• Korean Journal of Materials Research
• /
• v.14 no.5
• /
• pp.338-342
• /
• 2004

Ni-Zn ferrite powder was obtained by wet method that was to be coprecipitated the metal nitrates, Fe($NO_3$)$_3$ㆍ$9H_2$O, Ni($NO_3$)$_2$ㆍ$6H_2$O, Zn($NO_3$)$_2$ㆍ$6H_2$O to make a high permeability material. The composition of the ferrite powder was $Fe_2$$O_3$ 52 mol%, NiO 14.4 mol%, ZnO 33.6 mol%. Ni-Zn ferrite powder was compounded by precipitating metal nitrates with NaOH in vessel at the synthetic temperature of $90^{\circ}C$ for 8 hours. Calcination temperature and sintering temperature were $700^{\circ}C$ and $1150^{\circ}C$～$1250^{\circ}C$, respectively, for 2 hours. And the other ferrite powder was also prepared by the wet ball milling that was to be mixed the metal oxides as same as the above chemical composition. We studied the properties of the powder and the electromagnetic characteristics of the sintered cores obtained from there two different processes. Wet direct process produced smaller particle size with narrower distribution of the size and more purified ferrite whose sintered cores had high permeability and high magnetization.

• Journal of Powder Materials
• /
• v.10 no.5
• /
• pp.344-347
• /
• 2003

Pure tantalum powder has been produced by combining Na as a reducing agent, $K_2$TaF$_{7}$ as feed material, KCl and KF as a diluent in a stainless steel (SUS) bomb, using the method of metallothermic reduction. And we examined various types of after-treatment that affect the high purification of powder. A significant amount of impurities contained in recovered powder was removed in various conditions of acid washing. In particular, 20% (HCl + HNO$_3$) was effective in removing heavy metal impurities such as Fe, Cr and Ni, 8% H$_2$SO$_4$ + 8% $Al_2$(SO$_4$)$_3$ in removing fluorides such as K and F from non-reactive feed material, and 2% $H_2O$$_2$ + 1 % HF in removing oxides that formed during reaction. Significant amounts of oxygen and part of light metal impurities could be removed through deoxidation and heat treatment process. On the other hand, because it is difficult to remove completely heavy metal impurities such as Fe, Cr, and Ni through acid washing or heat treatment process if their contents are too high, it is considered desirable to inhibit these impurities from being mixed during the reduction process as much as possible.

• Journal of Powder Materials
• /
• v.10 no.2
• /
• pp.129-135
• /
• 2003

Nanocrystalline powders of $MnFeP_{1-x}As_x$(x=0.45-0.6) have been synthesized by mechanochemical reaction at room temperature using high-energy ball milling from mixtures of Mn, Fe, P, and As Powders. It has been found that a mechanically induced self-propagating reaction (MSR) occurs within 2 hours of milling and it produces very fine polycrystalline powder having a hexagonal $Fe_2P$ structure. Further milling up to 24 hours did not change the crystalline and average particle sizes or the phase composition of the milling product. When x is 0.65, no reaction among the reactants has been observed even after 24 hours of milling. As the P content decreases in $MnFeP_{1-x}As_x$, the incubation time for the MSR has increased and the lattice constants in both a and c axes have changed.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2005.04a
• /
• pp.12-12
• /
• 2005

• Journal of the Korean Ceramic Society
• /
• v.31 no.1
• /
• pp.55-61
• /
• 1994

Mn-Zn ferrite powder was obtained by wet method that was to be coprecipitated the metal ions of Fe2+, Mn2+ and Zn2+ with alkali solution. The target composition of the ferrite powder was 52 mol% Fe2O3, 24 mol% MnO, and 24 mol% ZnO, that was based on the region of high permeability. And the other ferrite powder was prepared by the dry method that was to be mixed the metal oxides as the above chemical composition. The wet method was compared with dry method for the powder properties and the electromagnetic characteristics of sintered cores. The synthesized powder by wet method was smaller particle size, narrower particle distribution, and higher purity than that of dry method. The initial permeability of sintered sample prepared by the wet method was 14000~28000, on the other side, 9000~15500 in case of the dry method.

• Journal of Korea Foundry Society
• /
• v.10 no.1
• /
• pp.64-70
• /
• 1990

In order to lower the cabon content of sintered products below the solubility of austenite, Fe-oxide was added to cast iron powder of which matrix was pearlite. And the effects of it on some sintering properties and mechanical properties were investigated. Roughly speaking, the linear shrinkage, density, and tensile strendth of sintered properties increased as the sintering temperature became higher, the size distribution of powder became finer, and the amount of Fe-oxide added became less. The maximum tensile strength of sintered products was $78㎏f/mm^2$ more or less, of which carbon content was 1.4% and sintering temperature was $1180^{\circ}C$.

• Journal of Magnetics
• /
• v.12 no.1
• /
• pp.49-52
• /
• 2007

We investigated annealing effect of microforged powders on magnetic properties and electromagnetic absorption behaviors for ferromagnetic Fe-Cr metal alloy powder-polymer composites. The coercive properties greatly decreased with annealing temperature and the magnetic permeability had significantly increased after microforging and subsequent annealing treatment, due to a reduction in lattice strain of the microforged powders. The power loss in the far field regime also had greatly increased after microforging and subsequent annealing treatment in frequency range from 50 MHz to 6 GHz. As a result, the electromagnetic absorption of ferromagnetic Fe-Cr alloy metal powder-polymer composites was highly improved because of the relaxation of the internal strain during annealing process.

• Journal of Powder Materials
• /
• v.11 no.4
• /
• pp.328-332
• /
• 2004

Fe nanopowders were successfully synthesized by plasma arc discharge (PAD) process using Fe rod. The influence of chamber pressure on the microstructure was investigated by means of X-ray Diffraction (XRD), Field Emission Scanning Electron Microscope (FE-SEM), Transmission Electron Microscopy (TEM) and X-ray Photoelectron Spectroscopy (XPS). The prepared particles had nearly spherical shapes and consisted of metallic cores (a-Fe) and oxide shells (Fe$_{3}$O$_{4}$), The powder size increased with increasing chamber pressure due to the higher dissolution and ejection rate of H$_2$ and gas density in the molten metal.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.597-598
• /
• 2006

Gas filtration at high temperature from industrial processes offers various advantages such as increasing process efficiency, improving heat recovery and materials resource recovery, etc. At the same time, it is an advanced environment protection technology. This paper describes a newly developed metallic filter element. The manufacturing process of sintered $Fe_3Al$ metallic powder and the mechanical and filtration characteristics of this filter element were investigated. In this work, the phase constituent changes of the $Fe_3Al$ powder during sintering were studied. The newly developed filter elements were found to have excellent corrosion resistance, good thermal resistance, high strength and high filtration efficiency.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.118-119
• /
• 2006

The development of Fe-based metal matrix composites (MMCs) with high content of hard phase has been approached by combining the use of advanced powder metallurgy techniques like high-energy milling (HEM), cold isostatic pressing (CIP) and vacuum sinterings. A 30% vol. of NbC particles was mixed with Fe powder by HEM in a planetary mill during 10h, characteristing the powder by the observation of morphology and microstructure by scanning electron microscopy (SEM). After of sintering process the variation of density, hardness,carbon content and the microstructural changes observed, permits to find the optimal conditions of processing. Afterwards, a heat treatment study was performed to study the hardenability of the composite.