal of the Korean Magnetics Society
• /
• v.4 no.1
• /
• pp.12-19
• /
• 1994

The crystallization behavior of the amorphous $Fe_{73.5}Cu_{1}Nb_{3}Si_{16.5}B_{6}$ alloy with isothermal annealing at $552^{\circ}C$ was studied by $M\"{o}ssbauer$ spectroscopy. The amorphous phase was revealed to coexist together with $Do_{3}-FeSi$ nanocrystalline and Cu-duster in annealed alloys by $M\"{o}ssbauer$ spectrum analysis. At the early stage of crystallization, Si content of FeSi is high due to the creation of Cu-cluster, and decreases with annealing until 60 minutes, which results in the increase in the mean hyperfine field of FeSi, and thereafter keeps constant. After 60 minutes, the decrease in the mean hyperfine field of the residual armrphous, in spite of a slight change in the volume fraction of the FeSi and the residual armrphous, is caused by the increase in the content of Nb and B in residual amorphous phase. Both directions of the hyperfine field, those of the FeSi and the residual amorphous, become randomly oriented in about 60 minutes. For FeSi and Cu-duster, the Avrami exponents are 0.51 and O.65, the activation energies are 2.35 eV and 2.44 eV, and the incubation times are 2.4 minutes and 0.8 minutes respectively. Earlier formation of Cu-duster than that of FeSi is coincidence with the fact that Cu atom promotes the nucleation of the FeSi.

• Journal of Powder Materials
• /
• v.24 no.2
• /
• pp.122-127
• /
• 2017

Fe-6.5 wt.% Si alloys are widely known to have excellent soft magnetic properties such as high magnetic flux density, low coercivity, and low core loss at high frequency. In this work, disc-shaped preforms are prepared by spark plasma sintering at 1223 K after inert gas atomization of Fe-6.5 wt.% Si powders. Fe-6.5 wt.% Si sheets are rolled by a powder hot-rolling process without cracking, and their microstructure and soft magnetic properties are investigated. The microstructure and magnetic properties (saturation magnetization and core loss) of the hot-rolled Fe-6.5 wt.% Si sheets are examined by scanning electron microscopy, electron backscatter diffraction, vibration sample magnetometry, and AC B-H analysis. The Fe-6.5 wt.% Si sheet rolled at a total reduction ratio of 80% exhibits good soft magnetic properties such as a saturation magnetization of 1.74 T and core loss ($W_{5/1000}$) of 30.7 W/kg. This result is caused by an increase in the electrical resistivity resulting from an increased particle boundary density and the oxide layers between the primary particle boundaries.

• Journal of Korea Foundry Society
• /
• v.33 no.3
• /
• pp.103-112
• /
• 2013

Effect of Fe and Mn contents on the tensile properties of Al-4 wt%Mg-0.9 wt%Si alloy system has been studied. Common phases of Al-4 wt%Mg-0.9 wt%Si alloy system were ${\alpha}$-Al, $Mg_2Si$, ${\alpha}-Al_{12}(Fe,Mn)_3Si$ and ${\beta}-Al_5FeSi$. As Fe content of Al-4 wt%Mg-0.9 wt%Si alloy system increased from 0.15 wt% to above 0.3 wt%, ${\beta}-Al_5FeSi$ compound appeared. When Mn content of the alloy increased from 0.3 wt% to 0.5 wt%, morphology of plate shaped ${\beta}-Al_5FeSi$ compound changed to chinese script ${\alpha}-Al_{12}(Fe,Mn)_3Si$. As Fe content of Al-4 wt%Mg-0.9 wt%Si-0.3 wt%Mn alloy increased from 0.15 wt% to 0.4 wt%, tensile strength of the as-cast alloy decreased from 191 MPa to 183 MPa and, elongation of the alloy also decreased from 8.0% to 6.2%. Decrease of these properties can be explained as the formation of plate shape, ${\beta}-Al_5FeSi$ phase with low Mn/Fe ratio of the alloy. However, when Mn content of Al-4 wt%Mg-0.9 wt%Si-0.3 wt%Fe alloy increased from 0.3 wt% to 0.5 wt%, tensile strength of as-cast alloy increased from 181 MPa to 194 MPa and, elongation of the alloy increased from 6.8% to 7.0%. These improvements attribute to the morphology change from ${\beta}-Al_5FeSi$ phase to chinese script, ${\alpha}-Al_{15}(Fe,Mn)_3Si_2$ phase shape-modified from with high Mn/Fe ratio of the alloy.

