• Journal of The Korean Society of Grassland and Forage Science
• /
• v.24 no.1
• /
• pp.11-20
• /
• 2004

This pot experiment was conducted to investigate the effects of combined micronutrient application($T_1$;control, $T_2$; Fe, $T_3$; Fe＋Mn, $T_4$: Fe＋Mn＋Cu, $T_5$ ; Fe＋Mn＋Cu＋Zn, $T_6$ ; Fe＋Mn＋Cu＋Zn＋Mo, $T_7$ ;Fe＋Mn＋Cu＋Zn＋Mo＋B) on forage performance of pure and mixed cultures of orchardgrass and white clover. This 4th part was related to the changes in the contents of micronutrients(Fe, Mn, Cu, Zn, Mo, and B) in forages. The results obtained are summarized as follows: 1. General differences have been showed in the contents of micronutrients based on the treatments, forage species, pure/mixed culture, cutting order, and additional fertilization, especially N. Compared to pure culture, orchardgrass showed relatively high contents of Mn and Zn, and low contents of B and Fe in mixed culture. White clover, however, tended to be exactly opposed to the above trends. The contents of Cu and Mo did not show any differences between pure and mixed cultures. 2. In relative comparison, the $T_7$ influenced negatively on the contents of Cu, Zn, and Mo in orchardgrass. The $T_7$ also influenced negatively on the contents of Mo in white clover. However, the $T_7$ influenced positively on the contents of Mn in orchardgrass, and also influenced positively on the contents of Fe, Mn, and Cu in white clover. Because of the antagonism between Fe and Mn, the Fe contents in both forages were significantly decreased by the $T_3$. Under the various conditions, the differences among Fe contents tended to be more significant in white clover than in orchardgrass. 3. At the $T_6$ and $T_7$, the Mo contents in both forages tended to be relatively high. The Mo contents, however, were somewhat decreased by the $T_7$ 7/. The Mo-toxicity, which was caused by the high Mo-contents, tended to be diminished, and was likely to be prevented by the optimum B/Mo ratio and B application($T_7$ ).

• Journal of The Korean Society of Grassland and Forage Science
• /
• v.24 no.2
• /
• pp.93-104
• /
• 2004

This pot experiment was conducted to investigate the effects of combined micronutrient application($T_1$; control, $T_2$; Fe, $T_3$; Fe+Mn, $T_4$; Fe+Mn+Cu, $T_5$ ; Fe+Mn+Cu+Zn, $T_6$ ; Fe+Mn+Cu+Zn+Mo, T$_{7}$; Fe+Mn+Cu+Zn + Mo + B) on forage performance of pure and mixed cultures of orchardgrass and white clover. The fifth part was concerned with the changes in the total and relative contents, uptake amounts, and mutual ratios. of micronutrients in forages. The results obtained are summarized as follows: 1. The relative contents(total contents of 6 micronutrients = 100%) of Fe and Mn were considerably influenced by the antagonism between Fe and Mn, and also were influenced by the differences in Mn-absorption between orchardgrass and white clover. Compared with pure culture, orchardgrass showed high relative contents of Mn, and low relative contents of Fe and B in mixed culture. White clover, however, tended to be exactly opposed to the above trends. In relative contents, the T$_6$ 6/ resulted generally in decrease of Fe. However the $T_7$ resulted in increase of Mn and B. In addition, the $T_7$ resulted in decrease of Cu and Zn in orchardgrass, and Mo in white clover. 2. In general, there were differences in the tendency between the yield changes and the uptake amounts of micronutrients. General differences have been showed in the uptake amounts and mutual ratios of micronutrients based on the forage species, pure/mixed culture, additional fertilization, and antagonism. The uptake amounts of total micronutrients were generally increased by the treatments with increased combination. In uptake amounts, the $T_7$ resulted in the increase of Mn and B, and decrease of Mo. 3. The mutual ratios of Fe/Mn, Fe/Cu, and Mn/Cu were considerably influenced by the antagonism between Fe and Mn. At the $T_7$ , very low ratio of Fe/Mo affected by the T6 tended to be somewhat improved because of the decrease of Mo content． The poor growth of forages at the $T_6$ was improved by the $T_7$ . This fact was likely to be caused by the adequate B/Mo ratio.

