• Nuclear Engineering and Technology
• /
• v.53 no.8
• /
• pp.2582-2590
• /
• 2021

The high-energy milling is one of the most extended techniques to produce Oxide dispersion strengthened (ODS) powder steels for nuclear applications. The consequences of the high energy mill process on the final powders can be measured by means of deformation level, size, morphology and alloying degree. In this work, an ODS ferritic steel, Fe-14Cr-5Al-3W-0.4Ti-0.25Y₂O₃-0.6Zr, was fabricated using two different mechanical alloying (MA) conditions (M_std and M_act) and subsequently consolidated by Spark Plasma Sintering (SPS). Milling conditions were set to evidence the effectivity of milling by changing the revolutions per minute (rpm) and dwell milling time. Differences on the particle size distribution as well as on the stored plastic deformation were observed, determining the consolidation ability of the material and the achieved microstructure. Since recrystallization depends on the plastic deformation degree, the composition of each particle and the promoted oxide dispersion, a dual grain size distribution was attained after SPS consolidation. M_act showed the highest areas of ultrafine regions when the material is consolidated at 1100 ℃. Microhardness and small punch tests were used to evaluate the material under room temperature and up to 500 ℃. The produced materials have attained remarkable mechanical properties under high temperature conditions.

• Korean Journal of Materials Research
• /
• v.9 no.10
• /
• pp.1018-1024
• /
• 1999

The effects of operating temperature and stress on degradation of components in high temperature steam generator were investigated. Several 2.25CrlMo tubes which had operated over 20 years and an unused 9CrlMoVNb tube were tested. For the former samples, the amount of $\textrm{M}_{6}\textrm{C}$ carbide and its size are increased with the aging or operating time. The precipitation behavior of carbides ($\textrm{M}_{2}\textrm{O}$, $\textrm{M}_{6}\textrm{C}$) is changed with the operating temperature of the tubes. However, unused 9CrlMoVNb samples show a different carbide precipitation process due to high chromium, vanadium, and niobium contents. The amount of Cr-rich $\textrm{M}_{23}\textrm{C}_{6}$ carbide is significantly increased with aging time, but that of $\textrm{M}_{6}\textrm{C}$ type carbide is rarely changed with aging time at elevated temperatures.

• Journal of Powder Materials
• /
• v.22 no.3
• /
• pp.197-202
• /
• 2015

In this study, porous stainless steel (STS316L) sintered body was fabricated by powder metallurgy method and its properties such as porosity, compressive yield strength, hardness, and permeability were evaluated. 67.5Fe-17Cr- 13Ni-2.5Mo (wt%) powder was produced by a water atomization. The atomized powder was classified into size with under $45{\mu}m$ and over $180{\mu}m$, and then they were compacted with various pressures and sintered at $1210^{\circ}C$ for 1 h in a vacuum atmosphere. The porosities of sintered bodies could be obtained in range of 20~53% by controlling the compaction pressure. Compressive yield strength and hardness were achieved up to 268 MPa and 94 Shore D, respectively. Air permeability was obtained up to $79l/min{\cdot}cm^2$. As a result, mechanical properties and air permeability of the optimized porous body having a porosity of 25~40% were very superior to that of Al alloy.