• Journal of Korea Foundry Society
• /
• v.31 no.1
• /
• pp.18-25
• /
• 2011

Effect of Fe and Mn contents on the tensile properties has been studied in Al-9wt%Si-0.3wt%Mg alloy. As Fe content of Al-9wt%Si-0.3wt%Mg-0.5wt%Mn alloy increased from 0.15wt% to 0.45wt%, tensile strength of as-cast alloy decreased from 192 MPa to 174 MPa, and elongation of the alloy also decreased from 4.8% to 4.2%. Decrease of these properties can be explained as the formation of plate shape, ${\beta}-Al_5FeSi$ phase with high Fe/Mn ratio of the alloy. However when Mn content of Al-9wt%Si-0.3wt%Mg-0.45wt%Fe alloy increased from 0.3wt% to 0.5wt%, tensile strength of T6 aged alloy increased from 265 MPa to 275 MPa, and elongation of the alloy increased from 2.3% to 3.6%. These improvements attribute to chinese script, ${\alpha}-Al_{15}(Mn,Fe)_3Si_2$ phase shape-modified from ${\beta}-Al_5FeSi$ phase with low Fe/Mn ratio of the alloy.

• Journal of Magnetics
• /
• v.2 no.1
• /
• pp.12-15
• /
• 1997

Fe-(3∼6.5wt%) Si alloy powders having a high magnetic induction(Bs) and a low core loss value for high frequency use were obtained by an extractive melt spinning as well as a centrifugal atomization technique. Sintered core rings made by the rapidly solidified Fe-6.5wt% Si powders exhibited the high frequency magnetic properties : megnetic induction(B8) of 1.23 T, coercivity(Hc) of 0.12 Oe, relative permeability(${\mu}$a) of 6321, and core loss(W10/50) of 1.27 W/kg from the rings of 1.1 mm thick. The magnetic induction values were found to be almost identical to those of non-oriented Fe-6.5wt% Si steel sheet and double the value of 6.5wt% Si sheet prepared by the CVD technique. The high frequency core losses(W) up to 10 kHz(W10/10k) were measured to be competitive to those of grain-oriented Fe-6.5wt% Si steel sheet.

• Journal of the Korean Magnetics Society
• /
• v.7 no.6
• /
• pp.293-298
• /
• 1997

$Fe_5Si_Xb_{5-x}$ (x=0, 1, 2, 3) powders were prepared by mechanical alloying, and their phases and magnetic properties were investigated by using XRD, TEM, Mossbauer spectroscopy and VSM. Starting elements are incorporated into $\alpha$-Fe in the early stage of mechanical alloying, and the stable phases are formed as the milling proceeds. After the annealing at 80$0^{\circ}C$ for 2 hours, it is found that the FeB and $Fe_2B$ phases coexist for the $Fe_5B_5$(x=0) composition. By substituting Si for B, the formation of $Fe_2B$ phase is restricted and the $Fe_5SiB_2$, $Fe_2Si_{0.4}B_{0.6}$ and paramagnetic phase begin to appear. The FeB phase has wide range of hyperfine magnetic field because it is not fully crystallized on the annealing at 800 $^{\circ}C$. On the contrary, others have good crystalline phases and show well-defined hyperfine magnetic field. Magnetic saturation is highest for the $Fe_5B_5$ composition where the amount of the $Fe_2B$ phase in large.