• Journal of Fashion Business
• /
• v.4 no.1
• /
• pp.25-32
• /
• 2000

The purpose of this study was to suggest the knowlege and scientific information of the damage according to the heavy metal exposure level of hair coloring manipulations. The study was investigated variations of the heavy metal contents(Pb, Zn, Cu, Mn, Fe, Ni) in hairdye and human hairs by 1 and 2 times of hair coloring manipulations. The results were as follows; 1. Mean heavy metal contents in colorant of hairdye were 0.250ppm(Pb), 33.650ppm(Zn), 0.800ppm(Cu), 0.675ppm(Mn), 31.050ppm(Fe), 1.700ppm(Ni). In oxidant of hairdye, It were 0.225ppm(Pb), 35.450ppm(Zn), 0.575ppm(Cu), 0.075ppm(Mn), 16.600ppm(Fe), 1.500ppm(Ni). 2. Mean heavy metal contents were 2.950ppm(Pb), 29.000ppm(Zn), 9.400ppm(Cu), 1.075ppm(Mn), 40.775ppm(Fe), 1.950ppm(Ni) in virgin hairs, 3.025ppm(Pb), 40.250ppm(Zn), 9.650ppm(Cu), 1.350ppm(Mn), 42.900ppm(Fe), 2.200ppm(Ni) in 1 time of coloring hairs, 3.350ppm(Pb), 51.650ppm(Zn), 10.950ppm(Cu), 1.475ppm(Mn), 44.350ppm(Fe), 2.225ppm(Ni) in 2 times of coloring hairs.

• Journal of Korea Foundry Society
• /
• v.33 no.2
• /
• pp.55-62
• /
• 2013

Effect of Fe and Mn contents on the castability of Al-4wt%Mg-0.9wt%Si system alloy has been studied. According to the analysis of cooling curve for Al-4wt%Mg-0.9wt%Si-0.3wt%Fe-0.3/0.5wt%Mn alloy, ${\alpha}-Al_{15}(Fe,Mn)_3Si_2$ and ${\beta}-Al_5FeSi$ phases crystallized above eutectic temperature of $Mg_2Si$. Therefore, these phases affected both the fluidity and shrinkage behaviors of the alloy during solidification. As Fe and Mn contents of Al-4wt%Mg-0.9wt%Si system alloy increased from 0.1 wt% to 0.4 wt% and from 0.3 wt% to 0.5 wt% respectively, the fluidity of the alloy decreased by 26% and 33%. When Fe content of the alloy increased from 0.1 wt% to 0.4 wt%, 23% decrease of macro shrinkage and 19% increase of micro shrinkage appeared. Similarly, Mn content of the alloy increased from 0.3 wt% to 0.5 wt%, 11% decrease of macro shrinkage and 14% increase of micro shrinkage appeared. Judging from the castability of the alloy, Al-4wt%Mg-0.9wt%Si alloy with low content of Fe and Mn, 0.1 wt% Fe and 0.3 wt% Mn, is recommendable.

• Journal of the Korean Society for Heat Treatment
• /
• v.4 no.4
• /
• pp.44-52
• /
• 1991

The effect of deformation temperature and manganes contents on the tensile properties of duplex stainless steels with the structure of both ferrite and austenite were investigate. For this investigation, Fe-19% Cr-5% Ni-4~8% Mn alloys were prepared. The result obtained from this experiment are summerized as follows. With decreasing deformation temperature, tensile strengths of duplex stainless steel increased. Elongation showd to be increased and then decreased after representing the highest value at specific temperature. Tensile properties of duplex stainless steel were controlled by TRIP behavior in this experimental range of austenite contents. Tensile strengths decreased with increasing Mn contents. With increasing Mn contents, elongation decreased in the high temperature region, but increased in the low temperature region. The peak temperature representing the maximum elongation were changed to low temperature and the width of peak appeared to be broaden with increasing Mn contents.

• Journal of The Korean Society of Grassland and Forage Science
• /
• v.24 no.4
• /
• pp.271-280
• /
• 2004

This pot experiment was conducted to investigate the effects of systematic variation appling of Fe, Mn, Cu, and Zn on forage performance of orchardgrass and white clover. The treatments of systematic variation were 0/100, 25/75, 50/50, 75/25, and $100/0\%$ in the Fe/Cu(trial-1), Mn/Zn(trial-2), and Fe+Cu/Mn+Zn(trial-3), respectively. The treatments of Fe/Mn/Cu/Zn(trial-4) were $70\%$ in main-element and $10\% in other 3 sub-elements, respectively. 1. Compared with orchadgrass, white clover showed relatively consistent differences in the content of micronutrients as influenced by treatments of the systematic variation. The contents of Mn and Cu in the forages were significantly influenced by the application rates of Mn and Cu, respectively. The contents of Fe and Zn in the forages, however, were not significantly different among these treatments. 2. Compared with orchardgrass in the Fe/cu trial, white clover had not only the low content of Cu but also the Cu content and yield of white clover were greatly decreased by the low rate of application of Cu. In the Mn/Zn trial, the $0/100\%$ resulted in the severe decrease of Mn-content in both forages. The low content of Mn in white clover tended to be negatively correlated to the Mn-chlorosis, inferior growth and flowering, and low yield. 3. In the Fe+Cu/Mn+Zn trial, the application with $0/100\%$ and $0/100\%$ resulted in the relatively great decrease of Cu and Mn contents, respectively. These traits in white clover tended to be negatively correlated to the inferior growth and flowering, and low yield 4. In the Fe/Mn/Cu/Zn trial, the content of every main-elements in the forages were increased especially in Mn. In addition, the contents of sub-elements were likely to be somewhat negatively influenced by the treatment of main-element respectively.

• Korean Journal of Plant Resources
• /
• v.20 no.1
• /
• pp.12-21
• /
• 2007

Ginsengs (1,2 3 years) from the Keumsan are analysed for the inorganic compounds and compared with the their soils from the granite, phyllite and shale areas. In the soils, the granite areas show high $Al_2O_3\;and\;Na_2O$ contents while the phyllite areas have high $Fe_2O_3,\;MnO\;and\;MgO$ contents. Positive correlations are shown in the $Al_2O_3-K_2O\;and\;Fe_2O_3-MgO$ pairs while negative correlations are shown in the $SiO_2-CaO$ pair. In the ginsengs, the shale areas are high in the most of the elements, but low in the granite areas. Compared with same soils of different ages, Al, Na and Ti contents of the ginsengs are high in the all areas. The shale areas are mainly high in the upper parts while the granite areas are mainly high in the root parts. Regardless of the localities, Fe, Mn and Ca contents are high in the upper parts while Ti contents are high in the root parts with differences of several times. Relative ratios between field soils and ginsengs (field soil/ginseng) suggest that the ginsengs show high Ca contents with differences of several ten times whereas the soils have high Na, Fe, Ti and Al contents with differences of several times. Regardless of the localities, the ratios of the Al, Mn and Na are high in the 2 year relative to the 3 year. Overall ratios between field soils and ginsengs are mainly big in the 2 year area relative to the 3 year area. It suggests that contents of the 3 year ginsengs are more similar to those of their soils relative to the 2 year and the ginsengs may absorpt eligible element contents with increasing ages.

• Journal of Korea Foundry Society
• /
• v.33 no.6
• /
• pp.233-241
• /
• 2013

Effect of Fe and Mn contents on the castability of Al-9wt%Si-xMg-yFe-zMn alloy has been studied. The alloy was composed of ${\alpha}$-Al phase, Al+eutectic Si phase, ${\beta}$-Al5FeSi compound and chinese script ${\alpha}$-$Al_{15}(Mn,Fe)_3Si_2$ compound. ${\beta}$-$Al_5FeSi$ and ${\alpha}$-$Al_{15}(Mn,Fe)_3Si_2$ compounds assumed to effect the fluidity and shrinkage behaviors of the alloy during solidification due to the crystallization of ${\alpha}$-$Al_{15}(Fe,Mn)_3Si_2$ and ${\beta}$-$Al_5FeSi$ compounds above eutectic temperature. As Fe and Mn contents of Al-9wt%Si-0.3wt%Mg system alloy increased from 0.15wt% to 0.6wt% and from 0.3wt% to 0.7wt%, fluidity of the alloy decreased by 5.7% and 3.3%, respectively. And as Mg content of Al-9wt%Si-0.45wt%Fe-0.5wt%Mn system alloy increased from 0.3wt% to 0.4wt%, fluidity of the alloy decreased by 8.6%. When Fe content of the alloy increased from 0.15wt% to 0.6wt%, macro shrinkage ratio decreased from 6.1% to 4.1%, and micro shrinkage ratio increased from 0.04% to 0.24%. Similarly, Mn content of the alloy increased from 0.3wt% to 0.7wt%, macro shrinkage ratio decreased from 6.0% to 4.5% and micro shrinkage ratio increased from 0.12% to 0.18%. Judging from the castability of the alloy, Al-9wt%Si-0.3wt%Mg alloy with low content of Fe and Mn, 0.1wt% Fe and 0.3wt% Mn, is recommendable.

• Journal of Korea Foundry Society
• /
• v.31 no.1
• /
• pp.18-25
• /
• 2011

Effect of Fe and Mn contents on the tensile properties has been studied in Al-9wt%Si-0.3wt%Mg alloy. As Fe content of Al-9wt%Si-0.3wt%Mg-0.5wt%Mn alloy increased from 0.15wt% to 0.45wt%, tensile strength of as-cast alloy decreased from 192 MPa to 174 MPa, and elongation of the alloy also decreased from 4.8% to 4.2%. Decrease of these properties can be explained as the formation of plate shape, ${\beta}-Al_5FeSi$ phase with high Fe/Mn ratio of the alloy. However when Mn content of Al-9wt%Si-0.3wt%Mg-0.45wt%Fe alloy increased from 0.3wt% to 0.5wt%, tensile strength of T6 aged alloy increased from 265 MPa to 275 MPa, and elongation of the alloy increased from 2.3% to 3.6%. These improvements attribute to chinese script, ${\alpha}-Al_{15}(Mn,Fe)_3Si_2$ phase shape-modified from ${\beta}-Al_5FeSi$ phase with low Fe/Mn ratio of the alloy.

• Journal of Korea Foundry Society
• /
• v.29 no.6
• /
• pp.270-276
• /
• 2009

After casting button-type small ingots of ternary Fe-Mn-S alloys which had three different Mn/S ratios (1, 5 and 70) in a vacuum arc furnace, the effect of the ratio on the sulfide formation was investigated. In case of the Mn/S ratio of 1, if alloy composition was located in an iron-rich corner on a Fe-Mn-S ternary phase diagram, only duplex MnS-FeS sulfide films were observed in the grain boundary. If the alloy composition was located in the miscibility gap area of the phase diagram, primary globular dendritic sulfides and dendritic sulfide slags were generated within the grain and tubular monotectic sulfides were also detected in the grain boundary. When the Mn/S ratio was 5, if the alloy composition was in the iron-rich corner, only bead-like sulfides were generated. On the other hand, if the composition was in the miscibility gap area, globular dendritic sulfides and dendritic sulfide slags were generated in the form of primary sulfide inclusions and rod-like eutectic sulfides were observed in the grain boundary. Especially, if the contents of Mn and S increased more in the miscibility gap area of the phase diagram, primary globular sulfides containing iron intrusions were observed. In case of Mn/S ratio of 70, if the contents of Mn and S was decreased in the Fe corner of the phase diagram, only bead-like sulfides were observed in the grain boundary. Despite the composition was outside the miscibility gap area of the phase diagram, if the contents of Mn and S increased, clusters of fine sulfide particles as well as fine spherical primary monophase sulfides were observed in the grain boundary.